CN104263162A - Water-resistant coating for hull deck and preparation method of water-resistant coating - Google Patents

Water-resistant coating for hull deck and preparation method of water-resistant coating Download PDF

Info

Publication number
CN104263162A
CN104263162A CN201410480934.XA CN201410480934A CN104263162A CN 104263162 A CN104263162 A CN 104263162A CN 201410480934 A CN201410480934 A CN 201410480934A CN 104263162 A CN104263162 A CN 104263162A
Authority
CN
China
Prior art keywords
parts
resistant coating
deck
water
iron oxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410480934.XA
Other languages
Chinese (zh)
Other versions
CN104263162B (en
Inventor
戴晓宸
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shaoguan Yangpeng Waterproof and Anticorrosion Engineering Co.,Ltd.
Original Assignee
Suzhou Yunshu New Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Yunshu New Material Technology Co Ltd filed Critical Suzhou Yunshu New Material Technology Co Ltd
Priority to CN201410480934.XA priority Critical patent/CN104263162B/en
Publication of CN104263162A publication Critical patent/CN104263162A/en
Application granted granted Critical
Publication of CN104263162B publication Critical patent/CN104263162B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention provides a water-resistant coating for a hull deck and a preparation method of the water-resistant coating. The coating comprises the following components in parts by mass: 15-30 parts of zinc acrylate, 15-30 parts of phenolic resin, 4-8 parts of polytetrafluoroethylene powder, 3-8 parts of diisooctyl phthalate, 13-25 parts of iron oxide red, 5-14 parts of talcum powder, 4-12 parts of barium sulfate, 0.08-0.15 part of chlorcosane, 0.1-0.3 part of methyl pyrrolidone, 3-7 parts of molybdenum disulfide, 0.2-0.4 part of manganese naphthenate and 2-5.5 parts of coal tar. The coating provided by the invention has excellent water resistance, atmosphere aging resistance, weather fastness, abrasive resistance and decay resistance, and can be used for protecting the deck for a long period of time.

Description

A kind of deck in ship structure water resistant coating and preparation method thereof
Technical field
The present invention relates to paint field, particularly relate to a kind of deck in ship structure water resistant coating and preparation method thereof.
Background technology
Ship is one of people's vehicles of going on a journey, and has the advantages such as quick, cheap.The deck of hull exposes in an atmosphere throughout the year, is often exposed to the elements, and its surface is easy to breakage, therefore needs to apply coating above deck, is used for protecting wooden or metal deck.The water resistance of the deck coating of current use has much room for improvement, can not be water-fast for a long time, and its corrosion-resistant, resistance to atmospheric aging, wear resisting property are not high, need again to brush after for some time.
Summary of the invention
The technical problem solved: for the shortcoming of existing deck in ship structure by performance deficiencies such as water-fast, corrosion-resistant, resistance to atmospheric agings, the invention provides a kind of deck in ship structure water resistant coating and preparation method thereof.
Technical scheme: a kind of deck in ship structure water resistant coating, in mass parts containing following composition: zinc acrylate resin 15 ~ 30 parts, 15 ~ 30 parts, resol, polytetrafluoroethylene powder 4 ~ 8 parts, dimixo-octyl phthalate 3 ~ 8 parts, red iron oxide 13 ~ 25 parts, talcum powder 5 ~ 14 parts, 4 ~ 12 parts, barium sulfate, clorafin 0.08 ~ 0.15 part, methyl-2-pyrrolidone 0.1 ~ 0.3 part, molybdenumdisulphide 3 ~ 7 parts, manganese naphthenate 0.2 ~ 0.4 part, 2 ~ 5.5 parts, coal tar.
A kind of deck in ship structure water resistant coating described above, in mass parts containing following composition: zinc acrylate resin 18 ~ 24 parts, 20 ~ 25 parts, resol, polytetrafluoroethylene powder 5 ~ 7 parts, dimixo-octyl phthalate 4 ~ 6 parts, red iron oxide 17 ~ 22 parts, talcum powder 7 ~ 10 parts, 7 ~ 10 parts, barium sulfate, clorafin 0.1 ~ 0.13 part, methyl-2-pyrrolidone 0.15 ~ 0.25 part, molybdenumdisulphide 4 ~ 5 parts, manganese naphthenate 0.25 ~ 0.37 part, 3.5 ~ 4.2 parts, coal tar.
The preparation process of a kind of deck in ship structure water resistant coating described above is as follows: red iron oxide, talcum powder, barium sulfate are mixed, be then ground to fineness≤120 μm; Then mix with resol, dimixo-octyl phthalate, clorafin, methyl-2-pyrrolidone, manganese naphthenate; Mix with zinc acrylate resin, polytetrafluoroethylene powder, coal tar again; Finally add molybdenumdisulphide, mixing gets product.
Beneficial effect: a kind of deck in ship structure water resistant coating provided by the invention and preparation method thereof, this coating has excellent water-fast, resistance to atmospheric aging, weather-proof, wear-resisting, corrosion resistance nature, can protect deck for a long time.
Embodiment
Describe the present invention below in conjunction with embodiment.
embodiment 1
The present embodiment provides a kind of deck in ship structure water resistant coating, in mass parts containing following composition: zinc acrylate resin 15 parts, 15 parts, resol, polytetrafluoroethylene powder 4 parts, dimixo-octyl phthalate 3 parts, red iron oxide 13 parts, talcum powder 5 parts, 4 parts, barium sulfate, clorafin 0.08 part, methyl-2-pyrrolidone 0.1 part, molybdenumdisulphide 3 parts, manganese naphthenate 0.2 part, 2 parts, coal tar.
A kind of preparation process of deck in ship structure water resistant coating is as follows: red iron oxide, talcum powder, barium sulfate are mixed, be then ground to fineness≤120 μm; Then mix with resol, dimixo-octyl phthalate, clorafin, methyl-2-pyrrolidone, manganese naphthenate; Mix with zinc acrylate resin, polytetrafluoroethylene powder, coal tar again; Finally add molybdenumdisulphide, mixing gets product.
embodiment 2
The present embodiment provides a kind of deck in ship structure water resistant coating, in mass parts containing following composition: zinc acrylate resin 18 parts, 20 parts, resol, polytetrafluoroethylene powder 5 parts, dimixo-octyl phthalate 4 parts, red iron oxide 17 parts, talcum powder 7 parts, 7 parts, barium sulfate, clorafin 0.1 part, methyl-2-pyrrolidone 0.15 part, molybdenumdisulphide 4 parts, manganese naphthenate 0.25 part, 3.5 parts, coal tar.
A kind of preparation process of deck in ship structure water resistant coating is as follows: red iron oxide, talcum powder, barium sulfate are mixed, be then ground to fineness≤120 μm; Then mix with resol, dimixo-octyl phthalate, clorafin, methyl-2-pyrrolidone, manganese naphthenate; Mix with zinc acrylate resin, polytetrafluoroethylene powder, coal tar again; Finally add molybdenumdisulphide, mixing gets product.
embodiment 3
The present embodiment provides a kind of deck in ship structure water resistant coating, in mass parts containing following composition: zinc acrylate resin 24 parts, 25 parts, resol, polytetrafluoroethylene powder 7 parts, dimixo-octyl phthalate 6 parts, red iron oxide 22 parts, talcum powder 10 parts, 10 parts, barium sulfate, clorafin 0.13 part, methyl-2-pyrrolidone 0.25 part, molybdenumdisulphide 5 parts, manganese naphthenate 0.37 part, 4.2 parts, coal tar.
A kind of preparation process of deck in ship structure water resistant coating is as follows: red iron oxide, talcum powder, barium sulfate are mixed, be then ground to fineness≤120 μm; Then mix with resol, dimixo-octyl phthalate, clorafin, methyl-2-pyrrolidone, manganese naphthenate; Mix with zinc acrylate resin, polytetrafluoroethylene powder, coal tar again; Finally add molybdenumdisulphide, mixing gets product.
The technical performance index of a kind of deck in ship structure water resistant coating of above-described embodiment 1 ~ embodiment 3, its detected result is as follows:
Detected result
Above the embodiment of the present invention is described in detail, for one of ordinary skill in the art, according to the thought of the embodiment of the present invention, all will change in specific embodiments and applications, in sum, this description should not be construed as limitation of the present invention.

