CA2646038C - Interlayer film for laminated glass and laminated glass - Google Patents

Interlayer film for laminated glass and laminated glass Download PDF

Info

Publication number
CA2646038C
CA2646038C CA2646038A CA2646038A CA2646038C CA 2646038 C CA2646038 C CA 2646038C CA 2646038 A CA2646038 A CA 2646038A CA 2646038 A CA2646038 A CA 2646038A CA 2646038 C CA2646038 C CA 2646038C
Authority
CA
Canada
Prior art keywords
laminated glass
interlayer film
sound
layer
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CA2646038A
Other languages
French (fr)
Other versions
CA2646038A1 (en
Inventor
Jiro Miyai
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sekisui Chemical Co Ltd
Original Assignee
Sekisui Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=38693870&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=CA2646038(C) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Sekisui Chemical Co Ltd filed Critical Sekisui Chemical Co Ltd
Publication of CA2646038A1 publication Critical patent/CA2646038A1/en
Application granted granted Critical
Publication of CA2646038C publication Critical patent/CA2646038C/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

An intermediate film for laminated glass and laminated glass having excellent sound insulation properties and particularly suitably used for a head-up display etc. where the driver can view both a forward field and instrument display at the same time without dropping their line of vision. The intermediate film for laminated glass is constructed from at least a pair of protective layers and a sound insulation layer sandwiched between the pair of protective layers. The intermediate film has a wedge shape cross-section, a cross-section wedge angle .theta. of 0.1 - 0.7 mrad, a maximum thickness of not more than 2000 µm, and a minimum thickness of not less than 400 µm. The minimum thickness of the sound insulation layer is not less than 20 µm.

Description

DESCRIPTION
INTERLAYER FILM FOR LAMINATED GLASS AND LAMINATED GLASS
TECHNICAL FIELD
[0001]
The present invention relates to an interlayer film for a laminated glass excellent in a sound-insulating property, which is preferably usable for a head up display and the like wherein a driver can look at the front view and an instrument display simultaneously without requiring to look down, and relates to a laminated glass.
BACKGROUND ART
[0002]
As so-called front glass, generally laminated glass composed of two opposed plate-like glass sheets and an interlayer film for a laminated glass sandwiched between the glass sheets has been used for the front face of an automobile, an aircraft or the like.
In recent years, from a viewpoint of safety improvement, with respect to, for example, a front glass for an automobile, it has been highly required to display an instrument display such as a speed information, which is automotive driving data, as a head up display (HUD) in the same visible field as the front glass.
Various kinds of HUD mechanisms have been developed so far. For example, there is a HUD mechanism whose HUD
display part is not in the front glass surface and by which the speed information and the like transmitted from a control unit is reflected to the front glass from a display unit on an instrumental panel to enable a driver to see the information at the same position as the front glass (that is, in the same visible field). For such a mechanism, since the laminated glass composing the front glass comprises two parallel glass sheets, there is a defective point that the instrument display reflected in the visible field of the driver is seen double.
[0003]
To deal with such a problem, Patent Document 1 discloses a laminated glass using an interlayer film for a laminated glass with a wedge shape having a prescribed wedge angle.
Such a laminated glass enables a convergence of the instrument display reflected by one glass sheet and the instrument display reflected by the other glass sheet upon one point in the visible field of the driver by adjusting the wedge angle, and the laminated glass can solve the conventional problem that the instrument display is seen double, and the driver's visible field is never interfered.
However, such a laminated glass has a problem of inferior sound-insulating property in particular.
Patent Document 1: Japanese Kokai Publication Hei-4-502525 DISCLOSURE OF THE INVENTION
PROBLEMS TO BE SOLVED BY THE INVENTION
[0004]
In view of the above-mentioned state of the art, the present invention aims to provide an interlayer film for a laminated glass excellent in a sound-insulating property, which is preferably usable for a head up display and the like wherein a driver can look at the front view and an instrument display simultaneously without requiring to look down, and aims to provide a laminated glass.
MEANS FOR SOLVING THE PROBLEMS
[0005]
The present invention provides interlayer film for a laminated glass, which comprises at least a pair of protection layers and a sound-insulating layer sandwiched between the pair of the protection layers, and which has a wedge shape as a cross-sectional shape, a wedge angle 19 of 0.1 to 0.7 mrad, the maximum thickness of 2000 pm or thinner, and the minimum thickness of 400 pm or thicker, the minimum thickness of the sound-insulating layer being 20 pm or thicker.
Hereinafter, the present invention will be described in detail.
[0006]
The present inventors made various investigations concerning causes of the inferiority of the sound-insulating property of the laminated glass using the interlayer film for a laminated glass with a wedge shape and accordingly have found that since the interlayer film for a laminated glass has a wedge angle, the thickness of the end forming the wedge angle is extremely thin as compared with the other end and sound vibration is transmitted to the inside of a vehicle through the thin portion. Further, the inventors of the present invention have found that the problem that the instrument display reflected to the visible field of a driver is seen double cannot be solved only by making the thickness of the end forming the edge angle in the interlayer film for a laminated glass thick enough not to transmit the sound vibration. Therefore, the inventors of the present invention have made further investigations to find that an interlayer film for a laminated glass having a sound-insulating layer and a protection layer with prescribed thickness and having a wedge angle in a prescribed range and a specified shape overcomes the problems in terms of the lightweight, cost and the like, has sufficient sound-insulating property and penetration resistance, enables a driver to simultaneously see the front view, a speed display and the like with no need for the driver to look down, and is preferably usable for a head up display.

