CA2528662A1 - Glove having improved donning characteristics - Google Patents
Glove having improved donning characteristics Download PDFInfo
- Publication number
- CA2528662A1 CA2528662A1 CA 2528662 CA2528662A CA2528662A1 CA 2528662 A1 CA2528662 A1 CA 2528662A1 CA 2528662 CA2528662 CA 2528662 CA 2528662 A CA2528662 A CA 2528662A CA 2528662 A1 CA2528662 A1 CA 2528662A1
- Authority
- CA
- Canada
- Prior art keywords
- article
- mass
- functionalized beads
- beads
- donning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
An elastomeric article includes a substrate body formed from an elastomeric material, and a plurality of functionalized beads covalently bonded to the elastomeric material.
Description
GLOVE HAVING IMPROVED DONNING CHARACTERISTICS
BACKGROUND OF THE INVENTION
Tightly fitting elastomeric articles, such as surgical and examination gloves, may be difficult to don due to blocking, the tendency of the glove to stick to itself. As a result, gloves often contain a powdered lubricant on the surface that contacts the skin of the wearer to facilitate donning. Most commonly, epichlorohydrin treated crosslinked cornstarch is dusted on the inner surface of the glove during manufacturing.
to while use of cornstarch does improve the donning characteristics of the glove, it may not be feasible for all applications. One such situation is the use of powders for surgical glove applications. If some of the powder inadvertently enters the surgical site, it may cause complications for the patient. For instance, the powder may carry an infectious agent or the patient may be allergic to the i5 powder.
Other techniques may be used to improve the donning characteristics of surgical and examination gloves. These techniques include, for example, manufacturing the glove from a modified latex, using an inner layer of a hydrophilic polymer, applying a slip coating to the inner surface of the glove, and 2o the like. However, as some degree of blocking may still occur with these techniques, there remains a need for a glove with improved donning characteristics.
SUMMARY OF THE INVENTION
25 The present invention generally relates to an elastomeric article, for example, a glove. The article includes a substrate body formed from an elastomeric material, and a plurality of functionalized beads covalently bonded to the elastomeric material. The functionalized beads may generally be formed from a polymer having a vinyl group. The vinyl group may be a carbon-carbon 3o vinyl group or an acrylate group. In some instances, the article may include from about 0.0001 mass % to about 10 mass % functionalized beads. In other instances, the article may include from about 0.001 mass % to about 5 mass functionalized beads. In yet other instances, the article may include from about 0.01 mass % to about 3 mass % functionalized beads.
The present invention also relates to an elastomeric article including a substrate body having a first surface, and a donning layer overlying the first surface, where the donning layer includes a polymeric material and a plurality of covalendy bonded functionalized beads. In some instances, the polymeric material may include a hydrogel. In some instances, the donning layer may include from about 0.01 mass % to about SO mass % functionalized beads. In other instances, the donning layer may include from about 1 mass % to about 50 mass % functionalized beads. In yet other instances, the donning layer may include from about 10 mass % to about 25 mass % functionalized beads.
to The present invention further relates to an elastomeric article including a substrate body formed from natural rubber, the substrate body having a first surface, a donning layer overlying the first surface, the donning layer formed from a hydrogel and a plurality of functionalized beads covalently bonded to the hydrogel, and a lubricant layer overlying at least a portion of the donning layer.
i5 The functionalized beads may generally be formed from a polymer having a vinyl group. The lubricant layer may include a silicone emulsion.
The present invention also relates to a composition for use in forming a textured article. The composition includes a polymeric material, and a plurality of functionalized beads covalently bonded to the polymeric material. In some 2o instances, the polymeric material may include a hydrogel.
BRIEF DESCRIPTION ~F THE DRAWINGS
FIG. 1 depicts an article that may be formed according to the present invention, namely a glove.
25 FIG. 2A depicts a schematic cross-sectional illustration of the article of FIG. 1 taken along a line 2-2, the article including a substrate body and a donning layer, where the donning layer includes a plurality of covalently bonded functionalized beads.
FIG. 2B depicts another schematic cross-sectional illustration of the 3o article of FIG. 1 taken along a line 2-2, the article including a substrate body, a donning layer, and a lubricant layer, where the donning layer includes a plurality of covalently bonded functionalized beads.
DESCRIPTION OF THE INVENTION
The present invention generally relates to an elastomeric article having improved donning characteristics, for example a condom or glove. As used herein, the term "elastomeric article" refers to an article formed predominantly from an elastomeric material. The axticle includes a plurality of functionalized beads on the wearer-contacting surface of the axticle to facilitate donning.
The beads are covalently bonded to the material that forms the article, so no separate binder material is needed to affix the beads to the article. The beads cause the overall surface area of the wearer-contacting surface to be reduced, thereby to facilitating donning. To better understand the present invention, a more detailed description is provided below.
An elastomeric article to be formed, for example, a glove 20 (FIG. 1) includes an inside, or wearer-contacting, surface 22 and an outside surface 24.
The inside surface 22 has a textured topography due to the presence of a z5 plurality of functionalized beads 34 (best seen in FIG.'s 2A and 2B) covalendy bonded to the material that forms the inside surface 22. As used herein, the term "inside surface" refers to the surface of the article that contacts the body of the wearer. As used herein, the term "outside surface" refers to the surface of the article that is distal from the body of the wearer. The beads do not extend 2o through the entire thickness of the glove, so the barrier properties of the glove are not compromised.
The glove includes a substrate body 26 having a first surface 28 and a second surface 30 (FIG. 2A-2B). As used herein, "first surface" refers to the surface of the substrate body proximal to the body of the wearer. As used 25 herein, "second surface" refers to the surface of the substrate body distal to the body of the wearer.
The article of the present invention may include a single layer or multiple layers as desired. In a single layer glove including only the substrate body, the first surface may form the inside surface of the glove. However, in a multi-layer 3o glove having additional layers proximal to the body of the wearer, the additional layer or layers may each form a portion of the inside surface, or the entire inside surface, as desired. Likewise, in a single layer glove including only the substrate body, the second surface may form the outside surface of the glove. However, in a multi-layer glove having additional layers distal from the body of the wearer, the additional layer or layers may each form a portion of the outside surface, or the entire outside surface, as desired.
For example, as depicted in FIG. 2A, the article may include a donning layer 32 overlying at least a portion of the first surface 28 of the substrate body 26. In such an article, the donning layer 32 forms at least a portion of the inside surface 22 of the glove 20. In some such embodiments, the donning layer may include a plurality of functionalized beads 34 covalently bonded to the material that forms the donning layer. As depicted in FIG. 2B, the article may also include other layers, such as a lubricant layer 36 that overlies at least a portion of to the donning layer 32. In such an article, the lubricant layer 36 forms at least a portion of the inside surface 22 of the glove 20.
The article of the present invention may be formed from any suitable elastomeric material, and by any suitable technique, for example dipping, spraying, tumbling, drying, and curing. As used herein, the term "elastomeric i5 material" refers to a polymeric material that is capable of being easily stretched or expanded, and will substantially return to its previous shape upon release of the stretching or expanding force. In one embodiment, the elastomeric material may include natural rubber, which is generally provided as a natural rubber latex.
In another embodiment, the elastomeric material may include nitrile butadiene 2o rubber, and in particular, may include carboxylated nitrite butadiene rubber. In other embodiments, the elastomeric material may include a styrene-ethylene butylene-styrene block copolymer, styrene-isoprene-styrene block copolymer, styrene-butadiene-styrene block copolymer, styrene-isoprene block copolymer, styrene-butadiene block copolymer, synthetic isoprene, chloroprene rubber, 25 polyvinyl chloride, silicone rubber, or a combination thereof.
The article of the present invention, for example, the glove 20, may include a donning layer 32 overlying at least a portion of the first surface 28 of the substrate body 26 (FIG. 2A). The donning layer may be formed from any polymeric material that is capable of facilitating donning of the glove. Some 3o examples of suitable materials for the donning layer 28 include, but are not limited to, polybutadienes, for example, 1,2-syndiotactic polybutadiene, polyurethanes, acrylic polymers, and the like.
In one embodiment, the polymeric material that forms the donning layer may include a hydrogel. As used herein, the term "hydrogel" refers to a polymeric material that is capable of absorbing more than 20% its weight in water while maintaining a distinct three-dimensional structure. A hydrogel may be formed from a variety of hydrophilic monomers. Examples of monomers that may be used to form a hydrogel that may be suitable for use with the present invention include hydroxy ethyl methacrylate (HEMA), hydroxy ethyl acrylate (HEA), methacrylic acid (MAA), acrylic acid (AA), vinyl pyrrolidone, acrylamide, dimethyl acrylamide, and so forth. While several hydrophilic monomers are set forth herein, it should be understood that any hydrophilic monomer may be polymerized to form a hydrogel that may be suitable for use with the present invention.
In some instances, it may be desirable to copolymerize a hydrophobic monomer with a hydrophilic monomer. By doing so, the mechanical properties and the performance characteristics of the resulting hydrogel may be modified for a particular application. Examples of such hydrophilic monomers include 2-ethyl hexyl acrylate (EHA), methyl methacrylate, styrene, butyl acrylate, hydroxy propyl methacrylate, and acrylated silicone oligomers. While several hydrophobic monomers are set forth herein, it should be understood that any hydrophobic monomer may be copolymerized with a hydrophilic monomer to form a hydrogel that may be suitable for use with the present invention.