Claims (3)

1. a deck in ship structure water resistant coating, is characterized in that, in mass parts containing following composition: zinc acrylate resin 15 ~ 30 parts, 15 ~ 30 parts, resol, polytetrafluoroethylene powder 4 ~ 8 parts, dimixo-octyl phthalate 3 ~ 8 parts, red iron oxide 13 ~ 25 parts, talcum powder 5 ~ 14 parts, 4 ~ 12 parts, barium sulfate, clorafin 0.08 ~ 0.15 part, methyl-2-pyrrolidone 0.1 ~ 0.3 part, molybdenumdisulphide 3 ~ 7 parts, manganese naphthenate 0.2 ~ 0.4 part, 2 ~ 5.5 parts, coal tar.
2. a kind of deck in ship structure water resistant coating according to claim 1, it is characterized in that, in mass parts containing following composition: zinc acrylate resin 18 ~ 24 parts, 20 ~ 25 parts, resol, polytetrafluoroethylene powder 5 ~ 7 parts, dimixo-octyl phthalate 4 ~ 6 parts, red iron oxide 17 ~ 22 parts, talcum powder 7 ~ 10 parts, 7 ~ 10 parts, barium sulfate, clorafin 0.1 ~ 0.13 part, methyl-2-pyrrolidone 0.15 ~ 0.25 part, molybdenumdisulphide 4 ~ 5 parts, manganese naphthenate 0.25 ~ 0.37 part, 3.5 ~ 4.2 parts, coal tar.
3. the preparation method of a kind of deck in ship structure water resistant coating as claimed in claim 1, it is characterized in that, the preparation process of the method is as follows: red iron oxide, talcum powder, barium sulfate are mixed, be then ground to fineness≤120 μm; Then mix with resol, dimixo-octyl phthalate, clorafin, methyl-2-pyrrolidone, manganese naphthenate; Mix with zinc acrylate resin, polytetrafluoroethylene powder, coal tar again; Finally add molybdenumdisulphide, mixing gets product.
CN201410480934.XA 2014-09-19 2014-09-19 A kind of deck in ship structure water resistant coating and preparation method thereof Active CN104263162B (en)