These findings have now led to completion of the present invention.
[0007]
An interlayer film for a laminated glass of the present invention comprises at least a pair of protection layers and a sound-insulating layer sandwiched between the pair of the protection layers.
[0008]
The minimum thickness of the sound-insulating layer is 20 pm in the lower limit. If it is thinner than 20 pm, sufficient sound-insulating property cannot be obtained.
The lower limit is preferably 30 pm and more preferably 40 pm. The upper limit is preferably 300 pm and more preferably 200 pm.
[0009]
As the thickness of the sound-insulating layer becomes thicker, a higher sound-insulating property can be obtained. The cross-sectional shape of the sound-insulating layer may be a wedge shape in consideration of the easiness in terms of formation and the like. In the case where the sound-insulating layer of the interlayer film for a laminated glass has a wedge shape, it has an excellent defoaming property of preventing foaming in the laminated glass.
In this description, the wedge shape means a shape which is wide in one end and becomes narrower toward the other end. Practical examples of the shape may be a trapezoidal shape and a triangular shape.
The sound-insulating layer may have partially a colored band.
The colored band can be obtained, for example, by inserting a polyvinyl acetal resin mixed with a coloring agent in a layer and extrusion-molding the resin at the time of extrusion-molding the sound-insulating layer.
[0010]

The sound-insulating layer is not particularly limited, however it is preferably to form the layer, for example, by using a plasticizer and a polyvinyl acetal resin.
5 [0011]
The plasticizer is not particularly limited and may include, for example, organic plasticizers such as monobasic organic acid esters and polybasic organic acid esters; and organic phosphoric acid ester plasticizers such as organic phosphoric acid esters and organic phosphorous acid esters.
[0012]
The monobasic organic acid ester plasticizers are not particularly limited and may include, for example, glycol esters obtained by reaction with glycols such as triethylene glycol, tetraethylene glycol, and tripropylene glycol and monobasic organic acids such as butyric acid, isobutyric acid, caproic acid, 2-ethylbutyric acid, heptylic acid, n-octylic acid, 2-ethylhexylic acid, pelargonic acid (n-nonylic acid), and decylic acid. Among them, triethylene glycol esters such as triethylene glycol dicaproate, triethylene glycol di-2-ethylbutanoate, triethylene glycol di-n-octanoate, triethylene glycol di-2-ethylhexanoate (3G0) are preferable.
[0013]
The polybasic organic acid ester plasticizers are not particularly limited and may include, for example, esters obtained by reaction of straight chain or branched alcohols having 4 to 8 carbon atoms and polybasic organic acids such as adipic acid, sebacic acid, and azelaic acid. Among them, dibutyl sebacate, dioctyl azelate, and dibutylcarbitol adipate are preferable.
[0014]
The organic phosphoric acid ester plasticizers are not particularly limited and may include, for example, tributoxyethyl phosphate, isodecylphenyl phosphate, and triisopropyl phosphate.
[0015]
Among the plasticizers, triethylene glycol di-2-ethylbutanoate and triethylene glycol di-2-ethylhexanoate (3G0) are preferably usable in particular.
[0016]
The content of the plasticizer in the sound-insulating layer is not particularly limited, however since a higher sound-insulating property can be obtained by adding a large quantity of a plasticizer and thereby softening the resin layer and absorbing the vibration of sound, it is preferably 40 parts by weight in the lower limit and 80 parts by weight in the upper limit to 100 parts by weight of a polyvinyl acetal resin. If it is less than 40 parts by weight, the sound-insulating property for the sound in a range about 5000 Hz may sometimes become insufficient and if it exceeds 80 parts by weight, bleeding out of the plasticizer occurs to lower the transparency and the adhesive property of the interlayer film for a laminated glass and the optical distortion of the obtained laminated glass may become significant in some cases. It is more preferably 50 parts by weight in the lower limit and 70 parts by weight in the upper limit.
[0017]
The polyvinyl acetal resin is not particularly limited, however the sound-insulating layer contains a large quantity of the plasticizer as described above, and therefore, the polyvinyl acetal resin is preferable to have high affinity even for a large quantity of the plasticizer.
Particularly preferable examples to be used are a polyvinyl acetal resin having an acetal group having 4 to 5 carbon atoms and having an acetylation degree of 4 to 30% by mole, a polyvinyl acetal resin having an acetal group having 6 to 10 carbon atoms, and a polyvinyl acetal resin having an acetalization degree of 70 to 85% by mole.
[0018]
The polyvinyl acetal resin can be obtained by acetalization of polyvinyl alcohol with aldehyde and generally includes an acetal group, an acetyl group, and a hydroxy group as side chains in an ethylene chain, which is a main chain.
[0019]
The average polymerization degree of the polyvinyl alcohol, which is a raw material for producing the polyvinyl acetal resin, is preferably 200 in the lower limit and 5000 in the upper limit. If it is lower than 200, the interlayer film for a laminated glass may sometimes be inferior in the penetration resistance and if it exceeds 5000, the strength of the laminated glass may sometimes become too high to use the glass for a front glass for a vehicle. It is more preferably 500 in the lower limit and 4000 in the upper limit and even more preferably 1000 in the lower limit and 3500 in the upper limit.
[0020]
An aldehyde having 4 to 5 carbon atoms to be used for producing the polyvinyl acetal resin having an acetal group having 4 to 5 carbon atoms is not particularly limited and may include, for example, n-butyraldehyde, isobutyraldehyde, and valeraldehyde. These aldehydes may be used alone or two or more of them may be used in combination. Among them, n-butyraldehyde and isobutyraldehyde are preferable to be used and n-butyraldehyde is even more preferable to be used in particular. Use of n-butyraldehyde strengthens the adhesive strength between neighboring layers. Further, resins may be synthesized in the same methods as those for producing commonly used polyvinyl butyral resin.
[0021]
With respect to the polyvinyl acetal resin having an acetal group having 4 to 5 carbon atoms, the acetylation degree is preferably 4% by mole in the lower limit and 30%
by mole in the upper limit. If it is lower than 4% by mole, the sound-insulating property is not exhibited sufficiently in some cases and if it exceeds 30% by mole, the reaction ratio of the aldehyde is considerably lowered in some cases.
It is more preferably 8% by mole in the lower limit and 24%
by mole in the upper limit and even more preferably 10% by mole in the lower limit.
The acetylation degree is a mole fraction calculated by dividing the average value of the quantity of ethylene groups to which the acetyl group is bonded by the total quantity of ethylene groups in the main chain.
[0022]
With respect to the polyvinyl acetal resin having an acetal group having 4 to 5 carbon atoms, the acetalization degree is preferably 40% by mole in the lower limit and 69%
by mole in the upper limit. If it is lower than 40% by mole, the compatibility for the plasticizer is worsened to make it impossible to add a necessary amount of the plasticizer to exhibit the sound-insulating property in some cases. On the other hand, a polyvinyl acetal resin having the acetalization degree exceeding 69% by mole is inferior in the production efficiency and becomes costly.
It is more preferably 50% by mole in the lower limit and 68% by mole in the upper limit.
[0023]
With respect to the polyvinyl acetal resin having an acetal group having 4 to 5 carbon atoms, a mixture of two or more kind polyvinyl acetal resins obtained by acetalization of polyvinyl alcohol with aldehydes having 4 carbon atoms or aldehydes having 5 carbon atoms.
Alternatively, a polyvinyl acetal resin obtained by acetalization of an aldehyde mixture containing an aldehyde other than the aldehyde having 4 to 5 carbon atoms in a range of lower than 30% by weight may be used.

