CA2411974A1 - Recording medium cartridge - Google Patents
Recording medium cartridge Download PDFInfo
- Publication number
- CA2411974A1 CA2411974A1 CA002411974A CA2411974A CA2411974A1 CA 2411974 A1 CA2411974 A1 CA 2411974A1 CA 002411974 A CA002411974 A CA 002411974A CA 2411974 A CA2411974 A CA 2411974A CA 2411974 A1 CA2411974 A1 CA 2411974A1
- Authority
- CA
- Canada
- Prior art keywords
- recording medium
- printed layer
- writing
- resin particles
- cartridge
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A recording medium cartridge in which the quality of external view can be prevented from deteriorating by protecting a writing print layer against damage at the time of ultrasonic welding. The ink layer (20) is obtained by adding a writing filler (21) and resin particles (22) having a mean particle size not smaller than that of the writing filler (21) into ink (23). The resin particles (22) abut against a welding horn (9) to prevent the writing filler (21) from being dropped off or deformed through ultrasonic vibration.
Description
5~: ,=r_~ ~ '~_' _ SPECIFICATION
RECORDING MEDIUM CARTRIDGE
TECHNICAL FIELD
The present invention relates to a recording medium cartridge housing, for example, an optical disk or a magneto-optical disk as a recording medium enabling recording/reproduction of information such as audio signals, image signals and the like, and relates more specifically to a recording medium cartridge comprising a printed layer which enables writing on the main surface of the cartridge body.
BACKGROUND ART
Currently, recording media for recording/reproducing music and images are widely prevalent in general. Of these media, a small disk cartridge referred to as a Mini.DiscTM (MD) is widely used not only indoors but outdoors as well as in vehicles.
This disk cartridge is made, as shown in Fig. 6, by rotatably housing an optical disk or a magneto-optical disk 4 inside a cartridge body 3 made by assembling an upper half 1 and a lower half 2 through ultrasonic welding. When not in use, a shutter 5 blocks an opening in the cartridge body 3, and adhesion of foreign material to the disk 4 is thus prevented Ordinarily, titles of the songs recorded on the disk cartridge are written on ar label sticker to be stuck on a main surface 3a of the cartridge body 3.
However, there is a possibility that the sticker would come off as the adhesiveness deteriorates due to changes over time, and as a result that the disk cartridge may become unejectable firom a reoordin.g/reproducing apparatus ~deck~.
In order to solve this, there are products in which a printed layer 8, which makes writing possible, is provided on the main surface 3a of the cartridge body 3 instead of the label sticker mentioned above. The conventional printed layer 8 comprises an ink 7 containing a writing-enabling filler 6, such as calcium carbonate, silica., protein powder, which makes writing possible. The filler 6 forms appropriate bumps and dents on the surface of the printed layer 8, and thus achieves writability Also, since the filler 6 has water absorbing properties, writing with water-based ink is made possible.
However, because the printed layer 8 containing the filler 6 is vulnerable to rubbing and friction, there is a problem in that it brings about a drop in aesthetic quality as the printed layer 8 is grazed and marred due to pressure welding between a welding horn 9 and the upper half 1 as shown in Fig. 8 at the time of ultrasonic welding of the upper and lower halves 1 and 2 in a step for manufacturing the disk cartridge. In other words, there is a problem in that by being subjected to ultrasonic vibration in a state where the writing-enabling filler 6 in the printed layer 8 and the welding horn 9 are in contact, the filler 6 falls out from the ink 7 or changes shape, thereby bringing about a drop in the aesthetic quality of the printed layer 8 and ultimately of the disk cartridge.
The present invention is proposed in view of the problems mentioned above, and makes it its issue to provide a recording medium cartridge capable of preventing a drop in aesthetic quality by preventing damage to the printed layer for writing during ultrasonic welding.
DISCLOSURE OF THE INVENTION
In solving the problems mentioned above, the recording medium cartridge of the present invention is characterized in that a writable printed layer printed on a main surface of a cartridge body comprises resin particles having an average.
particle diameter greater than or equal to the average particle diameter of a writing-enabling filler.
In the present invention, by bringing the resin particles having an average diameter greater than or equal to the average particle diameter of the writing-enabling frller in contact with a welding horn, ultrasonic vibration from the welding horn is received by the resin particles mentioned above. Thus, the falling out of the writing-enabling filler firom ink is avoided, and a drop in the aesthetic quality of the printed layer is prevented.
