CN103895384A - Formula of double-layer ordinary highlight printing paper coating - Google Patents
Formula of double-layer ordinary highlight printing paper coating Download PDFInfo
- Publication number
- CN103895384A CN103895384A CN201210577370.2A CN201210577370A CN103895384A CN 103895384 A CN103895384 A CN 103895384A CN 201210577370 A CN201210577370 A CN 201210577370A CN 103895384 A CN103895384 A CN 103895384A
- Authority
- CN
- China
- Prior art keywords
- pva
- coating
- printing paper
- formula
- double
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a formula of a double-layer ordinary highlight printing paper coating. An upper layer comprises the components of 30%-50% of PVA (224), 5%-15% of alcohol and 1%-2% of a surfactant; and a lower layer comprises the components of 30%-50% of PVA (240), 5%-15% of ethanol and 1%-2% of a surfactant. The invention employs a double-layer coating formula, the lower layer uses PVA (240) with high degree of polymerization to improve the adhesion of the coating with a substrate, and the upper layer employs PVA (224) with low degree of polymerization to improve the ink adsorption and color of the coating. Superposition of the two layers can improve the adhesion of the coating as well as the bleeding prevention ability of the coating.
Description
Technical field
The invention belongs to printing paper technical field, be specifically related to a kind of double-deck common high light printing paper coating formula.
Background technology
Common high light printing paper is as main printing consumables indoor and outdoor advertising and specialty description, with its high-gloss surface processing, more smooth pure whiter, high density, wide colour gamut, high definition and acutance, contrast effect is very distinct, blotting is rapid, and color rendition is effective, and blotting is rapid, the output of the most applicable full color photo, create the printing effect of professional phase tablet quality, easily support high-res (4800/5760dpi) printer, the advantages such as various ink-jet printers such as economical and practical complete compatible HP, EPSON, CANON have large market.But existing common high light printing paper mainly uses PVA as ink absorbing layer because of it, and PVA is a kind of water miscible polymer, spread and sink in and blend the bad disadvantage of adhesive force so common high light printing paper on the market mainly exists PVA to absorb water under wet environment.
Summary of the invention
The above-mentioned defect existing in order to overcome prior art field, the object of the invention is to, a kind of double-deck common high light printing paper coating formula is provided, solves the common printing paper of prior art and use PVA as ink absorbing layer, under wet environment, water suction is spread and sunk in and is blended the bad problem of adhesive force.
The common high light printing paper coating formula of bilayer provided by the invention, component and the proportioning thereof of described upper strata raw material are: PVA(224) 30%-50%, ethanol 5%-15%, surfactant 1%-2%; Component and the proportioning thereof of described lower floor raw material are: PVA(240) 30%-50%, and ethanol 5%-15%, surfactant 1%-2%; Described PVA(224) concentration be 10%, described PVA(240) concentration be 10%.
The common high light printing paper coating formula of bilayer provided by the invention, its beneficial effect is: adopt double-deck coating formulation, wherein lower floor adopts the PVA(240 of high polymerization degree), the adhesive force of raising coating and base material; Upper strata adopts the PVA(224 of low polymerization degree), absorbency and the color of raising coating, not only improved the adhesive force of coating but also increased simultaneously the anti-ability of spreading and sinking in and oozing of coating after two superimposed.
Detailed description of the invention
Below in conjunction with two embodiment, the common high light printing paper coating formula of bilayer provided by the invention is described in detail.
Embodiment mono-
Under room temperature, get concentration and be 10% PVA(224) 30%, ethanol 5%, surfactant 1% add the corresponding water yield and mix after mechanical agitation 20 minutes, be mixed with upper strata coating fluid; Get concentration and be 10% PVA(240) 30%, ethanol 5%, surfactant 1% add the corresponding water yield and mix after mechanical agitation 20 minutes, be mixed with lower floor's coating fluid; Then pass through line rod coating machine with the 30g ∕ ㎡ of lower floor, upper strata 100 g ∕ ㎡ coat on the high machine-glazed paper base of RC, after being dried, make sample at 60 DEG C.
Embodiment bis-
Under room temperature, get concentration and be 10% PVA(224) 50%, ethanol 15%, surfactant 2% add the corresponding water yield and mix after mechanical agitation 20 minutes, be mixed with upper strata coating fluid; Get concentration and be 10% PVA(240) 50%, ethanol 15%, surfactant 2% add the corresponding water yield and mix after mechanical agitation 20 minutes, be mixed with lower floor's coating fluid; Then pass through line rod coating machine with the 30g ∕ ㎡ of lower floor, upper strata 100 g ∕ ㎡ coat on the high machine-glazed paper base of RC, after being dried, make sample at 60 DEG C.
Comparative example
Under room temperature, get concentration and be 10% PVA(224) 30%, ethanol 5%, surfactant 1% is added the corresponding water yield and is mixed rear mechanical agitation 20 minutes, be mixed with coating fluid, then coat on the high machine-glazed paper base of RC with 130 g ∕ ㎡ by line rod coating machine, after being dried, make sample at 60 DEG C.
Embodiment mono-, embodiment bis-and comparative example specimen page are carried out to the original-pack dye ink printing test of EPSON1390 simultaneously, at 48 DEG C of temperature, in 80%RH climatic chamber, place 24 hours.Range estimation observation resolution chart, embodiment mono-, embodiment bis-specimen pages ooze without spreading and sinking in, and comparative example specimen page resolution chart edge spreads and sinks in and oozes obviously.
By embodiment mono-, embodiment bis-and comparative example specimen page, with placing after 3M tape-stripping 30 minutes, embodiment mono-, embodiment bis-specimen page coatings are by under sticky, and comparative example coating is stuck out.
Claims (2)
1. the common high light printing paper coating formula of bilayer, is characterized in that: component and the proportioning thereof of described upper strata raw material are: PVA(224) 30%-50%, and ethanol 5%-15%, surfactant 1%-2%; Component and the proportioning thereof of described lower floor raw material are: PVA(240) 30%-50%, and ethanol 5%-15%, surfactant 1%-2%.
2. the common high light printing paper coating formula of bilayer according to claim 1, is characterized in that: described PVA(224) concentration be 10%, described PVA(240) concentration be 10%.