CN102140249A - Method for quickly preparing silver/polypyrrole composite sol by adopting microwave method - Google Patents
Method for quickly preparing silver/polypyrrole composite sol by adopting microwave method Download PDFInfo
- Publication number
- CN102140249A CN102140249A CN 201010607616 CN201010607616A CN102140249A CN 102140249 A CN102140249 A CN 102140249A CN 201010607616 CN201010607616 CN 201010607616 CN 201010607616 A CN201010607616 A CN 201010607616A CN 102140249 A CN102140249 A CN 102140249A
- Authority
- CN
- China
- Prior art keywords
- silver
- polypyrrole
- complex sol
- preparing silver
- silver nitrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method for quickly preparing silver/polypyrrole composite sol. An oxidation-reduction reaction between a silver salt and a pyrrole monomer is a simple and effective method for preparing a silver/polypyrrole composite material, but has the defect of low dynamic reaction speed. In the invention, a method for adding a microwave external field irradiation solution into a reaction system is provided, so that the reaction speed is effectively increased, and the silver/polypyrrole composite sol is formed within 15-270 minutes.
Description
Technical field
The present invention relates to a kind of silver/polypyrrole complex sol preparation methods, be specifically related to utilize microwave technology to improve the method for the kinetic reaction speed between silver salt and the pyrrole monomer.
Background technology
Precious metal/conducting polymer composite is an important branch of metal/polymer composite material, all has important use at aspects such as biology, storage, electronics and catalysis.Utilizing the redox reaction between precious metal and the monomer is a kind of simple and effective method for preparing precious metal/conductive polymer composite, at present, utilize this method to prepare matrix materials such as comprising gold/polypyrrole, gold/polyaniline, silver/polypyrrole and silver/polyaniline.Yet, when preparation silver/Pt/Polypyrrole composite material, though find that being reflected on the thermodynamics between silver ions and the pyrrole monomer is feasible, but very slow [the Matthew C.Henry of kinetics speed that should react, Chen-Chan Hsueh, Brian P.Timko, Michael S.Freund, Reaction of pyrroleand chlorauric acid,: a new route to composite colloids, J.Electrochem.Soc.148 (11) (2001) D155-D161.], for example, do not having under the condition of illumination, forming silver/polypyrrole film in 0.5M Silver Nitrate+0.5M pyrroles's aqueous solution needs 48 hours [M.A.Breimer, G.Yevgeny, S.Sy, O.A.Sadik, Incorporation ofmetal nanoparticles in photopolymerized organic conducting polymers:A mechanistic insight, Nano Lett.1 (2001) 305-308.].Though ultraviolet light irradiation can shorten the required time of this process to a certain extent, still needs a few hours, and relevant other effectively improves the rarely seen report of method of this reaction kinetics speed.
Summary of the invention
The object of the invention is intended to propose a kind of method that simply and effectively prepares silver/polypyrrole complex sol fast, so that effectively solve the kinetics speed issue in the matrix material forming process.
Preparation method of the present invention comprises the steps:
(1) respectively Silver Nitrate and pyrrole monomer are dissolved in N, among the N '-dimethyl formamide (or ethylene glycol), mixed nitrate silver and pyrrole monomer solution then; Or successively Silver Nitrate and pyrrole monomer are dissolved in N, among the N '-dimethyl formamide (or ethylene glycol), to form the mixing solutions of Silver Nitrate and pyrrole monomer.The concentration of Silver Nitrate and pyrrole monomer is controlled at 0.01-2.0M;
(2) power range with microwave is set in 200-900W, and temperature is set in 30-150 ℃, and time set is at 15 minutes-270 minutes, the mixing solutions of step (1) is carried out microwave exposure, until the silver/polypyrrole complex sol that forms homogeneous;
Organic solvent N, N '-dimethyl formamide, or all have good solubility for Silver Nitrate and pyrrole monomer in the ethylene glycol, simultaneously microwave is had good absorption function, therefore help the uniform contact of two kinds of reactants, thereby improve the homogeneity and the speed of response of product.This microwave method has advantages such as simple to operate, that speed of response is fast.
