CA2780883C - Water purification cartridge using zirconium ion-exchange sorbents - Google Patents

Abstract

A cartridge having at least one layer containing sodium zirconium phosphate and at least one layer containing a combination of acid zirconium phosphate and alkaline hydrous zirconium oxide is described. Methods of using the cartridge for water purification are also described.

Description

WATER PURIFICATION CARTRIDGE USING ZIRCONIUM
ION-EXCHANGE SORBENTS
FIELD OF THE INVENTION
[0001] The present invention relates to water purification. More particularly, the present invention relates to ion-exchange materials and in particular, to zirconium ion-exchange materials that are useful in water purification.
BACKGROUND OF THE INVENTION

[0002] Typically, water from municipal water supplies, must be purified or treated, in order to reduce the level of contaminants present in the water to levels that are acceptable for consumption, or other human use. Contaminants which may be present in municipal tap water include, for example, toxic ionic contaminants, organic compounds, microbes, mold, and/or algae. The required standard of water quality varies depending upon application and may be regulated by various government agencies and trade organizations. Drinking water, for example, must meet the requirements of the National Secondary Drinking Water Regulations, issued by the U.S. Environmental Protection Agency (EPA). The water quality for water used in hemodialysis must meet standards set by the Association for the Advancement of Medical Instrumentation (AAMI) (and subsequently approved by the American National Standards Institute [ANSI]) (ANSI-AAMI water standards). The ANSI-AAMI water standards far exceed the standards required for drinking water. This is because, during dialysis, a large amount of water is almost directly in contact with the patient's blood (separated by only the thin semipermeable membrane of the dialyzer). As such, it is very important that contaminants which are typically present in tap water, be removed prior to use in dialysis.

[0003]
Sorption processes are generally ideal for removing contaminants from water.
Sorbent processes are operationally simple, require virtually no start-up time, and are forgiving toward fluctuations in feed compositions.

[0004]
Zirconium ion-exchange resins, and particularly, mixed bed ion-exchange resins, can provide useful sorbents for de-ionizing water and removing toxic contaminants in water.
Zirconium ion-exchange sorbents are safe and non-toxic. Zirconium resins can remove endotoxins (bacteria) and bacteria does not proliferate in zirconium ion-exchange resins, as they do in organic ion-exchange resins. The zirconium ion-exchange resins are also not vulnerable to attack by chlorine and are thermally stable so that they can be used to treat water, even at high temperatures. Zirconium ion-exchange resins provide a more economical and compact water purification system than conventional water purification systems, such as reverse osmosis (RO) systems, and organic ion-exchange resins. Zirconium ion-exchange resins can efficiently remove toxic inorganic chemicals, especially at high concentrations. Zirconium ion-exchange resins can be configured in a compact form for use in disposable water treatment devices.

[0005] In the past, zirconium ion-exchange sorbents which contain ZrP in the Na + form, for example Na+-ZrP, and HZO in the Cr form, for example HZO-Cl, could not be used effectively primarily because of the following factors:
(i) The adsorption capacity and selectivity of ZrP and HZO are affected by the form of counter ions carried by the ion-exchange materials. For example, deionization of water is not possible when ZrP is used in the Na + form (Na-ZrP) and HZO is used in the Cr form (HZO-C1-) due to the release of Na + and Cr ions by the ion-exchange reactions as follows:
Na¨ ZrP +M+(aq) ZrP +Na+(aq) (Reaction I) HZO ¨ a- +An (aq) ¨> HZO ¨ Air +o- (aq) (Reaction II) Thus, the mixing of ZrP and HZO in this case can, at most, produce the effect of water softening. The loading of the counter ions in these materials further reduces capacity for other ions and limit their use due to the selectivity of ionic adsorption. For example, HZO.Ac (where Ac- =acetate ion) has little adsorption capacity for chloride and nitrate because these anions lie below acetate in the affinity series.
(ii) Deionization of water is affected by leachable P043- from ZrP and Na from HZO; and (iii) The small particle size of Na+-ZrP and HZO-C1- results in high resistance to water flow.

[0006] Zirconium ion-exchange sorbents for purifying water, which contain only a mixture of acid zirconium phosphate (A7P) and alkaline hydrous zirconium oxide (NaHZ0), and no other zirconium ion-exchange resin, also suffer drawbacks. In conventional mixed bed ion-exchange resins, the displacement of previously adsorbed cationic contaminants (e.g. Ca2+, K , Mg21) from A7P by excessive hydrogen ions can be a problem due to the weak affinity of the contaminants that can cause a leakage problem. Also, cationic contaminants, with strong sorption affinity can displace each other after adsorption by A7P.

[0007] Accordingly, there is a need for a more effective sorbent for selective de-ionizing and removal of contaminants from water. There is also a need for sorbent that can remove the target contaminant without causing significant changes in pH or in the composition of the influent water as caused by the pH change.
SUMMARY OF THE PRESENT INVENTION

[0008] A feature of the present invention is to provide a cartridge for purifying water that avoids one or more of the above mentioned disadvantages.

[0009] Another feature of the present invention is to provide a cartridge for purifying water that can provide water having a Na content of 70 ppm or less.

[00010] Another feature of the present invention is to provide an improved ion-exchange material for purifying water that does not release Na+ ions into the water.

[00011] A further feature of the present invention is to provide a cartridge for purifying water that can provide water having a pH of about 6 to about 7.

[00012] An additional feature of the present invention is to provide a non-toxic cartridge for purifying water, that includes inorganic ion-exchange resins.

[00013] An additional feature of the present invention is to provide a cartridge for purifying water that is compact and economical.

[00014] Another feature of the present invention involves removing the organics and/or the endotoxins and/or chlorine and chloramines to meet ANSI-AAMI standards.

[00015] Additional advantages of the present invention will be set forth in part in the description that follows, and in part will be apparent from the description, or may be learned by practice of the present invention. The goals and advantages of the present invention will be realized and attained by means of the elements particularly pointed out in the appended claims.

[00016] To achieve the above noted goals and in accordance with the purposes of the present invention, as embodied and broadly described herein, the present invention provides a cartridge having a first layer having sodium zirconium phosphate (NaZrP), and a second layer having a combination of acid zirconium phosphate (AZP) and alkaline hydrous zirconium oxide (NaHZ0) in the cartridge. A layer(s) of activated carbon can be present, such as before the "first layer." The second layer can succeed the first layer. The first layer and the second layer can be separated by one or more separators, such as, filter paper. The NaZrP, the AZP, and/or the NaHZ0 can be particles having an average grain size of from about 25 microns to about 60 microns.

[00017] The cartridge can comprise a combination of AZP and NaHZ0 and can be present as a homogeneous mixture wherein the AZP and the NaHZ0 are uniformly distributed as a layer in the cartridge.
[000181 The present invention also provides a cartridge comprising a combination of AZP
and NaHZ0 in the cartridge, wherein the weight ratio of AZP to NaHZ0 can be varied.
[000191 The present invention further provides a method to purify water comprising passing water through the cartridge.
[000201 The present invention further provides a method to purify municipal water, waste water, well water, natural water, or any combination thereof.
[000211 The present invention provides a cartridge that can be used to purify water to meet ANSI-AAMI water standards for dialysis treatment or for other water purification standards.
[000221 The present invention provides a method for preparing purified fresh dialysate for dialysis comprising passing water through the cartridge, prior to conducting dialysis.
[000231 It is to be understood that both the foregoing general description and the following detailed description are exemplary only and are not restrictive of the present invention, as claimed.
BRIEF DESCRIPTION OF THE DRAWINGS
[000241 FIG. 1 is a schematic diagram of a cartridge according to various embodiments.
[00025] FIG. 2 is a schematic diagram of cartridges according to various embodiments.
[000261 FIG. 3 is a schematic diagram of a cartridge.
[000271 FIG. 4 is a table showing the purity level of effluent from a cartridge of the present invention.
[000281 FIG. 5 is a table showing the purity level of effluent from a cartridge of the present invention.