2o Furthermore, more than two monomers may be used to form a hydrogel for use with the present invention. For instance, a hydrogel may include various ratios of HEMA, MAA, and EHA. Any ratio may be suitable for a given application, and in one embodiment, the ratio of HEMA:MAA:EHA may be about 5:1:1. ~Uhere more hydrophobic character is desired in the hydrogel, the concentration of the EHA may be increased. Thus, the properties of the hydrogel may be modified for a given application.
In another embodiment, the polymeric material that forms the donning layer may include an unsaturated styrene-isoprene-styrene (SIS) block copolymer having tri- or radial-blocks. In one such embodiment, the SIS block copolymer 3o may have a polystyrene end block content of from about 10 mass % to about mass % of the total weight of the SIS block copolymer. In another such embodiment, the SIS block copolymer may have a polystyrene end block content of from about 15 mass % to about 18 mass % of the total weight of the SIS
block copolymer. Moreover, the molecular weight of the polystyrene end blocks may typically be at least about 5,000 grams per mole. Some examples of suitable mid-block unsaturated SIS block copolymers include, but are not limited to, Kraton~ D1107 available from I~raton Polymers and Vector~ 511 and Vector~
4111 available from Dexco Polymers of Houston, Texas.
In yet another embodiment, the polymeric material that forms the donning layer may include an unsaturated styrene-butylene-styrene (SBS) block copolymer. One example of an SBS block copolymer that may be suitable for use as a donning layer is commercially available from Dexco Polymers (Houston, Texas) under the trade name VECTOR~ 8508. VECTOR~ 8508 is believed to 1o be a linear, pure triblock copolymer (containing less than 1% diblock copolymer) produced using anionic polymerization. Another example of an SBS polymer that may be suitable for use as a donning layer is also commercially available from Dexco Polymers (Houston, Texas) under the trade name VECTORO
8550.
i5 ~~Uhile various polymeric materials that may be used to form the donning layer are set forth herein, it should be understood that any suitable polymeric material may be used as desired.
In accordance with the present invention, the substrate body or the donning layer may include a plurality of functionalized beads. The beads may 2o have any shape, and in some instances, may have a spherical shape. In other instances, the beads may have an elliptical shape. In yet other instances, the beads may have an irregular shape.
The functionalized beads may be formed from any material that is capable of being covalently bonded to the material that forms the substrate body or the 25 donning layer, provided that the bead does not plasticize, dissolve, dissociate, or otherwise degrade during formation of the article.
In general, the beads may be formed from any polymer having a vinyl group. The vinyl group may then be used to covalently bond the bead to the material that forms the substrate body or the donning layer, as desired. In some 3o embodiments, the material may include a carbon-carbon vinyl group. In other embodiments, the material may include an acrylate group.
The beads of the present invention may be formed in a variety of ways.
While various techniques are described herein, it should be understood that any other suitable technique may be used.
In one embodiment, the beads may be synthesized to contain the needed vinyl functionality. Where this technique is used, the vinyl functionality will likely be present throughout the functionalized bead. Such materials may include polymers, copolymers, terpolymers, and so forth, of monomers having a vinyl group, for example, hydroxy ethyl methacrylate (HEMA), hydroxy ethyl acrylate (HEA), methacrylic acid (MAA), acrylic acid (AA), vinyl pyrrolidone, acrylamide, dimethyl acrylamide, 2-ethyl hexyl acrylate (EHA), methyl methacrylate, styrene, butyl acrylate, hydroxy propyl methacrylate, and acrylated silicone oligomers, and so forth. ~X~hile several such monomers are set forth herein, it should be 1o understood that any polymeric bead having a vinyl functional group may be used with the present invention.
In another embodiment, the beads may be formed from a material having a hydroxyl functionality. The beads may then be reacted with a material having the needed vinyl group to introduce the vinyl group into the material that forms the bead. Examples of materials that include hydroxyl functionality include polyvinyl alcohol, silica, and copolymers of a monomer with vinyl functionality (e.g., vinyl alcohol) and another monomer (e.g., styrene, methyl methacrylate (MMA), ethylene, or propylene).
In yet another embodiment, the beads may be formed from a material that 2o does not have hydroxyl functionality, but that is capable of being subject to a surface conversion to produce hydroxyl groups on the surface of the bead.
Examples of such materials include polymethyl methacrylate (PMMA), polyethylene, polypropylene, melamine resin, carboxylated melamine resin, polyvinyltoluene, polystyrene, copolymers of styrene and butadiene, copolymers of styrene and vinyltoluene, copolymers of styrene and divinylbenzene, and copolymers of styrene and methacrylic acid. Such beads may then be subjected to a surface conversion process by which a hydroxyl group is introduced into the starting material. For example, PMMA may be subjected to a transesterification process to introduce a hydroxyl group. Other materials, such as polypropylene 3o and polyethylene, may be, for example, exposed to ozone followed by heating to introduce the needed hydroxyl functionality. While exemplary oxidative techniques are set forth herein, it should be understood by those skilled in the art that other oxidative techniques may be employed as desired. The hydroxyl group may then be subsequently converted to an acrylate group by reacting it with an appropriate chemistry.
Thus, in one instance, the starting material may include a plurality of PMMA beads, which do not contain the needed vinyl functionality for later covalent attachment to the substrate body or the donning layer. The PMMA
beads may be suspended in aqueous ethylene glycol. Using acidic or basic conditions to catalyze a transesterification reaction, the methyl group of the PMMA are replaced with hydroxyl groups. The hydroxyl groups are then available for reaction with, for example, 2-isocyanatoethyl methacrylate. The to isocyanate portion of the 2-isocyanatoethyl methacrylate reacts with the hydroxyl-modified PMMA beads to result in a surface acrylated functional bead.
In another instance, the hydroxyl groups may be reacted with glycidyl methacrylate. In this instance, the epoxy portion of the glycidyl methacrylate reacts with hydroxyl-modified PMMA beads to also result in a surface acrylated i5 functional bead.
The bead having the vinyl functionality may then be covalently bonded to the material that forms the substrate body. Where a donning layer is included in the article of the present invention, it may be desirable to covalently bond the beads 34 to the material that forms the donning layer 32 (FIG. 2A). As stated 2o above, the functionalized beads may be formed in a variety of manners, including direct synthesis of the functionalized beads and surface conversion of polymeric beads (transesterification coupled with reaction with an appropriate chemistry to attach an acrylate group to the surface). In one instance, the functionalized bead may be covalently bonded to a hydrogel donning layer, which may, for example, 25 be formed from HEMA and other monomers described above. To do so, the functionalized beads may be suspended in, for example, an aqueous solution of the monomers used to form the hydrogel donning layer and a free radical initiator. When free radical polymerization is initiated, the monomers form polymer chains that grow in length and also incorporate the functionalized beads 3o into the structure via the acrylate functionality of the beads. Thus, the beads axe covalently bonded to the hydrogel polymeric material used to form the donning layer of the glove.
The beads may be present in any suitable amount that facilitates donning without compromising the physical integi.~ty of the donning layer or impeding its s purpose. In some embodiments, the beads may be present in an amount of about 0.01 mass % to about 80 mass % of the resulting (dried) donning layer.
In other embodiments, the beads may be present in an amount of about 1 mass to about 50 mass % of the resulting (dried) donning layer. In yet other embodiments, the beads may be present in an amount of about 10 mass % to about 25 mass % of the resulting (dried) donning layer.
In some instances, the resulting (dried) donning layer may be present in an amount of about 5 mass % of the resulting (solidified) glove. Thus, in one embodiment, the functionalized beads may be present in an amount of from 1o about 0.0001 mass % to about 10 mass % of the resulting (solidified) glove.
In another embodiment, the functionalized beads may be present in an amount of from about 0.001 mass % to about 5 mass % of the resulting (solidified) glove.
In yet another embodiment, the functionalized beads may be present in an amount of from about 0.01 mass % to about 3 mass % of the resulting (solidified) glove.
In some embodiments, a lubricant layer 36 (FIG. 2B) may also overlie at least a portion of the donning layer 32 to aid in donning the article. In one embodiment, the lubricant layer may include a silicone or silicone-based component. As used herein, the term "silicone" generally refers to a broad 2o family of synthetic polymers that have a repeating silicon-oxygen backbone, including, but not limited to, polydimethylsiloxane and polysiloxanes having hydrogen-bonding functional groups selected from the group consisting of amino, carboxyl, hydroxyl, ether, polyether, aldehyde, ketone, amide, ester, and thiol groups. In some embodiments, polydimethylsiloxane and/or modified polysiloxanes may be used as the silicone component in accordance with the present invention. Some suitable modified polysiloxanes that may be used in the present invention include, but are not limited to, phenyl-modified polysiloxanes, vinyl-modified polysiloxanes, methyl-modified polysiloxanes, fluoro-modified polysiloxanes, alkyl-modified polysiloxanes, alkoxy-modified polysiloxanes, 3o amino-modified polysiloxanes, and combinations thereof.