BRIEF DESCRTPTION OF THE DRAWINGS
RECORDING MEDIUM CARTRIDGE
TECHNICAL FIELD
The present invention relates to a recording medium cartridge housing, for example, an optical disk or a magneto-optical disk as a recording medium enabling recording/reproduction of information such as audio signals, image signals and the like, and relates more specifically to a recording medium cartridge comprising a printed layer which enables writing on the main surface of the cartridge body.
BACKGROUND ART
Currently, recording media for recording/reproducing music and images are widely prevalent in general. Of these media, a small disk cartridge referred to as a Mini.DiscTM (MD) is widely used not only indoors but outdoors as well as in vehicles.
This disk cartridge is made, as shown in Fig. 6, by rotatably housing an optical disk or a magneto-optical disk 4 inside a cartridge body 3 made by assembling an upper half 1 and a lower half 2 through ultrasonic welding. When not in use, a shutter 5 blocks an opening in the cartridge body 3, and adhesion of foreign material to the disk 4 is thus prevented Ordinarily, titles of the songs recorded on the disk cartridge are written on ar label sticker to be stuck on a main surface 3a of the cartridge body 3.
However, there is a possibility that the sticker would come off as the adhesiveness deteriorates due to changes over time, and as a result that the disk cartridge may become unejectable firom a reoordin.g/reproducing apparatus ~deck~.
In order to solve this, there are products in which a printed layer 8, which makes writing possible, is provided on the main surface 3a of the cartridge body 3 instead of the label sticker mentioned above. The conventional printed layer 8 comprises an ink 7 containing a writing-enabling filler 6, such as calcium carbonate, silica., protein powder, which makes writing possible. The filler 6 forms appropriate bumps and dents on the surface of the printed layer 8, and thus achieves writability Also, since the filler 6 has water absorbing properties, writing with water-based ink is made possible.
However, because the printed layer 8 containing the filler 6 is vulnerable to rubbing and friction, there is a problem in that it brings about a drop in aesthetic quality as the printed layer 8 is grazed and marred due to pressure welding between a welding horn 9 and the upper half 1 as shown in Fig. 8 at the time of ultrasonic welding of the upper and lower halves 1 and 2 in a step for manufacturing the disk cartridge. In other words, there is a problem in that by being subjected to ultrasonic vibration in a state where the writing-enabling filler 6 in the printed layer 8 and the welding horn 9 are in contact, the filler 6 falls out from the ink 7 or changes shape, thereby bringing about a drop in the aesthetic quality of the printed layer 8 and ultimately of the disk cartridge.
The present invention is proposed in view of the problems mentioned above, and makes it its issue to provide a recording medium cartridge capable of preventing a drop in aesthetic quality by preventing damage to the printed layer for writing during ultrasonic welding.
DISCLOSURE OF THE INVENTION
In solving the problems mentioned above, the recording medium cartridge of the present invention is characterized in that a writable printed layer printed on a main surface of a cartridge body comprises resin particles having an average.
particle diameter greater than or equal to the average particle diameter of a writing-enabling filler.
In the present invention, by bringing the resin particles having an average diameter greater than or equal to the average particle diameter of the writing-enabling frller in contact with a welding horn, ultrasonic vibration from the welding horn is received by the resin particles mentioned above. Thus, the falling out of the writing-enabling filler firom ink is avoided, and a drop in the aesthetic quality of the printed layer is prevented.
BRIEF DESCRTPTION OF THE DRAWINGS
Fig. 1 is a perspective view illustrating the configuration of a disk cartridge as a recording medium cartridge according to a mode for carrying out the present invention, and the relationship between the disk cartridge mentioned above, a reference table of the recording/reproducing apparatus and pressure springs Fig. 2 is a sectional view schematically illustrating the configuration of the printed layer which is printed on a main surface of a cartridge body of the same disk cartridge Fig. 3 is a diagram explaining the relationship between the printed layer mentioned above and a welding horn during ultrasonic welding Fig. 4 is a diagram illustrating the vibrational characteristics of the cartridge body according to an embodiment of the present invention Fig. 5 is a perspective view illustrating an example of a modification of the configuration of the disk cartridge according to a mode of the present invention Fig. 6 is a perspective view illustrating one example of the configuration of a conventional disk cartridge Fig. 7 is a sectional view illustrating in a simplified manner the configuration of a conventional printed layer and Fig. 8 is a diagram explaining the relationship between a conventional printed layer and a welding horn during ultrasonic welding.