[00029] FIG. 6 is a table showing the purity level of effluent from a cartridge of the present invention.
[00030] FIG. 7 is a table showing the purity level of effluent from a cartridge of the present invention.
[00031] FIG. 8 is a table showing the purity level of effluent from a cartridge of the present invention.
DETAILED DESCRIPTION OF THE INVENTION
[00032] The present invention relates, in part, to a water purification cartridge or sorbent cartridge or a cartridge to purify substances, such as liquids, using inorganic ion-exchange material and/or sorbents. The cartridge can be used with a variety of feed waters to remove at least a portion, all, or substantially all contaminants present in the water.
The cartridge can produce a consistent, high quality water supply to meet the requirements of food, beverage, and/or health industries. The purified water can be used, for example, in cooking, drinking, hot and cold beverage production, brewing, washing and/or ice making. Water purified in accordance with the present invention can also be used in dialysis systems, as well as for medical, pharmaceutical, or industrial or residential-related purposes.
[00033] The cartridge can be a compact column that contains at least two layers of zirconium ion-exchange resins. The cartridge can purify water from a water supply, such as a municipal water supply that has a water quality that meets or even fails to meet the EPA Primary and Secondary drinking water standards at the maximum allowable contamination level (MACL).
[00034] The cartridge can be used to purify water to meet the ANSI-AAMI
requirement for purifying water used for dialysate. The cartridge of the present invention can remove Na+

and Cl- ions from a municipal water supply in order to meet the ANSI-AAMI
water quality standard for dialysate preparation. The cartridge can, for example, be used to reduce Na+ content in water to 70 ppm or less (e.g., 65 ppm to 1 ppm, 50 ppm to 5 ppm), in accordance with the ANSI-AAMI requirement. The cartridge can be used for single dialysis treatments to avoid bacterial proliferation and/or can further remove endotoxins to meet ANSI-AAMI
standards.
[00035] The cartridge can remove at least a portion of one or more of the following: toxic cations and anions, organics, chlorine, chloramine, microbes, mold, algae, silt particles, and/or colloidal matter. The cartridge can remove hardness metals, Ca2+, Mg2+, as well as excessive K+, and excessive Na, from water. The cartridge can be used to efficiently remove from municipal water other toxic inorganic contaminants, such as aluminum, fluoride, and nitrate, even when such contaminants are present at high levels. For each of these impurities, the present invention can remove some, almost all, or all of these impurities and/or contaminants.
[00036] The cartridge can comprise zirconium ion-exchange resins. The cartridge can comprise, or consist essentially of or consist of a first layer having sodium zirconium phosphate (NaZrP), and a second layer having a mixed-bed or combination of acid zirconium phosphate (AZP) and alkaline hydrous zirconium oxide (NaHZ0). The first layer can comprise, or consist essentially of, or consist of NaZrP. The second layer can comprise, or consist essentially of, or consist of AZP and NaHZO. For purposes of the present invention, sodium zirconium phosphate or NaZrP, means the Na + form of zirconium phosphate (ZrP) or acid ZrP
titrated by NaOH to a pH of from about 6.0 to about 7.4, and preferably, a pH of from about 6.5 to about 7Ø NaZrP
can have the following chemical and physical properties:
Composition: (1-1)õ (Na)(Zr02)(OH-)y(PO4)1.8-2 n 1120, or Na Wt%: 4-6; Zr02 Wt%: 34-37; Phosphate Wt%: 41-43; H20: 14-18 wt%

Ion-exchange formula: [Zr02 (OH)y (PO4)2l2- =
Structural formula: same as for AZP below except one, two, three, or more of the Hare replaced with Na+in the formula.
[00037] For purposes of the present invention, acid zirconium phosphate, or AZP, means the H+ form of zirconium phosphate. AZP can have the following chemical and physical properties:
Composition: (f14)x (Zr02) (OH)y (PO4)1.8-2.0 = n H20 Ion-exchange formula: [Zr02 (OH)y (PO4)212- = ll+x Structural formula:
po0 H20 cr POO OH H20 0 01-N
NV NV NV_0 -P
OH 0P0,W 0PO3H
-1 n wherein x for His 1.5 to 2.0, y for OH" is 05 to 0, and n for H20 and for the structural formula is 1 to 4. x, y, and n can be any decimal in these ranges and can optionally be above or below these ranges. The AZP can have a hydrogen ion content of, for example, from about 2¨ 10 mEq Wig A713, from about 4 ¨ 8 mEq H47g AZP, or from about 5 ¨ 7 mEq 11+4 AZP. The AZP can have a pH in water (1 g/100 ml) of, for example, about 0.5 ¨5, or about 1 ¨ 3, and a pH in brine (1 g/100 ml) of, for example, about 0 ¨ 5, or about 0.5 ¨ 1.5.
[00038] For purposes of the present invention, alkaline hydrous zirconium oxide, or NaHZO, means the alkaline form of hydrous zirconium oxide (ZrO(OH)2), in which the zirconium oxide is hydroxylated. NaHZ0 can have the following chemical and physical properties:

Composition: Nat x Zr02 (01-1-)y = n H20 Ion-exchange formula: Zr02 = 01-1-Structural formula:
011- ................................. Na4 0 _________ Zr 0 ____ Zr ______ 0 ____ OW ------------------------------------ Na+
wherein x for Na+ is 1, y for OI-1- is 2 to 4 and n for H20 is 4 to 6, and x, y, and n can be any decimal in these ranges and can optionally be above or below these ranges. The NaHZO can have a Na+ content Na: Zr02 (molar ratio) in a range of, for example, from about 0.5: 1.5, about 1: 1, or about 1.5 : 0.5, and/or have a hydroxyl ion content in a range of, for example, about 3 -12 mEq Off/10 g NaHZO, about 5 - 10 mEq OH-/10 g NaHZO, or about 6- 9 mEq OH-/10 g NaHZO. The NaHZO can have a pH in water (1 g/100 ml) of, for example, about 7 -14, about 9 - 12, or about 10 - 11.
[00039] The present invention, in part, is based on the following mechanisms: (1) binding by NaZrP of Ca2+, IC+, Mg; and/or toxic trace metals present in water, in exchange for release of Na; (2) binding of Nat, released into the water in (1) to ZrP, in exchange for release of Hi.; (3) binding of anionic contaminants in the water to NaHZO, in exchange for release of OH. The reactions of (2) and (3), or the ion-exchange interaction which takes place at the second or "mixed-bed" layer, can proceed as shown below:
ZrP - H+ +Na+¨> ZrP - Na+ +H+
Zr02 - Off +An- -3 Zr02 - An- +OH-H+ +0H- ¨> H20 [00040] It should be understood that the phrase "substantially all" or "almost all," as used herein, can represent an amount of about, for example, 90% - 99.9%, 95% to 99%, 96% to 99.9%, 55% - 99.9%, 60% - 80%, or 65% - 70%, by weight, based on the total amount of contaminants or impurities present.
[00041] As described in more detail below, the combination of An" and NaHZO, or the mixed-bed layer of the cartridge can efficiently and simultaneously adsorb cations and anions from water in exchange for release of H+ and OH. In contrast, when ZrP in the H+ form (i.e.
H+-ZrP) is used alone, the adsorption capacity for other metal ions in water, particularly Ca2+, Mg2+, K, and Na, is greatly reduced. It is believed that these metal ions cannot easily displace the 1-1+ ions which have a high affinity for ZrP. Also, when using the acid ZrP alone, the H+ ions are not easily displaced by other metals when the pH of water in contact with the acid ZrP bed is low. It is believed that the adsorption capacity of ZrP increases with higher pH of the water.
The affinity series of ZrP for cations can be expressed as follows:
(NH4 + >H4->Cu2 Ba2 +, Pb2+, Ag +, Cd2 +, Hg2+, Zn >Cr+3, Mn2+, Fe +2 >Ca2+
>Na+, Mg2+, K4) [00042]
Similarly, when HZO in the OH- form (i.e. HZO-OH) is used alone, the adsorption capacity for other anions in water is greatly reduced because of the high affmity of HZO for OH- ions. It is believed that the anions cannot easily displace the OH-ions due to the ion-exchange reaction. Also, when using the alkaline HZ/3 alone, the OH- ions are not easily displaced by other anions when the pH of water in contact with the alkaline HZO bed is high. It is believed that adsorption capacity of HZO increases with lower pH of the material. The affinity series of HZO for anions can be expressed as follows:
P043- >OH- >Chromate >F-, arsenate, selenate, NO3-, S042- >C1-[00043] The cartridge of the present invention can deionize water effectively. The cartridge can include a cartridge having a zirconium sorbent layer comprising ZrP in the Na+
form, followed by a separate zirconium sorbent layer comprising a blended mixture of acid zirconium phosphate, for example, H+-ZrP and alkaline hydrous zirconium oxide, for example, HZ0-0H- . The ZrP in the Na+ form can remove all of the cations in the feed water other than Na+. The ZrP in the Na+ form can remove, for example, Ca2+, Mg2+, K+, NH4, and all the other transitional and heavy metal ions by the ion exchange reaction described previously (Reaction I). The released Na+ from this layer is then removed by the H+-ZrP
in the succeeding layer that has a blended mixture of H+-ZrP and HZO-OH-. This is feasible because the OH- ion of the alkaline HZ0 tends to extract the H+ from the H+-ZrP and promote ion-exchange with the Na+ ion in water. In other words, the ion exchange reaction of Na+ in water with H+ in ZrP is promoted because of elevation of pH by the alkaline HZO. The reaction can be illustrated as follows:
H+-ZrP +Na+(aq) +0H- (aq) Na+¨ ZrP +H20 (Reaction III) The H+-ZrP can also capture any leakage of other metal ions from the previous Na+-ZrP layer in this way. The preceding layer of Na+-ZrP removes the K+, Mg2+, and Ca2+
because the affinity of H+-ZrP for these cations are very weak. Without the Na+-ZrP layer, the K+, Mg2+, and Ca2+
can displace each other in the H+-ZrP ¨containing layer causing leakage of all these metals, as described previously.
[00044] The alkaline HZ0 in the OH- form of the mixed-bed layer can remove anions in the feed water. The H+ ions of the H+-ZrP tend to extract the OH- ion from the HZO-OW and promote ion-exchange with the anions in water. In other words, the pH of water in contact with HZ0 -40H- is lowered by the H+-ZrP. The reaction can be illustrated as follows:

HZO-0H - +An- (aq) +H+(aq) 4 HZO ¨ An- +H20 (Reaction IV) 1000451 Thus, upon blending of H+-ZrP and HZO-0H, the capacity of simultaneous adsorption of both cations and anions is greatly increased because the pH of the aqueous medium in contact with the material is then close to neutral. The reaction mechanism of the mixed bed H+-ZP/HZ0-0H- layer for deionizing or desalinating water can be represented by the following expressions:
Desalination:
H+-ZrP/HZ0-0H- +Na+(aq) (aq) 4 Na+-ZrP/HZO-C1- +H20 (Reaction V) Deionization:
H+-ZrP/HZ0-0H- +M+(aq) +An- (aq) 4 M+-ZrP/HZO - Air +H20 (Reaction VI) 1000461 As shown in Reactions V and VI above, in the mixed bed layer, cations and anions can be removed simultaneously from water in exchange for release of H+
and OW ions which combine to produce water molecules regardless of ionic selectivity because the layers are not loaded with other counter ions. Chemicals derived from processing and slight dissociation of ZrP and HZO in water (e.g. phosphate from ZrP; Na + from HZO) can also be removed. For example, phosphate derived from ZrP and Na + derived from HZO, can also be removed from the water. The phosphate can be adsorbed by HZO, whereas the sodium is removed by the AZP and due to Rxn III above.
1000471 The H+-ZrP/HZ0-0H- mixed-bed layer and the Na+-ZrP layer can be used for treating or purifying water. The H+-ZrP/HZ0-0H- blended layer and the Na+-ZrP
layer are chemically stable under general conditions and do not dissociate in water to produce soluble Zr at detectable levels. Furthermore, the H+-ZrP, HZO-OH - , and the Na+-ZrP, offer little resistance to water flow as the particle size for these chemicals can be 45-90 microns (or sizes below or above this range).
[00048] The cartridge with the H+-ZrP/HZ0-0H- blended layer and the Na+-ZrP
layer, can remove toxic inorganic contaminants from water with high efficiency. For example, the cartridge can remove about 85-100 % , such as 90-100%, 92-100%, 96-100%, 98-100%, 99-100%, or 99.8-100% by weight of toxic inorganic contaminants from water, based on the total amount of toxic inorganic contaminants present. The cartridge can remove the toxic organics, endotoxins, chlorines, and/or chloramines that allow the cartridge to produce water quality that satisfies ANSI-AAMI standards for dialysis (2007, 2008, or 2009 standards).
The cartridge can purify municipal water and render the water safe for human consumption and use. The cartridge can provide a product water having a water quality that complies with the ANSI-AAMI standard for renal dialysis. Unless stated otherwise, all standards are the ones in place as of 2007, 2008, and/or 2009.
[00049] As described previously, removal of Ca2+, K+ Mg2+ by the first or NaZrP-containing layer, prevents displacement of these metals in the succeeding second layer containing the AZP/NaHZ0 combination. Consequently, leakage of these metals into the product water is prevented. Further, the cationic ion-exchange properties of the H+ form of ZrP
(i.e. AZP) when acting alone, for example, in a separate layer in a cartridge, does not readily release H+ in exchange for Na+, or other cations that may be present in tap water. When in the presence of a base, however, the base can serve to extract the H+ ions out from AZP which are then replaced by the cation adsoibed. Accordingly, when blended with NaHZO, for example, as a homogeneous mixture, the ion-exchange properties of AZP can be affected. The ability of AZP, for example, to release fl+ in exchange for other cations increases. A
combination of AZP

and NaHZO can efficiently adsorb cations from tap water. Without wishing to be bound to any theory, one possible reason may be that the OH- groups present in NaHZO, and their interaction with H+ in AZP, may be responsible for the altered ion-exchange properties.
[00050] The anionic ion-exchange properties of NaHZO, having adsorption capacities for P042-, F, S042- and other anions, can be altered when acted upon by an acidic pH, for example, a pH less than 7. In the presence of acid, the NaHZO can be alkaline in water, releasing 0H
ions in exchange for adsorption of other anions. The release of OH- ions can remove acid entities from water (CO2 gas or H+ ions) and help keep the pH of the product water in an acceptable range (e.g., pH of 6.0 to 7.4).
[00051] The combination of A71' and NaHZO can be present as a homogeneous mixture, wherein the AZP and the NaHZO are uniformly distributed or mixed amongst each other, for instance, as one or more layers, in the cartridge. The present invention also relates, in part, to combinations of AZP and NaHZO wherein the weight ratio of AZP to NaHZO can be varied. By adjusting (e.g., lowering or raising) the proportion of NaHZO, for example, the combination of AZP and NaHZO can further control the pH of the purified product water.
[00052] The NaZrP can be present in the cartridge as at least one layer.
The NaZrP can be present in at least one layer as NaZrP particles. The NaZrP particles can be present in at least one layer alone or in combination with other materials described herein. The NaZrP particles can have an average size of, for example, about 25 microns to about 60 microns.
[00053] The combination of AZP and NaHZO can be present together in the cartridge as at least one layer. The cartridge can comprise at least two layers and the cartridge can comprise at least one other layer comprising NaZrP. The combination of AZP and NaHZO
can be present in the cartridge as AZP particles and NaHZ0 particles having an average size, for example, of from about 25 microns to about 60 microns.
[00054] The NaZrP can be prepared by reacting aqueous solutions of a zirconium salt and phosphoric acid or can be prepared using a solid Zr compound(s) with phosphoric acid(s). The aqueous solutions of a zirconium salt and phosphoric acid can be reacted in a reactor vessel fitted with an agitator. The solutions can be allowed to react in the reaction vessel at room temperature with a moderate agitator rate. Then, while maintaining agitation at the same speed, the slurry of the precipitate can be titrated to a pH of about 6.0 to 7.4, or around 6.5 to 7.0, for instance, by adding 50% NaOH. After titration, the material can be allowed to sit again for 30 minutes without agitation. The reaction forms a slurry that is filtered and washed and then dried such as to a moisture level of 16 to 20 weight percent Loss on Drying (LOD). Other LODs are possible.
The product can be a free-flowing powder having a particle size range of 5-150 microns. The NaZrP can comprise, for example, particles having an average particle size of about 10 - 80 microns, about 25 - 60 microns, about 25 - 45 microns, about 30 ¨ 60 microns, about 45-90 microns, about 70 ¨ 100 microns, or about 100 ¨ 150 microns. Using sol-gel techniques, the particle size can be controlled. The NaZrP can be prepared, for example, by following the methods described in U.S. Patent No. 7,566,432.
[00055] The AZP can be prepared by a reaction between aqueous solutions of a zirconium salt and phosphoric acid or can be prepared using a solid zirconium compound(s) with phosphoris acid(s). The reaction forms a gelatinous precipitate that is filtered and washed until excessive phosphoric acid is removed, and then dried in an oven, such as to a moisture level of from about 12 to 18 weight percent Loss on Drying (LOD). Other LODs are possible. The final product after drying can be a fine powder or granules, such as with an irregular form. The AZT' can comprise, for example, particles having an average particle size of about 5 - 100 microns, about 10 - 80 microns, about 25 - 60 microns, or about 25 - 45 microns. The average grain size is not limited to these ranges and can be sizes above or below these ranges.
Using sol-gel techniques, the particle size can be controlled.
[00056] The AZP can be prepared, for example, by following the methods disclosed in U.S. Patent 6,818,196. Briefly, AZP can be prepared by heating zirconium oxychloride (ZOC) with soda ash to form sodium zirconium carbonate, and treating the sodium zirconium carbonate with caustic soda to form alkaline hydrous zirconium oxide. An aqueous slurry of the alkaline hydrous zirconium oxide can then be heated while adding phosphoric acid and an acid zirconium phosphate recovered. An aqueous slurry of the AZP can also be titrated with a basic agent, such as caustic soda, until a desired pH is reached, for example, a pH of from about 5 to about 7.
[00057] Alternatively, the AZP can be prepared by heating an aqueous mixture of basic zirconium sulfate (BZS) and phosphoric acid at a sufficient temperature (e.g., 180 F - 190 F) and for a sufficient time (e.g., 1 - 2 hr) to form acid zirconium phosphate precipitate. Then the solution can be cooled and the acid zirconium phosphate can be filtered and washed to reduce unreacted leachable phosphate levels. The AZP particles can be further dried, for example, at about 120 F ¨ 170 F. The AZP particles can have a BET surface area of less than 2 m2/g. By way of example, the AZP can be prepared as described in Example 1.
[00058] The AZP can be prepared, for example, by following the methods disclosed in U.S. Patent Application Publication 2006/0140840. Briefly, AZP can be prepared by preparing a solution of zirconium oxychloride (ZOC) and an organic chemical additive in water, and then titrating with concentrated hydrochloric acid (HC1) to fully dissolve the precipitate. This ZOC
solution is then added to a solution of phosphoric acid to produce a slurry of AZT precipitate.