Examples of some suitable phenyl-modified polysiloxanes include, but are not limited to, dimethyldiphenylpolysiloxane copolymers, dimethyl and methylphenylpolysiloxane copolymers, polymethylphenylsiloxane, and methylphenyl and dimethylsiloxane copolymers. Phenyl modified polysiloxanes that have a relatively low phenyl content (less than about 50 mole %) may be particularly effective in the present invention. For example, the phenyl-modified polysiloxane may be a Biphenyl-modified silicone, such as a diphenylsiloxane-modified dimethylpolysiloxane. In some embodiments, the phenyl modified s polysiloxane contains phenyl units in an amount from about 0.5 mole % to about 50 mole %. In other embodiments, the phenyl-modified polysiloxane contains phenyl units in an amount less than about 25 mole %. In yet other embodiments, the phenyl modified polysiloxane contains phenyl units in an amount less than about 15 mole %. In one particular embodiment, a 1o diphenylsiloxane-modified dimethylpolysiloxane may be used that contains diphenylsiloxane units in an amount less than about 5 mole %. In still another embodiment, a diphenylsiloxane-modified dimethylpolysiloxane may be used that contains diphenylsiloxane units in an amount less than about 2 mole %.
The diphenylsiloxane-modified dimethylpolysiloxane may be synthesized by 15 reacting diphenylsiloxane with dimethylsiloxane.
As indicated above, fluoro-modified polysiloxanes may also be used with the present invention. For instance, one suitable fluoro-modified polysiloxane that may be used is a trifluoropropyl modified polysiloxane, such as a trifluoropropylsiloxane modified dimethylpolysiloxane. A
2o trifluoropropylsiloxane modified dimethylpolysiloxane maybe synthesized by reacting methyl, 3,3,3 trifluoropropylsiloxane with dimethylsiloxane. The fluoro-modified silicones may contain from about 5 mole % to about 95 mole % of fluoro groups, such as trifluoropropylsiloxane units. In another embodiment, the fluoro-modified silicones maycontain from about 40 mole % to about 60 2s mole %-of fluoro groups. In yet another embodiment, a trifluoropropylsiloxane-modified dimethylpolysiloxane may be used that contains 50 mole trifluoropropylsiloxane units.
Other modified polysiloxanes may be utilized With the present invention.
For instance, some suitable vinyl modified polysiloxanes include, but are not 30 limited to, vinyldimethyl terminated polydimethylsiloxanes, vinylmethyl and dimethylpolysiloxane copolymers, vinyldimethyl terminated vinylmethyl and dimethylpolysiloxane copolymers, divinylmethyl terminated polydimethylsiloxanes, and vinylphenylmethyl terminated polydimethy3siloxanes.
Further, some methyl modified polysiloxanes that may be used include, but are not limited to, dimethylhydro terminated polydimethylsiloxanes, methylhydro and dimethylpolysiloxane copolymers, methylhydro terminated methyloctyl siloxane copolymers and methylhydro and phenylmethyl siloxane copolymers.
In addition, some examples of amino-modified polysiloxanes include, but are not limited to, polymethyl (3-aminopropyl)-siloxane and polymethyl [3-(2-aminoethyl) aminopropyl]-siloxane.
The particular polysiloxanes described above are meant to include hetero-or co-polymers formed from polymerization or copolymerization of dimethylsiloxane cyclics and diphenylsiloxane cyclics or trifluoropropylsiloxane 1o cyclics with appropriate endcapping units. Thus, for example, the terms "diphenyl modified dimethylpolysiloxanes" and "copoloymers of diphenylpolysiloxane and dimethylpolysiloxane" may be used interchangeably.
Moreover, other examples of polysiloxanes that may be used with the present invention are described in U.S. Patents 5,742,943 to Chen and 6,306,514 to i5 Weikel, et al., which are incorporated herein in their entirety by reference thereto for all purposes.
In some embodiments, the lubricant layer may include a silicone emulsion.
One such silicone emulsion that may be suitable for use with the present invention is DC 365, a pre-emulsified silicone (35% TSC) that is commercially 2o available from Dow Corning Corporation (Midland, Michigan). DC 365 is believed to contain 40-70 mass % water, 30-60 mass % methyl-modified polydimethylsiloxane, 1-5 mass % propylene glycol, 1-5 mass % polyethylene glycol sorbitan monolaurate, and 1-5 mass % octylphenoxy polyethoxy ethanol.
Another silicone emulsion that may be suitable for use with the present 25 invention is SM 2140, commercially available from GE Silicones (~Xjaterford, New York). SM 2140 is a pre-emulsified silicone (50% TSC) that is believed to contain 30-60 mass % water, 30-60 mass % amino-modified polydimethylsiloxane, 1-5% ethoxylated nonyl phenol, 1-5 mass % trimethyl-4-nonyloxypolyethyleneoxy ethanol, and minor percentages of acetaldehyde, 3o formaldehyde, and 1,4 dioxane. Another silicone emulsion that may be suitable for use with the present invention is SM 2169 available from GE Silicones (~Xjaterford, New York). SM 2169 is a pre-emulsified silicone that is believed to contain 30-60 mass % water, 60-80 mass % polydimethylsiloxa.ne, 1-5 mass polyoxyethylene lauryl ether, and a small amount of formaldehyde. Yet another silicone that may be suitable for use with the present invention is commercially available from GE Silicones (~X~aterford, New York) under the trade name AF-60. AF-60 is believed to contain polydimethylsiloxane, acetylaldehyde, and small percentages of emulsifiers. If desired, these pre-emulsified silicones may be diluted with water or other solvents prior to use.
In another embodiment, the lubricant layer may contain a quaternary ammonium compound, such as that commercially available from Goldschmidt Chemical Corporation of Dublin, Ohio under the trade name VERISOFT~
BTMS. VERISOFT~ BTMS is believed to contain behnyl trimethyl sulfate and 1o cetyl alcohol. Thus for example, in one embodiment, the lubricant layer includes a quaternary ammonium compound such as VERISOFT~ BTMS and a silicone emulsion such as SM X169.
In another embodiment, the lubricant may include, for example, a cationic surfactant (e.g., cetyl pyridinium chloride), an anionic surfactant (e.g., sodium lauryl sulfate), a nonionic surfactant, an amphoteric surfactant, or a combination thereo f.
In some embodiments, one or more cationic surfactants may be used.
Examples of cationic surfactants that may be suitable for use with the present invention include, for example, behenetrimonium methosulfate, 2o distearyldimonium chloride, dimethyl dioctadecyl ammonium chloride, cetylpyridinium chloride, methylbenzethonium chloride, hexadecylpyridinium chloride, hexadecyltrimethylammonium chloride, benzalkonium chloride, dodecylpyridinium chloride, the corresponding bromides, hydroxyethylheptadecylimidazolium halides, coco aminopropyl betaine, and coconut alkyldimethylammonium betaine. Additional cationic surfactants that may be used include methyl bis(hydrogenated tallow amidoethyl)-2-hydroxyethly ammonium methyl sulfate, methyl bis(tallowamido ethyl)-2-hydroxyethyl ammonium methyl sulfate, methyl bis(soya amidoethyl)-2-hydroxyethyl ammonium methyl sulfate, methyl bis(canola amidoethyl)-2-hydroxyethyl 3o ammonium methyl sulfate, methyl bis(tallowamido ethyl)-2-tallow imidazolinium methyl sulfate, methyl bis(hydrogenated tallowamido ethyl)-2-hydrogenated tallow imidazolinium methyl sulfate, methyl bis (ethyl tallowate)-2-hydroxyethyl ammonium methyl sulfate, methyl bis(ethyl tallowate)-2-hydroxyethyl ammonium methyl sulfate, dehydrogenated tallow dimethyl ammonium chloride, didecyl dimethyl ammonium chloride, dioctyl dimethyl ammonium chloride, octyl decyl dimethyl ammonium chloride diamidoamine ethoxylates, diamidoamine imidazolines, and quaternary ester salts.
In some embodiments, one or more nonionic surfactants may be used.
Nonionic surfactants typically have a hydrophobic base, such as a long chain alkyl group or an alkylated aryl group, and a hydroplvlic chain comprising a certain number (e.g., 1 to about 30) of ethoxy and/or propoxy moieties.
Examples of some classes of nonionic surfactants that may be used include, but 1o are not limited to, ethoxylated alkylphenols, ethoxylated and propoxylated fatty alcohols, polyethylene glycol ethers of methyl glucose, polyethylene glycol ethers of sorbitol, ethylene oxide-propylene oxide block copolymers, ethoxylated esters of fatty (C$ -C18) acids, condensation products of ethylene oxide with long chain amines or amides, condensation products of ethylene oxide with alcohols, and mixtures thereof.
Specific examples of suitable nonionic surfactants include, but are not limited to, methyl gluceth-10, PEG-20 methyl glucose distearate, PEG-20 methyl glucose sesquistearate, Cm-15 p~e~-20, ceteth-8, ceteth-12, dodoxynol-12, laureth-15, PEG-20 castor oil, polysorbate 20, steareth-20, polyoxyethylene-10 2o cetyl ether, polyoxyethylene-10 stearyl ether, polyoxyethylene-20 cetyl ether, polyoxyethylene-10 oleyl ether, polyoxyethylene-20 oleyl ether, an ethoxylated nonylphenol, ethoxylated octylphenol, ethoxylated dodecylphenol, or ethoxylated fatty (CG -C2~ alcohol, including 3 to 20 ethylene oxide moieties, polyoxyethylene-20 isohexadecyl ether, polyoxyethylene-23 glycerol laurate, polyoxy-ethylene-20 glyceryl stearate, PPG-10 methyl glucose ether, PPG-20 methyl glucose ether, polyoxyethylene-20 sorbitan monoesters, polyoxyethylene-80 castor oil, polyoxyethylene-15 tridecyl ether, polyoxy-ethylene-6 tridecyl ether, laureth-2, laureth-3, laureth-4, PEG-3 castor oil, PEG 600 dioleate, PEG 400 dioleate, oxyethanol, 2,6,8-trimethyl-4-nonyloxypolyethylene oxyethanol;
octylphenoxy polyethoxy ethanol, nonylphenoxy polyethoxy ethanol, 2,6,8-trimethyl-4-nonyloxypolyethylene alkyleneoxypolyethyleneoxyethanol, alkyleneoxypolyethyleneoxyethanol; alkyleneoxypolyethyleneoxyethanol, and mixtures thereof.
