Publication numberCN102728577 B
Publication typeGrant
Application numberCN 201210205774
Publication date19 Nov 2014
Filing date21 Jun 2012
Priority date21 Jun 2012
Also published asCN102728577A
Publication number201210205774.9, CN 102728577 B, CN 102728577B, CN 201210205774, CN-B-102728577, CN102728577 B, CN102728577B, CN201210205774, CN201210205774.9
Inventors董清世, 黄文瑞, 程小路
Applicant信义汽车部件(芜湖)有限公司
Export CitationBiBTeX, EndNote, RefMan
External Links: SIPO, Espacenet
Method for improving surface tension of glass plastic accessory
CN 102728577 B
Abstract  translated from Chinese
本发明提供一种应用于玻璃生产技术领域的提高玻璃塑料附件表面张力的工艺方法,所述的提高玻璃塑料附件表面张力的工艺方法的步骤为:1)向用于加热玻璃塑料附件的加热容器(1)内加入去离子水(3);2)向加热容器(1)内放入玻璃塑料附件(2)前,加热去离子水(3),然后放入玻璃塑料附件(2)进行热煮;3)对加热容器(1)内的去离子水(3)持续加热20—60min。 The present invention provides a process for the field of applied technology to improve the production of glass glass plastic attachment surface tension, said process for glass-plastic attachment surface tension to improve the steps of: 1) the heating vessel for heating glass-plastic attachments deionized (1) water (3); 2) the heating vessel (1) into a glass-plastic attachment (2) before heating deionized water (3), and then placed in a glass plastic accessories (2) heat cook; 3) heating the container (deionized water 1) (3) heating was continued for 20-60min. 采用本发明的技术方案,在不破坏玻璃塑料附件材质情况下,不仅可以更好的去除塑料件表面残留的脱模剂、油脂,达到最佳清洁效果,提高玻璃塑料附件在粘接工艺中的稳定性。 The technical solution of the present invention, in the plastic attachment material without damaging the glass case, not only can better remove the plastic surface residual mold release agents, grease, to achieve the best cleaning results, improve glass plastic attachments in the bonding process stability. 同时,能够避免现有技术中采用化学试剂对人体、环境的负面影响,达到环保之效果。 At the same time, be able to avoid the negative impact of the prior art using chemicals on the human body, the environment, to achieve environmental protection effect.
Claims(3)  translated from Chinese
1.一种提高玻璃塑料附件表面张力的工艺方法,所述的提高玻璃塑料附件表面张力的工艺方法的步骤为: 1)向用于加热玻璃塑料附件的加热容器(I)内加入去离子水(3); 2)向加热容器⑴内放入玻璃塑料附件⑵前,加热去离子水(3),然后放入玻璃塑料附件⑵进行热煮; 3)对加热容器(I)内的去离子水(3)持续加热20— 60min ; 对所述的玻璃塑料附件(2)进行热煮时,不同的玻璃塑料附件(2)应分批在玻璃容器(I)热煮或在不同的玻璃容器(I)中热煮; 对玻璃塑料附件(2)进行热煮时,每次热煮时更换去离子水(3); 向加热容器⑴内放入玻璃塑料附件⑵前,将去离子水⑶的温度加热到90C —100C之间; 其特征在于:对加热容器(I)内的去离子水(3)持续加热时,对去离子水(3)的加热温度保持在90C — 100C之间; 所述的玻璃塑料附件(2)热煮完成后,对玻璃塑料附件(2)进行晾干,然后再对玻璃塑料附件(2)进行后续作业。 1. A process for improving the surface tension of the glass plastic attachments The process of glass-plastic attachment surface tension of the improvement the steps of: 1) the heating container (I) for heating glass-plastic attachments within deionized water (3); 2) forward into a heated container glass plastic accessory ⑴ ⑵, heated deionized water (3), and then placed in a plastic glass annex ⑵ heat cook; 3) heating the container (I) in the deionized Water (3) for heating 20- 60min; when the glass plastic accessories (2) heat and cook, different glass plastic accessories (2) should be in batches in a glass container (I) or a hot cooked in different glass containers (I) in the heat and cook; when glass plastic accessories (2) heat and cook, deionized water each time you replace hot cooked (3); placed into the heating vessel ⑴ ⑵ glass plastic accessory before, deionized water ⑶ heated to a temperature of between 90 C -100 C; wherein: when deionized water heating vessel (I) within the (3) for heating, to deionized water (3) is maintained at a heating temperature of 90 C - between 100 C; plastic accessory after the glass (2) hot boiled completed, the glass-plastic attachment (2) to dry, and then glass plastic accessories (2) follow-up operations.
2.根据权利要求1所述的提高玻璃塑料附件表面张力的工艺方法,其特征在于:所述的加热容器(I)设置为通过电加热方式加热的结构。 2. A process according to increase the surface tension of the glass-plastic attachment according to claim 1, characterized in that: a heating vessel (I) according to the heating by the electric heating structure.
3.根据权利要求2所述的提高玻璃塑料附件表面张力的工艺方法,其特征在于:对加热容器(I)内的去离子水(3)持续加热时,加热时间控制在30— 40min之间。 3. A process of increasing the glass surface tension of the plastic accessory according to claim 2, wherein: deionized water heating vessel (I) within the (3) for heating, the heating time control between 30- 40min .
Description  translated from Chinese
一种提高玻璃塑料附件表面张力的工艺方法 A process for glass-plastic attachment surface tension increase