[0024]
An aldehyde having 6 to 10 carbon atoms to be used for producing the polyvinyl acetal resin containing an acetal group having 6 to 10 carbon atoms is not particularly and may include, for example, aliphatic, aromatic, or alicyclic aldehydes such as n-hexyl aldehyde, 2-ethylbutyraldehyde, n-heptaldehyde, n-octyl aldehyde, n-nonyl aldehyde, n-decyl aldehyde, benzaldehyde, and cinnamaldehyde. These aldehydes may be used alone or two or more of them may be used in combination. Among them, aldehydes having 6 to 8 carbon atoms are preferably usable.
If the number of carbon atoms of the aldehyde exceeds 10, the rigidity of the polyvinyl acetal to be obtained becomes low and the sound-insulating property may be deteriorated in some cases.
[0025]
With respect to the polyvinyl acetal resin having an acetalization degree of 70 to 85% by mole, the acetalization degree is preferably 70% by mole in the lower limit and 85% by mole in the upper limit. If it is lower than 70% by mole, the sound-insulating property is not exhibited sufficiently in some cases and if it exceeds 85%
by mole, the reaction ratio of the aldehyde to be used at the time of producing the polyvinyl acetal resin may be considerably decreased in some cases. It is more preferably 72% by mole in the lower limit and 82% by mole in the upper limit.
The acetalization degree is a mole fraction calculated by dividing the average value of the quantity of ethylene groups to which the acetal group is bonded by the total quantity of ethylene groups in the main chain.
[0026]
A production method of the polyvinyl acetal resin is not particularly limited and may be, for example, a method for obtaining a resin powder by dissolving polyvinyl alcohol in hot water, keeping the obtained aqueous polyvinyl alcohol solution at a prescribed temperature, adding the aldehyde and a catalyst to the solution, promoting acetalization reaction, keeping the reaction 5 solution at a prescribed high temperature, and thereafter carrying out steps of neutralization, washing with water, and drying.
[0027]
The sound-insulating layer is sandwiched between a 10 pair of protection layers.
The protection layer prevents the adhesive property between the interlayer film for a laminated glass and glass from lowering because of bleeding out of a large quantity of the plasticizer contained in the sound-insulating layer.
Further, the protection layer has a role to provide the penetration resistance to the interlayer film for a laminated glass to be obtained. Further, the protection layer also has a function of adjusting the shape of the entire interlayer film for a laminated glass to be a wedge shape.
[0028]
The thickness of the protection layer may be adjusted in a manner that the film thickness of the entire interlayer film for a laminated glass is to be in a range as described below and is thus not particularly limited.
The cross-sectional shape of the pair of the protection layers is preferably the wedge shape or a combination of the wedge shape and a rectangular shape.
[0029]
The protection layer is not particularly limited, however it preferably comprises a polyvinyl acetal resin containing a plasticizer.
[0030]
The polyvinyl acetal resin to be used for the protection layer is not particularly limited and may be, for example, a polyvinyl acetal resin having an acetylation degree of 3% by mole or lower, 3 to 4 carbon atoms of an acetal group, and an acetalization degree of 60 to 70% by mole.
[0031]
The plasticizer to be used for the protection layer is not particularly limited and the plasticizers same as those to be used for the sound-insulating layer may be used.
[0032]
The content of the plasticizer in the protection layer is not particularly limited, however it is preferably 25 parts by weight in the lower limit and 55 parts by weight in the upper limit to 100 parts by weight of the polyvinyl acetal resin. If it is lower than 25 parts by weight, the adhesive property to the glass may become insufficient in some cases. Further, if it exceeds 55 parts by weight, bleeding out occurs to lower the transparency and the adhesive property of the interlayer film for a laminated glass and the optical distortion of the obtained laminated glass may become significant. It is more preferably 30 parts by weight in the lower limit and 50 parts by weight in the upper limit.
[0033]
Further, the protection layer may have partially a colored band.
The colored band can be obtained by inserting a polyvinyl acetal resin and the like mixed with a coloring agent in a layer and extrusion-molding the resin at the time of extrusion-molding the protection layer.
[0034]
In order to adjust the convenience and the shape in the production method, a shape assisting layer may be layered on at least one layer of the pair of the protection layers.
[0035]