Additional nonionic surfactants that may be used include water soluble alcohol ethylene oxide condensates that are the condensation products of a secondary aliphatic alcohol containing between about 8 to about 18 carbon atoms in a straight or branched chain configuration condensed with between s about 5 to about 30 moles of ethylene oxide. Such nonionic surfactants are commercially available under the trade name Tergitol~ from Union Carbide Corp., Danbury, Conn. Specific examples of such commercially available nonionic surfactants of the foregoing type are Ci1 -Ci5 secondary all~anols condensed with either 9 moles of ethylene oxide (Tergitol~ 15-S-9) or 12 moles of ethylene ~ oxide (Tergitol~ 15-S-12) marketed by Union Carbide Corp., (Danbury, Conn.).
Other suitable nonionic surfactants include the polyethylene oxide condensates of one mole of alkyl phenol containing from about 8 to 18 carbon atoms in a straight- or branched chain all~yl group with about 5 to 30 moles of ethylene oxide. Specific examples of alliyl phenol ethoxylates include nonyl condensed with about 9.5 moles of ethylene oxide per mole of nonyl phenol, dinonyl phenol condensed with about 12 moles of ethylene oxide per mole of phenol, dinonyl phenol condensed with about 15 moles of ethylene oxide per mole of phenol and diisoctylphenol condensed with about 15 moles of ethylene oxide per mole of phenol. Commercially available nonionic surfactants of this type include Igepal~ CO-630 (a nonyl phenol ethoxylate) marketed byISP Core.
(Wayne, N.J.). Suitable non-ionic ethoxylated octyl and nonyl phenols include those having from about 7 to about 13 ethoxyunits.
In some embodiments, one or more amphoteric surfactants maybe used.
2s One class of amphoteric surfactants that maysuitable for use with the present invention includes the derivatives of secondary and tertiary amines having aliphatic radicals that are straight chain or branched, where one of the aliphatic substituents contains from about 8 to 18 carbon atoms and at least one of the aliphatic substituents contains an anionic water-solubilizing group, such as a 3o carboxy, sulfonate, or sulfate group. Some examples of amphoteric surfactants include, but are not limited to, sodium 3-(dodecylamino)propionate, sodium 3-(dodecylamino)-propane-1-sulf onate, sodium 2- (dodecyiamino) ethyl self ate, sodium 2-(dimethylamino)octadecanoate, disodium 3-(N carboxymethyl-dodecylamino)propane-1-sulfonate, sodium 1-carboxymethyl 2-undecylimidazole, disodium octadecylirninodiacetate, and sodium N, N bis(2-hydroxyethyl)-2-sulfato-3-dodecoxypropylamine.
Additional classes of suitable amphoteric surfactants include phosphobetaines and phosphitaines. For instance, some examples of such amphoteric surfactants include, but are not limited to, sodium coconut N
methyl taurate, sodium oleyl N methyl taurate, sodium tall oil acid N methyl taurate, cocodimethylcarboxymethylbetaine, lauryldimethylcarboxymethylbetaine, lauryldimethylcarboxyethylbetaine, cetyldimethylcarboxymethylbetaine, sodium palmitoyl N methyl taurate, oleyldimethylgammacarboxypropylbetaine, lauryl 1o bis-(2-hydroxypropyl)-carboxyethylbetaine, di-sodium oleamide PEG-2 sulfosuccinate, laurylamido-bis-(2-hydroxyethyl) propylsultaine, la,ury3.-bis-(2-hydroxyethyl) carboxymethylbetaine, cocoamidodimethylpropylsultaine, stearylamidodimethylpropylsultaine, TEA oleamido PEG-2 sulfosuccinate, disodium oleamide MEA sulfosuccinate, disodium oleamide MIPA
sulfosuccinaxe, disodium ricinoleamide MEAsulfosuccinate, disodium undecylenamide MEA sulfosuccinate, disodium wheat germamido MEA
sulfosuccinate, disodium wheat germamido PEG-2 sulfosuccinate, disodium isostearamideo MEA sulfosuccinate, cocoamido propyl monosodium phosphitaine, lauric myristic amido propyl monosodium phosphitaine, 2o cocoamido disodium 3-hydroxypropyl phosphobetaine, lauric myristic amido disodium 3-hydroxypropyl phosphobetaine, lauric myristic amido glyceryl phosphobetaine, lauric myristic amido carboxy disodium 3-hydroxypropyl phosphobetaine, cocoamphoglycinate, cocoamphocarboxyglycinate, capryloamphocarboxyglycinate, lauroamphocarboxyglycinate, lauroamphoglycinate, capryloamphocarboxypropionate, lauroamphocarboxypropionate, cocoamphopropionate, cocoamphocarboxypropionate, dihydroxyethyl tallow glycinate, and mixtures thereof .
In certain instances, one or more anionic surfactants may be used.
3o Suitable anionic surf actants include, but are not limited to, alkyl sulfates, alliyl ether sulfates, alliyl ether sulfonates, sulfate esters of an all~ylphenoxy polyoxyethylene ethanol, alpha-olefin sulfonates, beta alkoxy alkane sulfonates, all~ylauryl self onates, alliyl monoglyceride sulfates, all~yl monoglyceride sulf onates, allyl carbonates, alkyl ether carboxylates, fatty acids, sulf osuccinates, sarcosinates, octoxynol or nonoxynol phosphates, taurates, fatty taurides, fatty acid amide polyoxyethylene sulfates, isethionates, or mixtures thereof.
Particular examples of some suitable anionic surfactants include, but are not limited to, C$ -C18 alkyl sulfates, C$ -C18 fatty acid salts, C$ -C18 alkyl ether sulfates having one or two moles of ethoxylation, C8 -C1$ alkamine oxides, C8 C1$ alkoyl sarcosinates, C$ -C1$ sulfoacetates, C$ -C1$ sulfosuccinates, C$ -C1$ alkyl Biphenyl oxide disulfonates, C$ -C1$ alkyl carbonates, C$ -C1$ alpha-olefin sulfonates, methyl ester sulfonates, and blends thereof. The C$ -C1$ alkyl group may be straight chain (e.g., lauryl) or branched (e.g., 2-ethylhexyl). The cation of 1o the anionic surfactant may be an alkali metal (e.g., sodium or potassium), ammonium, C1 -Cø alkylammonium (e.g., mono-, di-, tri), or C1 -C3 alkanolammonium (e.g., mono-, di-, tri).
Specific examples of such anionic surfactants include, but are not limited to, lauryl sulfates, octyl sulfates, 2-ethylhexyl sulfates, lauramine oxide, decyl i5 sulfates, tridecyl sulfates, cocoates, lauroyl sarcosinates, lauryl sulfosuccinates, linear C1o Biphenyl oxide disulfonates, lauryl sulfosuccinates, lauryl ether sulfates (1 and 2 moles ethylene oxide), myristyl sulfates, oleates, stearates, tallates, ricinoleates, cetyl sulfates, and so forth.
Alternatively, any other treatment may be applied to the inside surface to 2o impart the desired attribute to the glove. Other such treatments include emollients that may provide skin health benefits, antimicrobials, and so forth.
The article of the present invention features enhanced donning characteristics. The presence of covalently bonded functionalized beads within the article decreases the overall coefficient of friction of the surface and permits 25 the glove to be donned more readily. Further, since the particles axe chemically covalently bonded the article, no additional binder is needed. This provides a processing advantage over other particulate compositions that require use of a binder to ensure that particles will not inadvertently dissociate from the glove.
Additionally, where a lubricant is utilized in accordance with the present 3o invention, donning is further enhanced.
The invention may be embodied in other specific forms without departing from the scope and spirit of the inventive characteristics thereof. The present embodiments therefore are to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims rather than by the foregoing description, and all changes which come within the meaning and range of equivalency of the claims are therefore intended to be embraced therein.
BACKGROUND OF THE INVENTION
Tightly fitting elastomeric articles, such as surgical and examination gloves, may be difficult to don due to blocking, the tendency of the glove to stick to itself. As a result, gloves often contain a powdered lubricant on the surface that contacts the skin of the wearer to facilitate donning. Most commonly, epichlorohydrin treated crosslinked cornstarch is dusted on the inner surface of the glove during manufacturing.
to while use of cornstarch does improve the donning characteristics of the glove, it may not be feasible for all applications. One such situation is the use of powders for surgical glove applications. If some of the powder inadvertently enters the surgical site, it may cause complications for the patient. For instance, the powder may carry an infectious agent or the patient may be allergic to the i5 powder.
Other techniques may be used to improve the donning characteristics of surgical and examination gloves. These techniques include, for example, manufacturing the glove from a modified latex, using an inner layer of a hydrophilic polymer, applying a slip coating to the inner surface of the glove, and 2o the like. However, as some degree of blocking may still occur with these techniques, there remains a need for a glove with improved donning characteristics.
