CN102260397B - Transparent chlorinated polyethylene thermoplastic material - Google Patents
Transparent chlorinated polyethylene thermoplastic material Download PDFInfo
- Publication number
- CN102260397B CN102260397B CN 201110195578 CN201110195578A CN102260397B CN 102260397 B CN102260397 B CN 102260397B CN 201110195578 CN201110195578 CN 201110195578 CN 201110195578 A CN201110195578 A CN 201110195578A CN 102260397 B CN102260397 B CN 102260397B
- Authority
- CN
- China
- Prior art keywords
- low pressure
- chlorination
- pressure polyethylene
- polyethylene
- chlorinated polyethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to the technical field of plastic products, in particular to a transparent chlorinated polyethylene thermoplastic material. The technical scheme is that: the transparent chlorinated polyethylene thermoplastic material consists of 80 to 95 mass percent of chloroethylene polymer and 5 to 20 mass percent of chlorinated polyethylene, wherein the chlorinated polyethylene consists of two kinds of high density chlorinated polyethylene B1 and B2 with different parameters; the high density chlorinated polyethylene B1 accounts for 2.5 to 10 percent of the total mass of the material, and has the chlorine content of 37-42 percent, the residual value of 0-30 percent and the swell value of 10-70 percent; and the high density chlorinated polyethylene B2 accounts for 2.5 to 10 percent of the total mass of the material, and has the chlorine content of 37-42 percent, the residual value of 50-70 percent and the swell value of 1-2 percent. The chlorinated polyethylene has simple components; the preparation method is simple, convenient and low in cost; and the thermoplastic material prepared from the chlorinated polyethylene has good toughness and transparency and good light fastness and weather change resistance.
Description
Technical field
The present invention relates to the plastic products technology field, be specifically related to transparent chlorinated polyethylene thermoplastic material.
Background technology
Existing vinyl chloride-base polymer is to the poor stability of light and heat, more than 100 ℃ or through long-time exposure in sunshine, will decompose and produce hydrogenchloride, and further autocatalytically decomposed, and causes variable color, and physical and mechanical properties also descends rapidly.
Summary of the invention
For defects, the invention relates to take vinyl chloride-base polymer as the basis, produce thermoplastic material transparent, easy processing by adding a kind of specific chlorinatedpolyethylene, this thermoplastic material has good wilfulness and good fast light weather variation performance simultaneously.
The present invention is achieved by the following technical solutions:
Transparent chlorinated polyethylene thermoplastic material forms by accounting for vinyl chloride-base polymer that total mass per-cent is 80-95% and the chlorinatedpolyethylene of 5-20%: described chlorinatedpolyethylene is comprised of chlorination low pressure polyethylene B1 and the B2 of two kinds of different Parameter Conditions; Wherein: the per-cent that chlorination low pressure polyethylene B1 accounts for total mass is 2.5-10%, the cl content of chlorination low pressure polyethylene B1 is that 37%-42%, residual value 0-30%, swell value are 10%-70%, chlorination low pressure polyethylene B2 accounts for the 2.5-10% of total mass, and the cl content of chlorination low pressure polyethylene B2 is 37%-42%, residual value 50-70%, swell value 1-2%;
For better technique effect, also comprise following preferred version:
The vinyl chloride-base polymer weight percent is 86-92%; The weight ratio of chlorination low pressure polyethylene B1 is 4-7%, and cl content is 38%-40%, residual value 0-25%, swell value 20%-50%; Chlorination low pressure polyethylene B2 weight percent is 4-7%, and cl content is 38%-41%, residual 50-60%, swell value 1%.
The preparation method of chlorination low pressure polyethylene B1 is with density 0.940-0.955g/cm
3, melting index MFI190/5 is that the low pressure polyethylene of 0.1-5g/10min is to pass into chlorine reaction in the 10%-35% hydrochloric acid soln to make in aqeous suspension or in concentration, wherein chlorination begins temperature 50-100 ℃, the chlorination end temp is 120-130 ℃; The preparation method of chlorination low pressure polyethylene B2 is to be 0.955-0.965g/c m with density
3, melting index MFI190/5 is the low pressure polyethylene of 20-65g/10min, be in the hydrochloric acid solution of 10%-35% at aqeous suspension or in concentration, add account for the silicone oil of liquid mass than the silicic acid of 0-2% and 0-1% after, passing into chlorine reaction makes, wherein to begin temperature be 50-100 in chlorination, and the chlorination end temp is 110-120 ℃.