ak 02646028 2013-08-13 The shape assisting layer is not particularly limited and the resin same as that of the protection layer may be used.
The thickness of the shape assisting layer may be adjusted in a manner that the film thickness, the wedge angle and the like of the interlayer film for a laminated glass to be obtained are to be in a range as described below.
[0036]
The sound-insulating layer, the protection layer, and/or the shape assisting layer may contain, if necessary, conventionally known additives such as an ultraviolet ray absorbent, an adhesive strength control agent, a photostabilizer, a surfactant, a flame retardant, an antistatic agent, a moisture prevention agent, and a coloring agent.
[0037]
The sound-insulating layer, the protection layer, and/or the shape assisting layer are preferable to contain a heat insulating agent.
If the interlayer film for a laminated glass contains the heat insulating agent in any one of the layers, the interlayer film for a laminated glass is provided with an excellent heat insulating property.
The heat insulating agent is not particularly limited and may include, for example, inorganic heat insulating agents such as tin-doped indium oxide, antimony-doped tin oxide, and lanthanum hexaboride; and organic heat insulating agents such as copper complex compounds and phthalocyanine-metal complexes.
Accordingly, in one aspect of the present invention, there is provided an interlayer film for a laminated glass, which comprises at least a pair of protection layers and a sound-insulating layer sandwiched between the pair of the protection layers, and which has a wedge shape as a cross-ak 02646028 2013-08-13 12a sectional shape, a wedge angle 0 of 0.1 to 0.7 mrad, the maximum thickness of 2000 pm or thinner, and the minimum thickness of 400 pm or thicker, the minimum thickness of the sound-insulating layer being 20 pm or thicker, and wherein the sound-insulating layer is selected from the group consisting of 1) a layer which comprises 40 to 80 parts by weight of a plasticizer to 100 parts by weight of a polyvinyl acetal resin having an acetalization degree of 70 to 85% by mole, 2) a layer which comprises 40 to 80 parts by weight of a plasticizer to 100 parts by weight of a polyvinyl acetal resin having an acetal group having 4 to 5 carbon atoms and having an acetylation degree of 4% by mole or more, and 3) a layer which comprises 40 to 80 parts by weight of a plasticizer to 100 parts by weight of a polyvinyl acetal resin having an acetal group having 6 to 10 carbon atoms.
[0037A]
In another aspect, the present invention resides in an interlayer film for a laminated glass, which, comprises at least a pair of protection layers and a sound-insulating layer sandwiched between the pair of the protection layers,and which has a wedge shape as a cross-sectional shape, a wedge angle 0 of 0.1 to 0.7 mrad, the maximum thickness of 2000 pm or thinner, and the minimum thickness of 400 pm or thicker, the minimum thickness of the sound-insulating layer being 20 pm or thicker, wherein the protection layer contains 25 to 55 parts by weight of a plasticizer to 100 parts by weight of a polyvinyl acetal resin having an acetylation degree of 3% by mole or lower, 3 to 4 carbon atoms of an acetal group, and an acetalization degree of 60 to 70% by mole, and wherein the sound-insulating layer contains 40-80 parts by weight of a plasticizer to 100 parts by weight of a polyvinyl acetal resin.