技术领域 Technical Field

[0001] 本发明属于玻璃生产技术领域,更具体地说,是涉及一种提高玻璃塑料附件表面张力的工艺方法。 [0001] The present invention belongs to the field of glass production, and more particularly, to a method for increasing the surface tension of the glass plastic attachment process method.

背景技术 Background

[0002]为提高玻璃塑料附件的表面张力,提高玻璃塑料附件在粘接工艺中的稳定性,需对玻璃塑料部件表面进行清洁。 [0002] In order to improve the surface tension of glass-plastic attachments, raise a glass plastic accessory stability in the bonding process, the need to clean the surface of glass plastic parts. 现有技术中,是采用丁酮或酒精对玻璃塑料附件进行浸泡、晾干处理。 The prior art is the use of methyl ethyl ketone or alcohol glass plastic attachment for soaking, drying process. 不过现有的这种方法,化学试剂使用量较大,成本较高,废弃的丁酮或酒精对人体、环境有负面影响,不利于环保。 However, this conventional method, a large amount of chemicals, high cost, waste butanone or alcohol have adverse effects on humans and the environment is not conducive to environmental protection. 与此同时,部分玻璃塑料附件即使在使用丁酮或酒精浸泡处理后,仍处理不掉材料表面脱模剂、油脂,从而影响玻璃塑料附件在粘贴工艺中的稳定性。 At the same time, part of the glass-plastic accessory even when using methyl ethyl ketone or alcohol soaking, still can not afford to deal with surface mold release agents, grease, thus affecting the stability of glass-plastic attachment paste Process.

发明内容 DISCLOSURE

[0003] 本发明所要解决的技术问题是:针对现有技术的不足,提供一种能够避免玻璃塑料附件粘接中的化学试剂对人体、环境的负面影响,同时提高玻璃塑料附件表面张力的提高玻璃塑料附件表面张力的工艺方法。 [0003] The technical problem to be solved is: for the deficiencies of the prior art and to provide a way to avoid the negative effects of glass-plastic attachment adhesive chemicals to humans, the environment, while improving the glass-plastic attachment surface tension increase glass-plastic attachment process for surface tension.

[0004] 要解决以上所述的技术问题,本发明采取的技术方案为: [0004] To solve the technical problems described above, the present invention adopts the technical scheme:

[0005] 本发明为一种提高玻璃塑料附件表面张力的工艺方法,所述的提高玻璃塑料附件表面张力的工艺方法的步骤为: [0005] The present invention relates to a process for glass-plastic attachment surface tension increase, the improved process for glass-plastic attachment surface tension of the steps of:

[0006] I)向用于加热玻璃塑料附件的加热容器内加入去离子水; [0006] I) into the heating vessel for heating glass-plastic attachments deionized water;

[0007] 2)向加热容器内放入玻璃塑料附件前,加热去离子水,然后放入玻璃塑料附件进行热煮; [0007] 2) before heating the container into the glass into the plastic attachments, heated deionized water, then put in a glass plastic attachments for heat and cook;

[0008] 3)对加热容器内的去离子水持续加热20— 60min。 [0008] 3) deionized water is heated in the vessel continued heating 20- 60min.

