CN104212301A - High-adhesion paint for automobile chassis and preparation method of high-adhesion paint - Google Patents
High-adhesion paint for automobile chassis and preparation method of high-adhesion paint Download PDFInfo
- Publication number
- CN104212301A CN104212301A CN201410456355.1A CN201410456355A CN104212301A CN 104212301 A CN104212301 A CN 104212301A CN 201410456355 A CN201410456355 A CN 201410456355A CN 104212301 A CN104212301 A CN 104212301A
- Authority
- CN
- China
- Prior art keywords
- parts
- iron oxide
- automobile chassis
- paint
- diatomite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides high-adhesion paint for an automobile chassis and a preparation method of the high-adhesion paint. The paint comprises the following components in parts by mass: 5-8 parts of melamine-formaldehyde resin, 6-12 parts of xylene, 1.6-2.8 parts of dioctyl phthalate, 0.8-1.2 parts of epoxy modified acrylic resin, 1.6-2.2 parts of iron oxide black, 1-1.4 parts of iron oxide red, 0.6-1 part of diatomite, 0.02-0.05 part of organic bentonite, 0.4-0.8 part of benzotriazole, 0.015-0.025 part of tributyl phosphate, 0.8-1.6 parts of ethylene glycol monobutyl ether and 1-2 parts of butanone. The paint provided by the invention has the advantages of fast speed in surface drying and actual drying, good adhesion, high mechanical strength and excellent corrosion resistance, thereby being the paint with excellent comprehensive performances for the automobile chassis.
Description
Technical field
The present invention relates to paint field, relate in particular to high adhesive force paint and preparation method thereof for a kind of automobile chassis.
Background technology
Automobile chassis is comprised of power train, running gear, steering system and braking system four parts.Chassis effect is supporting, motor car engine and each parts thereof are installed, shaping automobile moulded, and accept the power of engine, and make automobile produce motion, guarantee normally to travel.All there is defect with sticking power, physical strength, the antiseptic property of coating in the chassis of using at present, can not meet current people's user demand.
Summary of the invention
The technical problem solving: the shortcoming existing for existing chassis paint, the invention provides high adhesive force paint and preparation method thereof for a kind of automobile chassis.
Technical scheme: a kind of automobile chassis paints with high adhesive force, in mass parts, contain following composition: 5～8 parts of terpolycyantoamino-formaldehyde resins, 6～12 parts of dimethylbenzene, 1.6～2.8 parts of o-phthalic acid dibutyl esters, 0.8～1.2 part of epoxy modified acrylic resin, 1.6～2.2 parts of iron oxide blacks, 1～1.4 part of red iron oxide, 0.6～1 part, diatomite, 0.02～0.05 part of organobentonite, 0.4～0.8 part of benzotriazole, 0.015～0.025 part of tributyl phosphate, 0.8～1.6 part of ethylene glycol monobutyl ether, 1～2 part of butanone.
Further, described a kind of automobile chassis contains following composition with high adhesive force paint in mass parts: 6.5 parts of terpolycyantoamino-formaldehyde resins, 9 parts of dimethylbenzene, 2.2 parts of o-phthalic acid dibutyl esters, 1 part of epoxy modified acrylic resin, 1.9 parts of iron oxide blacks, 1.2 parts of red iron oxides, 0.8 part, diatomite, 0.035 part of organobentonite, 0.6 part of benzotriazole, 0.02 part of tributyl phosphate, 1.2 parts of ethylene glycol monobutyl ethers, 1.5 parts of butanone.
A preparation method for high adhesive force paint for automobile chassis, the preparation process of the method is as follows: first in batching kettle, add terpolycyantoamino-formaldehyde resin, dimethylbenzene, epoxy modified acrylic resin, ethylene glycol monobutyl ether and butanone, stirring and dissolving; Add again iron oxide black, red iron oxide, diatomite and organobentonite, mix; Then with shredder, grind, to the μ m of fineness≤60, add o-phthalic acid dibutyl ester, benzotriazole and tributyl phosphate, mix rear filtration, get product.
Beneficial effect: high adhesive force paint and preparation method thereof for a kind of automobile chassis provided by the invention, the surface drying of this coating and doing solid work rapidly, sticking power is good, and physical strength is high, and antiseptic property is excellent, is the automobile chassis coating of excellent combination property.
Embodiment
Below in conjunction with embodiment, the present invention is described in further detail.
embodiment 1
The present embodiment provides a kind of automobile chassis to paint with high adhesive force, in mass parts, contains following composition: 5 parts of terpolycyantoamino-formaldehyde resins, 6 parts of dimethylbenzene, 1.6 parts of o-phthalic acid dibutyl esters, 0.8 part of epoxy modified acrylic resin, 1.6 parts of iron oxide blacks, 1 part of red iron oxide, 0.6 part, diatomite, 0.02 part of organobentonite, 0.4 part of benzotriazole, 0.015 part of tributyl phosphate, 0.8 part of ethylene glycol monobutyl ether, 1 part of butanone.