12b [0038]
BRIEF DESCRIPTION OF THE DRAWINGS
[Fig. 1] Fig. 1 is a drawing schematically showing a cross-sectional drawing of an interlayer film for a laminated glass of the present invention.
[Fig. 2] Fig. 2 is a drawing schematically showing a cross-sectional drawing of an interlayer film for a laminated glass of another embodiment of the present invention.
[Fig. 3] Fig. 3 is a drawing schematically showing a cross-sectional drawing of an interlayer film for a laminated glass of another embodiment of the present invention.
[Fig. 4] Fig. 4 is a drawing schematically showing a cross-sectional drawing of an interlayer film for a laminated glass of another embodiment of the present invention.
Practical Examples of cross-sectional drawings of the interlayer film for a laminated glass of the present invention comprising at least the protection layers and the sound-insulating layer may be those shown in the schematic , drawings of Figs. 1 to 4.
The interlayer film for a laminated glass shown in Fig. 1 comprises the sound-insulating layer 2 with a cross-sectional shape of the rectangular shape sandwiched between the protection layers 1 with a cross-sectional shape of the wedge shape.
The interlayer film for a laminated glass shown in Fig. 2 comprises the sound-insulating layer 2 with a cross-sectional shape of the wedge shape sandwiched between the protection layers 1 with a cross-sectional shape of the wedge shape.
The interlayer film for a laminated glass shown in Fig. 3 comprises the sound-insulating layer 2 with a cross-sectional shape of the rectangular shape sandwiched between the protection layer 1 with a cross-sectional shape of the wedge shape and the protection layer 1 with a cross-sectional shape of the rectangular shape.
The interlayer film for a laminated glass shown in Fig. 4 comprises the sound-insulating layer 2 with a cross-sectional shape of the rectangular shape sandwiched between the protection layers 1 with a cross-sectional shape of the rectangular shape and further a shape assisting layer 3 with a cross-sectional shape of the wedge shape laminated on the surface of one of the protection layer.
Among them, the interlayer film for a laminated glass shown in Fig. 2 is preferably since it has an excellent defoaming property of generating no foam at the time of producing a laminated glass.
[0039]
The interlayer film for a laminated glass of the present invention comprising at least the protection layers and sound-insulating layer has a wedge angle 0 of the cross-section of 0.1 mrad in the lower limit and 0.7 mrad in the upper limit. The wedge angle 0 of the cross-section of the interlayer film for a laminated glass means an acute angle formed at the crossing point of extended two sides as shown as the wavy lines in the cross-sectional drawings of Figs. 1 to 4.
If the wedge angle 19 is lower than 0.1 mrad, an instrument display for speed information and the like transmitted from a control unit is seen double and thus cannot display well and if it exceeds 0.7 mrad, the instrument display is seen double in the visible field of a driver. It is more preferably 0.2 mrad in the lower limit and 0.6 mrad in the upper limit [0040]
The maximum thickness of the interlayer film for a laminated glass of the present invention is 2000 pm in the upper limit. The maximum thickness is the portion 4 as shown in Fig. 1.
If the maximum thickness exceeds 2000 pm, the thickness is too thick to instill the laminated glass easily as the front glass in a vehicular body in some cases.
It is more preferably 1500 pm in the upper limit.
[0041]
The minimum thickness of the interlayer film for a laminated glass of the present invention is 400 um in the lower limit. The minimum thickness is the portion 5 as shown in Fig. 1.
If the minimum thickness is thinner than 400 pm, it becomes impossible to obtain a sufficient sound-insulating property and the penetration resistance to impact becomes weak. It is more preferably SOO pm in the lower limit.
[0042]
A method for producing the sound-insulating layer, the protection layer, and the shape assisting layer is not particularly limited and may be, for example, methods involving adding a plasticizer and additives, added based on the necessity, to a polyvinyl acetal resin, kneading the mixture, and molding the mixture. The kneading method is not particularly limited and may be, for example, methods using an extruder, a Plastograph, a kneader, a Bumbury's mixer, a calender roll, or the like. Among them, a method using an extruder is preferable since it is suitable for 5 continuous production.
[0043]
A method for producing the interlayer film for a laminated glass of the present invention comprising at least the sound-insulating layers and protection layer is 10 not particularly limited and may be methods involving producing the protection layers and the sound-insulating layer and thermally laminating the layers; molding the protection layers and the sound-insulating layer by co-extrusion; and molding the protection layers and the sound-15 insulating layer by co-extrusion, layering the shape assisting layer on the surface of at least one of the protection layers, and thermally laminating the layers.
[0044]
Since the cross-sectional shape of the interlayer film for a laminated glass is formed in a wedge shape by combining at least shapes of the sound-insulating layers and the protection layer, the sound-insulating property is provided and the speed information and the like transmitted from the control unit can be reflected on the front glass from the display unit of a instrumental panel and therefore, a driver can simultaneously see the front view, speed display and the like without looking down and the interlayer film for a laminated glass can be used preferably for a head up display.
[0045]
A laminated glass obtained using the interlayer film for a laminated glass of the present invention is also an aspect of the present invention.
[0046]
The laminated glass of the present invention comprises at least the interlayer film for a laminated glass of the present invention sandwiched between a pair of glass sheets.
The glass sheets to be used are not particularly limited and may be conventionally known transparent plate glass. Further, organic glass of polycarbonate, polymethyl methacrylate or the like may be used in place of inorganic glass.
A method for producing laminated glass of the present invention is not particularly limited and conventionally known methods can be employed.
It is preferable to sandwich only one interlayer film for a laminated glass between a pair of glass sheets since the laminated glass production is easy, however in terms of the properties and functions such as stability, a plurality of interlayer films for a laminated glass may be sandwiched between a pair of glass sheets to produce a laminated glass.
EFFECTS OF THE INVENTION
[0047]
According to the present invention, it is made possible to provide an interlayer film for a laminated glass excellent in a sound-insulating property, which is preferably usable for a head up display and the like wherein a driver can look at the front view and an instrument display simultaneously without requiring to look down, and to provide a laminated glass.
BEST MODE FOR CARRYING OUT THE INVENTION
[0048]
Hereinafter, the present invention will be described in details with reference to examples, however the present invention is not limited to these examples.
[0049]
(Example 1) (1) Production of a sound-insulating layer A sound-insulating layer was produced by adding 65 parts by weight of triethylene glycol di-2-ethylhexanoate (3G0) as a plasticizer to 100 parts by weight of a polyvinyl acetal resin having an acetylation degree of 12%
by mole, 4 as the number of carbon atoms of the acetal group, and an acetalization degree of 65% by mole, sufficiently kneading the mixture by a mixing roll, and extrusion-molding the mixture. The thickness of the sound-insulating layer was as shown in Table 1.
[0050]
(2) Production of a protection layer A protection layer was produced by adding 38 parts by weight of triethylene glycol di-2-ethylhexanoate (3G0) as a plasticizer to 100 parts by weight of a polyvinyl acetal resin having an acetylation degree of 1% by mole, 4 as the number of carbon atoms of the acetal group, and an acetalization degree of 68% by mole, sufficiently kneading the mixture by a mixing roll, and extrusion-molding the mixture.
[0051]