The precipitate is then filtered and washed. The AZP particles can have a BET
surface area greater than 10 m2/g. By way of example, AZP can be prepared as described in Example 2.
[00059] Alkaline hydrous zirconium oxide can be prepared by the reaction of a zirconium salt, for example, BZS, or its solution in water (for instance, by a sol-gel method) with an alkali metal (or alkali metal compound) at ambient temperature, to form a NaHZ0 precipitate. The NaHZ0 particles can be filtered and washed until the anions of the zirconium salt are completely removed, and then preferably air dried, or dried in an oven at mild temperature (e.g., 60 F to less than 90 F) to a moisture level, for instance, of from about 25 - 30 weight percent LOD or lower, to form a free-flowing powder. Other LODs can be achieved, although higher temperature (e.g.
90 F - 120 F ) and/or long drying time (e.g. 24 - 48 hrs) to achieve a lower moisture level (i.e., 40 weight percent LOD) can convert the zirconium-hydroxide bond to a zirconium-oxide bond and reduce the adsorption capacity as well as alkalinity of the anion-exchange material. The drying temperatures refer to the nominal temperature in the oven or dryer. The NaHZ0 can comprise particles having an average grain size of about 10 - 100 microns, about 20 - 80 microns, about 25 - 60 microns, or about 25 - 40 microns. The average grain size is not limited to these ranges and can be sizes above or below these ranges. The NaHZ0 can have a BET
surface area of less than 2 m2/g. By way of example, the NaHZ0 can be prepared as described in Example 3.
[00060] The NaHZ0 can be prepared, for example, by following the methods disclosed in U.S. Patent Application Publication 2006/0140840. Briefly, this method of preparing NaHZ0 involves adding an aqueous solution of ZOC, titrated with concentrated HC1, to an aqueous solution of caustic soda. The HC1 addition can prevent excessive gelation during the precipitation process as well as to promote particle growth. The NaHZ0 particles can have a BET surface area of greater than 10 m2/g. By way of example, the NaHZ0 can be prepared as described in Example 4.
[00061] The cartridge can contain granular activated carbon (GAC). The GAC
can be present as a separate layer in the cartridge. The cartridge can comprise, consist essentially of, or consists of at least three layers, wherein one layer of the cartridge can comprise GAC, and the remaining two layers can comprise ion-exchange resins. For example, one layer of the cartridge can comprise GAC, another layer can comprise NaZrP, and the remaining layer can comprise a combination of AZP/NaHZO. The GAC can be useful to bind and remove chlorines, chloramines, organics, H2S, and/or microbes present in the water. It is preferable that a GAC
layer be disposed before or precede the ion-exchange resins present in the cartridge. Also, the layer of activated carbon can be disposed before the zirconium sorbents so that toxic trace metals leached out from the layer of activated carbon can be removed by the zirconium sorbents.
[00062] The cartridge can be functional in a wide range of temperatures.
The cartridge can be functional in a temperature range of 0 C - 100 C, such as, 20 C - 90 C, 30 C - 70 C , or 40 C -80 C.
[00063] Various filter media sections or sorbent materials within a tubular housing or cartridge can be used with the NaZrP, AZP and NaHZ0 of the present invention.
The housing or cartridge can, for example, include one or more additional ion-exchange sections, one or more additional GAC sections. The cartridge can include filter media, such as one or more separator pads, filter pads, or filter paper, to separate the layers of the cartridge and/or to provide additional filtering of the water. The housing or cartridge can include a carbon pre-filter, such as a carbon pad, for removing turbidity, chlorine, chloramine, microbes, and/or other particles in the water, such as silt and/or colloidal matter. The carbon pad can make the cartridge more compact.

18 It should be understood, however, that while a carbon pre-filter can be included, a carbon pre-filter is not required in the cartridge.
[00064] The housing of the cartridge can be made from any material, for example, any suitable impermeable polymeric and/or glass material. The housing or cartridge can be made from polycarbonate. The housing or cartridge can have any suitable shape, for example, the housing or cartridge can be cylindrical, rectangular, or square shaped.
[00065] The cartridge can be configured to purify water in any desired amount. The dimensions of a housing or cartridge, and/or the amount of components in the cartridge, which would be necessary to purify a desired quantity of water, can be readily determined. For example, a cartridge suitable for purifying 10 liters of water can be configured as follows. The cartridge can have a height of about 6.0", an internal diameter of about 2", and a thickness of about 0.05". The cartridge can include various filter media sections or layers. At least one section or layer of the cartridge can include NaZrP in an amount of about 10¨
80 g, for example about 20 g, 30 g, 40 g, 50 g, 60 g, or 70 g, per cartridge. At least one section or layer of the cartridge can include a combination of A713 and NaHZO, wherein the AZP in the AZP/NaHZ0-containing layer can be used in an amount, for example, of from about 40 ¨ 100 g, for example, 50 g, 60 g, 70 g, 80 g, 90 g, or 100 g per cartridge. The NaHZ0 in the AZINNaHZO-containing layer can be used in amount, for example, of from about 70¨ 130 g, for example, 80 g, 90 g, 100 g, 110, or 120 g per cartridge. The cartridge can include at least one section or layer having granular activated carbon, in an amount of from 40 - 100 g, for example, 50 g, 60 g, 70 g, 80 g, or 90 g. As a more specific example, a 5-inch diameter column can contain from about 2,000 g to 2,500 g of zirconium sorbent material which can treat 300 to 500 gallons of water. For instance,