[0009] 对所述的玻璃塑料附件进行热煮时,不同的玻璃塑料附件应分批在玻璃容器热煮或在不同的玻璃容器中热煮。 [0009] When glass plastic accessory according to heat and cook, different glass plastic attachments should cook in batches in hot glass containers or glass containers in different hot cook.

[0010] 对玻璃塑料附件进行热煮时,每次热煮时更换去离子水。 [0010] When glass plastic attachments heat and cook, heat cook every time replace deionized water.

[0011] 向加热容器内放入玻璃塑料附件前,将去水离子的温度加热到90C—100C之间。 Before [0011] into the heating container into the glass-plastic attachments, will go to water heated to a temperature of ions between 90 C-100 C.

[0012] 对加热容器内的去离子水持续加热时,对去离子水的加热温度保持在90C —100C之间。 When [0012] Deionized water was heated on the continuous heating vessel for heating deionized water maintained at a temperature between 90 C -100 C.

[0013] 对加热容器内的去离子水持续加热时,加热时间控制在30— 40min之间,所述的玻璃塑料附件热煮完成后,对玻璃塑料附件进行晾干,然后再对玻璃塑料附件进行后续作业。 [0013] When deionized water is heated in the container is heated, the heating time control between 30- 40min, glass plastic accessory after the heat of the boiled completed, the glass-plastic attachments to dry, and then glass plastic accessory subsequent operations.

[0014] 所述的加热容器设置为通过电加热方式加热的结构。 Heating vessel [0014] is set by the electrically heated heating structure.

[0015] 采用本发明的技术方案,能得到以下的有益效果: [0015] The technical solution of the present invention, the following advantageous effects can be obtained:

[0016] 本发明所述的提高玻璃塑料附件表面张力的工艺方法,在不破坏玻璃塑料附件材质情况下,使用高温热煮的工艺方法,不仅可以更好的去除塑料件表面残留的脱模剂、油月旨,达到最佳清洁效果,提高玻璃塑料附件在粘接工艺中的稳定性。 [0016] A process to improve the surface of glass-plastic accessory of the present invention tension without breaking the glass in the plastic attachment material, the use of high-temperature process heat cooking method can not only better to remove mold release agent remaining on the surface of plastic parts Oil month aims to achieve the best results, to improve the stability of the glass bonding process the plastic accessory of. 同时,采用热煮的工艺方法,能够避免现有技术中采用化学试剂对人体、环境的负面影响,达到环保之效果。 Meanwhile, cook the hot process method, it is possible to avoid the negative effects of chemicals used in the prior art to humans, the environment, to achieve environmental protection effect.

附图说明 Brief Description

[0017] 下面对本说明书各附图所表达的内容及图中的标记作出简要的说明: [0017] The following expression for the contents of this specification, the drawings and symbols in the figures to make brief description:

[0018] 图1为提高玻璃塑料附件表面张力的加热容器的结构示意图; [0018] Figure 1 is a schematic view of a glass container to improve the structure of the heating surface tension of the plastic accessory;

[0019] 图2为本发明的提高玻璃塑料附件表面张力的工艺方法的工艺流程图; [0019] FIG. 2 of the present invention to improve the process for glass-plastic attachment surface tension of the process flow diagram;

[0020] 图中标记:1、加热容器;2、玻璃塑料附件;3、去离子水。 [0020] FIG labeled: 1, heating the container; 2, glass plastic attachments; 3, deionized water.

具体实施方式 DETAILED DESCRIPTION

[0021] 下面对照附图,通过对实施例的描述,对本发明的具体实施方式如所涉及的各构件的形状、构造、各部分之间的相互位置及连接关系、各部分的作用及工作原理等作进一步的详细说明: [0021] The following reference to the drawings, through the description of the embodiments, the present invention relates to specific embodiments as the shape and structure of each member, and connection of the mutual position between the parts, the role of each part and principle etc. for further details:

[0022] 如附图1、附图2所示,本发明为一种提高玻璃塑料附件表面张力的工艺方法,所述的提高玻璃塑料附件表面张力的工艺方法的步骤为: Step [0022] As Figure 1, shown in Figure 2, the present invention is a process for improving the surface tension of the glass plastic attachments The process of glass-plastic attachment surface tension of the improvement are:

