CN102719198A - Glue used for plastic - Google Patents
Glue used for plastic Download PDFInfo
- Publication number
- CN102719198A CN102719198A CN2011102512142A CN201110251214A CN102719198A CN 102719198 A CN102719198 A CN 102719198A CN 2011102512142 A CN2011102512142 A CN 2011102512142A CN 201110251214 A CN201110251214 A CN 201110251214A CN 102719198 A CN102719198 A CN 102719198A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight parts
- plastics
- glue special
- methyl methacrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a glue used for plastic, comprising 50-70 weight parts of alpha-cyanoacrylate, 2-8 weight parts of methyl methacrylate graft latex, 4-9 weight parts of vinyl acetate emulsion, 5-10 weight parts of zinc oxide, 2-6 weight parts of casein, 1-4 weight parts of glycerin, 2-5 weight parts of natural rubber, 10-15 weight parts of phenolic resin, 3-7 weight parts of curing agent, and 2-7 weight parts of toluene. The glue disclosed herein can be used for rapid bonding of various plastic products, especially for small area bonding between plastics and small area bonding between plastic and other material. The glue disclosed herein has the advantages of strong bonding force, no whitening, short curing time, and no brittleness, etc.
Description
Technical field
The present invention relates to a kind of glue composition, relate to a kind of plastics glue special specifically.
Background technology
Plastics are one type and have plastic synthesized polymer material that it and viton, synthon have formed current daily life indispensable three big synthetic materialss.Specifically, plastics are to be staple with natural or synthetic resins, add various additives, under conditions such as certain temperature and pressure, can mould and process definite shape, keep the material of shape invariance at normal temperatures.The kind of common plastics has; PPT plastics, ABS plastic, PVC, PE and PP etc., that plastics have is in light weight, excellent chemical stability, excellent electrical insulation capability, be heat poor conductor, have sound deadening shock absorption effect, the physical strength wide and higher plurality of advantages such as specific tenacity that distribute.Plastics are used in tubing, sanitary ware, lagging material, light transmissive material etc. mostly, and visible plastics and our daily life are inseparable.
Though plastics have so many benefit and of many uses; Perhaps damage but used of a specified duration or because of the improper use meeting plastics have been ruptured, because there is not a kind of sticking glue of being stained with plastics that is specifically designed in the prior art, people just use the general glue of some on the market some and plastics are stained with sticking; But often effect is undesirable; Have at last the plastics that damage are thrown away, this way not only sinks money, and is unfavorable for environmental protection; The plastic garbage contaminate environment has become a difficult problem of environmental pollution, is become by people " white pollution ".If a kind of glue of being stained with sticking plastics that is specifically designed to is arranged; So just have a large amount of plastics and repaired utilization, need not be thrown away, saved mint of money; Simultaneously also solve the plastics problem of environment pollution caused, how to provide a kind of plastics glue special to become the urgent demand of people.
Summary of the invention
The objective of the invention is to overcome deficiency of the prior art, a kind of plastics glue special is provided.
The objective of the invention is to realize: a kind of plastics glue special through following scheme; The weight part of said each composition of plastics glue special is: 50～70 parts of alpha-cyano acrylic acid esters, 2～8 parts in methyl methacrylate-grafted latex, 4～9 parts of acetate emulsions; 5～10 parts in zinc oxide; 2～6 parts of casein food grade, 1～4 part of glycerine, 2～5 parts of tree elastomers, 10～15 parts in resol, 3～7 parts in solidifying agent, 2～7 parts of toluene.
As preferred version of the present invention; The weight part of said each composition of plastics glue special is: 55～65 parts of alpha-cyano acrylic acid esters, 3～7 parts in methyl methacrylate-grafted latex, 5～8 parts of acetate emulsions; 6～9 parts in zinc oxide; 3～5 parts of casein food grade, 2～3 parts of glycerine, 3～4 parts of tree elastomers, 11～14 parts in resol, 4～6 parts in solidifying agent, 3～6 parts of toluene.
As preferred plan of the present invention; The weight part of said each composition of plastics glue special is: 60 parts of alpha-cyano acrylic acid esters, 4 parts in methyl methacrylate-grafted latex, 6 parts of acetate emulsions; 8 parts in zinc oxide; 4 parts of casein food grade, 2.5 parts of glycerine, 3.5 parts of tree elastomers, 12 parts in resol, 5 parts in solidifying agent, 4 parts of toluene.
Said solidifying agent is silicon rubber sealant or polyurethane glue.
TEB 3K content in the said methyl methacrylate-grafted latex is 20%.
Table one: the parameter of measured plastics glue special of the present invention in the conventional environment of 25 ℃ of temperature, humidity 70%:
| Product performance | Bonding between plastics and the other materials, the bonding between plastics and the plastics |
| Viscosity (mpa.s) | 130 |
| TR (℃) | -45～80 |
| Tensile strength (kg/cm 2) | 170 |
| Shearing resistance (Mpa) | 21 |
| Outward appearance/packing | 20g/ props up, and 100g/ props up |
| Curing speed (s) | 6-12 |
The invention has the advantages that: plastics glue special of the present invention can be used for the bonding fast of various plastic cement products; The small area that is particularly suitable between plastic cement and the plastic cement is bonding; The small area that also can be used between plastics and the other materials is bonding, and it is strong that plastics glue special of the present invention has a bonding force, no albefaction; Set time is fast, advantages such as no fragility.