BEST MODES FOR CARRYING OUT THE INVENTION .
Below, modes for carrying out the present invention are explained with reference to the drawings. In the present mode, explanations are given with the disk cartridge for MiniDiscsTM (MDs) mentioned above taken as an example of a recording medium cartridge.
A disk cartridge 10 aa;ording to the present mode is made by, as shown in Fig. 1, constructing a cartridge body 13 by combining an upper half 11 and a lower half 12 comprising a synthetic resin material, and by rotatably housing a magneto-optical disk (hereinafter referred to as a dish 14 as a recording medium inside this cartridge body 13. Further, a shutter 15 which can be opened and closed is provided in the cartridge body 13, and when not in use, the shutter 15 blocks an opening in the cartridge body 13, thereby preventing adhesion and so forth of foreign material to the disk 14.
The disk cartridge 10, when inserted in a recording/reproducing apparatus, has the shutter 15 opened, while reference holes not shown in drawing in the lower half 12 are engaged by a pair of reference pins 17, 17 of a reference table 16 on the recording/reproducing apparatus side, the lower surface of the lower half 12 is placed on a pair of receiving sections 18, 18 of the reference table 16, and the disk cartridge is thus supported horizontally Further, the outer edge portions of the upper surface of the upper half 11 elastically contact a pair of pressure springs 19, 19, and the disk cartridge 10 is thus held.
In a state where the disk cartridge 10 is thus held, the disk 14 is held to a disk table not shown in drawing with a chuck, and is driven to rotate by a spindle motor. Further, reoording/reproducing operations are performed by an optical head or a magnetic head facing the disk 14 through the opening from which the shutter 15 is removed.
On the other hand, a printed layer 20 according to the present invention is provided in the outer edge portion or approximately the center portion of the main surface 13a (the upper surface of the upper half 11) of the cartridge body 13.
The printed layer 20 mainly comprises, as shown in Fig. 2, a medium constituting an ink 23, a writing-enabling filler 21 which is contained in the ink 23 and makes writing possible, and resin particles 22 which are contained in the ink 23 and have an average particle diameter greater than or equal to the average diameter of the writing-enabling filler 21.
For the medium, a product in which vinyl chloride/acrylic resin or the like is used as a binder, and to which a diluting solvent or adjuvant is added is used. For the writing-enabling filler 21, generally, porous particles such as calcium carbonate and silica are employed for ink receiving effects, but protein powder of pulverized ox-hide may also be included for the purpose of further increasing water absorbanoe.
Next, for the resin particles 22, polyurethane resin whose modulus of bending elasticity is 98MPa or above and 980MPa or below (1000~10000kgf/cm2), and whose average particle diameter is 10~.m is used. Because the average diameter of the writing-enabling filler 21 mentioned above is smaller than or equal to lOwm, resin particles of a larger or equal average diameter are employed For the particle diameter of the resin particles 22, 5~.m or above and 20~,m or below are optimal. If the particle diameter of the resin particles 22 is smaller than 5~,m, they become buried between the writing-enabling filler 21, and adequate effects cannot be achieved. Also, when the particle diameter of the resin particles 22 is greater than 20~,m, not only is it impossible to pass through the mesh of a screen, but the difference in height between the writing-enabling filler 21 becomes greater and writability is compromised.
In addition, as the printing method for the printed layer 20, a silk-screen method employing a stencil printing plate of approximately 180250 mesh (mesh indicates the size of the mesh per inch) is optimal. In this case, the thicl~ess of the ink 23 formed is approximately 5~,m~10~,m.
In addition, the optimal content ratio for the resin particles 22 is 3 weight parts or above and 10 weight parts or below. At 2 weight parts or below, there is not enough resin particles 22, and vibrations from a welding horn cannot be received adequately. Further, in the case of the present mode, the upper limit of the content ratio of the resin particles 22 is 10 weight parts. In order to obtain the desired writability for the printed layer 20, approximately 20 weight parts of the writing-enabling filler 21 has to be added, but for the ink, it is preferable that the total filler (components other than the medium and solvent) not exceed 30 weight parts, and if it does, the durability of the ink drops considerably, and inferior adhesion occurs between itself and the base material. Therefore, it is undesirable that the upper limit of the content ratio of the resin particles 22 exceed 10 weight parts.
