CN102643594A - Durable fresh-maintained preservative primer - Google Patents
Durable fresh-maintained preservative primer Download PDFInfo
- Publication number
- CN102643594A CN102643594A CN2011100429583A CN201110042958A CN102643594A CN 102643594 A CN102643594 A CN 102643594A CN 2011100429583 A CN2011100429583 A CN 2011100429583A CN 201110042958 A CN201110042958 A CN 201110042958A CN 102643594 A CN102643594 A CN 102643594A
- Authority
- CN
- China
- Prior art keywords
- component
- jupocin
- corrosion primer
- zinc
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a durable fresh-maintained preservative primer. Raw materials of the primer comprises a component A and a component B, wherein the consumption of the component B is 5-15 percent by weight that of the component A; the component A comprises the following components in percentage by weight: 20-50 percent of epoxy resin, 10-30 percent of phosphate, 1-10 percent of additive, 5-20 percent of diluting agent and 15-35 percent of solvent; and the component B comprises the following components in percentage by weight: 50-80 percent of curing agent and 20-50 percent of solvent. Compared with the prior art, the durable fresh-maintained preservative primer disclosed by the invention has the advantages of favorable adhesive force, strong laminated coating property, tough and tensile paint film, impact resistance, convenience in construction, long preservative effect cycle, favorable construction matching property and particularly excellent salt spray resistance.
Description
Technical field
The present invention relates to a kind of priming paint, especially relate to a kind of Jupocin anti-corrosion primer.
Background technology
Building such as skeleton construction, steelwork, steel structure concrete composite structure body is fast because of its speed, and construction pollution is little, and is in light weight, and is convenient to moulding, short construction period, and anti-seismic performance is good etc., and advantage is grown in strength rapidly; Simultaneously, be accompanied by developing rapidly of steelwork industry, the anticorrosion of steel structure priming paint that matches therewith just become anticorrosion industry developing direction.
Existing anti-corrosion primer kind is a lot, but epoxy resin is an existing market kind the most widely owing to its distinctive character, and such anti-corrosion primer has good acid resistance, alkali resistance; Advantage such as low shrink, preservative property are strong; But weathering resistance is more weak, so everybody has done a large amount of work to the modified epoxy anti-corrosion primer, and sophisticated product has been arranged; As epoxy zinc-enriched paint the most widely in the market; But also exist function outstanding, need disadvantage, lack on the market that some are energy-conservation, aseptic production efficiently through aspects such as sandblasting, metallic element consumption are big.
Summary of the invention
The object of the invention is exactly to provide in order to overcome the defective that above-mentioned prior art exists that a kind of sticking power is good, interlayer can cover the Jupocin anti-corrosion primer that the type of being coated with is strong, paint film is tough and tensile.
The object of the invention can be realized through following technical scheme:
The Jupocin anti-corrosion primer is characterized in that, the raw material of this priming paint comprises A component and B component, and the consumption of B component is the 5-15wt% of A component, and wherein, described A component comprises following composition and weight percent content:
Epoxy resin 20-50,
Phosphoric acid salt 10-30,
Auxiliary agent 1-10,
Thinner 5-20,
Solvent 15-35;
Described B component comprises following composition and weight percent content:
Solidifying agent 50-80,
Solvent 20-50.
Described epoxy resin is bisphenol A epoxide resin.
Described phosphoric acid salt is for coating zn phosphate, zinc borate, zinc molybdate, phosphagel phosphaljel zinc, aluminum borate zinc or the molybdic acid aluminium zinc of handling.
Described auxiliary agent is inorganic assistant agent or organic additive.
Described inorganic assistant agent is organo montmorillonite, silicon oxide, titanium oxide, aluminum oxide, zinc oxide, zinc-aluminium scale, iron mica scale or glass flake.
Described organic additive is a silane coupling agent.
Described thinner is an ether compound, is selected from propylene oxide propyl ether, diglycidylether, phenyl glycidyl ether, glycidyl allyl ether, epoxy propane butyl ether, glycerol epoxy resin, ethylene glycol diglycidylether or the diglycidyl ether catechol one or more.
Described solvent is pimelinketone or propyl carbinol.
Described solidifying agent is a macromolecule resin class solidifying agent, is selected from polyamide-amide tree shaped polymer, resol, modified phenolic resins or terpolycyantoamino-formaldehyde resin.
Compared with prior art, sticking power of the present invention is good, and it is strong that interlayer can cover the type of being coated with, and paint film is tough and tensile, and is shock-resistant, and convenient construction, preservative effect cycle are long, especially has excellent salt fog resistance.
Embodiment
Below in conjunction with specific embodiment the present invention is elaborated.
Embodiment 1
The Jupocin anti-corrosion primer, its prescription is as shown in table 1.
Table 1
Respectively A component and B set of dispense are made earlier by prescription in the above-mentioned table that afterwards remix is even, the consumption of B component is the 10wt% of A component, and mixing evenly is coated in the product and gets final product then.
Following table is that embodiment 1 compares with epoxy zinc rich primer salt fog performance:
Table 2 embodiment 1 and epoxy zinc rich primer salt fog performance comparison
Epoxy zinc rich primer is used in through on the steel plate of sandblast, and about average film thickness 80 μ m, theoretical consumption is at 380g, and embodiment 1 is made on the steel plate of artificial rust cleaning, and theoretical consumption is at 238g, and build also can reach 80 μ m.
Embodiment 2
The Jupocin anti-corrosion primer, its prescription is as shown in table 3.
Table 3
Respectively A component and B set of dispense are made earlier by prescription in the above-mentioned table that afterwards remix is even, the consumption of B component is the 5wt% of A component, and mixing evenly is coated in the product and gets final product then.
