CN105128478A - Low-temperature heat-sealing package film and preparation method thereof - Google Patents
Low-temperature heat-sealing package film and preparation method thereof Download PDFInfo
- Publication number
- CN105128478A CN105128478A CN201510433060.7A CN201510433060A CN105128478A CN 105128478 A CN105128478 A CN 105128478A CN 201510433060 A CN201510433060 A CN 201510433060A CN 105128478 A CN105128478 A CN 105128478A
- Authority
- CN
- China
- Prior art keywords
- layer
- temperature
- sealing
- low
- heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a low-temperature heat-sealing package film and a preparation method thereof. The heat-sealing package film includes an A layer, a B layer and a C layer, wherein the A layer is a low-temperature heat-sealing layer, the B layer is a core layer and the C layer is a printing layer. The A layer includes 40-45% of a polyester aluminum-plated film, 47-50% of polypropylene resin and 3-5% of a VM3980 thermoplastic elastomer; the B layer includes 97-99% of polypropylene and 1-3% of an anti-static smooth master batch; and the C layer includes 96-98% of polypropylene and 2-4% of an anti-adhesion agent. The preparation method includes the following steps: material blending, melt extrusion, sheet casting, longitudinal stretch, transversal stretch, drawing and trimming, rolling-up, cutting and production of the finish product. The package film reduces solvent pollution due to thin film printing and pre-coating treatment, is reduced in processing cost, and is reduced in cost and is environment-friendly. The method reduces the initial heat-sealing temperature of the heat-sealing package film and increases sealing strength of the package film product.
Description
Technical field
The present invention relates to film and preparation method thereof, be specifically related to a kind of low-temperature heat-sealing packaging film and preparation method thereof.
Background technology
Along with the environmental consciousness of domestic press strengthens day by day, development and application nuisanceless, free of contamination " green " materials and process is imperative.Heat-sealing bag is widely used in the fields such as daily chemical products packaging, food and medicine packaging.Because when product is filled, leaking the most easily appears in packaging bag heat-sealing, and the damage of packaging bag also occurs in heat seal lands when reality uses, and therefore good heat-sealing film effectively can improve the barrier property of packaging film entirety.At present, domestic packaging film sealing tech generally adopts gluing sealing mode, there is following shortcoming: 1, add user's manufacturing procedure; 2, adding users processing cost; 3, environmental protection is unfavorable for; 4, heat-sealing temperature is high, and sealing intensity is low.
Summary of the invention
The object of the present invention is to provide a kind of low-temperature heat-sealing packaging film and preparation method thereof, directly reach packaging film sealing by the mode of heating, be conducive to environmental protection; By reducing heat-sealing temperature, improving sealing intensity, thus improving packaging film product quality.
The object of the invention is to be achieved by following component and using method.
A kind of low-temperature heat-sealing packaging film, be made up of A layer, B layer, C layer, it is characterized in that: described A layer is Low Temperature Thermal sealing, B layer is sandwich layer, and C layer is printed layers; Wherein,
A layer: the polyester of 40-45% is aluminized, the acrylic resin of 47-50%, the VM3980 thermoplastic elastomer of 3-5%;
B layer: 97%-99% polypropylene, 1%-3% antistatic smooth master batch;
C layer: the anti-anti-adhesive agent of 96%-98% polypropylene, 2%-4%.
The each layer thickness profile of described A, B, C: Low Temperature Thermal sealing A is 0.8-5 microns, and sandwich layer B is 7-40 microns, and printed layers C is 1-3 microns.
Described low-temperature heat-sealing packaging film thickness is 10-45 microns.
The preparation method of described low-temperature heat-sealing packaging film, comprise the following steps: comprise the following steps: batch mixing, melt extrude, slab, longitudinal stretching, cross directional stretch, traction trimming, rolling, cut, finished product, it is characterized in that: described in melt extrude middle extrusion temperature and be 190-260 DEG C, die head temperature is 230-255 DEG C; In described slab process, chilling roller and tank temperature are 25-50 DEG C; In described longitudinal stretching process, longitudinal preheat temperature is 116-145 DEG C, and longitudinal drawing temperature is 120-135 DEG C, and longitudinal setting temperature is 128-145 DEG C, and longitudinal stretching ratio is 4-6 times; In described cross directional stretch process, horizontal preheat temperature is 160-175 DEG C, and transverse drawing temperature is 150-168 DEG C, and horizontal setting temperature is 160-170 DEG C, and cross directional stretch ratio is 7-10 times.
Beneficial effect of the present invention:
1, by adding VM3980 thermoplastic elastomer, the initial heat-sealing temperature of heat-sealing material is reduced;
2, Low Temperature Thermal sealer of the present invention is at 85 degree of-95 degree and heat sealable;
3, during sealing, heating-up temperature reduces, and is conducive to energy-conservation;
4, because seal under low-temperature condition, Low Temperature Thermal sealer because of heat distortion, can not improve Low Temperature Thermal sealer product quality.