19 the ratio of zirconium material (combined amount of NaZrP and AZP) to water treated can be about 2 grams to 10 grams of zirconium material per gallon of water to be treated.
[00066] The AZP and NaHZ0 can be present in any desired weight ratio. The weight ratio of NaHZ0 : AZP can range, for example, from about 0.2 : 0.8 to about 0.8 : 0.2, from about 0.5 : 0.5 to about 0.6 : 0.4, or from about 0.22 : 0.78 to about 0.33 : .67.
The weight ratio of NaHZ0 : AZP can be, for example, 0.4 : 0.6. The various weight ratios of AZP
and NaHZ0 can provide a mixture having any desired pH. A mixture of AZP and NaHZ0 can have a pH, for example, from about 3 to about 9, from about 3 to about 7, from about 3.5 to about 4, from about 4 to about 5.5, or from about 5.5 to about 6.
[00067] The NaZrP can be ZrP that is titrated to have any desired pH, for example, a pH
of from about 5.5 to about 7.5, from about 6.0 to about 7.0, or from about 6.5 to about 7Ø
Preferably, the ZrP is titrated to a pH of about 6.0 to about 7.4 or about 6.5 to about 7Ø
[00068] The zirconium ion-exchange resins are thermally stable and can be used to treat water even at high temperatures. The cartridge can be used to purify water of any temperature, for example, 1 C ¨ 40 C, or 10 C ¨ 30 C, or 20 C ¨ 35 C. The zirconium ion-exchange resins can have a mesoporosity level (total pore vol.) of 0.03 to 0.08 mug and/or a BET surface area of 1 to 30 m2/g with respect to ZP and a BET surface area of 20 to 100 m2/g for HZO. The mesoporosity of the zirconium ion-exchange resins can help to reduce microorganisms, endotoxins, chlorines, and/or chloramines in feed water. The zirconium ion-exchange resins can be at least partially or entirely resistant to bacterial proliferation.
[00069] The cartridge can be used to purify water having any level of contamination. The cartridge can remove toxic inorganic chemicals, even when the contaminants are present at high concentrations. The cartridge can, for example, be used to purify water having one or more or all of the characteristics described in Table 1 below. Any combination of two or more characteristics is possible. The amounts provided are upper limits and the cartridge can achieve these levels or even lower levels, such as 10%, 20%, 30%, 40%, or 50% lower levels than shown in Table!.
Table 1. Endurance Limits of Feed Water Quality and Delivery Tested TDS 500 ppm Water hardness 150 ppm CaCO3 Maximum contamination level of heavy 1000 ppm metals and aluminum Maximum contamination level of calcium, 100 ppm magnesium Maximum contamination level of anions; 100 ppm fluoride, sulfate, nitrate, arsenate Contamination level of organic challenged 1500 ppm Bacteria 106 CFU/ml Endotoxin 104 EU/ml Ionic level of feed water 800 micromhos PH of feed water 4-9 Temperature of feed water 1 C ¨ 40 C
Flow rate (5" ID) Maximum 600 ml/lmin Delivery pressure head 60 psi [00070] In general, a cartridge of the present invention can achieve one or more of the specific purity levels set forth in any one or more of Tables 3, 5-7, 8, 23, 22-23, or Figs. 4-8.
[00071] The cartridge can contain one or more layers or zones of the NaZrP, ATP
particles and NaHZ0 particles, wherein the cartridge has a plurality of filter media sections (or layers) including an arrangement, starting from a first end (inlet) and ending at a second end (outlet), an NaZrP section, a composite AZP/NaHZ0 section. As stated previously, the cartridge can optionally contain an activated carbon section.

1000721 Cartridges, as an option, do not have any other layers containing zirconium and/or zirconium containing components, other than the NaZrP, AZP, NaHZ0 layers as described herein.
[00073] Cartridges for water purification can be configured as shown, for example, in FIG.
1 and FIG. 2. As shown in FIG. 1, a cartridge (1) can have a first end having an inlet (2), and a second end having an outlet (4). Although not shown in the figures, the inlet can have control valve or pressure regulator to control the flow of water into the cartridge.
The first end can be opposite from or opposing the second end. The cartridge can have a first layer containing NaZrP
(NaZrP-containing layer) (6), and a second layer containing a combination of AZP and NaHZ0 (NaHZO/AZP- containing layer) (8). The first or NaZrP-containing layer (6) can be disposed nearer to the inlet (2) than the second or NaHZO/AZP-containing layer (8). The second layer (8) can succeed the first layer (6). The second layer (8) can be disposed nearer to the outlet (4) than the first layer (6). The NaZrP-containing layer (6) can remove toxic heavy metals, ammonia, NH4, amine, K+, and/or hardness metals, such as Ca2+ and Mg2+. The AZP in the AZP/NaHZO-containing layer (8) can remove Na + in the water, as well as microbes, mold, and/or algae in the water. The NaHZ0 in the AZP/NaHZO-containing layer (8) can remove toxic anions in the water, such as sulfate, nitrate, fluoride, chromate, selenate, and/or arsenate.
[00074] The cartridge (1) can have various filter media sections, for example, various filter media sections within a tubular housing or cartridge can be used with the NaZrP, AZP, NaHZO, GAC, of the present invention. FIG. 2 shows one arrangement of filter media sections in the cartridge (1). As shown in FIG. 2, the cartridge (1) can have a first layer containing NaZrP
(6), and a second layer containing a combination of AZP and NaHZ0 (8), as described above for FIG. 1. The cartridge (1) may contain a carbon pad (10) adjacent the inlet (2). The carbon pad (10) can remove chlorines, chloramines, microbes, and/or other particles in water, such as, silt, and/or colloidal matter. The carbon pad (10) can be any suitable carbon pad known in the art.
A layer of GAC (12) can succeed or be disposed immediately after the carbon pad (10). The GAC (12) can remove chlorine, chloramine, organics, H2S, and/or microbes. The GAC (12) can be disposed adjacent the first or NaZrP-containing layer (6). A separator pad (14) can separate the GAC (12) and the NaZrP-containing layer (6). The separator pad (14) can remove turbidity of water. Filter paper (16) can be disposed between the first layer (6) and the second layer (8), to separate the first layer (6) and the second (8). A filter pad (18) can be disposed between the AZP/NaHZO-containing layer and the outlet (4). The filter pad (18) can prevent leakage of particles, provide packing support for the particulate material, and/or prevent channeling.
[00075] A method to purify water can comprise passing water through a cartridge of the present invention, as detailed above. Water that is purified by the cartridge can have a pH of about 5.8 to about 7.5, such as, about 6.0 to about 7.4, or about 6.0 to about 7Ø Water that is purified by the cartridge can have a Na+ content of below 70 ppm, or 0 ppm to about 70 ppm, for example, 1 ppm to 60 ppm, or from about 15 ppm to about 50 ppm.
[00076] The cartridge for water purification can be utilized to purify tap water, municipal water, municipal drinking water, waste water, well water, and/or natural water. Waste water is understood to mean any water that has been adversely affected in quality by anthropogenic influence. Waste water can include liquid waste discharged by domestic residences, commercial properties, industry, and/or agriculture and can encompass a wide range of potential contaminants and concentrations. It should be understood that natural water can be water obtained from any natural source, for example, surface water, well water, precipitated water, and/or desalinated sea water.

[00077] Using the cartridge, water can be treated to reduce the level of contaminants to acceptable levels. Water that is purified by the cartridge can meet standards set forth for drinking water or human consumption by, such as, standards set forth by the U.S. Environmental Protection Agency (EPA) and the Food and Drug Administration (FDA). For example, water that is purified by the cartridge can achieve a level of purity that meets the requirements of the National Secondary Drinking Water Regulations, issued by the EPA and in place in 2007,2008, or 2009.
[00078] Water that is purified by the cartridge can meet the ANSI-AAMI
Water Standards for Dialysis. As such, the cartridge can be used to supply water to a hemodialysis machine or dialysis system. Purified, fresh dialysate for dialysis can be prepared by first passing tap water, to be used as a base for the dialysate, through the cartridge before entering the dialyzer.
Contaminants present in tap water, such as, toxic metal ions, non-metal ions, and chlorine, can be removed (to acceptable limits) by the cartridge, prior to using the water as a base for dialysate.
The dialyzer can be in fluid communication with the blood of a patient.
[00079] The present invention includes the following aspects/embodiments/features in any order and/or in any combination:
1. The present invention relates to a cartridge comprising:
a first end having an inlet;
a second end opposing the first end, the second end having an outlet;
a first layer comprising sodium zirconium phosphate (NaZrP); and a second layer comprising a combination of acid zirconium phosphate (AZP) and alkaline hydrous zirconium oxide (NaHZ0); wherein the first layer is disposed nearer to the inlet than the second layer, and the second layer succeeds the first layer.
2. The cartridge of any preceding or following embodiment/feature/aspect, wherein:
a) the first layer consists essentially of NaZrP; and b) the second layer consists essentially of a combination of AZP and NaHZO.
3. The cartridge of any preceding or following embodiment/feature/aspect, wherein:
a) the first layer consists of NaZrP; and b) the second layer consists of a combination of A711 and NaHZO.
4. The cartridge of any preceding or following embodiment/feature/aspect, wherein the second layer immediately succeeds the first layer.
5. The cartridge of any preceding or following embodiment/feature/aspect, wherein the first layer and the second layer are separated by filter paper.
6. The cartridge of any preceding or following embodiment/feature/aspect, wherein the NaZrP, the AZP and the NaHZO are particles having an average grain size of from about 25 microns to about 60 microns.
7. The cartridge of any preceding or following embodiment/feature/aspect, wherein the NaZrP, the AZP and the NaHZO are particles having an average grain size of from about 25 microns to about 60 microns; wherein, the first layer comprises about 20 g of NaZrP; and wherein the second layer comprises about 50 g AZP and 80 g NaHZO.
8. The cartridge of any preceding or following embodiment/feature/aspect, wherein the combination of AZP and NaHZO has a pH of from about 3 to about 7.
9. The cartridge of any preceding or following embodiment/feature/aspect, wherein the combination of AZP and NaHZO has a pH of from about 3.5 to about 4.