Following table is that embodiment 2 compares with epoxy zinc rich primer salt fog performance:
Table 4 embodiment 2 and epoxy zinc rich primer salt fog performance comparison
Epoxy zinc rich primer is used in through on the steel plate of sandblast, and about average film thickness 80 μ m, theoretical consumption is at 380g, and embodiment 2 is made on the steel plate of artificial rust cleaning, and theoretical consumption is at 230g, and build also can reach 80 μ m.
Embodiment 3
The Jupocin anti-corrosion primer, its prescription is as shown in table 5.
Table 5
Respectively A component and B set of dispense are made earlier by prescription in the above-mentioned table that afterwards remix is even, the consumption of B component is the 15wt% of A component, and mixing evenly is coated in the product and gets final product then.
Following table is that embodiment 3 compares with epoxy zinc rich primer salt fog performance:
Table 6 embodiment 3 and epoxy zinc rich primer salt fog performance comparison
Epoxy zinc rich primer is used in through on the steel plate of sandblast, and about average film thickness 80 μ m, theoretical consumption is at 380g, and embodiment 3 is made on the steel plate of artificial rust cleaning, and theoretical consumption is at 234g, and build also can reach 80 μ m.
Embodiment 4
The Jupocin anti-corrosion primer; It is characterized in that; The raw material of this priming paint comprises A component and B component; The consumption of B component is the 5wt% of A component, and wherein, the A component comprises following composition and content: bisphenol A epoxide resin 20kg, the zn phosphate 30kg that coat to handle, organo montmorillonite 10kg as auxiliary agent, diglycidylether 5kg as thinner, 15kg pimelinketone as solvent; The B component comprises following composition and content: 80kg polyamide-amide tree shaped polymer is as solidifying agent, and the 20kg pimelinketone is as solvent.
Respectively A component and B set of dispense are made earlier by above-mentioned prescription that afterwards remix is even, promptly obtain the Jupocin anti-corrosion primer, be coated in the product and get final product.
Embodiment 5
The Jupocin anti-corrosion primer; It is characterized in that; The raw material of this priming paint comprises A component and B component; The consumption of B component is the 10wt% of A component, and wherein, the A component comprises following composition and content: bisphenol A epoxide resin 50kg, the aluminum borate zinc 10kg that coat to handle, zinc-aluminium scale 1kg as the mixture 20kg of auxiliary agent, ethylene glycol diglycidylether and glycerol epoxy resin as thinner, 19kg pimelinketone as solvent; The B component comprises following composition and content: 70kg resol is as solidifying agent, and the 30kg pimelinketone is as solvent.
Respectively A component and B set of dispense are made earlier by above-mentioned prescription that afterwards remix is even, promptly obtain the Jupocin anti-corrosion primer, be coated in the product and get final product.
Embodiment 6
The Jupocin anti-corrosion primer; It is characterized in that; The raw material of this priming paint comprises A component and B component; The consumption of B component is the 15wt% of A component, and wherein, the A component comprises following composition and content: bisphenol A epoxide resin 30kg, the molybdic acid aluminium zinc 20kg that coat to handle, silane coupling agent 5kg as the mixture 10kg of auxiliary agent, ethylene glycol diglycidylether and glycerol epoxy resin as thinner, 35kg propyl carbinol as solvent; The B component comprises following composition and content: the 60kg terpolycyantoamino-formaldehyde resin is as solidifying agent, and the 40kg propyl carbinol is as solvent.
Respectively A component and B set of dispense are made earlier by above-mentioned prescription that afterwards remix is even, promptly obtain the Jupocin anti-corrosion primer, be coated in product surface and get final product.
Claims (9)
1. a Jupocin anti-corrosion primer is characterized in that, the raw material of this priming paint comprises A component and B component, and the consumption of B component is the 5-15wt% of A component, and wherein, described A component comprises following composition and weight percent content:
Epoxy resin 20-50,
Phosphoric acid salt 10-30,
Auxiliary agent 1-10,
Thinner 5-20,
Solvent 15-35;
Described B component comprises following composition and weight percent content:
Solidifying agent 50-80,
Solvent 20-50.
2. a kind of Jupocin anti-corrosion primer according to claim 1 is characterized in that described epoxy resin is bisphenol A epoxide resin.
3. a kind of Jupocin anti-corrosion primer according to claim 1 is characterized in that, described phosphoric acid salt is for coating zn phosphate, zinc borate, zinc molybdate, phosphagel phosphaljel zinc, aluminum borate zinc or the molybdic acid aluminium zinc of handling.
4. a kind of Jupocin anti-corrosion primer according to claim 1 is characterized in that described auxiliary agent is inorganic assistant agent or organic additive.
5. a kind of Jupocin anti-corrosion primer according to claim 4 is characterized in that, described inorganic assistant agent is organo montmorillonite, silicon oxide, titanium oxide, aluminum oxide, zinc oxide, zinc-aluminium scale, iron mica scale or glass flake.
6. a kind of Jupocin anti-corrosion primer according to claim 4 is characterized in that described organic additive is a silane coupling agent.
7. a kind of Jupocin anti-corrosion primer according to claim 1; It is characterized in that; Described thinner is an ether compound, is selected from propylene oxide propyl ether, diglycidylether, phenyl glycidyl ether, glycidyl allyl ether, epoxy propane butyl ether, glycerol epoxy resin, ethylene glycol diglycidylether or the diglycidyl ether catechol one or more.
8. a kind of Jupocin anti-corrosion primer according to claim 1 is characterized in that described solvent is pimelinketone or propyl carbinol.
9. a kind of Jupocin anti-corrosion primer according to claim 1 is characterized in that described solidifying agent is a macromolecule resin class solidifying agent, is selected from polyamide-amide tree shaped polymer, resol, modified phenolic resins or terpolycyantoamino-formaldehyde resin.