CA2587944A1 - Composition with enhanced heat resistance property - Google Patents

Composition with enhanced heat resistance property Download PDF

Info

Publication number
CA2587944A1
CA2587944A1 CA002587944A CA2587944A CA2587944A1 CA 2587944 A1 CA2587944 A1 CA 2587944A1 CA 002587944 A CA002587944 A CA 002587944A CA 2587944 A CA2587944 A CA 2587944A CA 2587944 A1 CA2587944 A1 CA 2587944A1
Authority
CA
Canada
Prior art keywords
composition
insulation
polymer
parts
antioxidant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CA002587944A
Other languages
French (fr)
Other versions
CA2587944C (en
Inventor
Thomas S. Lin
Jeffrey M. Cogen
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Union Carbide Corp
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Publication of CA2587944A1 publication Critical patent/CA2587944A1/en
Application granted granted Critical
Publication of CA2587944C publication Critical patent/CA2587944C/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

Compositions including a polymer, a primary antioxidant, a secondary antioxidant, and a metal deactivator selected from at least one of 2,2′-oxamido bis[ethyl 3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate] and oxalyl bis(benzylidenehydrazide), are disclosed. The compositions can also include a light stabilizer. The compositions can be used to manufacture insulations for wire and cable. The compositions have improved long-term heat aging and also retain their color when exposed to heat. A method of making an insulation for a conductor, such as a wire or a cable, made from a composition is also provided.

Claims (40)

1. A composition comprising:
a. a polymer;

b. a metal deactivator selected from at least one of 2,2'-oxamido bis[ethyl 3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate] and oxalyl bis(benzylidenehydrazide);

c. a primary antioxidant; and d. a secondary antioxidant.
2. The composition of claim 1, wherein the primary antioxidant comprises a hindered phenol antioxidant.
3. The composition of claim 2, wherein the hindered phenol antioxidant comprises pentaerythrityl-tetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate].
4. The composition of claim 1, wherein the secondary antioxidant comprises a thiosynergist.
5. The composition of claim 4, wherein the thiosynergist comprises pentaerythritol tetrakis (B-laurylthiopropionate).
6. The composition of claim 1, wherein the polymer comprises a polyolefin, a thermoplastic elastomer, a thermoplastic olefin, a thermoplastic vulcanizate, or a combination thereof.
7. The composition of claim 6, wherein the polyolefin comprises polypropylene, polyethylene, polyisoprene, polybutadiene, ethylene vinyl acetate, ethylene ethyl acrylate and combinations thereof.
8. The composition of claim 1, wherein the metal deactivator is included at about 0.05 to about 10 parts by weight per about 100 parts by weight of the polymer.
9. The composition of claim 1, wherein the hindered phenol is included at about 0.05 to about 10 parts by weight per about 100 parts by weight of the polymer.
10. The composition of claim 1, wherein the thiosynergist is included at about 0.05 to about 30 parts by weight per about 100 parts by weight of the polymer.
11. The composition of claim 1, further comprising a light stabilizer that is included at about 0.05 to about 10 parts by weigh per about 100 parts by weight of the polymer.
12. The composition of claim 1, further comprising a hindered amine light stabilizer.
13. The composition of claim 12, wherein the light stabilizer comprises reaction products of 1,6-hexanediamine, N,N'-bis(2,2,6,6-tetramethyl-4-piperidinyl)-polymer with 2,4,6-trichloro-1,3,5-triazine with N-butyl-l-butanamine and N-butyl-2,2,6,6-tetramethyl-4-piperidinamine.
14. The composition of claim 1, wherein the composition has improved heat aging when compared to compositions not including the metal deactivator when assessed by at least one of ISO 6722 or LV-112 heat aging method.
15. The composition of claim 14, further comprising a cross-linking agent.
16. A composition comprising:

a. a polymer;

b. a metal deactivator selected from at least one of 2,2'-oxamido bis[ethyl 3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate] and oxalyl bis(benzylidenehydrazide);

