CN102513688A - Keyhole repairing welding method for friction stir welding of thick plate aluminum alloy - Google Patents
Keyhole repairing welding method for friction stir welding of thick plate aluminum alloy Download PDFInfo
- Publication number
- CN102513688A CN102513688A CN2011103738911A CN201110373891A CN102513688A CN 102513688 A CN102513688 A CN 102513688A CN 2011103738911 A CN2011103738911 A CN 2011103738911A CN 201110373891 A CN201110373891 A CN 201110373891A CN 102513688 A CN102513688 A CN 102513688A
- Authority
- CN
- China
- Prior art keywords
- keyhole
- friction stir
- aluminum alloy
- welding
- stir welding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a keyhole repairing welding method for friction stir welding of a thick plate aluminum alloy. The method is characterized by comprising the following steps of: filling a filling plug which is made of the same material as a mother plate into a keyhole position, wherein the shape and size of the filling plug are matched with those of the keyhole; and after filling, performing secondary repairing welding with a friction stir welding process. Due to the adoption of the method disclosed by the invention, the problem of keyholes formed on the thick plate aluminum alloy in a friction stir welding process is solved by using the conventional conditions, the product rejection rate can be lowered greatly, and the tendency of cracks generated by melting repairing adopted for an aluminum alloy which can be thermally treated and strengthened can be eliminated effectively.
Description
Technical field
The present invention relates to a kind of thick aluminum alloy plate friction stir welding keyhole method for repairing and mending.
Background technology
In the two-sided friction stir welding welding process of thick aluminum alloy plate, often stay keyhole at the workpiece position while welding behind the involuntary stoppage, after finishing, the product welding needs to eliminate keyhole.Present method is to preset end tab before the aluminum alloy section agitating friction welding, puts the keyhole problem though solved the receipts welding position to a certain extent, presets that unexpected the parking stays the keyhole problem in the complicated and unresolved welding process of the method for end tab.Therefore, seek a kind of new be used for aluminum alloy stirring friction welding keyhole method for repairing and mending to reduce product rejection rate with enhance productivity most important.
Summary of the invention
The purpose of this invention is to provide a kind of thick aluminum alloy plate friction stir welding keyhole repairing welding method that is used for; Solve thick aluminum alloy plate and adopted the keyhole problem that produces in the friction stir welding welding process; Can reduce product rejection rate greatly on the one hand, can effectively solve heat-treatable strengthened aluminium alloy melting welding on the other hand and block up the tendency of welding and cracking.
For realizing above-mentioned purpose; The present invention provides a kind of thick aluminum alloy plate friction stir welding keyhole repairing welding method; It is characterized in that: dose in the keyhole position with the filling of mother metal homogeneity and block up, its shape is complementary with size and keyhole, selects for use friction stir welding technology to carry out the secondary repairing after cramming again and welds.
Friction stir welding technology: rotating speed 1200-600 commentaries on classics/min; Weld fast 1000-200mm/min.
Through method of the present invention; Utilize existing condition to solve thick aluminum alloy plate and adopt the keyhole problem that produces in the friction stir welding welding process; On the one hand can reduce product rejection rate greatly, can effectively solve heat-treatable strengthened aluminium alloy on the other hand and adopt melting to repair and the tendency that cracks.
Description of drawings
Fig. 1 is that the present invention welds the keyhole sketch map;
Fig. 2 is that aluminium alloy is filled bridging structure sketch map;
Fig. 3 is a sketch map after the repair by welding.
The specific embodiment
Embodiment 1
With reference to Fig. 1, Fig. 2, Fig. 3, keyhole 2 appears in 10mm slab parts 1 welding process and after, dose with the filling of mother metal homogeneity stifledly 4 in the keyhole position, its shape is complementary with size and keyhole, selects rotating speed 1200 commentaries on classics/min after cramming again for use; The friction stir welding soldering tip 5 that welds fast 600mm/min carries out secondary and repairs welding, the 3rd, weld seam.Through pull test analysis, tensile strength 185MPa; It is qualified that the Metallographic Analysis differential is organized.
Embodiment 2
25mm slab parts, friction stir welding technology: rotating speed 900 commentaries on classics/min; Weld fast 400mm/min.Through pull test analysis, tensile strength 175MPa; It is qualified that the Metallographic Analysis differential is organized.
Embodiment 3
35mm slab parts, friction stir welding technology: rotating speed 720 commentaries on classics/min; Weld fast 180mm/min.Through pull test analysis, tensile strength 170MPa; It is qualified that the Metallographic Analysis differential is organized.
Claims (2)
1. thick aluminum alloy plate friction stir welding keyhole repairing welding method is characterized in that: dose with the filling of mother metal homogeneity stifledly in the keyhole position, its shape is complementary with size and keyhole, selects for use friction stir welding technology to carry out secondary after cramming again and repairs welding.
2. thick aluminum alloy plate friction stir welding keyhole repairing welding method according to claim 1 is characterized in that friction stir welding technology: rotating speed 1200-600 commentaries on classics/min; Weld fast 1000-200mm/min.