(3) Production of an interlayer film for a laminated glass The obtained sound-insulating layer was sandwiched between a pair of protection layers and thermally laminated to produce an interlayer film for a laminated glass with a cross-sectional shape of the wedge shape. The thickness of the interlayer film for a laminated glass and the wedge angle of the cross-section were as shown in Table 1. The cross-sectional shape was as shown in Fig. 2.
[0052]
(Example 2) A sound-insulating layer was produced by adding 65 parts by weight of triethylene glycol di-2-ethylhexanoate (3G0) as a plasticizer to 100 parts by weight of a polyvinyl acetal resin having an acetylation degree of 1%
by mole, 6 as the number of carbon atoms of the acetal group, and an acetalization degree of 65% by mole, sufficiently kneading the mixture by a mixing roll, and extrusion-molding the mixture. The thickness of the sound-insulating layer was as shown in Table 1.
Thereafter, a protection layer was produced and successively an interlayer film for a laminated glass was produced in the same manner as Example 1. The thickness of the interlayer film for a laminated glass and the wedge angle of the cross-section were as shown in Table 1. The cross-sectional shape was as shown in Fig. 2.
[0053]
(Example 3) A sound-insulating layer was produced by adding 63 parts by weight of triethylene glycol di-2-ethylhexanoate (3G0) as a plasticizer to 100 parts by weight of a polyvinyl acetal resin having an acetylation degree of 1%
by mole, 4 as the number of carbon atoms of the acetal group, and an acetalization degree of 78% by mole, sufficiently kneading the mixture by a mixing roll, and extrusion-molding the mixture. The thickness of the sound-insulating layer was as shown in Table 1.
Thereafter, a protection layer was produced and successively an interlayer film for a laminated glass was produced in the same manner as Example 1. The thickness of the interlayer film for a laminated glass and the wedge angle of the cross-section were as shown in Table 1. The cross-sectional shape was as shown in Fig. 2.
[0054]
(Comparative Example 1) A sound-insulating layer was produced by adding 65 parts by weight of triethylene glycol di-2-ethylhexanoate (3G0) as a plasticizer to 100 parts by weight of a polyvinyl acetal resin having an acetylation degree of 12%
by mole, 4 as the number of carbon atoms of the acetal group, and an acetalization degree of 65% by mole, sufficiently kneading the mixture by a mixing roll, and extrusion-molding the mixture. The thickness of the sound-insulating layer was as shown in Table 1.
Thereafter, a protection layer was produced and successively an interlayer film for a laminated glass was produced in the same manner as Example 1. The thickness of the interlayer film for a laminated glass and the wedge angle of the cross-section were as shown in Table 1. The cross-sectional shape was as shown in Fig. 2.
[0055]
(Comparative Example 2) A sound-insulating layer was produced by adding 65 parts by weight of triethylene glycol di-2-ethylhexanoate (3G0) as a plasticizer to 100 parts by weight of a polyvinyl acetal resin having an acetylation degree of 12%
by mole, 4 as the number of carbon atoms of the acetal group, and an acetalization degree of 65% by mole, sufficiently kneading the mixture by a mixing roll, and extrusion-molding the mixture. The thickness of the sound-insulating layer was as shown in Table 1.
Thereafter, a protection layer was produced and successively an interlayer film for a laminated glass was produced in the same manner as Example 1. The thickness of the interlayer film for a laminated glass and the wedge angle of the cross-section were as shown in Table 1. The cross-sectional shape was as shown in Fig. 2.
[0056]
(Comparative Example 3) A sound-insulating layer was produced by adding 65 parts by weight of triethylene glycol di-2-ethylhexanoate (3G0) as a plasticizer to 100 parts by weight of a polyvinyl acetal resin having an acetylation degree of 12%
by mole, 4 as the number of carbon atoms of the acetal group, and an acetalization degree of 65% by mole, sufficiently kneading the mixture by a mixing roll, and extrusion-molding the mixture. The thickness of the sound-insulating layer was as shown in Table 1.
Thereafter, a protection layer was produced and 5 successively an interlayer film for a laminated glass was produced in the same manner as Example 1. The thickness of the interlayer film for a laminated glass and the wedge angle of the cross-section were as shown in Table 1. The cross-sectional shape was as shown in Fig. 2.
10 [0057]
(Comparative Example 4) A sound-insulating layer was produced by adding 65 parts by weight of triethylene glycol di-2-ethylhexanoate (3G0) as a plasticizer to 100 parts by weight of a 15 polyvinyl acetal resin having an acetylation degree of 12%
by mole, 4 as the number of carbon atoms of the acetal group, and an acetalization degree of 65% by mole, sufficiently kneading the mixture by a mixing roll, and extrusion-molding the mixture. The thickness of the sound-20 insulating layer was as shown in Table 1.
Thereafter, a protection layer was produced and successively an interlayer film for a laminated glass was produced in the same manner as Example 1. The thickness of the interlayer film for a laminated glass and the wedge angle of the cross-section were as shown in Table 1. The cross-sectional shape was as shown in Fig. 2.
[0058]
<Evaluation>
The following evaluations were carried out for the interlayer films for a laminated glass obtained in Examples 1 to 3 and Comparative Examples 1 to 4. The results are shown in Table 1.
[0059]
(1) Sound-insulating property Each sample obtained by cutting obtained laminated glass into a size of 300 mm x 25 mm was vibrated by a vibration generating apparatus for a damping test (a vibrator G21-005D, manufactured by Shinken Co., Ltd.) and the vibration property obtained at that time was amplified by a mechanical impedance amplifier (XG-81, manufactured by RION Co., Ltd.) and the vibration spectrum was analyzed by an FFT spectrum analyzer (FFT analyzer HP3582A, manufactured by Yokogawa Hewlett Packard).
A graph showing the relation between sound frequency (Hz) and sound transmission loss (dB) at 20 C was produced from the ratio of loss factor and the resonance frequency of the glass measured in the manner to measure the minimum sound transmission loss (TL value) around a sound frequency of 2000 Hz and the evaluation was carried out based on the following standard. As the TL value is higher, the sound-insulating property is higher.
C): 35 dB or higher X: lower than 35 dB.
[0060]
(2) Occurrence of double image Each obtained laminated glass was disposed at a position of a front glass and display information was reflected upon the laminated glass from a display unit installed in a lower part and occurrence of a double image at a prescribed position was confirmed by eye observation and the evaluation was carried out based on the following standard.
C): No double image was confirmed.
X: A double image was confirmed.
[0061]
(3) Defoaming property evaluation A laminate body was produced by sandwiching each interlayer film for a laminated glass between two transparent float glass plates (length 30 cm, width 30 cm, thickness 3 mm).
The obtained laminate body was put in a rubber bag and held at a reduced pressure of -60 kPa (absolute pressure 16 kPa) for 10 minutes and heated in order that the temperature of the laminate body reach 100 C and then taken out of the rubber bag. Next, it was put in an autoclave and held at a temperature of 140 C and a pressure of 1.3 MPa for 10 minutes and then taken out of the autoclave after the temperature of the inside of the autoclave was decreased to 50 C. In such a manner, a laminated glass was produced.
The obtained laminated glass was heated in an oven at 200 C for 2 hours. Next, the laminated glass was taken out of the oven and after 3 hours, the appearance of the' laminated glass was observed with eyes. The number of sheets of the laminated glass in which foams with an outer diameter of 1 mm or larger were formed was investigated.
The number of the sheets of the laminated glass to be used in the test was 20. As the number of the sheets in which foams were formed was lower, the interlayer film for a laminated glass was found having a more excellent defoaming property. The results of the test were evaluated based on the following standard.
@: One sheet of laminated glass was found foaming.
C): Four sheets of laminated glass were found foaming.