On the other hand, in the present mode, the printed layer 20 is constructed not only as a printed layer for writing, but also as a vibration absorbing layer for suppressing the vibration of the car<xidge body 13 inside the reoording/reproducing apparatus.
In general, with respect to a disk cartridge in operation for recording/reproducing, vibration accompanying high-speed rotation of the spindle motor and the like on the recording/reproducing apparatus side is relayed to the cartridge body 13 from the reference pins 17, 17 of the reference table 16 and the receiving sections 18, 18. At the same time, vibration is relayed to the cartridge body 13 from the pressure springs 19, 19. The fact that the cartridge body 13 vibrates also affects, in no small part, the disk 14 in a rotating motion, and leads to the occurrence of axial run-out. For this reason, when the disk 14 vibrates, signals read by the optical head also changes, and this in turn affects the reproduced wave-forms of audio signals and the like, and as a result, there are adverse effects in that high-fidelity reproduction is not performed.
In the present mode, because the resin particles 22 constituting the printed layer 20 has an average particle diameter of 10~.m, and is relatively soft with a modules of bending elasticity of 98~980MPa, vibration absorbing effects are manifested, and it becomes possible to attenuate the vibration of the cartridge body 13. In other words, when vibration is relayed to the printed layer 20, the resin particles 22 vibrate, and vibrational energy is converted into heat energy, thereby attenuating vibration.
According to the disk cartridge 10 of the present mode thus constructed, because the resin particles 22, which have a large average particle diameter, in the printed layer 20 come into contact with the welding horn 9 when the upper half and the lower half 12 are welded ultrasonically by, as shown in Fig. 3, pressure.
welding the welding horn 9 of an ultrasonic welder onto the upper surface of the upper half 11 (the main surface 13a), direct contact between the writing-enabling filler 21 and the welding horn 9 is avoided. Therefore, the falling out of the writing-enabling filler 21 from the ink 23 or its changing shape is avoided by having the resin particles 22 receive the ultrasonic vibration from the welding horn 9. As a result, a drop in the aesthetic quality of the printed layer 20 and ultimately the disk cartridge 10 is prevented.
In addition, according to the present mode, because the printed layer 20 is also used as a vibration-absorbing layer, the vibration of the cartridge body 13 inside the reoording/reproducing apparatus is reduced, and high-fidelity reproduction operations may be achieved.
An experiment for studying the extent of damage to the printed layer 20 during ultrasonic welding was conducted, in which the printed layer 20 was formed with the composition indicated below <Composition of the Printed Layer>
Medium: 70 weight parts Protein powder: 8 weight parts Calcium carbonate: 10 weight parts Silica: 3 weight parts Solvent: 5 weight parts Resin particles: 4 weight parts In the experiment, polyurethane particles A having a modulus of bending elasticity of 68.6MPa, polyurethane particles B having a modulus of bending elasticity of 98MPa, polyurethane particles C having a modulus of bending elasticity of 980MPa, butadiene particles having a modulus of bending elasticity of 686MPa, acrylic particles A having a modulus of bending elasticity of 1372MPa and acrylic particles B having a modulus of bending elasticity of 3136MPa were used for the resin particles 22, and for each, the number of samples in which damage appeared on the surface of the printed layer 20 during ultrasonic welding to an extent that they were found aesthetically defective was studied.
The average particle diameter of the resin particles 22 was made lOwm for.
all particles. Also, the average particle diameter of the writing-enabling filler (calcium carbonate, silica and protein powder) mentioned above is 10~m or below Experiment results are shown in table 1. The number of trials (cartridges) was set at 10.
In addition, the ultrasonic welding conditions are similar to conventional conditions, where the pressure is 196kPa, the vibration frequency is 20kHz (vertical vibration), the application duration is 0.28 seconds and the retention time after ultrasonic vibration is stopped is approximately 0.1 seconds.
BEST MODES FOR CARRYING OUT THE INVENTION .
Below, modes for carrying out the present invention are explained with reference to the drawings. In the present mode, explanations are given with the disk cartridge for MiniDiscsTM (MDs) mentioned above taken as an example of a recording medium cartridge.