SUMMARY OF THE INVENTION
25 The present invention generally relates to an elastomeric article, for example, a glove. The article includes a substrate body formed from an elastomeric material, and a plurality of functionalized beads covalently bonded to the elastomeric material. The functionalized beads may generally be formed from a polymer having a vinyl group. The vinyl group may be a carbon-carbon 3o vinyl group or an acrylate group. In some instances, the article may include from about 0.0001 mass % to about 10 mass % functionalized beads. In other instances, the article may include from about 0.001 mass % to about 5 mass functionalized beads. In yet other instances, the article may include from about 0.01 mass % to about 3 mass % functionalized beads.
The present invention also relates to an elastomeric article including a substrate body having a first surface, and a donning layer overlying the first surface, where the donning layer includes a polymeric material and a plurality of covalendy bonded functionalized beads. In some instances, the polymeric material may include a hydrogel. In some instances, the donning layer may include from about 0.01 mass % to about SO mass % functionalized beads. In other instances, the donning layer may include from about 1 mass % to about 50 mass % functionalized beads. In yet other instances, the donning layer may include from about 10 mass % to about 25 mass % functionalized beads.
to The present invention further relates to an elastomeric article including a substrate body formed from natural rubber, the substrate body having a first surface, a donning layer overlying the first surface, the donning layer formed from a hydrogel and a plurality of functionalized beads covalently bonded to the hydrogel, and a lubricant layer overlying at least a portion of the donning layer.
i5 The functionalized beads may generally be formed from a polymer having a vinyl group. The lubricant layer may include a silicone emulsion.
The present invention also relates to a composition for use in forming a textured article. The composition includes a polymeric material, and a plurality of functionalized beads covalently bonded to the polymeric material. In some 2o instances, the polymeric material may include a hydrogel.
BRIEF DESCRIPTION ~F THE DRAWINGS
FIG. 1 depicts an article that may be formed according to the present invention, namely a glove.
25 FIG. 2A depicts a schematic cross-sectional illustration of the article of FIG. 1 taken along a line 2-2, the article including a substrate body and a donning layer, where the donning layer includes a plurality of covalently bonded functionalized beads.
FIG. 2B depicts another schematic cross-sectional illustration of the 3o article of FIG. 1 taken along a line 2-2, the article including a substrate body, a donning layer, and a lubricant layer, where the donning layer includes a plurality of covalently bonded functionalized beads.
DESCRIPTION OF THE INVENTION
The present invention generally relates to an elastomeric article having improved donning characteristics, for example a condom or glove. As used herein, the term "elastomeric article" refers to an article formed predominantly from an elastomeric material. The axticle includes a plurality of functionalized beads on the wearer-contacting surface of the axticle to facilitate donning.
The beads are covalently bonded to the material that forms the article, so no separate binder material is needed to affix the beads to the article. The beads cause the overall surface area of the wearer-contacting surface to be reduced, thereby to facilitating donning. To better understand the present invention, a more detailed description is provided below.
An elastomeric article to be formed, for example, a glove 20 (FIG. 1) includes an inside, or wearer-contacting, surface 22 and an outside surface 24.
The inside surface 22 has a textured topography due to the presence of a z5 plurality of functionalized beads 34 (best seen in FIG.'s 2A and 2B) covalendy bonded to the material that forms the inside surface 22. As used herein, the term "inside surface" refers to the surface of the article that contacts the body of the wearer. As used herein, the term "outside surface" refers to the surface of the article that is distal from the body of the wearer. The beads do not extend 2o through the entire thickness of the glove, so the barrier properties of the glove are not compromised.
The glove includes a substrate body 26 having a first surface 28 and a second surface 30 (FIG. 2A-2B). As used herein, "first surface" refers to the surface of the substrate body proximal to the body of the wearer. As used 25 herein, "second surface" refers to the surface of the substrate body distal to the body of the wearer.
The article of the present invention may include a single layer or multiple layers as desired. In a single layer glove including only the substrate body, the first surface may form the inside surface of the glove. However, in a multi-layer 3o glove having additional layers proximal to the body of the wearer, the additional layer or layers may each form a portion of the inside surface, or the entire inside surface, as desired. Likewise, in a single layer glove including only the substrate body, the second surface may form the outside surface of the glove. However, in a multi-layer glove having additional layers distal from the body of the wearer, the additional layer or layers may each form a portion of the outside surface, or the entire outside surface, as desired.
For example, as depicted in FIG. 2A, the article may include a donning layer 32 overlying at least a portion of the first surface 28 of the substrate body 26. In such an article, the donning layer 32 forms at least a portion of the inside surface 22 of the glove 20. In some such embodiments, the donning layer may include a plurality of functionalized beads 34 covalently bonded to the material that forms the donning layer. As depicted in FIG. 2B, the article may also include other layers, such as a lubricant layer 36 that overlies at least a portion of to the donning layer 32. In such an article, the lubricant layer 36 forms at least a portion of the inside surface 22 of the glove 20.
The article of the present invention may be formed from any suitable elastomeric material, and by any suitable technique, for example dipping, spraying, tumbling, drying, and curing. As used herein, the term "elastomeric i5 material" refers to a polymeric material that is capable of being easily stretched or expanded, and will substantially return to its previous shape upon release of the stretching or expanding force. In one embodiment, the elastomeric material may include natural rubber, which is generally provided as a natural rubber latex.
In another embodiment, the elastomeric material may include nitrile butadiene 2o rubber, and in particular, may include carboxylated nitrite butadiene rubber. In other embodiments, the elastomeric material may include a styrene-ethylene butylene-styrene block copolymer, styrene-isoprene-styrene block copolymer, styrene-butadiene-styrene block copolymer, styrene-isoprene block copolymer, styrene-butadiene block copolymer, synthetic isoprene, chloroprene rubber, 25 polyvinyl chloride, silicone rubber, or a combination thereof.
The article of the present invention, for example, the glove 20, may include a donning layer 32 overlying at least a portion of the first surface 28 of the substrate body 26 (FIG. 2A). The donning layer may be formed from any polymeric material that is capable of facilitating donning of the glove. Some 3o examples of suitable materials for the donning layer 28 include, but are not limited to, polybutadienes, for example, 1,2-syndiotactic polybutadiene, polyurethanes, acrylic polymers, and the like.
In one embodiment, the polymeric material that forms the donning layer may include a hydrogel. As used herein, the term "hydrogel" refers to a polymeric material that is capable of absorbing more than 20% its weight in water while maintaining a distinct three-dimensional structure. A hydrogel may be formed from a variety of hydrophilic monomers. Examples of monomers that may be used to form a hydrogel that may be suitable for use with the present invention include hydroxy ethyl methacrylate (HEMA), hydroxy ethyl acrylate (HEA), methacrylic acid (MAA), acrylic acid (AA), vinyl pyrrolidone, acrylamide, dimethyl acrylamide, and so forth. While several hydrophilic monomers are set forth herein, it should be understood that any hydrophilic monomer may be polymerized to form a hydrogel that may be suitable for use with the present invention.
In some instances, it may be desirable to copolymerize a hydrophobic monomer with a hydrophilic monomer. By doing so, the mechanical properties and the performance characteristics of the resulting hydrogel may be modified for a particular application. Examples of such hydrophilic monomers include 2-ethyl hexyl acrylate (EHA), methyl methacrylate, styrene, butyl acrylate, hydroxy propyl methacrylate, and acrylated silicone oligomers. While several hydrophobic monomers are set forth herein, it should be understood that any hydrophobic monomer may be copolymerized with a hydrophilic monomer to form a hydrogel that may be suitable for use with the present invention.
2o Furthermore, more than two monomers may be used to form a hydrogel for use with the present invention. For instance, a hydrogel may include various ratios of HEMA, MAA, and EHA. Any ratio may be suitable for a given application, and in one embodiment, the ratio of HEMA:MAA:EHA may be about 5:1:1. ~Uhere more hydrophobic character is desired in the hydrogel, the concentration of the EHA may be increased. Thus, the properties of the hydrogel may be modified for a given application.
In another embodiment, the polymeric material that forms the donning layer may include an unsaturated styrene-isoprene-styrene (SIS) block copolymer having tri- or radial-blocks. In one such embodiment, the SIS block copolymer 3o may have a polystyrene end block content of from about 10 mass % to about mass % of the total weight of the SIS block copolymer. In another such embodiment, the SIS block copolymer may have a polystyrene end block content of from about 15 mass % to about 18 mass % of the total weight of the SIS
block copolymer. Moreover, the molecular weight of the polystyrene end blocks may typically be at least about 5,000 grams per mole. Some examples of suitable mid-block unsaturated SIS block copolymers include, but are not limited to, Kraton~ D1107 available from I~raton Polymers and Vector~ 511 and Vector~
4111 available from Dexco Polymers of Houston, Texas.
In yet another embodiment, the polymeric material that forms the donning layer may include an unsaturated styrene-butylene-styrene (SBS) block copolymer. One example of an SBS block copolymer that may be suitable for use as a donning layer is commercially available from Dexco Polymers (Houston, Texas) under the trade name VECTOR~ 8508. VECTOR~ 8508 is believed to 1o be a linear, pure triblock copolymer (containing less than 1% diblock copolymer) produced using anionic polymerization. Another example of an SBS polymer that may be suitable for use as a donning layer is also commercially available from Dexco Polymers (Houston, Texas) under the trade name VECTORO
8550.
i5 ~~Uhile various polymeric materials that may be used to form the donning layer are set forth herein, it should be understood that any suitable polymeric material may be used as desired.