u.) co N.) N) )--- 1---.
cri o cri o 01 o HO
Di cp tr m I--, N.) (I) '--' 1¨, I-I
Sound¨insulating layer Interlayer film for a laminated glass Evaluation Cross¨

Minimum Maximum Wedge angle Minimum thickness Maximum thickness (mrad) sectional TL value Occurrence of Defoaming thickness thickness (ii m) (ii m) shape (dB) double image property s n o ( 0 rn) (gm) n.) o) Examplel 100 150 800 1200 O. 40 Fig.2 37 0 0 ( ) 11.

Example2 100 150 700 1100 _ 0.30 Fig.2 36 0 0 u..) op Example3 80 200 600 1200 0. 58 Fig.2 IQ
(A./
NI
o o co o1 Comparative 100 120 700 800 0. 08 Fig.2 37 0 x ko Examplel IL
Comparative 15 30 800 1200 0. 40 Fig.2 31 x 0 @
Example2 ¨
, Comparative 20 30 300 450 0. 30 Fig.2 31 x 0 0 Example3 Comparative 100 150 800 1600 0. 80 Fig.2 37 0 x Example4 [0063]
(Examples 4 and 5) Each interlayer film for a laminated glass was produced in the same manner as Example 1, except that the cross-sectional shape was adjusted to be the wedge shape as shown in Fig. 1 and the thickness of the sound-insulating layer, the thickness of the interlayer film for a laminated glass, and the wedge angle were changed as shown in Table 2.
[0064]
(Comparative Examples 5 and 6) Each interlayer film for a laminated glass was produced in the same manner as Example 1, except that the cross-sectional shape was adjusted to be the wedge shape as shown in Fig. 1 and the thickness of the sound-insulating layer, the thickness of the interlayer film for a laminated glass, and the wedge angle were changed as shown in Table 2.
[0065]
<Evaluation>
With respect to each interlayer film for a laminated glass obtained in Examples 4 and 5 and Comparative Examples 5 and 6, same evaluations carried out for Examples 1 to 3 and Comparative Examples 1 to 4 were carried out. The results are shown in Table 2.

w w u-i 0 u-t ,..-3 CD
0) Q
NJ

o Sound¨insulating layer Intedayer film for a laminated glass Evaluation iv Cross¨
(5) 11.
Minimum Maximum Wedge angle sectional TL
value Occurrence of Defoaming o) Minimum thickness Maximum thickness (mrad) o thickness thickness shape (p m) (u m) shape double image property u..) (Om) (pm) .
co Example4 100 100 800 1200 0. 40 Fig.1 36 I\.) o iv ¨
o (Si co Example5 110 110 600 1200 O. 58 Fig.1 35 O
, li) I
Comparative 100 100 800 890 0. 08 Fig.1 36 0 x 0 H
(5) Example5 _ Comparative 30 x 0 15 15 800 1200 0. 40 Fig.1 Example6 .

[0067]
(Example 6) An interlayer film for a laminated glass was produced in the same manner as Example 1, except that the cross-sectional shape was adjusted to be the wedge shape as shown in Fig. 3 and the thickness of the sound-insulating layer, the thickness of the interlayer film for a laminated glass, and the wedge angle were changed as shown in Table 3.
[0068]
(Comparative Example 7) An interlayer film for a laminated glass was produced in the same manner as Example 1, except that the cross-sectional shape was adjusted to be the wedge shape as shown in Fig. 3 and the thickness of the sound-insulating layer, the thickness of the interlayer film for a laminated glass, and the wedge angle were changed as shown in Table 3.
[0069]
<Evaluation>
With respect to each interlayer film for a laminated glass obtained in Example 6 and Comparative Example 7, same evaluations carried out for Examples 1 to 3 and Comparative Examples 1 to 4 were carried out. The results are shown in Table 3.

u.) co n) N) i---, 01 CD
c) (31 c) 01 c) u1 ¨ ,¨, P.) CD
Cr ----1 1--. 0 (D
L,k) Sound-insulating layer Interlayer film for a laminated glass Evaluation Cross-Minimum Maximum Wedge angle Minimum thickness Maximum thickness (mrad) sectional TL value Occurrence of Defoaming n thickness thickness e shap (it m) ( M m) shape double image property (0 rn) (gm) o , I\) 0.) 11.
0.) o u..) op Example6 100 100 wedge shape protection wedge shape protection 0. 40 Fig.3 36 0 0 0 n.) layer: 350 layer: 750 IQ o o op rectangular shape rectangular shape protection layer:350 protection layer:350 O
li) I
H

Comparative 100 100 wedge shape protection wedge shape protection 0. 08 Fig.3 36 0 x 0 Example7 layer:350 layer:450 rectangular shape rectangular shape protection layer:350 protection layer:350 ...

[0071]
(Examples 7 and 8) An interlayer film for a laminated glass was produced in the same manner as Example 1, except that the cross-sectional shape was adjusted to be the wedge shape as shown in Fig. 4 and the thickness of the sound-insulating layer, the thickness of the interlayer film for a laminated glass, and the wedge angle were changed as shown in Table 4. The shape assisting layer was produced by using the resin with the same composition as that of the resin used for producing the protection layer in Example 1.
[0072]
(Comparative Examples 8 and 9) An interlayer film for a laminated glass was produced in the same manner as Example 1, except that the cross-sectional shape was adjusted to be the wedge shape as shown in Fig. 4 and the thickness of the sound-insulating layer, the thickness of the interlayer film for a laminated glass, and the wedge angle were changed as shown in Table 4. The shape assisting layer was produced by using the resin with the same composition as that of the resin used for producing the protection layer in Example 1.
[0073]
<Evaluation>
With respect to each interlayer film for a laminated glass obtained in Examples 7 and 8 and Comparative Examples 8 and 9, same evaluations carried out for Examples 1 to 3 and Comparative Examples 1 to 4 were carried out. The results are shown in Table 4.