[0023] I)向用于加热玻璃塑料附件的加热容器I内加入去离子水3 ; [0023] I) into the heating vessel for heating glass-plastic Annex I of deionized water 3;

[0024] 2)向加热容器I内放入玻璃塑料附件2前,加热去离子水3,然后放入玻璃塑料附件2进行热煮; [0024] 2) I put into the heating container glass plastic attachment 2 front, 3 heated deionized water, then put in a glass annex 2 plastic heat cook;

[0025] 3)对加热容器I内的去离子水3持续加热20— 60min。 [0025] 3) deionized water heating vessel within 3 I continued heating 20- 60min.

[0026] 对所述的玻璃塑料附件2进行热煮时,不同的玻璃塑料附件2应分批在玻璃容器I热煮或在不同的玻璃容器I中热煮。 [0026] When glass plastic in Annex 2 of the heat and cook, different glass plastic Annex 2 batches in a glass container should I cook or heat in different glass container hot I cook.

[0027] 对玻璃塑料附件2进行热煮时,每次热煮时更换去离子水3。 [0027] When glass plastic Annex 2 hot to cook, heat and cook each time replacing the deionized water 3. 每次热煮时必须更换新的去离子水,同时不同材质的玻璃塑料附件不能混合进行水煮,因为混合热煮将大大影响玻璃塑料附件在粘接工艺中的稳定性。 Heat must be replaced every cook new deionized water, while different materials glass plastic attachments can not be boiled mix, because mixing of hot boiled will greatly affect the stability of the glass bonding process plastic accessory of.

[0028] 向加热容器I内放入玻璃塑料附件2前,将去水离子3的温度加热到90C—100C之间。 [0028] I put into the heated glass plastic container Annex 2 before the ions to the water is heated to a temperature of 3 between 90 C-100 C.

[0029] 对加热容器I内的去离子水3持续加热时,对去离子水3的加热温度保持在90C — 100C之间。 [0029] when I deionized water heating vessel within 3 continuous heating, the heating temperature of the deionized water 3 is maintained at 90 C - between 100 C.

[0030] 对加热容器I内的去离子水3持续加热时,加热时间控制在30—40min之间,所述的玻璃塑料附件2热煮完成后,对玻璃塑料附件2进行晾干,然后再对玻璃塑料附件2进行后续作业。 [0030] when I deionized water within the heating vessel 3 is heated, the heating time control between 30-40min, glass plastic accessory after the completion of the second heat and cook for 2 to dry glass plastic attachments, and then Annex 2 of the glass-plastic for subsequent operations.

[0031] 所述的加热容器I设置为通过电加热方式加热的结构。 Heating the container [0031] I said to heating by electric heating structure.

[0032] 本发明所述的提高玻璃塑料附件表面张力的工艺方法,在不破坏玻璃塑料附件材质情况下,使用高温热煮的工艺方法,不仅可以更好的去除塑料件表面残留的脱模剂、油月旨,达到最佳清洁效果,提高玻璃塑料附件在粘接工艺中的稳定性。 [0032] The process for increasing the glass surface of the plastic accessory of the present invention tension without breaking the glass in the plastic attachment material, the use of high-temperature process heat cooking method can not only better to remove mold release agent remaining on the surface of plastic parts Oil month aims to achieve the best results, to improve the stability of the glass bonding process the plastic accessory of. 同时,采用热煮的工艺方法,能够避免现有技术中采用化学试剂对人体、环境的负面影响,达到环保之效果。 Meanwhile, cook the hot process method, it is possible to avoid the negative effects of chemicals used in the prior art to humans, the environment, to achieve environmental protection effect.

[0033] 上面结合附图对本发明进行了示例性的描述,显然本发明具体的实现并不受上述方式的限制,只要采用了本发明的方法构思和技术方案进行的各种改进,或未经改进将本发明的构思和技术方案直接应用于其他场合的,均在本发明的保护范围内。 [0033] The above with reference to the present invention has been exemplary description, it is clear the specific implementation of the present invention is not limited to the above-described manner, the various uses of the present invention as long as the method of conception and technology improvement programs, with or without improve the ideas and techniques of the present invention is applied directly on other occasions, it is within the scope of the present invention.