Embodiment
Below in conjunction with specific embodiment the present invention is further specified.
Embodiment 1: a kind of plastics glue special, and the weight part of said each composition of plastics glue special is: 50 parts of alpha-cyano acrylic acid esters, 2 parts in methyl methacrylate-grafted latex; 4 parts of acetate emulsions, 5 parts in zinc oxide, 2 parts of casein food grade; 1 part of glycerine; 2 parts of tree elastomers, 10 parts in resol, 3 parts in solidifying agent, 2 parts of toluene, said solidifying agent is a silicon rubber sealant, the TEB 3K content in the said methyl methacrylate-grafted latex is 20%.
Embodiment 2: a kind of plastics glue special; The weight part of said each composition of plastics glue special is: 55 parts of alpha-cyano acrylic acid esters, 3 parts in methyl methacrylate-grafted latex, 5 parts of acetate emulsions; 6 parts in zinc oxide; 3 parts of casein food grade, 2 parts of glycerine, 3 parts of tree elastomers, 11 parts in resol, 4 parts in solidifying agent, 3 parts of toluene.Said solidifying agent is a polyurethane glue, and the TEB 3K content in the said methyl methacrylate-grafted latex is 20%.
Embodiment 3: a kind of plastics glue special; The weight part of said each composition of plastics glue special is: 60 parts of alpha-cyano acrylic acid esters, 4 parts in methyl methacrylate-grafted latex, 6 parts of acetate emulsions; 8 parts in zinc oxide; 4 parts of casein food grade, 2.5 parts of glycerine, 3.5 parts of tree elastomers, 12 parts in resol, 5 parts in solidifying agent, 4 parts of toluene.
Embodiment 4: the weight part of said each composition of plastics glue special is: 55～65 parts of alpha-cyano acrylic acid esters; 7 parts in methyl methacrylate-grafted latex; 8 parts of acetate emulsions, 9 parts in zinc oxide, 5 parts of casein food grade; 3 parts of glycerine, 4 parts of tree elastomers, 14 parts in resol, 6 parts in solidifying agent, 6 parts of toluene.
Embodiment 5: a kind of plastics glue special; The weight part of said each composition of plastics glue special is: 70 parts of alpha-cyano acrylic acid esters, 8 parts in methyl methacrylate-grafted latex, 9 parts of acetate emulsions; 10 parts in zinc oxide; 6 parts of casein food grade, 4 parts of glycerine, 5 parts of tree elastomers, 15 parts in resol, 7 parts in solidifying agent, 7 parts of toluene.
The method of use of plastics glue special of the present invention is: use dried cotton or sand paper that the dust of commissure, greasy dirt etc. are removed, with then surface of cleaning; Turn on blue bottle cover, bottleneck if any glue earlier with cotton with the glue wiped clean, use after putting syringe needle or PE dropper again, be able to control glue flow, guarantee bonding effect; Dripped droplet plastics glue special of the present invention by commissure, carrying out bondingly at once, and be retained to till the sclerosis, the setting time several seconds is not waited, and can reach practical intensity, and can obtain maximum intensity after 24 hours in about 30 minutes; Use back cleaning bottleneck, and blue bottle cover is screwed; Leave plastics glue special of the present invention in shady and cool dry place after finishing using.
Should be noted that at last; Above content is only in order to explain technical scheme of the present invention; But not to the restriction of protection domain of the present invention; The simple modification that those of ordinary skill in the art carries out technical scheme of the present invention perhaps is equal to replacement, does not all break away from the essence and the scope of technical scheme of the present invention.
Claims (6)
1. plastics glue special; It is characterized in that: the weight part of said each composition of plastics glue special is: 50～70 parts of alpha-cyano acrylic acid esters, 2～8 parts in methyl methacrylate-grafted latex, 4～9 parts of acetate emulsions; 5～10 parts in zinc oxide; 2～6 parts of casein food grade, 1～4 part of glycerine, 2～5 parts of tree elastomers, 10～15 parts in resol, 3～7 parts in solidifying agent, 2～7 parts of toluene.
2. according to the described plastics glue special of claim 1; It is characterized in that: the weight part of said each composition of plastics glue special is: 55～65 parts of alpha-cyano acrylic acid esters, 3～7 parts in methyl methacrylate-grafted latex, 5～8 parts of acetate emulsions; 6～9 parts in zinc oxide; 3～5 parts of casein food grade, 2～3 parts of glycerine, 3～4 parts of tree elastomers, 11～14 parts in resol, 4～6 parts in solidifying agent, 3～6 parts of toluene.
3. according to the described plastics glue special of claim 2; It is characterized in that: the weight part of said each composition of plastics glue special is: 60 parts of alpha-cyano acrylic acid esters, 4 parts in methyl methacrylate-grafted latex, 6 parts of acetate emulsions; 8 parts in zinc oxide; 4 parts of casein food grade, 2.5 parts of glycerine, 3.5 parts of tree elastomers, 12 parts in resol, 5 parts in solidifying agent, 4 parts of toluene.
4. according to the described plastics glue special of each claim in the claim 1,2 or 3, it is characterized in that: said solidifying agent is silicon rubber sealant or polyurethane glue.
5. according to the described plastics glue special of each claim in the claim 1,2 or 3, it is characterized in that: the TEB 3K content in the said methyl methacrylate-grafted latex is 20%.
6. according to the described plastics glue special of claim 4, it is characterized in that: the TEB 3K content in the said methyl methacrylate-grafted latex is 20%.