A disk cartridge 10 aa;ording to the present mode is made by, as shown in Fig. 1, constructing a cartridge body 13 by combining an upper half 11 and a lower half 12 comprising a synthetic resin material, and by rotatably housing a magneto-optical disk (hereinafter referred to as a dish 14 as a recording medium inside this cartridge body 13. Further, a shutter 15 which can be opened and closed is provided in the cartridge body 13, and when not in use, the shutter 15 blocks an opening in the cartridge body 13, thereby preventing adhesion and so forth of foreign material to the disk 14.
The disk cartridge 10, when inserted in a recording/reproducing apparatus, has the shutter 15 opened, while reference holes not shown in drawing in the lower half 12 are engaged by a pair of reference pins 17, 17 of a reference table 16 on the recording/reproducing apparatus side, the lower surface of the lower half 12 is placed on a pair of receiving sections 18, 18 of the reference table 16, and the disk cartridge is thus supported horizontally Further, the outer edge portions of the upper surface of the upper half 11 elastically contact a pair of pressure springs 19, 19, and the disk cartridge 10 is thus held.
In a state where the disk cartridge 10 is thus held, the disk 14 is held to a disk table not shown in drawing with a chuck, and is driven to rotate by a spindle motor. Further, reoording/reproducing operations are performed by an optical head or a magnetic head facing the disk 14 through the opening from which the shutter 15 is removed.
On the other hand, a printed layer 20 according to the present invention is provided in the outer edge portion or approximately the center portion of the main surface 13a (the upper surface of the upper half 11) of the cartridge body 13.
The printed layer 20 mainly comprises, as shown in Fig. 2, a medium constituting an ink 23, a writing-enabling filler 21 which is contained in the ink 23 and makes writing possible, and resin particles 22 which are contained in the ink 23 and have an average particle diameter greater than or equal to the average diameter of the writing-enabling filler 21.
For the medium, a product in which vinyl chloride/acrylic resin or the like is used as a binder, and to which a diluting solvent or adjuvant is added is used. For the writing-enabling filler 21, generally, porous particles such as calcium carbonate and silica are employed for ink receiving effects, but protein powder of pulverized ox-hide may also be included for the purpose of further increasing water absorbanoe.
Next, for the resin particles 22, polyurethane resin whose modulus of bending elasticity is 98MPa or above and 980MPa or below (1000~10000kgf/cm2), and whose average particle diameter is 10~.m is used. Because the average diameter of the writing-enabling filler 21 mentioned above is smaller than or equal to lOwm, resin particles of a larger or equal average diameter are employed For the particle diameter of the resin particles 22, 5~.m or above and 20~,m or below are optimal. If the particle diameter of the resin particles 22 is smaller than 5~,m, they become buried between the writing-enabling filler 21, and adequate effects cannot be achieved. Also, when the particle diameter of the resin particles 22 is greater than 20~,m, not only is it impossible to pass through the mesh of a screen, but the difference in height between the writing-enabling filler 21 becomes greater and writability is compromised.
In addition, as the printing method for the printed layer 20, a silk-screen method employing a stencil printing plate of approximately 180250 mesh (mesh indicates the size of the mesh per inch) is optimal. In this case, the thicl~ess of the ink 23 formed is approximately 5~,m~10~,m.
In addition, the optimal content ratio for the resin particles 22 is 3 weight parts or above and 10 weight parts or below. At 2 weight parts or below, there is not enough resin particles 22, and vibrations from a welding horn cannot be received adequately. Further, in the case of the present mode, the upper limit of the content ratio of the resin particles 22 is 10 weight parts. In order to obtain the desired writability for the printed layer 20, approximately 20 weight parts of the writing-enabling filler 21 has to be added, but for the ink, it is preferable that the total filler (components other than the medium and solvent) not exceed 30 weight parts, and if it does, the durability of the ink drops considerably, and inferior adhesion occurs between itself and the base material. Therefore, it is undesirable that the upper limit of the content ratio of the resin particles 22 exceed 10 weight parts.
On the other hand, in the present mode, the printed layer 20 is constructed not only as a printed layer for writing, but also as a vibration absorbing layer for suppressing the vibration of the car<xidge body 13 inside the reoording/reproducing apparatus.