Automobile chassis is as follows by the preparation process of high adhesive force paint: first in batching kettle, add terpolycyantoamino-formaldehyde resin, dimethylbenzene, epoxy modified acrylic resin, ethylene glycol monobutyl ether and a butanone, stirring and dissolving; Add again iron oxide black, red iron oxide, diatomite and organobentonite, mix; Then with shredder, grind, to the μ m of fineness≤60, add o-phthalic acid dibutyl ester, benzotriazole and tributyl phosphate, mix rear filtration, get product.
embodiment 2
The present embodiment provides a kind of automobile chassis to paint with high adhesive force, in mass parts, contains following composition: 8 parts of terpolycyantoamino-formaldehyde resins, 12 parts of dimethylbenzene, 2.8 parts of o-phthalic acid dibutyl esters, 1.2 parts of epoxy modified acrylic resins, 2.2 parts of iron oxide blacks, 1.4 parts of red iron oxides, 1 part, diatomite, 0.05 part of organobentonite, 0.8 part of benzotriazole, 0.025 part of tributyl phosphate, 1.6 parts of ethylene glycol monobutyl ethers, 2 parts of butanone.
Automobile chassis is as follows by the preparation process of high adhesive force paint: first in batching kettle, add terpolycyantoamino-formaldehyde resin, dimethylbenzene, epoxy modified acrylic resin, ethylene glycol monobutyl ether and a butanone, stirring and dissolving; Add again iron oxide black, red iron oxide, diatomite and organobentonite, mix; Then with shredder, grind, to the μ m of fineness≤60, add o-phthalic acid dibutyl ester, benzotriazole and tributyl phosphate, mix rear filtration, get product.
embodiment 3
The present embodiment provides a kind of automobile chassis to paint with high adhesive force, in mass parts, contains following composition: 6.5 parts of terpolycyantoamino-formaldehyde resins, 9 parts of dimethylbenzene, 2.2 parts of o-phthalic acid dibutyl esters, 1 part of epoxy modified acrylic resin, 1.9 parts of iron oxide blacks, 1.2 parts of red iron oxides, 0.8 part, diatomite, 0.035 part of organobentonite, 0.6 part of benzotriazole, 0.02 part of tributyl phosphate, 1.2 parts of ethylene glycol monobutyl ethers, 1.5 parts of butanone.
Automobile chassis is as follows by the preparation process of high adhesive force paint: first in batching kettle, add terpolycyantoamino-formaldehyde resin, dimethylbenzene, epoxy modified acrylic resin, ethylene glycol monobutyl ether and a butanone, stirring and dissolving; Add again iron oxide black, red iron oxide, diatomite and organobentonite, mix; Then with shredder, grind, to the μ m of fineness≤60, add o-phthalic acid dibutyl ester, benzotriazole and tributyl phosphate, mix rear filtration, get product.
The technical performance index of high adhesive force paint for a kind of automobile chassis of above-described embodiment 1～embodiment 3, its detected result is as follows:
Detected result
Above the embodiment of the present invention is described in detail, for one of ordinary skill in the art, the thought according to the embodiment of the present invention, all will change in specific embodiments and applications, in sum, this description should not be construed as limitation of the present invention.
Claims (3)
1. an automobile chassis paints with high adhesive force, it is characterized in that, in mass parts, contain following composition: 5～8 parts of terpolycyantoamino-formaldehyde resins, 6～12 parts of dimethylbenzene, 1.6～2.8 parts of o-phthalic acid dibutyl esters, 0.8～1.2 part of epoxy modified acrylic resin, 1.6～2.2 parts of iron oxide blacks, 1～1.4 part of red iron oxide, 0.6～1 part, diatomite, 0.02～0.05 part of organobentonite, 0.4～0.8 part of benzotriazole, 0.015～0.025 part of tributyl phosphate, 0.8～1.6 part of ethylene glycol monobutyl ether, 1～2 part of butanone.
2. a kind of automobile chassis according to claim 1 paints with high adhesive force, it is characterized in that, in mass parts, contains following composition: 6.5 parts of terpolycyantoamino-formaldehyde resins, 9 parts of dimethylbenzene, 2.2 parts of o-phthalic acid dibutyl esters, 1 part of epoxy modified acrylic resin, 1.9 parts of iron oxide blacks, 1.2 parts of red iron oxides, 0.8 part, diatomite, 0.035 part of organobentonite, 0.6 part of benzotriazole, 0.02 part of tributyl phosphate, 1.2 parts of ethylene glycol monobutyl ethers, 1.5 parts of butanone.
3. the preparation method that for a kind of automobile chassis as claimed in claim 1, high adhesive force paints, it is characterized in that, the preparation process of the method is as follows: first in batching kettle, add terpolycyantoamino-formaldehyde resin, dimethylbenzene, epoxy modified acrylic resin, ethylene glycol monobutyl ether and butanone, stirring and dissolving; Add again iron oxide black, red iron oxide, diatomite and organobentonite, mix; Then with shredder, grind, to the μ m of fineness≤60, add o-phthalic acid dibutyl ester, benzotriazole and tributyl phosphate, mix rear filtration, get product.