W (,) Iv N
0-1 o 01 o Ln o Cn ¨ r--i HO
SID O
Sound¨insdlating layer Interlayer film for a laminated glass Evaluation Cross¨

Minimum Maximum Wedge angle Minimum thickness Maximum thickness (mrad) sectional TL value Occurrence of Defoaming .--, thickness = thickness shape (II m) ( II m) (d8) double image property (pm) (pm) .

wedge shape protection wedge shape protection layer: 200 layer: 200 Example7 100 100 rectangular shape rectangular shape protection 0. 40 Fig.4 36 0 0 0 protection layer: 200 layer: 200 shape assisting layer:400 shape assisting layer: 800 n I\) o) .i.
o) o wedge shape protection wedge shape protection u..) layer: 200 layer: 200 co Example8 100 100 rectangular shape rectangular shape protection 0. 58 Fig.4 36 0 0 0 n.) protection layer: 200 layer: 200 r'.) otiD o co shape assisting layer:400 shape assisting layer: 1050 O
li) I
.
H

Comparative wedge shape protection wedge shape protection 100 100 layer: 200 layer: 200 0, 08 Fig.4 36 0 x 0 Example8 rectangular shape rectangular shape protection protection layer: 200 layer: 200 shape assisting layer:400 shape assisting layer: 600 wedge shape protection wedge shape protection Comparative 15 15 layer:200 layer: 200 0. 40 Fig.4 30 x 0 0 Example9 rectangular shape rectangular shape protection protection layer: 285 layer: 285 shape assisting layer: 400 shape assisting layer: 800 INDUSTRIAL APPLICABILITY
[0075]
According to the present invention, it is made possible to provide an interlayer film for a laminated glass excellent in a sound-insulating property, which is preferably usable for a head up display and the like wherein a driver can look at the front view and an instrument display simultaneously without requiring to look down, and to provide a laminated glass.
[0076]
EXPLANATION OF SYMBOLS
[0077]
1 a protection layer 2 a sound-insulating layer 3 a shape assisting layer 4 the maximum thickness 5 the minimum thickness

Claims (16)

1. An interlayer film for a laminated glass, which comprises at least a pair of protection layers and a sound-insulating layer sandwiched between the pair of the protection layers, and which has a wedge shape as a cross-sectional shape, a wedge angle .theta. of 0.1 to 0.7 mrad, the maximum thickness of 2000 µm or thinner, and the minimum thickness of 400 µm or thicker, the minimum thickness of the sound-insulating layer being 20 µm or thicker, and wherein the sound-insulating layer is selected from the group consisting of 1) a layer which comprises 40 to 80 parts by weight of a plasticizer to 100 parts by weight of a polyvinyl acetal resin having an acetalization degree of 70 to 85% by mole, 2) a layer which comprises 40 to 80 parts by weight of a plasticizer to 100 parts by weight of a polyvinyl acetal resin having an acetal group having 4 to 5 carbon atoms and having an acetylation degree of 4% by mole or more, and 3) a layer which comprises 40 to 80 parts by weight of a plasticizer to 100 parts by weight of a polyvinyl acetal resin having an acetal group having 6 to 10 carbon atoms.
2. The interlayer film for a laminated glass according to claim 1, which further comprises a shape assisting layer laminated on at least one layer of the pair of the protection layers.
3. The interlayer film for a laminated glass according to claim 2, wherein the shape assisting layer contains a heat-insulating agent.
4. The interlayer film for a laminated glass according to claim 1, wherein the protection layer, and/or the sound-insulating layer contain a heat-insulating agent.
5. A laminated glass, which is obtained by using the interlayer film for a laminated glass according to any one of claims 1 to 4.
6. The interlayer film for a laminated glass according to claim 1, wherein the sound-insulating layer comprises 40 to 80 parts by weight of a plasticizer to 100 parts by weight of a polyvinyl acetal resin having an acetal group having 6 to 10 carbon atoms.
7. The interlayer film for a laminated glass according to claim 1, wherein the sound-insulating layer is a layer which comprises 40 to 80 parts by weight of a plasticizer to 100 parts by weight of a polyvinyl acetal resin having an acetalization degree of 70 to 85% by mole.
8. The interlayer film for a laminated glass according to claim 1, wherein the sound-insulating layer is a layer which comprises 40 to 80 parts by weight of a plasticizer to 100 parts by weight of a polyvinyl acetal resin having an acetal group having 4 to 5 carbon atoms and having an acetylation degree of 4% by mole or more.
9. An interlayer film for a laminated glass, which, comprises at least a pair of protection layers and a sound-insulating layer sandwiched between the pair of the protection layers, and which has a wedge shape as a cross-sectional shape, a wedge angle .theta. of 0.1 to 0.7 mrad, the maximum thickness of 2000 µm or thinner, and the minimum thickness of 400 µm or thicker, the minimum thickness of the sound-insulating layer being 20 µm or thicker, wherein the protection layer contains 25 to 55 parts by weight of a plasticizer to 100 parts by weight of a polyvinyl acetal resin having an acetylation degree of 3% by mole or lower, 3 to 4 carbon atoms of an acetal group, and an acetalization degree of 60 to 70% by mole, and wherein the sound-insulating layer contains 40-80 parts by weight of a plasticizer to 100 parts by weight of a polyvinyl acetal resin.
10. The interlayer film for a laminated glass according to claim 9, wherein the protection layer and/or the sound-insulating layer contain a heat-insulating agent.
11. A laminated glass, which is obtained by using the interlayer film for a laminated glass according to claim 10.
12. The interlayer film for a laminated glass according to claim 9, which further comprises a shape assisting layer laminated on at least one layer of the pair of the protection layers.
13. The interlayer film for a laminated glass according to claim 12, wherein the shape assisting layer contain a heat-insulating agent.
14. A laminated glass, which is obtained by using the interlayer film for a laminated glass according to claim 13.
15. A laminated glass, which is obtained by using the interlayer film for a laminated glass according to claim 12.
16. A laminated glass, which is obtained by using the interlayer film for a laminated glass according to claim 9.
CA2646038A 2006-05-12 2007-05-11 Interlayer film for laminated glass and laminated glass Active CA2646038C (en)