CN102863802A - Inner packaging material for Chinese tradition medicine, and preparation of inner packaging material - Google Patents
Inner packaging material for Chinese tradition medicine, and preparation of inner packaging material Download PDFInfo
- Publication number
- CN102863802A CN102863802A CN2012104096428A CN201210409642A CN102863802A CN 102863802 A CN102863802 A CN 102863802A CN 2012104096428 A CN2012104096428 A CN 2012104096428A CN 201210409642 A CN201210409642 A CN 201210409642A CN 102863802 A CN102863802 A CN 102863802A
- Authority
- CN
- China
- Prior art keywords
- packaging material
- inner packaging
- chinese medicine
- weighing
- heating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an inner packaging material for Chinese tradition medicine, and a preparation method of the inner packaging material, belonging to the technical field of the preparation of the packaging material and aiming at providing a high temperature- and low temperature-resistant inner packaging material for Chinese traditional medicine. The technical point of the inner packaging material for the Chinese tradition medicine is that: the material comprises the following components by weight: 40%-60% of a paraffin wax; 20%-40% of a resin compound; 10%-30% of a lubricant; 3%-13% of a toughening agent, and the sum of every component is 100%; the preparation method comprises the steps of: weighing every component, adding paraffin wax into a wax cooking pan, stirring, and heating at 140 DEG C-160 DEG C for 5-20 minutes; then adding the resin compound and a calcium salt modifier, uniformly stirring, and heating at 140 DEG C-160 DEG C for 45-75 minutes; finally adding the lubricant and the toughening agent, and heating at 140 DEG C-160 DEG C for 20-40 minutes to obtain a wax liquid; cooling to 60 DEG C-80 DEG C, making shell, loading pill, sealing, and printing to obtain the final product.
Description
Technical field
The present invention discloses a kind of wrapping material, specifically, is a kind of Chinese medicine inner packaging material, and the present invention also discloses this material preparation method, belongs to the wrapping material preparing technical field.
Background technology
Traditional Chinese medicine pill is generally packed with the wax shell, so that take care of and take.Because of the wax stable in properties, isolation performance is good, can prevent pill draw wet, damage by worms, the volatilization of oxidation and effective constituent.But be subjected to the factor affecting such as area, season, but wax shell in the market is affected by environment larger, in the easy deliquescing of hot summer weather environment, becomes fragile easily under cold environment.It is numerous and diverse to add the shell preparation section of waxing, and the interfering factors of technique and quality is many, do not shut etc. such as breach or pin hole, often since wax chitin amount problem have a strong impact on and produce and transportation.
Summary of the invention
For the problems referred to above, the present invention discloses a kind of can also can not becoming fragile at cold environment in the not deliquescing of hot summer weather environment, and has certain shock resistance Chinese medicine inner packaging material and preparation method thereof.
For addressing the above problem, last technical scheme of the present invention is such: this Chinese medicine inner packaging material is comprised of the component of following weight per-cent: paraffin 40% ~ 60%; Resene compound 20% ~ 40%; Lubricant 10% ~ 30%; Toughner 3% ~ 13%, each component sum is 100%.
Above-mentioned Chinese medicine inner packaging material is comprised of the component of following weight per-cent: paraffin 45% ~ 55%; Resene compound 25% ~ 35%; Lubricant 15% ~ 25%; Toughner 6% ~ 10%, each component sum is 100%.
Above-mentioned Chinese medicine inner packaging material also contains the calcium salt modifying agent of weight percent 0.2% ~ 2% in the described material, each component sum is 100%.
Further, above-mentioned Chinese medicine inner packaging material, described resene compound are rosin, calcification rosin, polymerized rosin, one of them of petroleum resin or their arbitrary combination.
Further, above-mentioned Chinese medicine inner packaging material, described lubricant are Vaseline, lanolin, Viscotrol C, plam oil, one of them of soybean oil or their arbitrary combination.
Further, above-mentioned Chinese medicine inner packaging material, described toughner are Resins, epoxy, acrylic polymer, one of them of ethylene-vinyl acetate copolymer or their combination.
Further, above-mentioned Chinese medicine inner packaging material, described calcium salt modifying agent are calcium chloride, calcium hydroxide, calcium oxide, calcium carbonate, one of them of Calcium hydrogen carbonate or their combination.
