CA2334789C - An insulating composition for communication cables - Google Patents
An insulating composition for communication cables Download PDFInfo
- Publication number
- CA2334789C CA2334789C CA002334789A CA2334789A CA2334789C CA 2334789 C CA2334789 C CA 2334789C CA 002334789 A CA002334789 A CA 002334789A CA 2334789 A CA2334789 A CA 2334789A CA 2334789 C CA2334789 C CA 2334789C
- Authority
- CA
- Canada
- Prior art keywords
- composition
- olefin polymer
- density
- polymer
- polymerisation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
An insulating composition for communication cables (2) is disclosed as well as a telesingle wire (2) which comprises the insulating composition and a telecommunication cable (1) which comprises a plurality of telesingle wires (2) including the insulating composition.
The insulating composition comprises a multimodal olefin poll(mer mixture, obtained by polymerisation of at least one .alpha.-olefin in more than one stage having a density of about 0.920-0.965 g/cm3, a melt flow rate (MFR2) of about 0.2-5 g/10 min, an FRR21/2 >= 60, and an environmental stress cracking resistance (ESCR) according to ASTM D 1693 A/10 % Igepal, of at least 500 hrs, said olefin polymer mixture comprising at least a first and a second olefin polymer, of which the first is selected from (a) a low molecular weight (MW) olefin polymer with a density of about 0.925-0.975 g/cm3 and a melt flow rate (MFR2) of about 300-20 000 g/10 min, and (b) a high molecular weight (MW) olefin polymer with a density of about 0.880-0.950 g/cm3 and a melt flow rate (MFR21) of about 0.5-20 g/10 min.
The insulating composition comprises a multimodal olefin poll(mer mixture, obtained by polymerisation of at least one .alpha.-olefin in more than one stage having a density of about 0.920-0.965 g/cm3, a melt flow rate (MFR2) of about 0.2-5 g/10 min, an FRR21/2 >= 60, and an environmental stress cracking resistance (ESCR) according to ASTM D 1693 A/10 % Igepal, of at least 500 hrs, said olefin polymer mixture comprising at least a first and a second olefin polymer, of which the first is selected from (a) a low molecular weight (MW) olefin polymer with a density of about 0.925-0.975 g/cm3 and a melt flow rate (MFR2) of about 300-20 000 g/10 min, and (b) a high molecular weight (MW) olefin polymer with a density of about 0.880-0.950 g/cm3 and a melt flow rate (MFR21) of about 0.5-20 g/10 min.
Description
AN INSULATING COMPOSITION FOR COMMUNICATION CABLES
Field of the inrnrention The present: invention relates to an insulating com-position for cornmunication cables which have insulated copper conductors and are used for data, video or voice transmission. More particularly, the present invention relates to an insulating composition for data transmis-sion wires of communication cables such as telesingle wires and coaxial cables.
Backaround of the invention Telecommunication cables are often comprised of a plurality of telesingle wires surrounded by a sheath. The number of telesingle wires may vary from a few in a data transmission cable up to about one thousand in a tele-phone cable. The sheath surrounding the bundle of tele-single wires corisists of at least one layer and may con-sist of two layers, an inner sheath layer and an outer sheath layer. Iri order to further protect and isolate the telesingle wires a filler such as petroleum jelly may in e.g. telephone cables be inserted in the voids between the telesingle wires and the sheath. Each telesingle wire normally consist;s of one solid 0.4-0.5 mm thick copper conductor surrounded by a 0.15-0.25 mm thick insulating layer. The overall thickness of a telesingle wire is thus only about 0. 7-1. 0 mm.
Another type of data transmission cable, is the so-called coaxial cable, where a central copper conduc-tor, typically from 0.5 up to 2 mm thick, is surrounded by an insulating layer up to 2 mm thick, and then by a coaxial metallic: screen which in turn is surrounded by an outer sheath.
The insulat;ing composition of the present invention is intended as the insulating layer of telesingle wires as well as of coaxial cables, but for the sake of simpli-city the invention will be explained and illustrated with reference to telesingle wires only. Generally, the pro-perties required. of a coaxial cable are substantially the same as those of a telesingle wire.
The insulating layer surrounding each telesingle conductor normally comprises a medium to high density polyethylene composition. The insulating layer may be solid, foamed, or a combination thereof such as foamed with an outer skin or foamed with both an inner and an outer skin. The foam is prepared by introducing a gas such as nitrogen, carbon dioxide, or a solid blowing agent such as e.g. azodicarbonamide (dec. temp. about 200 C) into the polymer composition. The skin/foam struc-ture is prepared by coextruding the polymer composition in two or three layers and foaming one of the coextruded layers.
