CN105778672A - Superfast-drying, anti-adhesion, and anticorrosion paint for casting pipes - Google Patents
Superfast-drying, anti-adhesion, and anticorrosion paint for casting pipes Download PDFInfo
- Publication number
- CN105778672A CN105778672A CN201410802822.1A CN201410802822A CN105778672A CN 105778672 A CN105778672 A CN 105778672A CN 201410802822 A CN201410802822 A CN 201410802822A CN 105778672 A CN105778672 A CN 105778672A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- liquid
- acrylic resin
- thermoplastic acrylic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to the field of paint manufacturing, and especially relates to a superfast-drying, anti-adhesion, and anticorrosion paint for casting pipes. The paint is characterized by comprising thermoplastic acrylic resin liquid, petroleum resin liquid, modified polyurethane resin, dispersant, bentonite, iron black, barite powder, xylene, cobalt naphthenate, chlorinated paraffin, and levelling agent. Compared with the conventional paint, the provided paint has the characteristics that the paint can be dried at a room temperature, and the drying speed is quick. The energy is saved and the consumption is reduced. The requirements of fast coating can be met. The paint can be sprayed on products at a room temperature, after 30 minutes the products can be piled together, and the products will not be adhered to each other. The processed products are suitable for streamline operation, the products are knocked with each other, the coating will not be damaged, and thus the problems of coating aging and cast pipe rusting due to outdoor storage and ocean transportation are solved.
Description
Technical field
The invention belongs to coating and manufacture field, particularly relate to a kind of ultrafast dry tissue adhesion cast tube anticorrosive paint.
Background technology
The lower water such as building, house and industrial drain pipe commonly use irony cast tube both at home and abroad at present, and its application, over to all parts of the country, is directly connected to commercial production and civilian installation.Due to exposed cast tube deposit in the open with transportation in will soon get rusty, corrode, therefore after cast tube produces, the method for commonly used sprayed coating is protected, it is prevented that cast tube gets rusty, corrode, the service life of prolongation iron and steel cast tube.
Domestic usual employing streamline application iron and steel cast tube, major part method be according to by preheating of heating after cast tube pretreatment, anticorrosion with painting coating, drying, cooling, piling, packaging program carry out.Commonly used anticorrosive paint easily occur after streamline application paint film crisp, weak to colliding with, then through paint film in certain time outdoor placement, sea transport process, the problems such as aging, cast tube gets rusty occur.
Summary of the invention
The present invention is directed to above-mentioned technical problem, it is provided that a kind of normal temperature drying, mutually collide with the ultrafast dry tissue adhesion cast tube anticorrosive paint that paint film does not fall off, anticorrosion has excellent weather resistance.
The technical solution adopted in the present invention is: a kind of ultrafast dry tissue adhesion cast tube anticorrosive paint, it is characterized in that, including thermoplastic acrylic resin liquid, Petropols liquid, modified polyurethane resin, dispersant, bentonite, ferrum is black, blanc fixe, dimethylbenzene, cobalt naphthenate, chlorinated paraffin, levelling agent, each component consists of according to mass fraction: thermoplastic acrylic resin liquid 22-32 part of 50%, Petropols liquid 5-17 part of 60%, modified polyurethane resin 14-24 part of 52%, dispersant 1-3 part, bentonite 0.1-2 part, iron black 11-21 part, blanc fixe 10-20 part, dimethylbenzene 1-7 part, tenor is cobalt naphthenate 0.01-0.2 part of 4%, chlorinated paraffin 0.5-2 part, levelling agent 0.1-2 part.
Each component consists of according to more high quality number: the thermoplastic acrylic resin liquid of 50% 27 parts, 60% Petropols liquid 12 parts, 52% modified polyurethane resin 19 parts, dispersant 2.2 parts, bentonite 1 part, iron black 16.9 parts, blanc fixe 15.5 parts, dimethylbenzene 3.8 parts, tenor be 4% cobalt naphthenate 0.1 part, chlorinated paraffin 1.5 parts, levelling agent 1 part.
The model of described thermoplastic acrylic resin liquid is A-01, the model of described Petropols liquid is C-9, the model of described modified polyurethane resin is CZ-7, the model of described dispersant is ZR-4010, described bentonitic model is BP-183B, described iron oxide black is 325 orders, and the model of described levelling agent is BYK-300.
The processing technique of a kind of ultrafast dry tissue adhesion cast tube anticorrosive paint, it is characterised in that comprise the steps:
A. 50 parts of dimethylbenzene are added in material-compound tanks, start stirring, be slowly added into 50 parts of thermoplastic acrylic resin, until thermoplastic acrylic resin is completely dissolved, stops stirring, filter and package, make 50% thermoplastic acrylic resin liquid standby；
B. 40 parts of toluene are added in material-compound tanks, start stirring, be slowly added into 60 parts of Petropols, until Petropols are completely dissolved, stop stirring, filter and package, make 60% Petropols liquid standby；
C. by the thermoplastic acrylic resin liquid of the 50% of formula ratio, 60% Petropols liquid, 52% modified polyurethane resin, dispersant weigh and gradually add in material-compound tank, start stirring, add bentonite, iron oxide black, blanc fixe, stir into mill base；
E. sand mill in the mill base prepared is ground, grind at present when fineness reaches 30 microns, become to disperse qualified mill base；
F. qualified for dispersion mill base is put into and joins paint can, start stirring, gradually add the chlorinated paraffin of formula ratio, tenor be 4% cobalt naphthenate, levelling agent and dimethylbenzene, filter and package after stirring.
