CN1115238C - Technology for making reinforced basic plastic meterial with stereoscopic decorative pattern - Google Patents
Technology for making reinforced basic plastic meterial with stereoscopic decorative pattern Download PDFInfo
- Publication number
- CN1115238C CN1115238C CN99109238A CN99109238A CN1115238C CN 1115238 C CN1115238 C CN 1115238C CN 99109238 A CN99109238 A CN 99109238A CN 99109238 A CN99109238 A CN 99109238A CN 1115238 C CN1115238 C CN 1115238C
- Authority
- CN
- China
- Prior art keywords
- plastic layer
- layer
- cloth
- embossing
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a method for manufacturing reinforced plastic base material with three-dimensional decoration, which comprises: step one, adhesive application: a cloth layer is coated with adhesive; step two, heating: the adhesive and a plastic layer are heated so as to raise a temperature and soften the plastic layer; step three, pressure and rolling: after the adhesive on the cloth layer and the plastic layer reach a predetermined temperature, the plastic layer is attached to the cloth layer, and is flattened by pressure at the same time, and the plastic layer and the cloth layer are tightly attached and bound to form a combination; step four, embossing and cooling at the same time: before the plastic layer of the combination is not cooled, an embossing tool of which the temperature is maintained at the temperature lower than the temperature of the plastic layer at the time is used for embossing a three-dimensional thread on the surface of the plastic layer.
Description
The present invention is relevant with the manufacture method of plastic basis material, particularly about a kind of reinforced plastics production method for base material with three-dimensional decoration.
Press, a kind of in order to be processed into handbag or in order to reinforced plastics base material as the luggage case liner, one plastic layer and a layer of cloth are fitted tightly, and waterproof and the air impermeability of using this plastic layer can be used as the top layer, and this layer of cloth then can be strengthened the intensity of this base material.
The manufacturing step of above-mentioned reinforced plastics base material is as follows:
One, gluing: coating one deck glue work agent on this layer of cloth;
Two, heat: simultaneously heating is toasted in this glue work agent and this plastic layer, show the glue work degree of agent in order to increase this glue, and make this plastic layer softening;
Three, fit to flatten: after the work agent of the glue on this layer of cloth and this plastic layer reach a predetermined temperature, this plastic layer is fitted on this layer of cloth, flattened simultaneously, make this plastic layer and this layer of cloth fit tightly bonding, form a combination;
Four, cooling: the combination after the pressing is cooled off, just can get above-mentioned reinforced plastics base material.
Because the top layer of above-mentioned base material is a plastic layer, so its texture is preferable; And in order to beautify the top layer of this base material, general dealer prints on the surface of this plastic layer in the mode of printing to establish predetermined decoration or style, pattern, trade mark etc.Yet this kind is only to be the plane lines with decoration or the pattern that mode of printing was produced, though this base material top layer is had certain beautification function, for the lifting aspect of its texture, effect is still not good.
In view of this main purpose of the present invention is to provide a kind of reinforced plastics production method for base material with three-dimensional decoration, is one can produce that the top layer has three-dimensional decoration and base material with preferable texture.
In order to the goal of the invention of taking off before reaching, manufacturing step of the present invention is as follows:
One, gluing: coating one deck glue work agent on this layer of cloth;
Two, heat: simultaneously heating is toasted in this glue work agent and this plastic layer, show the glue work degree of agent in order to increase this glue, and make this plastic layer softening;
Three, fit to flatten: after the work agent of the glue on this layer of cloth and this plastic layer reach a predetermined temperature, be about to this plastic layer and fit on this layer of cloth, flattened simultaneously, make this plastic layer and this layer of cloth fit tightly bonding, form a combination;
Four, embossing cools off simultaneously: before the plastic layer of this combination is still uncolled, four, embossing cools off simultaneously: before the plastic layer of combination is still uncolled,, importing is lower than plastic layer temperature and surperficial embossing wheel at that time because of having the cooling water of circulation to maintain with an inside with predetermined lines, on the surface of plastic layer, press and set out solid grain, and, make the plastic layer surface reach the effect of cooling and setting by the low temperature that embossing is taken turns;
By this, just can get a reinforced plastics base material with three-dimensional decoration.