10. The cartridge of any preceding or following embodiment/feature/aspect, wherein the combination of AZP and NaHZ0 has a pH of from about 5.5 to about 6.
11. The cartridge of any preceding or following embodiment/feature/aspect, wherein the A713 and NaHZ0 are each present in the combination in an amount to produce an NaHZ0 : AZP
weight ratio of from about 0.2 : 0.8 to about 0.8 : 0.2.
12. The cartridge of any preceding or following embodiment/feature/aspect, wherein the NaHZ0 : AZP weight ratio is from about 0.5 : 0.5 to about 0.6 : 0.4.
13. The cartridge of any preceding or following embodiment/feature/aspect, wherein the NaHZ0 : AZP weight ratio is about 0.4 : 0.6.
14. The cartridge of any preceding or following embodiment/feature/aspect, wherein the NaHZD : AZP weight ratio is from about 0.22 : 0.78 to about 0.33 : 0.67.
15. The cartridge of any preceding or following embodiment/feature/aspect, wherein the NaZrP has a pH of from about 6.0 to about 7.4.
16. The cartridge of any preceding or following embodiment/feature/aspect, wherein the NaZrP has a pH of from about 6.5 to about 7Ø
17. The cartridge of any preceding or following embodiment/feature/aspect, further comprising granular activated carbon (GAC).
18. The cartridge of any preceding or following embodiment/feature/aspect, wherein the GAC is present as a layer in the cartridge.
19. The cartridge of any preceding or following embodiment/feature/aspect, wherein the layer of GAC is disposed closer to the inlet than the first layer, and precedes the first layer.

20. The cartridge of any preceding or following embodiment/feature/aspect, further comprising a separator pad, the separator pad being disposed between the layer of GAC and the first layer.

21. The cartridge of any preceding or following embodiment/feature/aspect, further comprising a carbon pad, the carbon pad being disposed immediately after the inlet, and preceding the first layer.

22. The cartridge of any preceding or following embodiment/feature/aspect, further comprising a filter pad, the filter pad being disposed immediately before the outlet, and succeeding the second layer.

23. The cartridge of any preceding or following embodiment/feature/aspect, further comprising a carbon pad, a separator pad, and/or a filter pad.

24. The cartridge of any preceding or following embodiment/feature/aspect, wherein the cartridge does not comprise a carbon pad.

25. A method to purify water comprising passing the water through the cartridge of any preceding or following embodiment/feature/aspect.

26. The method of any preceding or following embodiment/feature/aspect, wherein said water is municipal drinking water.

27. The method of any preceding or following embodiment/feature/aspect, wherein said water is waste water.

28. The method of any preceding or following embodiment/feature/aspect, wherein said water is natural water.

29. The method of any preceding or following embodiment/feature/aspect, wherein Ca2+, K+, me+, toxic trace metals, or any combination thereof present in the water are substantially removed by the first layer.

30. The method of any preceding or following embodiment/feature/aspect, wherein toxic anionic contaminants, Nat, or any combination thereof present in the water are substantially removed by the second layer.

31. The method of any preceding or following embodiment/feature/aspect, wherein after passing said water through the cartridge of any preceding or following embodiment/feature/aspect, the water satisfies ANSI-AAMI water standard for dialysis treatment

32. A method for preparing purified fresh dialysate for dialysis comprising passing water through the cartridge of any preceding or following embodiment/feature/aspect, prior to conducting said dialysis.

33. The method of any preceding or following embodiment/feature/aspect, wherein said dialysis is performed using a portable dialysis system.
[00080] The present invention can include any combination of these various features or embodiments above and/or below as set forth in sentences and/or paragraphs.
Any combination of disclosed features herein is considered part of the present invention and no limitation is intended with respect to combinable features.
[00081] The following examples are given to illustrate the nature of the present invention.
It should be understood, however, that the present invention is not limited to the specific conditions or details set forth in these examples.

EXAMPLES
Example 1 [00082] About 500 gallons of contaminated feed water was treated using the cartridge of the present invention. The cartridge was about 5" in diameter and about 12" in height. The components of the cartridge were in the following order (as layers):
1. Particle filter pad 2. 1200 gm [W-ZP:HZ0-011] (55:45 wt ratio) 3. Filter paper 4. 500 gm [Na+-711 5. Carbon pad 6. 500 gm activated carbon (Calgon) 7. Carbon pad The specifications of the contaminated feed water are provided in Table 2 below. The specifications of the product (resulting) water quality are provided in Table 3 below. The water flow rate and pressure drop are provided in Table 4 below.
Table 2. Challenge test contaminated water quality TDS 420 ppm Silver 100 ppm PH 6.9 Mercury 100 ppm Sulfate 120 ppm Lead 500 ppb Nitrate 20 ppm Chromium 500 ppb Chloride 60 ppm Barium 600 ppb Fluoride 2 ppm Cadmium 100 ppb Arsenate 1 ppm Copper 4 ppm Calcium 40 ppm Iron (ferric) 4 ppm Magnesium 20 ppm Manganese 700 ppb Sodium 50 ppm Zinc 600 ppb Table 3. Product water quality (500 gal life test with flow rate at 1 liter/min) pH of effluent 6.0-6.7 Hardness (calcium & magnesium) 100% removal Microbes & mold Not detectable Toxic heavy metals 100% removal; below detection limit Toxic anions 100% removal; below detection limit (sulfate, nitrate, fluoride, arsenate, chromate, phosphate, etc.) Chlorine & chloramine 100% removal; below detection limit Leachable from cartridge Not detectable (except for very (chemicals, particles, etc.) minute amount of NaC1 <100 ppm) TDS (derived from small leakage of Initial 1 ppm NaC1 NaC1) After 100 gal 30 ppm NaCl After 200 gal 50 ppm NaC1 After 300 gal 65 ppm NaCl After 400 gal 70 ppm NaC1 Table 4. Pressure drop of 5" diameter model Flow Rate Pressure drop psi 0.5 L/min 12 0.8 L/min 18 1.5 L/min 26 Example 2 100083] About 100 gallons of impure water was treated at a challenge level of individual contaminant, using the same cartridge components as in Example 1. The water flow rate was 500 ml/min. The specifications of the resulting purified water are provided in Tables 5-7 below.