The invention have the benefit that
1, relative to the traditional coating application used there is normal temperature drying, the ultrafast feature such as dry, the advantage such as energy-saving and cost-reducing, meet the requirement of ready coating technique；
2, after product can spray 30 minutes at normal temperatures, piling is packed, and is suitable for assembly line work, and piling adhesion, the paint film that mutually collides with does not fall off；
3, product does not contain the harmful substances such as heavy metal, and environment protecting is good；
4, the acid and alkali resistance excellent performance of product, salt fog resistance, weatherability are prominent, product has reached the anti-corrosive properties of excellence and the unification of weatherability, solves pipeline open-air storage, marine transportation and the normal cast tube corrosion used and weather-proof problem, the service life extending supervisor of high degree.
Detailed description of the invention
Embodiment 1
The processing technique of a kind of ultrafast dry tissue adhesion cast tube anticorrosive paint, it is characterised in that comprise the steps:
A. 50 parts of dimethylbenzene are added in material-compound tanks, start stirring, be slowly added into 50 parts of thermoplastic acrylic resin A-01B, until thermoplastic acrylic resin A-01B is completely dissolved, stops stirring, filter and package, make 50% thermoplastic acrylic resin liquid A-01B standby；
B. 40 parts of toluene are added in material-compound tanks, start stirring, be slowly added into 60 parts of Petropols C-9, until Petropols C-9 is completely dissolved, stops stirring, filter and package, make 60% Petropols liquid C-9 standby；
C. by thermoplastic acrylic resin liquid A-01B30 part of 50%, 60% Petropols liquid C-914 part, 52% modified polyurethane resin CZ-721 part, dispersant ZR-40101 part weighs and gradually adds in material-compound tank, start stirring, add bentonite BP-183B0.5 part, 13 parts, the iron oxide black of 325 orders, blanc fixe 10 parts, stir into mill base；
E. sand mill in the mill base prepared is ground, grind at present when fineness reaches 30 microns, become to disperse qualified mill base；
F. qualified for dispersion mill base is put into and joins paint can, start stirring, gradually add the chlorinated paraffin 1.4 parts of formula ratio, tenor be 4% cobalt naphthenate 0.1 part, levelling agent BYK-3002 part and dimethylbenzene 7 parts, filter and package after stirring.
Embodiment 2
The processing technique of a kind of ultrafast dry tissue adhesion cast tube anticorrosive paint, it is characterised in that comprise the steps:
A. 50 parts of dimethylbenzene are added in material-compound tanks, start stirring, be slowly added into 50 parts of thermoplastic acrylic resin A-01B, until thermoplastic acrylic resin A-01B is completely dissolved, stops stirring, filter and package, make 50% thermoplastic acrylic resin liquid A-01B standby；
B. 40 parts of toluene are added in material-compound tanks, start stirring, be slowly added into 60 parts of Petropols C-9, until Petropols C-9 is completely dissolved, stops stirring, filter and package, make 60% Petropols liquid C-9 standby；
C. by thermoplastic acrylic resin liquid A-01B27 part of 50%, 60% Petropols liquid C-912 part, 52% modified polyurethane resin CZ-719 part, dispersant ZR-40102.2 part weighs and gradually adds in material-compound tank, start stirring, add bentonite BP-183B1 part, 16.9 parts, the iron oxide black of 325 orders, blanc fixe 15.5 parts, stir into mill base；
E. sand mill in the mill base prepared is ground, grind at present when fineness reaches 30 microns, become to disperse qualified mill base；
F. qualified for dispersion mill base is put into and joins paint can, start stirring, gradually add the chlorinated paraffin 1.5 parts of formula ratio, tenor be 4% cobalt naphthenate 0.1 part, levelling agent BYK-3001 part and dimethylbenzene 3.8 parts, filter and package after stirring.
Embodiment 3
The processing technique of a kind of ultrafast dry tissue adhesion cast tube anticorrosive paint, it is characterised in that comprise the steps:
A. 50 parts of dimethylbenzene are added in material-compound tanks, start stirring, be slowly added into 50 parts of thermoplastic acrylic resin A-01B, until thermoplastic acrylic resin A-01B is completely dissolved, stops stirring, filter and package, make 50% thermoplastic acrylic resin liquid A-01B standby；
B. 40 parts of toluene are added in material-compound tanks, start stirring, be slowly added into 60 parts of Petropols C-9, until Petropols C-9 is completely dissolved, stops stirring, filter and package, make 60% Petropols liquid C-9 standby；
C. by thermoplastic acrylic resin liquid A-01B22 part of 50%, 60% Petropols liquid C-916 part, 52% modified polyurethane resin CZ-717 part, dispersant ZR-40103 part weighs and gradually adds in material-compound tank, start stirring, add bentonite BP-183B2 part, 13 parts, the iron oxide black of 325 orders, blanc fixe 18 parts, stir into mill base；
E. sand mill in the mill base prepared is ground, grind at present when fineness reaches 30 microns, become to disperse qualified mill base；
F. qualified for dispersion mill base is put into and joins paint can, start stirring, gradually add the chlorinated paraffin 1.8 parts of formula ratio, tenor be 4% cobalt naphthenate 0.2 part, levelling agent BYK-3002 part and dimethylbenzene 5 parts, filter and package after stirring.