In accordance with the present invention, the substrate body or the donning layer may include a plurality of functionalized beads. The beads may 2o have any shape, and in some instances, may have a spherical shape. In other instances, the beads may have an elliptical shape. In yet other instances, the beads may have an irregular shape.
The functionalized beads may be formed from any material that is capable of being covalently bonded to the material that forms the substrate body or the 25 donning layer, provided that the bead does not plasticize, dissolve, dissociate, or otherwise degrade during formation of the article.
In general, the beads may be formed from any polymer having a vinyl group. The vinyl group may then be used to covalently bond the bead to the material that forms the substrate body or the donning layer, as desired. In some 3o embodiments, the material may include a carbon-carbon vinyl group. In other embodiments, the material may include an acrylate group.
The beads of the present invention may be formed in a variety of ways.
While various techniques are described herein, it should be understood that any other suitable technique may be used.
In one embodiment, the beads may be synthesized to contain the needed vinyl functionality. Where this technique is used, the vinyl functionality will likely be present throughout the functionalized bead. Such materials may include polymers, copolymers, terpolymers, and so forth, of monomers having a vinyl group, for example, hydroxy ethyl methacrylate (HEMA), hydroxy ethyl acrylate (HEA), methacrylic acid (MAA), acrylic acid (AA), vinyl pyrrolidone, acrylamide, dimethyl acrylamide, 2-ethyl hexyl acrylate (EHA), methyl methacrylate, styrene, butyl acrylate, hydroxy propyl methacrylate, and acrylated silicone oligomers, and so forth. ~X~hile several such monomers are set forth herein, it should be 1o understood that any polymeric bead having a vinyl functional group may be used with the present invention.
In another embodiment, the beads may be formed from a material having a hydroxyl functionality. The beads may then be reacted with a material having the needed vinyl group to introduce the vinyl group into the material that forms the bead. Examples of materials that include hydroxyl functionality include polyvinyl alcohol, silica, and copolymers of a monomer with vinyl functionality (e.g., vinyl alcohol) and another monomer (e.g., styrene, methyl methacrylate (MMA), ethylene, or propylene).
In yet another embodiment, the beads may be formed from a material that 2o does not have hydroxyl functionality, but that is capable of being subject to a surface conversion to produce hydroxyl groups on the surface of the bead.
Examples of such materials include polymethyl methacrylate (PMMA), polyethylene, polypropylene, melamine resin, carboxylated melamine resin, polyvinyltoluene, polystyrene, copolymers of styrene and butadiene, copolymers of styrene and vinyltoluene, copolymers of styrene and divinylbenzene, and copolymers of styrene and methacrylic acid. Such beads may then be subjected to a surface conversion process by which a hydroxyl group is introduced into the starting material. For example, PMMA may be subjected to a transesterification process to introduce a hydroxyl group. Other materials, such as polypropylene 3o and polyethylene, may be, for example, exposed to ozone followed by heating to introduce the needed hydroxyl functionality. While exemplary oxidative techniques are set forth herein, it should be understood by those skilled in the art that other oxidative techniques may be employed as desired. The hydroxyl group may then be subsequently converted to an acrylate group by reacting it with an appropriate chemistry.
Thus, in one instance, the starting material may include a plurality of PMMA beads, which do not contain the needed vinyl functionality for later covalent attachment to the substrate body or the donning layer. The PMMA
beads may be suspended in aqueous ethylene glycol. Using acidic or basic conditions to catalyze a transesterification reaction, the methyl group of the PMMA are replaced with hydroxyl groups. The hydroxyl groups are then available for reaction with, for example, 2-isocyanatoethyl methacrylate. The to isocyanate portion of the 2-isocyanatoethyl methacrylate reacts with the hydroxyl-modified PMMA beads to result in a surface acrylated functional bead.
In another instance, the hydroxyl groups may be reacted with glycidyl methacrylate. In this instance, the epoxy portion of the glycidyl methacrylate reacts with hydroxyl-modified PMMA beads to also result in a surface acrylated i5 functional bead.
The bead having the vinyl functionality may then be covalently bonded to the material that forms the substrate body. Where a donning layer is included in the article of the present invention, it may be desirable to covalently bond the beads 34 to the material that forms the donning layer 32 (FIG. 2A). As stated 2o above, the functionalized beads may be formed in a variety of manners, including direct synthesis of the functionalized beads and surface conversion of polymeric beads (transesterification coupled with reaction with an appropriate chemistry to attach an acrylate group to the surface). In one instance, the functionalized bead may be covalently bonded to a hydrogel donning layer, which may, for example, 25 be formed from HEMA and other monomers described above. To do so, the functionalized beads may be suspended in, for example, an aqueous solution of the monomers used to form the hydrogel donning layer and a free radical initiator. When free radical polymerization is initiated, the monomers form polymer chains that grow in length and also incorporate the functionalized beads 3o into the structure via the acrylate functionality of the beads. Thus, the beads axe covalently bonded to the hydrogel polymeric material used to form the donning layer of the glove.
The beads may be present in any suitable amount that facilitates donning without compromising the physical integi.~ty of the donning layer or impeding its s purpose. In some embodiments, the beads may be present in an amount of about 0.01 mass % to about 80 mass % of the resulting (dried) donning layer.
In other embodiments, the beads may be present in an amount of about 1 mass to about 50 mass % of the resulting (dried) donning layer. In yet other embodiments, the beads may be present in an amount of about 10 mass % to about 25 mass % of the resulting (dried) donning layer.
In some instances, the resulting (dried) donning layer may be present in an amount of about 5 mass % of the resulting (solidified) glove. Thus, in one embodiment, the functionalized beads may be present in an amount of from 1o about 0.0001 mass % to about 10 mass % of the resulting (solidified) glove.
In another embodiment, the functionalized beads may be present in an amount of from about 0.001 mass % to about 5 mass % of the resulting (solidified) glove.
In yet another embodiment, the functionalized beads may be present in an amount of from about 0.01 mass % to about 3 mass % of the resulting (solidified) glove.
In some embodiments, a lubricant layer 36 (FIG. 2B) may also overlie at least a portion of the donning layer 32 to aid in donning the article. In one embodiment, the lubricant layer may include a silicone or silicone-based component. As used herein, the term "silicone" generally refers to a broad 2o family of synthetic polymers that have a repeating silicon-oxygen backbone, including, but not limited to, polydimethylsiloxane and polysiloxanes having hydrogen-bonding functional groups selected from the group consisting of amino, carboxyl, hydroxyl, ether, polyether, aldehyde, ketone, amide, ester, and thiol groups. In some embodiments, polydimethylsiloxane and/or modified polysiloxanes may be used as the silicone component in accordance with the present invention. Some suitable modified polysiloxanes that may be used in the present invention include, but are not limited to, phenyl-modified polysiloxanes, vinyl-modified polysiloxanes, methyl-modified polysiloxanes, fluoro-modified polysiloxanes, alkyl-modified polysiloxanes, alkoxy-modified polysiloxanes, 3o amino-modified polysiloxanes, and combinations thereof.
Examples of some suitable phenyl-modified polysiloxanes include, but are not limited to, dimethyldiphenylpolysiloxane copolymers, dimethyl and methylphenylpolysiloxane copolymers, polymethylphenylsiloxane, and methylphenyl and dimethylsiloxane copolymers. Phenyl modified polysiloxanes that have a relatively low phenyl content (less than about 50 mole %) may be particularly effective in the present invention. For example, the phenyl-modified polysiloxane may be a Biphenyl-modified silicone, such as a diphenylsiloxane-modified dimethylpolysiloxane. In some embodiments, the phenyl modified s polysiloxane contains phenyl units in an amount from about 0.5 mole % to about 50 mole %. In other embodiments, the phenyl-modified polysiloxane contains phenyl units in an amount less than about 25 mole %. In yet other embodiments, the phenyl modified polysiloxane contains phenyl units in an amount less than about 15 mole %. In one particular embodiment, a 1o diphenylsiloxane-modified dimethylpolysiloxane may be used that contains diphenylsiloxane units in an amount less than about 5 mole %. In still another embodiment, a diphenylsiloxane-modified dimethylpolysiloxane may be used that contains diphenylsiloxane units in an amount less than about 2 mole %.
The diphenylsiloxane-modified dimethylpolysiloxane may be synthesized by 15 reacting diphenylsiloxane with dimethylsiloxane.
As indicated above, fluoro-modified polysiloxanes may also be used with the present invention. For instance, one suitable fluoro-modified polysiloxane that may be used is a trifluoropropyl modified polysiloxane, such as a trifluoropropylsiloxane modified dimethylpolysiloxane. A
2o trifluoropropylsiloxane modified dimethylpolysiloxane maybe synthesized by reacting methyl, 3,3,3 trifluoropropylsiloxane with dimethylsiloxane. The fluoro-modified silicones may contain from about 5 mole % to about 95 mole % of fluoro groups, such as trifluoropropylsiloxane units. In another embodiment, the fluoro-modified silicones maycontain from about 40 mole % to about 60 2s mole %-of fluoro groups. In yet another embodiment, a trifluoropropylsiloxane-modified dimethylpolysiloxane may be used that contains 50 mole trifluoropropylsiloxane units.