Table 5. Purity of product water-Cations Feed water Product water Heavy metals at challenge level 100 Below detection limit ppm Calcium at 40 ppm in feed Below detection limit Magnesium at 20 ppm in feed Below detection limit Aluminum at 1 ppm in feed Below detection limit Sodium at 50 ppm in feed 0-50 gallon below 5 ppm (Below 10 micromhos) 500-100 gallon below 12 ppm (Below 70 micromhos) Table 6. Purity of product water-Anions Feed water Product water Nitrate at 100 ppm in feed Below detection limit Fluoride at 100 ppm in feed Below detection limit Sulfate at 200 ppm in feed Below detection limit Phosphate at 200 ppm in feed Below detection limit Arsenate at 10 ppm in feed Below detection limit Selenate at 10 ppm in feed Below detection limit Chloride at 60 ppm in feed 0-50 gallons below 5 ppm 50-100 gallons below 20 ppm pH 0-50 gallons 5.5-7.0 50-100 gallons 5.0-5.5 Microorganisms at 106 CFU/ml Below 100 CFU/ml Endotoxin at 104 EU/ml (LAL testing) Complete removal Table 7. Purity of product water-Disinfectants Free chlorine at 2,ppm Below detection limit Chloramine at 2 ppm Below detection limit Organic at 1500 ppm low molecular Below detection limit wt (e.g. benzene, methylene, chloride) (HPLC test) Example 3 1000841 The removal efficiency of toxic chemicals from water using a cartridge having, aside from a monolayer of mixed H+-ZP:HZ0-0H-, no additional zirconium ion-exchange resins present. A carbon pad was below the layer and a particle filter pad was above.
The cartridge was about 5" in diameter and contained about 2250 gm of H+-ZP:HZ0-011-(blending ratio 1:1 by weight). The levels of adsorption of toxic chemicals from the contaminated water, with a flow rate of 500 ml/min, are provided in Table 8 below. The conductivity of the water during treatment is provided in Table 9 below.
Table 8. Removal of toxic chemicals Toxic Level Removal Level in Amount of ANSI-chemicals tested efficiency effluent water treated AAMI
before standard breakthrough (above ANSI-AAMI
standard) Al (soluble) 500 ppb 100% 0 ppb >150 gal 10 ppb F (NaF) 100 ppm 99.9% 0.1 ppm 90 gal 02 ppm SO4 200 ppm 100% 0 90 gal 100 ppm Pb (Pb(NO3)2) 10 ppm 100% 0 >150 gal 50 ppb NO3 (NaNO3) 200 ppm 100% 0 100 gal 2 ppm (N) NO3- 1000 100% Undetectable >70 gal 2 ppm (NaNO3) ppm (N) Ca/Mg 100 ppm 100% 0 >150 gal 4 ppm (hardness) (Ca) Cu (CuSO4) 100 ppm 100% _0 >150 gal 0.1 ppm As (arsenate) 10 ppm 100% 0 >150 gal 5 ppb Ba (BaC12) 100 ppm 100% 0 >150 gal 0.01 ppm Cd (CdC12) 100 ppm 100% 0 >150 gal 0.001 ppm Hg 10 ppm 100% 0 >150 gal 0.2 ppb (Hg(NO3)2) Ag (AgNO3) 10 ppm 100% 0 >150 gal 5 ppb Cr (CrC13) 100 ppm 100% 0 >150 gal 0.02 ppm Ca 500 ppm 500 ppm 400% 0.1 ppm >70 gal 4 ppm (Ca) Table 9. Conductivity monitoring during treatment of municipal water (NOTE: Conductivity of OKC tap water 130 micromhos) Amount of Conductivity Contaminants Notes water treated monitored detection (other than chlorine) After 10 gal 0.5 micromhos 0 Small rise due to 20 gal 1 micromhos 0 Release of very 30 gal 2 micromhos 0 Minute amount of 40 gal 2.5 micromhos 0 NaC1 previously 50 gal 4 micromhos 0 absorbed 60 gal 5 micromhos 0 70 gal 7 micromhos 0 80 gal 8 micromhos 0 90 gal 15 micromhos 8 ppm NaC1 100 gal 30 micromhos 18 ppm NaC1 Example 4 1000851 In this experiment, a cartridge (1" x 6-3/4") was used having 60 g of a monolayer mixed-bed layer of H+-ZP:HZ0-011-, no additional zirconium ion-exchange resins present. A
carbon pad was below this monolayer and a particle filter pad was above. The flow rate was 20 ml/min. The cartridge was tested for removal of toxic metals from about 70 gallons of contaminated municipal tap water. The column specifications for the cartridge are provided in Table 10 below. The cartridge contained about 60 gm of H+-ZrP/HZ0-0H- (1:1 wt ratio). The water had a temperature of 25 C and contained the additive contaminants shown in Table 11 below. The levels of adsorption by this cartridge are provided in Table 12 below.

Table 10. Column Specifications 1" ID H+-ZP:HZ0-011- (1:1) Column height 6 3/4 inches Flow rate 20 ml/min (1" ID) or 500 ml/min (5" ID) Table 11. Additive contaminants in test bath of 20 liter municipal tap water at 25 C:
(i) Cd (CdC12) 10 ppm (ii) Hg (Hg(NO3)2) 1 ppm (iii) Se (AA Stock) 10 ppm (iv) Fe (FeSO4) 10 ppm Table 12. Results¨Adsorption test results scaled up to 1500 gm of zirconium sorbents for treatment of about 70 gal water Toxic Level Removal Level in Amount of ANSI-chemicals tested in efficiency effluent water treated AAMI
bath before standard breakthrough (above ANSI-AAMI) Cd 7.5 ppm 100% <DL (0.01 >70 gal 0.001 ppm) ppm Hg 0.33 100% <DL (0.0005 >70 gal 0.2 ppb ppm ppm) Se 18 ppm 100% <DL (0.005 >70 gal 9 ppb ppm) Fe 10 ppm 100% <DL (0.5 ppb) >70 gal Example 5 [00086] Municipal water from Oklahoma City with added contaminants, was treated using a cartridge (5" x 7") having the following components (as layers) in order:
1. Particle filter pad 2. 1200 gm [H+-ZP:HZ0-0H] (1:1 wt ratio) 3. Carbon pad

34 4. 500 gm activated carbon (Calgon) 5. Carbon pad The column specifications are provided in Table 13 below.
Table 13. Column Specifications 5" ID model HtZP:HZ0-0H- (1:1) 1200 gm Calgon activated carbon 500 gm Carbon pads 2 Particle filter pad 1 100087] The purity level of effluent or level of contaminants present in the effluent from the cartridge is provided in the tables shown in FIGS. 4 and 5.
Example 6 1000881 The same design of cartridge as in Example 5 was used with a flow rate of 1 L/min. The column specifications for the zirconium cartridge are provided in Table 16 below.
The levels of contaminants per 10 gallons of feed water are provided in Table 17. The conductance change in the effluent water is provided in Table 18. The purity level of the effluent or level of contaminants present in the effluent is provided in the tables of FIGS. 6 and 7.
Table 16. Column Specifications 5" ID model HtZP:HZ0-011- (1:1) 1200 gm Calgon activated carbon 500 gm _ Carbon pads 2 Particle filter pad 1 Table 17. Feed water with added contaminants every 10 gallons NaF 0.2 gm BaC12 0.1 gm CaC12 0.2 gm KC1 0.2 gm Pb (NO3)2 0.1 gm Na arsenate 0.1 gm Amount of water to be treated 70 gal Flow rate of water 1 L/min Conductance of water 178 mhos Table 18. Conductance change of effluent water Feed water 180 mhos Initial effluent 2 mhos gal 0.7 mhos gal 0.5 mhos gal 1 mhos gal 2 mhos gal 5 }mhos gal 8 mhos gal 15 mhos gal 30 mhos Example 7 1000891 A cartridge (1" x 11.2") using a 100 g monolayer of Iii-ZP:HZ0-OH-was used as in Example 3 to test the removal efficiency of inorganic contaminants in municipal tap water from Oklahoma City, at a low temperature of about 5 C. The column specifications for the cartridge are provided in Table 19 below. The additive contaminants per 20 ml of the water/min are provided in Table 20 below. A description of the purity of the effluent or level of contaminants present in the effluent is provided in the table of FIG. 8.

Table 19. Column specifications 1" ID model 1-1+-ZP:HZ0-0H- 100 gm (1:1) Flow rate 20 ml/min Table 20. Additive contaminants for test bath of 20 liter of tap water Al Soluble 500 ppb F- (NaF) 100 ppm 5042- (NaSO4) 200 ppm Pb (Pb(NO3)2) 10 ppm NO3- (NaNO3) 200 ppm Ca/Mg (CaC12 + 100 ppm MgC12) Cu CuSO4 100 ppm As A arsenate 10 ppm Ba BaC12 100 ppm Cd CdC12 100 ppm Hg (Hg(NO3)2) 10 ppm Ag (AgNO3) 10 ppm Cr (CrC13) 100 ppm Example 8 1000901 The cartridge of the present invention was tested for removal of hardness metals.
The components of the cartridge were present in the following order (as layers):
1. Particle filter pad 2. 1200 gm [11+-ZP:HZ0-0H] (55:45 wt ratio) 3. Filter paper 4. 500 gm [Na+-711 5. Carbon pad The column specifications and test conditions are provided in Table 21 below.
The results of the test are provided in Table 22 below.