Description of drawings
Fig. 1 the inventive method is utilized the UV-Vis absorption spectrum of the Ag/PPy complex sol of microwave technology preparation, (A) in DMF solution; (B) in ethylene glycol solution.
Embodiment
Embodiment 1
As above-mentioned step, take by weighing the Silver Nitrate of 300mg and the pyrrole monomer of 0.55ml, be dissolved in respectively among the DMF of 40ml, then two kinds of solution are mixedly configured into Silver Nitrate+pyrroles's mixing solutions.After stirring, this mixing solutions being placed microwave device, is 500W at power, and temperature is under 70 ℃ of conditions, and microwave exposure obtains the Ag/PPy complex sol after 20 minutes, and its UV-Vis absorption spectrum figure is seen Figure 1A.
Embodiment 2
As above-mentioned step, take by weighing the Silver Nitrate of 300mg and the pyrrole monomer of 0.55ml, be dissolved in respectively among the DMF of 40ml, then two kinds of solution are mixedly configured into Silver Nitrate+pyrroles's mixing solutions.After stirring, this mixing solutions being placed microwave device, is 600W at power, and temperature is under 70 ℃ of conditions, and microwave exposure obtains the Ag/PPy complex sol after 30 minutes, and its UV-Vis absorption spectrum figure is seen Figure 1B.
Embodiment 3
As above-mentioned step, take by weighing the Silver Nitrate of 1.36g and the pyrrole monomer of 5.7ml, be dissolved in respectively among the DMF of 40ml, then two kinds of solution are mixedly configured into Silver Nitrate+pyrroles's mixing solutions.After stirring, this mixing solutions being placed microwave device, is 900W at power, and temperature is under 80 ℃ of conditions, and microwave exposure obtains the Ag/PPy complex sol after 5 minutes;
Embodiment 4
As above-mentioned step, take by weighing the Silver Nitrate of 68mg and the pyrrole monomer of 0.29ml, be dissolved in respectively in the ethylene glycol of 20ml, then two kinds of solution are mixedly configured into Silver Nitrate+pyrroles's mixing solutions.After stirring, this mixing solutions being placed microwave device, is 900W at power, and temperature is under 90 ℃ of conditions, and microwave exposure obtains the Ag/PPy complex sol after 60 minutes.
Embodiment 5
As above-mentioned step, take by weighing the Silver Nitrate of 680g and the pyrrole monomer of 2.8ml, be dissolved in respectively in the ethylene glycol of 20ml, then two kinds of solution are mixedly configured into Silver Nitrate+pyrroles's mixing solutions.After stirring, this mixing solutions being placed microwave device, is 900W at power, and temperature is under 30 conditions, and microwave exposure obtains the Ag/PPy complex sol after 60 minutes.
Claims (5)
1. a method for preparing silver/Pt/Polypyrrole composite material fast is characterized in that it comprises the steps:
(1) respectively Silver Nitrate and pyrrole monomer are dissolved in in a kind of organic solvent;
(2) above-mentioned silver nitrate solution and pyrroles's solution are mixed;
(3) mixing solutions with step (2) carries out microwave exposure, until the silver/polypyrrole complex sol that forms homogeneous.
2. the quick method for preparing silver/polypyrrole complex sol according to claim 1, organic solvent is N, N '-dimethyl formamide, or a kind of in the ethylene glycol.
3. the quick method for preparing silver/polypyrrole complex sol according to claim 1, the concentration range that it is characterized in that this Silver Nitrate is at 0.01-2.0M.
4. the quick method for preparing silver/polypyrrole complex sol according to claim 1, the preferable range of concentration that it is characterized in that this pyrroles is at 0.01-2.0M.
5. the quick method for preparing silver/polypyrrole complex sol according to claim 1, the power range that it is characterized in that microwave is at 200-900W, and temperature range is set in 30-150 ℃, and time set was at 15-270 minute.