In general, with respect to a disk cartridge in operation for recording/reproducing, vibration accompanying high-speed rotation of the spindle motor and the like on the recording/reproducing apparatus side is relayed to the cartridge body 13 from the reference pins 17, 17 of the reference table 16 and the receiving sections 18, 18. At the same time, vibration is relayed to the cartridge body 13 from the pressure springs 19, 19. The fact that the cartridge body 13 vibrates also affects, in no small part, the disk 14 in a rotating motion, and leads to the occurrence of axial run-out. For this reason, when the disk 14 vibrates, signals read by the optical head also changes, and this in turn affects the reproduced wave-forms of audio signals and the like, and as a result, there are adverse effects in that high-fidelity reproduction is not performed.
In the present mode, because the resin particles 22 constituting the printed layer 20 has an average particle diameter of 10~.m, and is relatively soft with a modules of bending elasticity of 98~980MPa, vibration absorbing effects are manifested, and it becomes possible to attenuate the vibration of the cartridge body 13. In other words, when vibration is relayed to the printed layer 20, the resin particles 22 vibrate, and vibrational energy is converted into heat energy, thereby attenuating vibration.
According to the disk cartridge 10 of the present mode thus constructed, because the resin particles 22, which have a large average particle diameter, in the printed layer 20 come into contact with the welding horn 9 when the upper half and the lower half 12 are welded ultrasonically by, as shown in Fig. 3, pressure.
welding the welding horn 9 of an ultrasonic welder onto the upper surface of the upper half 11 (the main surface 13a), direct contact between the writing-enabling filler 21 and the welding horn 9 is avoided. Therefore, the falling out of the writing-enabling filler 21 from the ink 23 or its changing shape is avoided by having the resin particles 22 receive the ultrasonic vibration from the welding horn 9. As a result, a drop in the aesthetic quality of the printed layer 20 and ultimately the disk cartridge 10 is prevented.
In addition, according to the present mode, because the printed layer 20 is also used as a vibration-absorbing layer, the vibration of the cartridge body 13 inside the reoording/reproducing apparatus is reduced, and high-fidelity reproduction operations may be achieved.
An experiment for studying the extent of damage to the printed layer 20 during ultrasonic welding was conducted, in which the printed layer 20 was formed with the composition indicated below <Composition of the Printed Layer>
Medium: 70 weight parts Protein powder: 8 weight parts Calcium carbonate: 10 weight parts Silica: 3 weight parts Solvent: 5 weight parts Resin particles: 4 weight parts In the experiment, polyurethane particles A having a modulus of bending elasticity of 68.6MPa, polyurethane particles B having a modulus of bending elasticity of 98MPa, polyurethane particles C having a modulus of bending elasticity of 980MPa, butadiene particles having a modulus of bending elasticity of 686MPa, acrylic particles A having a modulus of bending elasticity of 1372MPa and acrylic particles B having a modulus of bending elasticity of 3136MPa were used for the resin particles 22, and for each, the number of samples in which damage appeared on the surface of the printed layer 20 during ultrasonic welding to an extent that they were found aesthetically defective was studied.
The average particle diameter of the resin particles 22 was made lOwm for.
all particles. Also, the average particle diameter of the writing-enabling filler (calcium carbonate, silica and protein powder) mentioned above is 10~m or below Experiment results are shown in table 1. The number of trials (cartridges) was set at 10.
In addition, the ultrasonic welding conditions are similar to conventional conditions, where the pressure is 196kPa, the vibration frequency is 20kHz (vertical vibration), the application duration is 0.28 seconds and the retention time after ultrasonic vibration is stopped is approximately 0.1 seconds.
Material Poly- Poly- Poly- ButadiAcrylicAcrylicConven urethaneurethaneurethaneene A B tionally A B C
Modules of ~n~g 68.6 98 980 686 1372 3136 elasticity __.
MPa cm2) (700) (1000) (10000) (7000)(14000)(32000)._.
Number g/10 0/10 0/10 0/10 4/10 10/10 10/10 dama Fmm table 1, in cases where the conventional printed layer which does not contain resin particles and where the acrylic particles B having a modules of bending elasticity of 3136 MPa were employed, damage was found in all of the samples. In particular, in the samples containing acrylic particles, not only was there damage to the writing-enabling filler, but the acrylic particles themselves were also separated from the printed layer.
A tendency for the amount of damage to decrease as the modules of elasticity becomes smaller was indicated, and at 98~980MPa, no damage was found.