Table 21. Column Specifications and Test Conditions H+-71):HZ0-0H- (55:45) 1200 gm NatZP (preceding layer) 500 gm Pressure 30 psi Flow rate 850 ml/min Table 22. Removal of hardness metals Volume Time (mm) pH (strip) Ca2+(ppm) Mg2+ (PM)Na processed (PM) (ppm) Start Bath 6.9 48 20.6 40 30 min 6.8 gallon 6.8 0 0 0.4 60 min 13.6 gallon 6.6 0 0 0.29 120 min 26.95 6.7 0.05 0.02 0.6 gallon 180 min 40.4 gallon 5.8 0.02 0.03 51 240 min 54 gallon 5.6 0.03 0.07 69 300 mm 67.4 gallon 5.5 0.04 0.04 33 360 min 80.8 gallon 5.0 0.05 0.06 33 420 mm 94 gallon 5.0 0.03 0.10 69 480 min 100 gallon 5.0 0.06 0.4 69 Example 9 [00091] The cartridge of the present invention was tested for removal of hardness metals (Ca24), common toxic anions (F- and sulfate), and disinfectants, at challenge levels. The components of the cartridge were present in the following order (as layers):
1. Particle filter pad 2. 130 gm [H+-ZP:HZ0-0H1 (50:80 wt ratio) 3. Filter paper 4. 20 gm [Na+-Z13]
5. Separator pad 6. 50 gm activated carbon (Calgon) 7. Carbon pad The cartridge was configured as shown in FIG. 2. The amount of NaZrP in the first layer (6) was about 20 gm by weight. The amount of AZP and NaHZ0 in the mixed-bed layer (8) was about 50 gm:80 gm by weight. The amount of activated carbon in the layer of granular activated carbon (12) was about 50 gm. The inlet (2) of the zirconium cartridge was about 2" in diameter.
The results of the test are provided in Table 23 below.
Table 23 pH Chlorine Ca2+ F- SO4 Na+
(ppm) (PP111) (ppm) (ppm) (PM) Bath 7.89 8.5 120 2.41 1204 44.67 (ANSI-AAMI for Na+
40 7 is 70 ppm) 1 6.12 0 10 0.02 <0 26.0 'Chlorine is 2 5.52 0 0 0.01 <0 16.6 completely removed.
3 5.25 0 0 0.01 <0 18.5 =pH of product water 4 5.16 0 0 0.01 50 28.5 in composite is 5.82 5.30 0 0 0.01 <0 39.4 =TDS is below 100 6 5.53 0 0 0.01 <0 44.4 ppm in effluent 7 5.55 0 0 0.01 <0 47.6 composite 8 5.52 0 0 0.01 <50 49.5 9 5.55 0 0 0.01 <0 50.7 Composite 5.82 0 0 0.01 <50 35.9 [00092] For this test, samples were taken at every liter effluent. The composite sample in the table reflects a mixture of all the effluent samples (1-9). Chlorine analysis performed by Hack total chlorine test kit. The Ca2+ analysis was performed using LaMotte total hardness test kit (as CaCO3). As can be seen in Table 23, Ca2+, and S042- was completely removed in the effluent for every liter sample, and was below the detection limit in the composite. Also, Na+
was lowered from 45 ppm in the untreated bath to 35 ppm in the effluent composite.
[00093] When an amount, concentration, or other value or parameter is given as either a range, preferred range, or a list of upper preferable values and lower preferable values, this is to be understood as specifically disclosing all ranges formed from any pair of any upper range limit or preferred value and any lower range limit or preferred value, regardless of whether ranges are separately disclosed. Where a range of numerical values is recited herein, unless otherwise stated, the range is intended to include the endpoints thereof, and all integers and fractions within the range.
It is not intended that the scope of the invention be limited to the specific values recited when defining a range.
1000941 Other embodiments of the present invention will be apparent to those skilled in the art from consideration of the present specification and practice of the present invention disclosed herein. It is intended that the present specification and examples be considered as exemplary only with a true scope of the invention being indicated by the following claims and equivalents thereof.

Claims (33)

WHAT IS CLAIMED IS:

1. A cartridge comprising:

a first end having an inlet;

a second end opposing the first end, the second end having an outlet;
a first layer comprising sodium zirconium phosphate (NaZrP); and a second layer comprising a combination of acid zirconium phosphate (AZP) and alkaline hydrous zirconium oxide (NaHZO); wherein the first layer is disposed nearer to the inlet than the second layer, and the second layer succeeds the first layer.

2. The cartridge of claim 1, wherein:

a) the first layer consists essentially of NaZrP; and b) the second layer consists essentially of a combination of AZP and NaHZO.

3. The cartridge of claim 1, wherein:

a) the first layer consists of NaZrP; and b) the second layer consists of a combination of AZP and NaHZO.

4. The cartridge of claim 1, wherein the second layer immediately succeeds the first layer.

5. The cartridge of claim 1, wherein the first layer and the second layer are separated by filter paper.

6. The cartridge of claim 1, wherein the NaZrP, the AZP and the NaHZO are particles having an average grain size of from about 25 microns to about 60 microns.

7. The cartridge of claim 1, wherein the NaZrP, the AZP and the NaHZO are particles having an average grain size of from about 25 microns to about 60 microns;
wherein, the first layer comprises about 20 g of NaZrP; and wherein the second layer comprises about 50 g AZP
and 80 g NaHZO.

8. The cartridge of claim 1, wherein the combination of AZP and NaHZO has a pH
of from about 3 to about 7.

9. The cartridge of claim 1, wherein the combination of AZP and NaHZO has a pH
of from about 3.5 to about 4.

10. The cartridge of claim 1, wherein the combination of AZP and NaHZO has a pH of from about 5.5 to about 6.

11. The cartridge of claim 1, wherein the AZP and NaHZO are each present in the combination in an amount to produce an NaHZO : AZP weight ratio of from about 0.2 : 0.8 to about 0.8 : 0.2.

12. The cartridge of claim 1, wherein the NaHZO : AZP weight ratio is from about 0.5 : 0.5 to about 0.6 : 0.4.

13. The cartridge of claim 1, wherein the NaHZO : AZP weight ratio is about 0.4: 0.6.

14. The cartridge of claim 1, wherein the NaHZO : AZP weight ratio is from about 0.22 :
0.78 to about 0.33 : 0.67.

15. The cartridge of claim 1, wherein the NaZrP has a pH of from about 6.0 to about 7.4.

16. The cartridge of claim 1, wherein the NaZrP has a pH of from about 6.5 to about 7Ø

17. The cartridge of claim 1, further comprising granular activated carbon (GAC).

18. The cartridge of claim 17, wherein the GAC is present as a layer in the cartridge.

19. The cartridge of claim 18, wherein the layer of GAC is disposed closer to the inlet than the first layer, and precedes the first layer.

20. The cartridge of claim 18, further comprising a separator pad, the separator pad being disposed between the layer of GAC and the first layer.

21. The cartridge of claim 1, further comprising a carbon pad, the carbon pad being disposed immediately after the inlet, and preceding the first layer.

22. The cartridge of claim 1, further comprising a filter pad, the filter pad being disposed immediately before the outlet, and succeeding the second layer.

23. The cartridge of claim 1, further comprising a carbon pad, a separator pad, and/or a filter pad.

24. The cartridge of claim 1, wherein the cartridge does not comprise a carbon pad.

25. A method to purify water comprising passing the water through the cartridge of claim 1.

26. The method of claim 25, wherein said water is municipal drinking water.

27. The method of claim 25, wherein said water is waste water.

28. The method of claim 25, wherein said water is natural water.

29. The method of claim 25, wherein Ca2+, K+, Mg2+, toxic trace metals, or any combination thereof present in the water are substantially removed by the first layer.

30. The method of claim 25, wherein toxic anionic contaminants, Na+ , or any combination thereof present in the water are substantially removed by the second layer.

31. The method of claim 25, wherein after passing said water through the cartridge of claim 1, the water satisfies ANSI-AAMI water standard for dialysis treatment

32. A method for preparing purified fresh dialysate for dialysis comprising passing water through the cartridge of claim 1, prior to conducting said dialysis.

33. The method of claim 32, wherein said dialysis is performed using a portable dialysis system.