In order to allow your juror can more clearly understand the present invention, cooperate following diagram to be described in more detail in now after; Wherein:
Fig. 1 is a process block diagram of the present invention;
Fig. 2 is the schematic diagram of a preferred embodiment of the present invention.
See also Fig. 1, step of the present invention is one in regular turn, gluing; Two, heat; Three, pressing; Four, embossing cools off simultaneously.
See also Fig. 2, the implementation with above-mentioned steps is as follows now:
At first, furl on the wheel 30, this layer of cloth 11 and this plastic layer 21 are furled with identical speed connecing together to establish to one from layer of cloth volume 10 and one plastic layer volume 20 layer of cloths of pulling out 11 and plastic layer 21 respectively; And be drawn out to respectively in the process that is furled at this layer of cloth 11 and plastic layer 21, be must be via the following step:
One, gluing: draw this layer of cloth 11 glue coating wheel 40 of passing through, make this glue coating wheel 40 can be coated with the agent of one deck glue work equably to the one side of this layer of cloth 11.
Two, heat: draw this layer of cloth 11 of gluing and this plastic layer 21 one group of heating group 50 of forming by most heating tubes 51 of passing through respectively, these heating tubes 51 can be spent the glue work agent and this plastic layer 21 difference heat temperature raising to 120 degree and 180 that are coated with on this layer of cloth 11, use the sticking outstanding degree that increases this glue work agent, and make this plastic layer 21 softening, in order to fitting on any surface.
Three, fit to flatten: this has been heated to predetermined temperature plastic layer 21 and this layer of cloth 11 imports in a pair of running roller 60 together, make this to running roller 60 can with this layer of cloth 11 and this plastic layer 21 be fitted and roll-in is smooth, and make this plastic layer 21 fit tightly bonding with this city's layer 11, form a combination A.
Four, embossing cools off simultaneously: this combination A is led soon through embossing wheel 70, make this embossing wheel 70 extrude predetermined solid grain in this surface before the still uncolled sclerosis in plastic layer 21 surfaces of this combination A; And the inside of this embossing wheel 70 imports the cool water that circulation is arranged, use plastic layer 21 temperature at that time that the temperature of keeping this embossing wheel 70 is lower than this combination A, and cool off this plastic layer 21 surfaces when can coexist embossing, make the solid grain setting on these plastic layer 21 surfaces.
By this, can produce just that the top layer has three-dimensional decoration and the reinforced plastics base material 1 that can promote whole texture.
Again, because above-mentioned manufacture method is can a link-up operation, and does not also need additionally to increase too much equipment,, cheap for manufacturing cost so the speed of production of method is fast.
According to the above, the goal of the invention that the present invention takes off before can reaching really.
Claims (1)
1. have the reinforced plastics production method for base material of three-dimensional decoration, its step is as follows:
One, gluing: coating one deck glue work agent on layer of cloth;
Two, heat:,, and make plastic layer softening in order to the glue work degree of increase glue work agent simultaneously to glue work agent and plastic layer heat temperature raising;
Three, press bonding roller is flat: after the work agent of the glue on the layer of cloth and plastic layer reach a predetermined temperature, be about to plastic layer and fit on the layer of cloth, flattened simultaneously, make plastic layer and layer of cloth fit tightly bonding, form a combination;
It is characterized in that:
Four, embossing cools off simultaneously: before the plastic layer of combination is still uncolled,, importing is lower than plastic layer temperature and surperficial embossing wheel at that time because of having the cooling water of circulation to maintain with an inside with predetermined lines, on the surface of plastic layer, press and set out solid grain, and, make the plastic layer surface reach the effect of cooling and setting by the low temperature that embossing is taken turns;
By this, just can get the reinforced plastics base material of the three-dimensional decoration of a tool.