Other modified polysiloxanes may be utilized With the present invention.
For instance, some suitable vinyl modified polysiloxanes include, but are not 30 limited to, vinyldimethyl terminated polydimethylsiloxanes, vinylmethyl and dimethylpolysiloxane copolymers, vinyldimethyl terminated vinylmethyl and dimethylpolysiloxane copolymers, divinylmethyl terminated polydimethylsiloxanes, and vinylphenylmethyl terminated polydimethy3siloxanes.
Further, some methyl modified polysiloxanes that may be used include, but are not limited to, dimethylhydro terminated polydimethylsiloxanes, methylhydro and dimethylpolysiloxane copolymers, methylhydro terminated methyloctyl siloxane copolymers and methylhydro and phenylmethyl siloxane copolymers.
In addition, some examples of amino-modified polysiloxanes include, but are not limited to, polymethyl (3-aminopropyl)-siloxane and polymethyl [3-(2-aminoethyl) aminopropyl]-siloxane.
The particular polysiloxanes described above are meant to include hetero-or co-polymers formed from polymerization or copolymerization of dimethylsiloxane cyclics and diphenylsiloxane cyclics or trifluoropropylsiloxane 1o cyclics with appropriate endcapping units. Thus, for example, the terms "diphenyl modified dimethylpolysiloxanes" and "copoloymers of diphenylpolysiloxane and dimethylpolysiloxane" may be used interchangeably.
Moreover, other examples of polysiloxanes that may be used with the present invention are described in U.S. Patents 5,742,943 to Chen and 6,306,514 to i5 Weikel, et al., which are incorporated herein in their entirety by reference thereto for all purposes.
In some embodiments, the lubricant layer may include a silicone emulsion.
One such silicone emulsion that may be suitable for use with the present invention is DC 365, a pre-emulsified silicone (35% TSC) that is commercially 2o available from Dow Corning Corporation (Midland, Michigan). DC 365 is believed to contain 40-70 mass % water, 30-60 mass % methyl-modified polydimethylsiloxane, 1-5 mass % propylene glycol, 1-5 mass % polyethylene glycol sorbitan monolaurate, and 1-5 mass % octylphenoxy polyethoxy ethanol.
Another silicone emulsion that may be suitable for use with the present 25 invention is SM 2140, commercially available from GE Silicones (~Xjaterford, New York). SM 2140 is a pre-emulsified silicone (50% TSC) that is believed to contain 30-60 mass % water, 30-60 mass % amino-modified polydimethylsiloxane, 1-5% ethoxylated nonyl phenol, 1-5 mass % trimethyl-4-nonyloxypolyethyleneoxy ethanol, and minor percentages of acetaldehyde, 3o formaldehyde, and 1,4 dioxane. Another silicone emulsion that may be suitable for use with the present invention is SM 2169 available from GE Silicones (~Xjaterford, New York). SM 2169 is a pre-emulsified silicone that is believed to contain 30-60 mass % water, 60-80 mass % polydimethylsiloxa.ne, 1-5 mass polyoxyethylene lauryl ether, and a small amount of formaldehyde. Yet another silicone that may be suitable for use with the present invention is commercially available from GE Silicones (~X~aterford, New York) under the trade name AF-60. AF-60 is believed to contain polydimethylsiloxane, acetylaldehyde, and small percentages of emulsifiers. If desired, these pre-emulsified silicones may be diluted with water or other solvents prior to use.
In another embodiment, the lubricant layer may contain a quaternary ammonium compound, such as that commercially available from Goldschmidt Chemical Corporation of Dublin, Ohio under the trade name VERISOFT~
BTMS. VERISOFT~ BTMS is believed to contain behnyl trimethyl sulfate and 1o cetyl alcohol. Thus for example, in one embodiment, the lubricant layer includes a quaternary ammonium compound such as VERISOFT~ BTMS and a silicone emulsion such as SM X169.
In another embodiment, the lubricant may include, for example, a cationic surfactant (e.g., cetyl pyridinium chloride), an anionic surfactant (e.g., sodium lauryl sulfate), a nonionic surfactant, an amphoteric surfactant, or a combination thereo f.
In some embodiments, one or more cationic surfactants may be used.
Examples of cationic surfactants that may be suitable for use with the present invention include, for example, behenetrimonium methosulfate, 2o distearyldimonium chloride, dimethyl dioctadecyl ammonium chloride, cetylpyridinium chloride, methylbenzethonium chloride, hexadecylpyridinium chloride, hexadecyltrimethylammonium chloride, benzalkonium chloride, dodecylpyridinium chloride, the corresponding bromides, hydroxyethylheptadecylimidazolium halides, coco aminopropyl betaine, and coconut alkyldimethylammonium betaine. Additional cationic surfactants that may be used include methyl bis(hydrogenated tallow amidoethyl)-2-hydroxyethly ammonium methyl sulfate, methyl bis(tallowamido ethyl)-2-hydroxyethyl ammonium methyl sulfate, methyl bis(soya amidoethyl)-2-hydroxyethyl ammonium methyl sulfate, methyl bis(canola amidoethyl)-2-hydroxyethyl 3o ammonium methyl sulfate, methyl bis(tallowamido ethyl)-2-tallow imidazolinium methyl sulfate, methyl bis(hydrogenated tallowamido ethyl)-2-hydrogenated tallow imidazolinium methyl sulfate, methyl bis (ethyl tallowate)-2-hydroxyethyl ammonium methyl sulfate, methyl bis(ethyl tallowate)-2-hydroxyethyl ammonium methyl sulfate, dehydrogenated tallow dimethyl ammonium chloride, didecyl dimethyl ammonium chloride, dioctyl dimethyl ammonium chloride, octyl decyl dimethyl ammonium chloride diamidoamine ethoxylates, diamidoamine imidazolines, and quaternary ester salts.
In some embodiments, one or more nonionic surfactants may be used.
Nonionic surfactants typically have a hydrophobic base, such as a long chain alkyl group or an alkylated aryl group, and a hydroplvlic chain comprising a certain number (e.g., 1 to about 30) of ethoxy and/or propoxy moieties.
Examples of some classes of nonionic surfactants that may be used include, but 1o are not limited to, ethoxylated alkylphenols, ethoxylated and propoxylated fatty alcohols, polyethylene glycol ethers of methyl glucose, polyethylene glycol ethers of sorbitol, ethylene oxide-propylene oxide block copolymers, ethoxylated esters of fatty (C$ -C18) acids, condensation products of ethylene oxide with long chain amines or amides, condensation products of ethylene oxide with alcohols, and mixtures thereof.
Specific examples of suitable nonionic surfactants include, but are not limited to, methyl gluceth-10, PEG-20 methyl glucose distearate, PEG-20 methyl glucose sesquistearate, Cm-15 p~e~-20, ceteth-8, ceteth-12, dodoxynol-12, laureth-15, PEG-20 castor oil, polysorbate 20, steareth-20, polyoxyethylene-10 2o cetyl ether, polyoxyethylene-10 stearyl ether, polyoxyethylene-20 cetyl ether, polyoxyethylene-10 oleyl ether, polyoxyethylene-20 oleyl ether, an ethoxylated nonylphenol, ethoxylated octylphenol, ethoxylated dodecylphenol, or ethoxylated fatty (CG -C2~ alcohol, including 3 to 20 ethylene oxide moieties, polyoxyethylene-20 isohexadecyl ether, polyoxyethylene-23 glycerol laurate, polyoxy-ethylene-20 glyceryl stearate, PPG-10 methyl glucose ether, PPG-20 methyl glucose ether, polyoxyethylene-20 sorbitan monoesters, polyoxyethylene-80 castor oil, polyoxyethylene-15 tridecyl ether, polyoxy-ethylene-6 tridecyl ether, laureth-2, laureth-3, laureth-4, PEG-3 castor oil, PEG 600 dioleate, PEG 400 dioleate, oxyethanol, 2,6,8-trimethyl-4-nonyloxypolyethylene oxyethanol;
octylphenoxy polyethoxy ethanol, nonylphenoxy polyethoxy ethanol, 2,6,8-trimethyl-4-nonyloxypolyethylene alkyleneoxypolyethyleneoxyethanol, alkyleneoxypolyethyleneoxyethanol; alkyleneoxypolyethyleneoxyethanol, and mixtures thereof.
Additional nonionic surfactants that may be used include water soluble alcohol ethylene oxide condensates that are the condensation products of a secondary aliphatic alcohol containing between about 8 to about 18 carbon atoms in a straight or branched chain configuration condensed with between s about 5 to about 30 moles of ethylene oxide. Such nonionic surfactants are commercially available under the trade name Tergitol~ from Union Carbide Corp., Danbury, Conn. Specific examples of such commercially available nonionic surfactants of the foregoing type are Ci1 -Ci5 secondary all~anols condensed with either 9 moles of ethylene oxide (Tergitol~ 15-S-9) or 12 moles of ethylene ~ oxide (Tergitol~ 15-S-12) marketed by Union Carbide Corp., (Danbury, Conn.).