A technical scheme is such after of the present invention: the preparation method of this Chinese medicine inner packaging material in turn includes the following steps:
(1) takes by weighing weight percent: paraffin 40% ~ 60%; Resene compound 20% ~ 40%; Lubricant 10% ~ 30%; Toughner 3% ~ 13%, calcium salt modifying agent 0.2% ~ 2%, each component sum is 100%, and is for subsequent use;
(2) paraffin that step (1) is taken by weighing drops into and boils in the paraffin pan, stirs, 140 ℃ ~ 160 ℃ heating 5-20 minute; Add again resene compound and calcium salt modifying agent that step (1) takes by weighing, stir, continue 140 ℃ ~ 160 ℃ heating 45-75 minute;
(3) add at last lubricant and the toughner that step (1) takes by weighing, 140 ℃ ~ 160 ℃ heating 20 ~ 40 minutes, namely get wax liquid;
(4) treat that the wax liquid that step (3) prepares is cooled to 60 ℃ ~ 80 ℃, realize shell processed, fill ball, sealing, printing all processes at shell dress envelope board automatically processed, and get final product.
Compared with prior art, the Chinese medicine inner packaging material soft or hard that provides of the present invention is suitable, can also can not become fragile at cold environment in the not deliquescing of hot summer weather environment, and has certain shock resistance, the round and smooth light of outward appearance.The paraffin of choosing in this prescription has physics plasticity-, and as the main component of wax shell, its advantage is even structure, is easy to after the melting mix with raw material; The rosin based compound is mainly used in regulating the soft durometer of wax shell; Lubricant can increase the flexibility of wax shell, regulates the fragility of wax shell, plays the profit effect; Toughner has thermoplasticity, can increase elasticity and the density of wax shell, improves the resistance to low temperature of wax shell; The calcium salt modifying agent can increase the hardness of wax shell, improves the resistance to elevated temperatures of wax shell; These component scientific formulas, also low temperature resistant so that wrapping material provided by the invention are namely high temperature resistant, and the preparation method is simple, can adapt to the wax shell of the large production of automatization, and the continuity of adopting the wax shell to pack these specialty industries to traditional Chinese medicine pill has great importance.
Summary of the invention
Below in conjunction with embodiment; claim of the present invention is described in further detail; but do not consist of any limitation of the invention, the modification of the limited number of time that anyone makes in interest field of the present invention is still in claim protection domain of the present invention.
Embodiment 1
Paraffin 1600g
Rosin 950g
Plam oil 150g
Yellow Vaselin 250g
Solid epoxy 120g
Calcium chloride 5g
Calcium hydroxide 10g
(1) take by weighing paraffin 1600g, rosin 950g, plam oil 150g, Yellow Vaselin 250g, Resins, epoxy 120g, for subsequent use;
(2) the paraffin input that takes by weighing is boiled in the paraffin pan, stir, about 10 minutes of 140 ℃ ~ 160 ℃ heating; Add again the rosin that takes by weighing, add simultaneously the calcium salt modifying agent, stir, continue about 1 hour of 140 ℃ ~ 160 ℃ heating;
(3) add at last plam oil, Yellow Vaselin and the toughner that takes by weighing, about 0.5 hour of 140 ℃ ~ 160 ℃ heating, namely get wax liquid;
(4) treat that wax liquid is cooled between 60 ℃ ~ 80 ℃, realize shell processed, dress ball, sealing, printing all processes at shell dress envelope board automatically processed, and get final product.
Embodiment 2
Paraffin 1600g
Petroleum resin 570g
Rosin 290g
Lanolin 350g
Solid propenoic acid resin 190g
Calcium chloride 30g
Calcium oxide 30g
The preparation method is with embodiment 1
Embodiment 3
Paraffin 1600g
Polymerized rosin 800g
Calcification rosin 160g
Viscotrol C 260g
Yellow Vaselin 230g
Ethylene-vinyl acetate copolymer (molecular weight 2000) 190g
Calcium carbonate 32g
The preparation method is with embodiment 1
Embodiment 4
Paraffin 1600g
Polymerized rosin 700g
Viscotrol C 260
Soybean oil 2400g
Ethylene-vinyl acetate copolymer (molecular weight 2000) 120g
Calcium hydroxide 50g
Calcium hydrogen carbonate 26g
The preparation method is with embodiment 1
Experimental example 1
The wax shell crash resistance of prescription preparation of the present invention can be tested
Method: get the sample of some amount, naturally fall rear observation from the 0.75m eminence, calculate broken quantity.
Result: without Fragmentation Phenomena, prove that the wax shell crash resistance of prescription preparation of the present invention can be good.
Experimental example 2
The ventilative experiment of the wax shell negative pressure of prescription preparation of the present invention
Method: get the sample of some amount, be placed in the water, under negative pressure 0.027Mpa, kept 2 minutes, observe, calculate the quantity of water inlet.
The result: ventilative water inlet quantity is 0, proves prescription of the present invention by the automatic wax shell well-tended appearance of preparation of board, and it is desirable to receive the base of a fruit, does not exist breach or pin hole the phenomenon such as not to shut, and stopping property is qualified.