Low pressure polyethylene melting index MFI190/5 among the chlorination low pressure polyethylene B1 preparation method is 0.3-0.35g/10min, and chlorination begins temperature 70-90 ℃; Low pressure polyethylene melting index MFI190/5 among the described chlorination low pressure polyethylene B2 preparation method is 40-55g/10min, and chlorination begins temperature 70-90 ℃.
Be not less than 100 ℃, be not higher than under the temperature of its fusing point preroasting 5-300 minute before the raw material low pressure polyethylene chlorination of chlorination low pressure polyethylene B1 or B2.
The polymkeric substance that the preferred K value of vinyl chloride-base polymer is 55-65.
Chlorinatedpolyethylene among the present invention forms simple, and the preparation method is simple and convenient, with low cost, utilizes its synthetic thermoplastic material to have good toughness, transparency and good fast light weather and changes performance.
Depending on the content of its chlorination low pressure polyethylene, can be processed into other type spares such as section bar, film, casting casting die.Because its particle is thin and evenly, be well suited for to adopt and be dry mixed forming technique and process, need not to add elasticizer, only need to add as requested, help to enhance the transparency, strengthen processing characteristics and resistance to deterioration.
Embodiment
Embodiment 1
A kind of transparent chlorinated polyethylene thermoplastic material is that to be 55 vinyl chloride-base polymer form with 20% chlorinatedpolyethylene for 80% K value by accounting for total mass per-cent: chlorinatedpolyethylene is by two kinds of different Parameter Conditions
Chlorination low pressure polyethylene B1 and B2 form; Wherein: the per-cent that chlorination low pressure polyethylene B1 accounts for total mass is 10%, the cl content of chlorination low pressure polyethylene B1 is 37%, residual value 0, swell value are 10%, chlorination low pressure polyethylene B2 accounts for 10% of total mass, and the cl content of chlorination low pressure polyethylene B2 is 37%, residual value 50%, swell value 1%.
Embodiment 2
A kind of transparent chlorinated polyethylene thermoplastic material, be that to be 65 vinyl chloride-base polymer form with 5% chlorinatedpolyethylene for 95% K value by accounting for total mass per-cent: described chlorinatedpolyethylene is comprised of chlorination low pressure polyethylene B1 and the B2 of two kinds of different Parameter Conditions; Wherein: the per-cent that chlorination low pressure polyethylene B1 accounts for total mass is 2.5%, the cl content of chlorination low pressure polyethylene B1 is 42%, residual value 30%, swell value are 70%, chlorination low pressure polyethylene B2 accounts for 2.5% of total mass, and the cl content of chlorination low pressure polyethylene B2 is 42%, residual value 70%, swell value 2%.
Embodiment 3
A kind of transparent chlorinated polyethylene thermoplastic material, be that to be 60 vinyl chloride-base polymer form with 12.5% chlorinatedpolyethylene for 87.5% K value by accounting for total mass per-cent: described chlorinatedpolyethylene is comprised of chlorination low pressure polyethylene B1 and the B2 of two kinds of different Parameter Conditions; Wherein: the per-cent that chlorination low pressure polyethylene B1 accounts for total mass is 6%, the cl content of chlorination low pressure polyethylene B1 is 40%, residual value 15%, swell value are 40%, chlorination low pressure polyethylene B2 accounts for 6.5% of total mass, and the cl content of chlorination low pressure polyethylene B2 is 40%, residual value 60%, swell value 1.5%.
Embodiment 4
A kind of transparent chlorinated polyethylene thermoplastic material, be that to be 63 vinyl chloride-base polymer form with 14% chlorinatedpolyethylene for 86% K value by accounting for total mass per-cent: described chlorinatedpolyethylene is comprised of chlorination low pressure polyethylene B1 and the B2 of two kinds of different Parameter Conditions; Wherein: chlorination low pressure polyethylene B1 accounts for total mass
Per-cent is 6%, and the cl content of chlorination low pressure polyethylene B1 is 40%, residual value 25%, swell value are 20%, and chlorination low pressure polyethylene B2 accounts for total mass 8%, and the cl content of chlorination low pressure polyethylene B2 is 41%, residual value 60%, swell value 1%.