Products application of the present invention is the anticorrosion of lower water (on the ground) and industrial drain pipe outer wall in building, house etc., extends the service life of cast tube；
Product of the present invention is by the interspersed use of modified polyurethane resin, thermoplastic acrylic resin and Petropols, prominent quick-drying, anticorrosion and weather-proof effect, adapt to normal temperature quick-drying streamline coating process requirement, by using iron oxide black, blanc fixe to strengthen anti-corrosive properties and the hardness of paint film of product, used additives is made to realize the effect of tissue adhesion；
This patent passes through the comprehensive study of resin, color stuffing, auxiliary agent, solvent etc. and reasonably combined, product is made to solidify at normal temperatures, under quick-drying condition, after streamline application, during cast tube piling, paint film does not produce adhesion, mutually the collision adeciduate characteristic of paint film, and cast tube outdoor storage or marine transportation do not produce corrosion and film efflorescence.
The iron and steel cast tube coating the present invention is tested, and concrete test result is as follows:
Above 3 embodiments of the present invention are described in detail, but content has been only presently preferred embodiments of the present invention, it is impossible to be considered the practical range for limiting the present invention.All equalizations made according to the present patent application scope change and improvement etc., all should still belong within the patent covering scope of the present invention.
Claims (4)
1. a ultrafast dry tissue adhesion cast tube anticorrosive paint, it is characterized in that, including thermoplastic acrylic resin liquid, Petropols liquid, modified polyurethane resin, dispersant, bentonite, ferrum is black, blanc fixe, dimethylbenzene, cobalt naphthenate, chlorinated paraffin, levelling agent, each component consists of according to mass fraction: thermoplastic acrylic resin liquid 22-32 part of 50%, Petropols liquid 5-17 part of 60%, modified polyurethane resin 14-24 part of 52%, dispersant 1-3 part, bentonite 0.1-2 part, iron black 11-21 part, blanc fixe 10-20 part, dimethylbenzene 1-7 part, tenor is cobalt naphthenate 0.01-0.2 part of 4%, chlorinated paraffin 0.5-2 part, levelling agent 0.1-2 part.
2. the ultrafast dry tissue adhesion cast tube anticorrosive paint of one according to claim 1, it is characterized in that, each component consists of according to more high quality number: the thermoplastic acrylic resin liquid of 50% 27 parts, 60% Petropols liquid 12 parts, 52% modified polyurethane resin 19 parts, dispersant 2.2 parts, bentonite 1 part, iron black 16.9 parts, blanc fixe 15.5 parts, dimethylbenzene 3.8 parts, tenor be 4% cobalt naphthenate 0.1 part, chlorinated paraffin 1.5 parts, levelling agent 1 part.
3. the ultrafast dry tissue adhesion cast tube anticorrosive paint of one according to claim 1, it is characterized in that, the model of described thermoplastic acrylic resin liquid is A-01, the model of described Petropols liquid is C-9, the model of described modified polyurethane resin is CZ-7, and the model of described dispersant is ZR-4010, and described bentonitic model is BP-183B, described iron oxide black is 325 orders, and the model of described levelling agent is BYK-300.
4. the processing technique of a ultrafast dry tissue adhesion cast tube anticorrosive paint, it is characterised in that comprise the steps:
A. 50 parts of dimethylbenzene are added in material-compound tanks, start stirring, be slowly added into 50 parts of thermoplastic acrylic resin, until thermoplastic acrylic resin is completely dissolved, stops stirring, filter and package, make 50% thermoplastic acrylic resin liquid standby；
B. 40 parts of toluene are added in material-compound tanks, start stirring, be slowly added into 60 parts of Petropols, until Petropols are completely dissolved, stop stirring, filter and package, make 60% Petropols liquid standby；
C. by the thermoplastic acrylic resin liquid of the 50% of formula ratio, 60% Petropols liquid, 52% modified polyurethane resin, dispersant weigh and gradually add in material-compound tank, start stirring, add bentonite, iron oxide black, blanc fixe, stir into mill base；
E. sand mill in the mill base prepared is ground, grind at present when fineness reaches 30 microns, become to disperse qualified mill base；
F. qualified for dispersion mill base is put into and joins paint can, start stirring, gradually add the chlorinated paraffin of formula ratio, tenor be 4% cobalt naphthenate, levelling agent and dimethylbenzene, filter and package after stirring.