c. a primary antioxidant comprising a hindered phenol antioxidant;
and d. a secondary antioxidant comprising a thiosynergist.
17. The composition of claim 16, further comprising a hindered amine light stabilizer.
18. An insulation for a wire or a cable, the insulation comprising a composition comprising:

a. a polymer;

b. a metal deactivator selected from at least one of 2,2'-oxamido bis[ethyl 3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate] and oxalyl bis(benzylidenehydrazide);

c. a primary antioxidant; and d. a secondary antioxidant.
19. The insulation of claim 18, wherein the primary antioxidant comprises a hindered phenol antioxidant.
20. The insulation of claim 18, wherein the hindered phenol comprises pentaerythrityl-tetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate].
21. The insulation of claim 18, wherein the secondary antioxidant comprises a thiosynergist.
22. The insulation of claim 21, wherein the thiosynergist comprises pentaerythritol tetrakis (B-laurylthiopropionate).
23. The insulation of claim 18, wherein the polymer comprises a polyolefin, a thermoplastic elastomer, a thermoplastic olefin, a thermoplastic vulcanizate, or a combination thereof.
24. The insulation of claim 23, wherein the polyolefin comprises polypropylene, polyethylene, polyisoprene, polybutadiene, ethylene vinyl acetate, ethylene ethyl acrylate and combinations thereof.
25. The insulation of claim 18, wherein the metal deactivator is included at about 0.05 to about 10 parts by weight per about 100 parts by weight of the polymer.
26. The insulation of claim 18, wherein the hindered phenol is included at about 0.05 to about 10 parts by weight per about 100 parts by weight of the polymer.
27. The insulation of claim 18, wherein the thiosynergist is included at about 0.05 to about 30 parts by weight per about 100 parts by weight of the polymer.
28. The insulation of claim 18, further comprising a light stabilizer that is included at about 0.05 to about 10 parts by weight per about 100 parts by weight of the polymer.
29. The insulation of claim 18, further comprising a hindered amine light stabilizer.
30. The insulation of claim 29, wherein the light stabilizer comprises reaction products of 1,6-hexanediamine, N,N'-bis(2,2,6,6-tetramethyl-4-piperidinyl)-polymer with 2,4,6-trichloro-1,3,5-triazine with N-butyl-1-butanamine and N-butyl-2,2,6,6-tetramethyl-4-piperidinamine.
31. The insulation of claim 18, wherein the polymer is crosslinked.
32. The insulation of claim 18, wherein the composition has an improved property when subjected to heat aging when compared to compositions not including the metal deactivator when assessed by at least one of ISO 6722 or LV-112 heat aging method.
33. The insulation of claim 32, further comprising a cross-linking agent.
34. An insulation for a wire or a cable, the insulation comprising a composition comprising:

a. a polymer;

b. a metal deactivator selected from at least one of 2,2'-oxamido bis[ethyl 3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate] and oxalyl bis(benzylidenehydrazide);

c. a primary antioxidant comprising a hindered phenol antioxidant;
and d. a secondary antioxidant comprising a thiosynergist.
35. The insulation of claim 34, further comprising a hindered amine light stabilizer.
36. A method of making an insulation, the method comprising:

a. blending a polymer, a primary antioxidant, a secondary antioxidant, and a metal deactivator selected from at least one of 2,2'-oxamido bis[ethyl 3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate] and oxalyl bis(benzylidenehydrazide) to form a composition; and b. forming the composition into a desired shape around a conductor.
37. The method of claim 36, wherein the conductor comprises a wire or a cable.
38. The method of claim 36, wherein the forming comprises extruding the composition.
39. The method of claim 36, wherein the forming comprises molding the composition.
40. The method of claim 36, further comprising crosslinking the composition.
CA2587944A 2004-11-30 2005-10-26 Composition with enhanced heat resistance property Expired - Fee Related CA2587944C (en)