On the other hand, with urethane resin particles of which the modules of elasticity is below 98MPa, damage to the printed layer was found again. It is inferred that this is because the resin particles are too soft, and ultrasonic vibration is directly relayed to the writing-enabling filler particles.
Next, vibrational characteristics of the disk cartridge 10 to which the printed layer 20 of the present invention is implemented were studied. With respect to the experiment method, a Laser Doppler Vibrometer was used, and the vibration of the cartridge body 13 when the disk cartridge 10 is inserted in a recording/reproduang apparatus and is put under playing conditions wa.s measured.
The portion that was measured was the center portion of the upper half 11. The results thereof are shown in Fig. 4 (solid line). The vertical axis is the output proportional to the vibration amplitude, and the horizontal axis is the frequency.
For comparison, the vibrational characteristics of a conventional disk cartridge (in the present example, only an ink layer in which neither resin particles nor writing-enabling fillers are contained) are indicated with a dotted line.
In addition, in the experiment, the polyurethane particles C shown in table 1 were used for the resin particles 22. Further, the printed portions were, as shown in Fig.
1, the outer edge portions of the cartridge body 13 and approximately the center portion of the main surface 13 a, and were the same for the conventional disk cartridge.
As is evident from Fig. 4, it can be seen that with the cartridge according to the present invention, vibration is attenuated compared to the conventional cartridge. In particular, the peak output at 150Hz is greatly reduced (-110.1dB) from the conventional value (-100.9dB). As a result, it was found that the printed layer of the present invention may be used effectively not only as a printed layer for writing, but also as a vibration absorbing layer.
Modes for carrying out the present invention are explained above, but naturally, the present invention is not limited thereto, and various modifications based onthe technical spirit of the present invention are possible.
For example, in the mode above, the printed layer 20 is formed on the outer edge portions and approximately the center portion of the main surface 13a of the cartridge body 13, however, it is not limited thereto, and as shown in Fig. 5, for example, the printed layer 20 may also be formed on the entire area of the main surface 13a.
In addition, an ink of a solvent type is used in the mode above, but W
curable resin may also be used as the medium. In this case, the blending ratio of the respective components is the same as in the case of the solvent type ink.
Further, in the mode above, an example where the present invention is applied to the disk cartridge of a MiniDiscTM (MD) is explained, but other than that, the present invention may be applied not only to flexible disks (FD), and cartridge type optical disks or magneto-optical disks, but also to tape form recording medium cartridges (cassettes).
As described above, aooording . to the recording medium cartridge of the present invention, the effects (1)~(6) indicated below may be achieved.
(1) In constructing a cartridge body by ultrasonically welding upper and lower halves, a printed layer for writing formed on the main surface thereof does not become grazed and damaged, and a drop in aesthetic quality may be prevented.
Modules of ~n~g 68.6 98 980 686 1372 3136 elasticity __.
MPa cm2) (700) (1000) (10000) (7000)(14000)(32000)._.
Number g/10 0/10 0/10 0/10 4/10 10/10 10/10 dama Fmm table 1, in cases where the conventional printed layer which does not contain resin particles and where the acrylic particles B having a modules of bending elasticity of 3136 MPa were employed, damage was found in all of the samples. In particular, in the samples containing acrylic particles, not only was there damage to the writing-enabling filler, but the acrylic particles themselves were also separated from the printed layer.
A tendency for the amount of damage to decrease as the modules of elasticity becomes smaller was indicated, and at 98~980MPa, no damage was found.
On the other hand, with urethane resin particles of which the modules of elasticity is below 98MPa, damage to the printed layer was found again. It is inferred that this is because the resin particles are too soft, and ultrasonic vibration is directly relayed to the writing-enabling filler particles.
Next, vibrational characteristics of the disk cartridge 10 to which the printed layer 20 of the present invention is implemented were studied. With respect to the experiment method, a Laser Doppler Vibrometer was used, and the vibration of the cartridge body 13 when the disk cartridge 10 is inserted in a recording/reproduang apparatus and is put under playing conditions wa.s measured.
The portion that was measured was the center portion of the upper half 11. The results thereof are shown in Fig. 4 (solid line). The vertical axis is the output proportional to the vibration amplitude, and the horizontal axis is the frequency.