Detailed description of the invention
Do to illustrate into a line to low-temperature heat-sealing packaging film of the present invention and preparation method thereof below in conjunction with specific embodiment:
Embodiment 1: three layer of die head, for 20 microns of Low Temperature Thermal sealers
The polyester of Low Temperature Thermal sealing A:40% is aluminized, the acrylic resin of 47%, the VM3980 thermoplastic elastomer of 3%;
Sandwich layer B:97% polypropylene, 1% antistatic smooth master batch;
Printed layers C:96% polypropylene, 2% anti-anti-adhesive agent.
Each layer thickness profile: Low Temperature Thermal sealing A is 3 microns, sandwich layer B is 15 microns, and printed layers C is 2 microns.
Above-mentioned raw materials by batch mixing, melt extrude, slab, longitudinal stretching, cross directional stretch, traction trimming, rolling, then finished product is cut, extrude middle extrusion temperature and be 190-260 DEG C, die head temperature is 248 DEG C, and in slab process, chilling roller and tank temperature are 32 DEG C; Longitudinal preheat temperature is 116-142 DEG C, and longitudinal drawing temperature is 126-135 DEG C, and longitudinal setting temperature is 140 DEG C, and longitudinal stretching ratio is 4.9 times; In described cross directional stretch process, horizontal preheat temperature is 166-174 DEG C, and transverse drawing temperature is 152-155 DEG C, and horizontal setting temperature is 165 DEG C, and cross directional stretch ratio is 9 times.
Embodiment 2:
The polyester of Low Temperature Thermal sealing A:45% is aluminized, the acrylic resin of 50%, the VM3980 thermoplastic elastomer of 5%;
Sandwich layer B:99% polypropylene, 3% antistatic smooth master batch;
Printed layers C layer: 98% polypropylene, 4% anti-anti-adhesive agent.
Each layer thickness profile: Low Temperature Thermal sealing A is 3 microns, sandwich layer B is 15 microns, and printed layers C is 2 microns.
Above-mentioned raw materials by batch mixing, melt extrude, slab, longitudinal stretching, cross directional stretch, traction trimming, rolling, then finished product is cut, extrude middle extrusion temperature and be 190-260 DEG C, die head temperature is 248 DEG C, and in slab process, chilling roller and tank temperature are 32 DEG C; Longitudinal preheat temperature is 116-142 DEG C, and longitudinal drawing temperature is 126-135 DEG C, and longitudinal setting temperature is 140 DEG C, and longitudinal stretching ratio is 4.9 times; In described cross directional stretch process, horizontal preheat temperature is 166-174 DEG C, and transverse drawing temperature is 152-155 DEG C, and horizontal setting temperature is 165 DEG C, and cross directional stretch ratio is 9 times.
In the present embodiment, described antitack agent is synthetic silica or stearic amide; Described antistatic additive is fatty acid ester, ethoxylated amine or diethanol amine; Described slipping agent main component is erucyl amide, fatty acid amide and oleamide.
The above is only preferred embodiment of the present invention, not does any pro forma restriction to the present invention; Any those of ordinary skill in the art, do not departing under technical solution of the present invention ambit, the Method and Technology content of above-mentioned prompting all can be utilized to make many possible variations and modification to technical solution of the present invention, or be revised as the Equivalent embodiments of equivalent variations.Therefore, every content not departing from technical solution of the present invention, according to technical spirit of the present invention to any simple modification made for any of the above embodiments, equivalent replacement, equivalence change and modification, all still belongs in the scope of technical solution of the present invention protection.
Claims (4)
1. a low-temperature heat-sealing packaging film, is made up of A layer, B layer, C layer, it is characterized in that: described A layer is Low Temperature Thermal sealing, and B layer is sandwich layer, and C layer is printed layers; Wherein,
A layer: the polyester of 40%-45% is aluminized, the acrylic resin of 47%-50%, the VM3980 thermoplastic elastomer of 3%-5%;
B layer: 97%-99% polypropylene, 1%-3% antistatic smooth master batch;
C layer: the anti-anti-adhesive agent of 96%-98% polypropylene, 2%-4%.
2. low-temperature heat-sealing packaging film according to claim 1, is characterized in that: each layer thickness profile of described A, B, C: Low Temperature Thermal sealing A is 0.8-5 microns, and sandwich layer B is 7-40 microns, and printed layers C is 1-3 microns.
3. low-temperature heat-sealing packaging film according to claim 1, is characterized in that: described low-temperature heat-sealing packaging film thickness is 10-45 microns.
4. prepare the method for low-temperature heat-sealing packaging film according to claim 1, comprise the following steps: batch mixing, melt extrude, slab, longitudinal stretching, cross directional stretch, traction trimming, rolling, cut, finished product, it is characterized in that: described in melt extrude middle extrusion temperature and be 190-260 DEG C, die head temperature is 230-255 DEG C; In described slab process, chilling roller and tank temperature are 25-50 DEG C; In described longitudinal stretching process, longitudinal preheat temperature is 116-145 DEG C, and longitudinal drawing temperature is 120-135 DEG C, and longitudinal setting temperature is 128-145 DEG C, and longitudinal stretching ratio is 4-6 times; In described cross directional stretch process, horizontal preheat temperature is 160-175 DEG C, and transverse drawing temperature is 150-168 DEG C, and horizontal setting temperature is 160-170 DEG C, and cross directional stretch ratio is 7-10 times.