Experimental example 3
The wax shell thermal deformation resistant experiment of prescription preparation of the present invention
Method: (1) gets the sample of some amount, and packing is placed in 55 ℃ of baking ovens routinely, takes out after 2 hours and observes, and calculates the quantity of weak and limp distortion.
(2) get the sample of some amount, packing is placed in 50 ℃ of baking ovens routinely, takes out after 8 hours and observes, and calculates the quantity of weak and limp distortion.
(3) get the sample of some amount, packing is placed in 55 ℃ of baking ovens routinely, takes out after 5.5 hours and observes, and calculates the quantity of weak and limp distortion.
The result: the shape phenomenon of collapsing does not appear in experiment (1).
The shape phenomenon of collapsing does not appear in experiment (2).
Experiment (3) 13% the sample shape phenomenon that occurs collapsing.
The result proves that the wax shell heat resistanceheat resistant of prescription preparation of the present invention is functional, can safekeeping in summer.
Experimental example 4
The wax shell of prescription of the present invention preparation is cold-resistant to fall broken experiment
Method: get the sample of some amount, packing is placed on 2 ℃ of refrigerators placements 7 hours routinely, takes out rear naturally falling from the 0.75m eminence and observes behind concrete floor, calculates broken quantity.
The result: the percentage of damage of sample is 25%, proves that the wax shell of prescription preparation of the present invention has good cold performance.
Claims (9)
1. a Chinese medicine inner packaging material is characterized in that, is comprised of the component of following weight per-cent: paraffin 40% ~ 60%; Resene compound 20% ~ 40%; Lubricant 10% ~ 30%; Toughner 3% ~ 13%, each component sum is 100%.
2. Chinese medicine inner packaging material according to claim 1 is characterized in that, is comprised of the component of following weight per-cent: paraffin 45% ~ 55%; Resene compound 25% ~ 35%; Lubricant 15% ~ 25%; Toughner 6% ~ 10%, each component sum is 100%.
3. Chinese medicine inner packaging material according to claim 1 and 2 is characterized in that, also contains the calcium salt modifying agent of weight percent 0.2% ~ 2% in the described material, and each component sum is 100%.
4. Chinese medicine inner packaging material according to claim 1 and 2 is characterized in that, described resene compound is rosin, calcification rosin, polymerized rosin, one of them of petroleum resin or their arbitrary combination.
5. Chinese medicine inner packaging material according to claim 1 and 2 is characterized in that, described lubricant is Vaseline, lanolin, Viscotrol C, plam oil, one of them of soybean oil or their arbitrary combination.
6. want 1 or 2 described Chinese medicine inner packaging materials according to right, it is characterized in that, described toughner is Resins, epoxy, acrylic resin, one of them of ethylene-vinyl acetate copolymer or their combination.
7. Chinese medicine inner packaging material according to claim 3 is characterized in that, described calcium salt modifying agent is calcium chloride, calcium hydroxide, calcium oxide, calcium carbonate, one of them of Calcium hydrogen carbonate or their combination.
8. the preparation method of claim 1 or 2 described Chinese medicine inner packaging materials is characterized in that, in turn includes the following steps:
(1) take by weighing by weight percentage each component, for subsequent use;
(2) paraffin that step (1) is taken by weighing drops into and boils in the paraffin pan, stirs, 140 ℃ ~ 160 ℃ heating 5-20 minute; Add again the resene compound that step (1) takes by weighing, stir, continue 140 ℃ ~ 160 ℃ heating 45-75 minute;
(3) add at last lubricant and the toughner that step (1) takes by weighing, 140 ℃ ~ 160 ℃ heating 20-40 minute, namely get wax liquid;
(4) treat that the wax liquid that step (3) prepares is cooled to 60 ℃ ~ 80 ℃, at shell dress envelope board automatically processed shell processed, dress ball, sealing, printing all processes, and get final product.
9. the preparation method of Chinese medicine inner packaging material claimed in claim 3 is characterized in that, in turn includes the following steps:
(1) take by weighing by weight percentage each component, for subsequent use;
(2) paraffin that step (1) is taken by weighing drops into and boils in the paraffin pan, stirs, 140 ℃ ~ 160 ℃ heating 5-20 minute; Add again resene compound and calcium salt modifying agent that step (1) takes by weighing, stir, continue 140 ℃ ~ 160 ℃ heating 45-75 minute;
(3) add at last lubricant and the toughner that step (1) takes by weighing, 140 ℃ ~ 160 ℃ heating 20-40 minute, namely get wax liquid;
(4) treat that the wax liquid that step (3) prepares is cooled to 60 ℃ ~ 80 ℃, at shell dress envelope board automatically processed shell processed, dress ball, sealing, printing all processes, and get final product.