For comparison, the vibrational characteristics of a conventional disk cartridge (in the present example, only an ink layer in which neither resin particles nor writing-enabling fillers are contained) are indicated with a dotted line.
In addition, in the experiment, the polyurethane particles C shown in table 1 were used for the resin particles 22. Further, the printed portions were, as shown in Fig.
1, the outer edge portions of the cartridge body 13 and approximately the center portion of the main surface 13 a, and were the same for the conventional disk cartridge.
As is evident from Fig. 4, it can be seen that with the cartridge according to the present invention, vibration is attenuated compared to the conventional cartridge. In particular, the peak output at 150Hz is greatly reduced (-110.1dB) from the conventional value (-100.9dB). As a result, it was found that the printed layer of the present invention may be used effectively not only as a printed layer for writing, but also as a vibration absorbing layer.
Modes for carrying out the present invention are explained above, but naturally, the present invention is not limited thereto, and various modifications based onthe technical spirit of the present invention are possible.
For example, in the mode above, the printed layer 20 is formed on the outer edge portions and approximately the center portion of the main surface 13a of the cartridge body 13, however, it is not limited thereto, and as shown in Fig. 5, for example, the printed layer 20 may also be formed on the entire area of the main surface 13a.
In addition, an ink of a solvent type is used in the mode above, but W
curable resin may also be used as the medium. In this case, the blending ratio of the respective components is the same as in the case of the solvent type ink.
Further, in the mode above, an example where the present invention is applied to the disk cartridge of a MiniDiscTM (MD) is explained, but other than that, the present invention may be applied not only to flexible disks (FD), and cartridge type optical disks or magneto-optical disks, but also to tape form recording medium cartridges (cassettes).
As described above, aooording . to the recording medium cartridge of the present invention, the effects (1)~(6) indicated below may be achieved.
(1) In constructing a cartridge body by ultrasonically welding upper and lower halves, a printed layer for writing formed on the main surface thereof does not become grazed and damaged, and a drop in aesthetic quality may be prevented.
(2) The printed layer mentioned above can be used effectively not only as a writing layer, but also as a vibration absorbing layer for the cartridge body, and functions of high-fidelity recording/reproduang can be secured.
(3) Damage to the printed layer during ultrasonic welding of the upper and lower halves may be prevented by suppressing the falling out and change in shape of a writing-enabling filler caused by ultrasonic vibration.
(4) Direct contact between the writing-enabling filler and a welding horn may be avoided, and damage to the printed layer during ultrasonic welding of the upper and lower halves may be prevented.
(5) Writability may be secured while preventing damage to the printed layer, and further, inferior adhesion with the base material may be suppressed.
(6) It can be made to function effectively not only as a writing layer, but also as a vibration absorbing layer.
(3) Damage to the printed layer during ultrasonic welding of the upper and lower halves may be prevented by suppressing the falling out and change in shape of a writing-enabling filler caused by ultrasonic vibration.
(4) Direct contact between the writing-enabling filler and a welding horn may be avoided, and damage to the printed layer during ultrasonic welding of the upper and lower halves may be prevented.
(5) Writability may be secured while preventing damage to the printed layer, and further, inferior adhesion with the base material may be suppressed.
(6) It can be made to function effectively not only as a writing layer, but also as a vibration absorbing layer.
Claims (6)
1. In a recording medium cartridge comprising, on a main surface of a cartridge body having upper and lower halves in which a recording medium is housed, a printed layer containing a writing-enabling filler, wherein said recording medium cartridge is characterized in that said printed layer contains resin particles having an average particle diameter greater than or equal to the average particle diameter of said writing-enabling filler.
2. The recording medium cartridge according to claim 1, characterized in that said printed layer is formed as a vibration absorbing layer for suppressing vibrations of said cartridge body inside a recording/reproducing apparatus.
3. The recording medium cartridge according to claim 2, characterized in that the modulus of bending elasticity of said resin particles is 98MPa or above and 980MPa or below
4. The recording medium cartridge according to claim 3, characterized in that the particle diameter of said resin particles is 20µm or below.
5. The recording medium cartridge according to claim 3, characterized in that the amount of said resin particles contained is 3 weight parts or above and 10 weight parts or below
6. The recording medium cartridge according to claim 2, characterized in that said printed layer is formed at least on an outer edge portion of the main surface of said cartridge body and on approximately a center portion of said main surface.