Other suitable nonionic surfactants include the polyethylene oxide condensates of one mole of alkyl phenol containing from about 8 to 18 carbon atoms in a straight- or branched chain all~yl group with about 5 to 30 moles of ethylene oxide. Specific examples of alliyl phenol ethoxylates include nonyl condensed with about 9.5 moles of ethylene oxide per mole of nonyl phenol, dinonyl phenol condensed with about 12 moles of ethylene oxide per mole of phenol, dinonyl phenol condensed with about 15 moles of ethylene oxide per mole of phenol and diisoctylphenol condensed with about 15 moles of ethylene oxide per mole of phenol. Commercially available nonionic surfactants of this type include Igepal~ CO-630 (a nonyl phenol ethoxylate) marketed byISP Core.
(Wayne, N.J.). Suitable non-ionic ethoxylated octyl and nonyl phenols include those having from about 7 to about 13 ethoxyunits.
In some embodiments, one or more amphoteric surfactants maybe used.
2s One class of amphoteric surfactants that maysuitable for use with the present invention includes the derivatives of secondary and tertiary amines having aliphatic radicals that are straight chain or branched, where one of the aliphatic substituents contains from about 8 to 18 carbon atoms and at least one of the aliphatic substituents contains an anionic water-solubilizing group, such as a 3o carboxy, sulfonate, or sulfate group. Some examples of amphoteric surfactants include, but are not limited to, sodium 3-(dodecylamino)propionate, sodium 3-(dodecylamino)-propane-1-sulf onate, sodium 2- (dodecyiamino) ethyl self ate, sodium 2-(dimethylamino)octadecanoate, disodium 3-(N carboxymethyl-dodecylamino)propane-1-sulfonate, sodium 1-carboxymethyl 2-undecylimidazole, disodium octadecylirninodiacetate, and sodium N, N bis(2-hydroxyethyl)-2-sulfato-3-dodecoxypropylamine.
Additional classes of suitable amphoteric surfactants include phosphobetaines and phosphitaines. For instance, some examples of such amphoteric surfactants include, but are not limited to, sodium coconut N
methyl taurate, sodium oleyl N methyl taurate, sodium tall oil acid N methyl taurate, cocodimethylcarboxymethylbetaine, lauryldimethylcarboxymethylbetaine, lauryldimethylcarboxyethylbetaine, cetyldimethylcarboxymethylbetaine, sodium palmitoyl N methyl taurate, oleyldimethylgammacarboxypropylbetaine, lauryl 1o bis-(2-hydroxypropyl)-carboxyethylbetaine, di-sodium oleamide PEG-2 sulfosuccinate, laurylamido-bis-(2-hydroxyethyl) propylsultaine, la,ury3.-bis-(2-hydroxyethyl) carboxymethylbetaine, cocoamidodimethylpropylsultaine, stearylamidodimethylpropylsultaine, TEA oleamido PEG-2 sulfosuccinate, disodium oleamide MEA sulfosuccinate, disodium oleamide MIPA
sulfosuccinaxe, disodium ricinoleamide MEAsulfosuccinate, disodium undecylenamide MEA sulfosuccinate, disodium wheat germamido MEA
sulfosuccinate, disodium wheat germamido PEG-2 sulfosuccinate, disodium isostearamideo MEA sulfosuccinate, cocoamido propyl monosodium phosphitaine, lauric myristic amido propyl monosodium phosphitaine, 2o cocoamido disodium 3-hydroxypropyl phosphobetaine, lauric myristic amido disodium 3-hydroxypropyl phosphobetaine, lauric myristic amido glyceryl phosphobetaine, lauric myristic amido carboxy disodium 3-hydroxypropyl phosphobetaine, cocoamphoglycinate, cocoamphocarboxyglycinate, capryloamphocarboxyglycinate, lauroamphocarboxyglycinate, lauroamphoglycinate, capryloamphocarboxypropionate, lauroamphocarboxypropionate, cocoamphopropionate, cocoamphocarboxypropionate, dihydroxyethyl tallow glycinate, and mixtures thereof .
In certain instances, one or more anionic surfactants may be used.
3o Suitable anionic surf actants include, but are not limited to, alkyl sulfates, alliyl ether sulfates, alliyl ether sulfonates, sulfate esters of an all~ylphenoxy polyoxyethylene ethanol, alpha-olefin sulfonates, beta alkoxy alkane sulfonates, all~ylauryl self onates, alliyl monoglyceride sulfates, all~yl monoglyceride sulf onates, allyl carbonates, alkyl ether carboxylates, fatty acids, sulf osuccinates, sarcosinates, octoxynol or nonoxynol phosphates, taurates, fatty taurides, fatty acid amide polyoxyethylene sulfates, isethionates, or mixtures thereof.
Particular examples of some suitable anionic surfactants include, but are not limited to, C$ -C18 alkyl sulfates, C$ -C18 fatty acid salts, C$ -C18 alkyl ether sulfates having one or two moles of ethoxylation, C8 -C1$ alkamine oxides, C8 C1$ alkoyl sarcosinates, C$ -C1$ sulfoacetates, C$ -C1$ sulfosuccinates, C$ -C1$ alkyl Biphenyl oxide disulfonates, C$ -C1$ alkyl carbonates, C$ -C1$ alpha-olefin sulfonates, methyl ester sulfonates, and blends thereof. The C$ -C1$ alkyl group may be straight chain (e.g., lauryl) or branched (e.g., 2-ethylhexyl). The cation of 1o the anionic surfactant may be an alkali metal (e.g., sodium or potassium), ammonium, C1 -Cø alkylammonium (e.g., mono-, di-, tri), or C1 -C3 alkanolammonium (e.g., mono-, di-, tri).
Specific examples of such anionic surfactants include, but are not limited to, lauryl sulfates, octyl sulfates, 2-ethylhexyl sulfates, lauramine oxide, decyl i5 sulfates, tridecyl sulfates, cocoates, lauroyl sarcosinates, lauryl sulfosuccinates, linear C1o Biphenyl oxide disulfonates, lauryl sulfosuccinates, lauryl ether sulfates (1 and 2 moles ethylene oxide), myristyl sulfates, oleates, stearates, tallates, ricinoleates, cetyl sulfates, and so forth.
Alternatively, any other treatment may be applied to the inside surface to 2o impart the desired attribute to the glove. Other such treatments include emollients that may provide skin health benefits, antimicrobials, and so forth.
The article of the present invention features enhanced donning characteristics. The presence of covalently bonded functionalized beads within the article decreases the overall coefficient of friction of the surface and permits 25 the glove to be donned more readily. Further, since the particles axe chemically covalently bonded the article, no additional binder is needed. This provides a processing advantage over other particulate compositions that require use of a binder to ensure that particles will not inadvertently dissociate from the glove.
Additionally, where a lubricant is utilized in accordance with the present 3o invention, donning is further enhanced.
The invention may be embodied in other specific forms without departing from the scope and spirit of the inventive characteristics thereof. The present embodiments therefore are to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims rather than by the foregoing description, and all changes which come within the meaning and range of equivalency of the claims are therefore intended to be embraced therein.
Claims (17)
1. An elastomeric article comprising:
a substrate body including an elastomeric material; and a plurality of functionalized beads covalently bonded to the elastomeric material.
a substrate body including an elastomeric material; and a plurality of functionalized beads covalently bonded to the elastomeric material.
2. The article of claim 1, comprising from about 0.0001 mass % to about 10 mass % functionalized beads.
3. The article of claim 1, comprising from about 0.001 mass % to about 5 mass % functionalized beads.
4. The article of claim 1, comprising from about 0.01 mass % to about 3 mass % functionalized beads.
5. The article of claim 1, wherein the article is a glove.
6. An elastomeric article comprising:
a substrate body having a first surface; and a donning layer overlying the first surface, the donning layer comprising a polymeric material and a plurality of covalently bonded functionalized beads.
a substrate body having a first surface; and a donning layer overlying the first surface, the donning layer comprising a polymeric material and a plurality of covalently bonded functionalized beads.
7. The article of claim 6, wherein the polymeric material comprises a hydrogel.
8. The article of claim 6, wherein the polymeric material comprises 1,2-syndiotactic polybutadiene.
9. The article of claim 6, wherein the donning layer comprises from about 0.01 mass % to about 80 mass % functionalized beads.
10. The article of claim 6, wherein the donning layer comprises from about 1 mass % to about 50 mass % functionalized beads.
11. The article of claim 6, wherein the donning layer comprises from about 10 mass % to about 25 mass % functionalized beads.
12. An elastomeric article comprising:
a substrate body comprising natural rubber, the substrate body having a first surface;
a donning layer overlying the first surface, the donning layer comprising a hydrogel and a plurality of functionalized beads covalently bonded to the hydrogel; and a lubricant layer overlying at least a portion of the donning layer.
a substrate body comprising natural rubber, the substrate body having a first surface;
a donning layer overlying the first surface, the donning layer comprising a hydrogel and a plurality of functionalized beads covalently bonded to the hydrogel; and a lubricant layer overlying at least a portion of the donning layer.
13. The article of claim 12, wherein the lubricant layer comprises a silicone emulsion.
14. The article of claim 1, 6, or 12, wherein the functionalized beads comprise a polymer having a vinyl group.
15. The article of claim 14, wherein the vinyl group is selected from the group consisting of a carbon-carbon vinyl group and an acrylate group.
16. A composition for use in forming a textured article comprising:
a polymeric material; and a plurality of functionalized beads covalently bonded to the polymeric material.
a polymeric material; and a plurality of functionalized beads covalently bonded to the polymeric material.
17. The composition of claim 16, wherein the polymeric material comprises a hydrogel.