Embodiment 5
A kind of transparent chlorinated polyethylene thermoplastic material, be that to be 58 vinyl chloride-base polymer form with 8% chlorinatedpolyethylene for 92% K value by accounting for total mass per-cent: described chlorinatedpolyethylene is comprised of chlorination low pressure polyethylene B1 and the B2 of two kinds of different Parameter Conditions; Wherein: the per-cent that chlorination low pressure polyethylene B1 accounts for total mass is 4%, the cl content of chlorination low pressure polyethylene B1 is 38%, residual value 1%, swell value are 50%, chlorination low pressure polyethylene B2 accounts for total mass 4%, and the cl content of chlorination low pressure polyethylene B2 is 38%, residual value 50%, swell value 1%.
Embodiment 6
A kind of transparent chlorinated polyethylene thermoplastic material, on the basis of embodiment 1, wherein the preparation method of chlorination low pressure polyethylene B1 is with density 0.940g/cm
3, melting index MFI190/5 is that the low pressure polyethylene of 0.1g/10min is to pass into chlorine reaction in 10% hydrochloric acid soln to make in aqeous suspension or in concentration, the amount of hydrochloric acid medium be institute's input low pressure polyethylene amount 3-30 doubly.Wherein chlorination begins temperature 50 C, and the chlorination end temp is 120 ℃; The preparation method of chlorination low pressure polyethylene B2 is to be 0.955g/c m with density
3, melting index MFI190/5 is the low pressure polyethylene of 20g/10min, at aqeous suspension or in concentration is 10% hydrochloric acid solution, passes into chlorine reaction and makes, wherein to begin temperature be 50 ℃ in chlorination, the chlorination end temp is 110 ℃.
Embodiment 7
A kind of transparent chlorinated polyethylene thermoplastic material, on the basis of embodiment 2, wherein the preparation method of chlorination low pressure polyethylene B1 is with density 0.955g/cm
3, melting index MFI190/5 be the low pressure polyethylene of 5g/10min in aqeous suspension or in concentration 35% hydrochloric acid soln, pass into chlorine reaction and make, chlorine wherein
Melt 100 ℃ of beginning temperature, the chlorination end temp is 130 ℃; The preparation method of chlorination low pressure polyethylene B2 is to be 0.965g/c m with density
3, melting index MFI190/5 is the low pressure polyethylene of 65g/10min, at aqeous suspension or in concentration is 35% hydrochloric acid solution, add account for the silicone oil of liquid mass than 2% silicic acid and 1% after, pass into chlorine reaction and make, wherein to begin temperature be 100 in chlorination, and the chlorination end temp is 120 ℃.
Embodiment 8
A kind of transparent chlorinated polyethylene thermoplastic material, on the basis of embodiment 3, the preparation method of chlorination low pressure polyethylene B1 is with density 0.950g/cm
3, melting index MFI190/5 is that the low pressure polyethylene of 2.5g/10min was 100 ℃ of preroastings 300 minutes
, thenIn aqeous suspension or in concentration be to pass into chlorine reaction in 22.5% hydrochloric acid soln to make, wherein chlorination begins 75 ℃ of temperature, and the chlorination end temp is 125 ℃; The preparation method of described chlorination low pressure polyethylene B2 is to be 0.960g/c m with density
3, melting index MFI190/5 is that the low pressure polyethylene of 40g/10min was 110 ℃ of preroastings 200 minutes, then at aqeous suspension or in concentration is 22.5% hydrochloric acid solution, add account for the silicone oil of liquid mass than 1% silicic acid and 0.5% after, passing into chlorine reaction makes, wherein to begin temperature be 75 in chlorination, and the chlorination end temp is 115 ℃.
Embodiment 9
A kind of transparent chlorinated polyethylene thermoplastic material, on the basis of embodiment 4, the preparation method of chlorination low pressure polyethylene B1 is with density 0.945g/cm
3, melting index MFI190/5 is that the low pressure polyethylene of 0.3g/10min was 115 ℃ of preroastings 150 minutes, then be to pass into chlorine reaction in 20% hydrochloric acid soln to make in aqeous suspension or in concentration, wherein chlorination begins temperature 70 C, and the chlorination end temp is 123 ℃; The preparation method of described chlorination low pressure polyethylene B2 is to be 0.958g/c m with density
3, melting index MFI190/5 is that the low pressure polyethylene of 55g/10min was 120 ℃ of preroastings 100 minutes, then at aqeous suspension or in concentration is 22% hydrochloric acid solution, add account for the silicone oil of liquid mass than 1.5% silicic acid and 0.6% after, passing into chlorine reaction makes, wherein to begin temperature be 70 in chlorination, and the chlorination end temp is 116 ℃.
Embodiment 10
A kind of transparent chlorinated polyethylene thermoplastic material, on the basis of embodiment 5, the preparation method of chlorination low pressure polyethylene B1 is with density 0.952g/cm
3, melting index MFI190/5 is that the low pressure polyethylene of 0.35g/10min was 120 ℃ of preroastings 80 minutes, then be to pass into chlorine reaction in 15% hydrochloric acid soln to make in aqeous suspension or in concentration, wherein chlorination begins 90 ℃ of temperature, and the chlorination end temp is 128 ℃; The preparation method of described chlorination low pressure polyethylene B2 is to be 0.962g/c m with density
3, melting index MFI190/5 is that the low pressure polyethylene of 40g/10min was 125 ℃ of preroastings 5 minutes, then at aqeous suspension or in concentration is 16% hydrochloric acid solution, add account for the silicone oil of liquid mass than 1.2% silicic acid and 0.4% after, passing into chlorine reaction makes, wherein to begin temperature be 90 in chlorination, and the chlorination end temp is 118 ℃.
Above embodiment only is part preferred version of the present invention; within protection scope of the present invention; those skilled in the art are reassembled into above-mentioned each technical characterictic other technical scheme fully; perhaps select other identical or close methods for preparing chlorinatedpolyethylene; but realize the same same technical problem that solves with this programme; realize identical effect, therefore identical with this programme substance, all fall within the protection domain of this programme.
Claims (6)
1. transparent chlorinated polyethylene thermoplastic material, it is characterized in that, form by accounting for vinyl chloride-base polymer that total mass per-cent is 80-95% and the chlorinatedpolyethylene of 5-20%: described chlorinatedpolyethylene is comprised of chlorination low pressure polyethylene B1 and the B2 of two kinds of different Parameter Conditions; Wherein: the per-cent that chlorination low pressure polyethylene B1 accounts for total mass is 2.5-10%, the cl content of chlorination low pressure polyethylene B1 is that 37%-42%, residual value 0-30%, swell value are 10%-70%, chlorination low pressure polyethylene B2 accounts for the 2.5-10% of total mass, and the cl content of chlorination low pressure polyethylene B2 is 37%-42%, residual value 50-70%, swell value 1-2%.
2. transparent chlorinated polyethylene thermoplastic material according to claim 1, it is characterized in that: described vinyl chloride-base polymer mass ratio is 86-92%; The weight ratio of chlorination low pressure polyethylene B1 is 4-7%, and cl content is 38%-40%, residual value 0-25%, swell value 20%-50%; Chlorination low pressure polyethylene B2 weight ratio is 4-7%, and cl content is 38%-41%, residual 50-60%, swell value 1%.
3. transparent chlorinated polyethylene thermoplastic material according to claim 2, it is characterized in that: the preparation method of described chlorination low pressure polyethylene B1 is with density 0.940-0.955g/cm
3, melting index MFI190/5 is that the low pressure polyethylene of 0.1-5g/10min is to pass into chlorine reaction in the 10%-35% hydrochloric acid soln to make in aqeous suspension or in concentration, wherein chlorination begins temperature 50-100 ℃, the chlorination end temp is 120-130 ℃; The preparation method of described chlorination low pressure polyethylene B2 is to be 0.955-0.965g/c m with density
3, melting index MFI190/5 is the low pressure polyethylene of 20-65g/10min, be in the hydrochloric acid solution of 10%-35% at aqeous suspension or in concentration, add account for the silicone oil of liquid mass than the silicic acid of 0-2% and 0-1% after, passing into chlorine reaction makes, wherein to begin temperature be 50-100 in chlorination, and the chlorination end temp is 110-120 ℃.
4. transparent chlorinated polyethylene thermoplastic material according to claim 3, it is characterized in that: the low pressure polyethylene melting index MFI190/5 among the described chlorination low pressure polyethylene B1 preparation method is 0.3-0.35g/10min, and chlorination begins temperature 70-90 ℃; Low pressure polyethylene melting index MFI190/5 among the described chlorination low pressure polyethylene B2 preparation method is 40-55g/10min.
5. it is characterized in that according to claim 3 or 4 described transparent chlorinated polyethylene thermoplastic materials: be not less than 100 ℃, be not higher than under the temperature of its fusing point preroasting 5-300 minute before the raw material low pressure polyethylene chlorination of described chlorination low pressure polyethylene B1 or B2.
6. according to the described transparent chlorinated polyethylene thermoplastic material of the arbitrary claim of 1-4, it is characterized in that: the K value of vinyl chloride-base polymer is 55-65.