Particularly important characteristics of the in-sulating layer of a telesingle wire are good process-ability, high thermo-oxidative stability, high environ-mental stress cracking resistance (ESCR), and good sur-face finish. The importance of good processability is illustrated by the fact that the copper conductor is coated with the insulating layer in a thickness of only 0.15-0.25 mm at a coating speed of up to about 2500 m/min. In addition the coating must be very even and any exposure of the copper conductor must be avoided because of the risk of short circuiting, overhearing and other signal disturbances. An uneven thickness of the insulating layer also leads to capacitance variations.
Further, the telesingle wires of a telecommunication cable are often exposed to very severe temperature con-ditions and in hot countries the telesingle wires may be exposed to temperatures as high as about 70-90 C. In order to achieve a good thermal resistance various stabilizers like thermooxidation stabilizers and metal deactivators are normally added to the insulating compo-sition, but such stabilisers are expensive and it would be desirable if the use thereof could be reduced or eliminated. Further still, the fillers such as petroleum jelly and the copper conductor often have a deleterious influence on the insulation, particularly when the tele-single wire is exposed to high temperatures. In order to withstand this deleterious influence the insulating com-position should have a high ESCR. Finally, the surface finish of the insulating layer must be high in order to avoid formation of dust when twisting the telesingle wires.
From the above it is evident that the insulating layer of telesinc3le wires is exposed to a number of very disparate conditions and strains and should display a combination of very specific and to a certain extent contradictory characteristics, particularly with regard to processability, thermo-oxidative stability, and ESCR.
An improvement in one or more of these characteristics and a reduction of the amount of stabilisers added would be very desirable and represent an important technical advance.
In this connection it should be mentioned that a bimodal cable-sheathing composition is known through WO
97/03124. This cable-sheathing composition consists of a multimodal olefiri polymer mixture, obtained by polymeri-sation of at least one a-olefin in more than one stage and having a density of about 0.915-0.955 g/cm3 and a melt flow rate of about 0.1-3.0 g/10 min, said olefin polymer mixture comprising at least a first and a second olefin polymer, of which the first has a density and a melt flow rate selected from (a) about 0.930-0.975 g/cm3 and about 50-2000 g/10 min and (b) about 0.88-0.93 g/cm3 and about 0.01-0.8 g/10 min. It should be stressed that this composition is not an insulating composition for telesingle wires, but a cable-sheathing composition, i.e.
a composition for the outer sheathing of a cable, e.g.
the sheathing surrounding a bundle of telesingle wires as mentioned previously. The properties required of a cable-sheathing composition are not the same as those of an insulating composition for a telesingle wire. Thus, high mechanical strength and low shrinkage are particularly important to a cable-sheathing, while processability and surface finish are less critical. On the contrary, thermo-oxidative stability, ESCR, and in particular processability are of decisive importance to the insula-tion of a telesi:ngle wire. These different requirements in properties of a cable-sheathing versus an insulation for a telesingle wire means that a composition optimized for a cable-sheathing would not be useful as an insula-tion for a telesingle wire and vice versa.
Summary of the invention It has now been found that the above goals may be achieved by a communication cable such as a telesingle wire or a coaxial cable with an insulating layer which, instead of a uniinodal polyethylene plastic as used in conventional insialating layers of telesingle wires, comprises a multimodal olefin polymer mixture having certain specified values of the molecular weight distribution and the environmental stress cracking resistance (ESCR) together with certain specified values of density and melt flow rate, both as regards the poly-mer mixture and as regards the polymer fractions forming part thereof.
The present invention thus provides an insulating composition for communication cables such as telesingle wires and coaxial cables, characterised in that it comprises a mult:imodal olefin polymer mixture, obtained by polymerisation of at least one a-olefin in more than one stage, having a density of about 0.920-0.965 g/cm3, a melt flow rate (MFR2) of about 0.2-5 g/10 min, an FRR21/2 _60, and an environmental stress cracking resistance (ESCR) according to ASTM D 1693 A/10% Igepal, of at least 500 hrs, said olefin polymer mixture comprising at least a first and a second olefin polymer, of which the first is selected from (a) a low molecular weight (MW) olefin polymer with a density of about 0.925-0.975 g/cm3 and a melt flow rate (MFR2) of about 300-20 000 g/10 min, and (b) a high molecular weight (MW) olefin polymer with a density of about. 0.880-0.950 g/cm3 and a melt flow rate 5 (MFR21) of about 0.5-20 g/10 min.
By the "modality" of a polymer is meant the struc-ture of the molecular-weight distribution of the polymer,.
i.e. the appearance of the curve indicating the number of molecules as a function of the molecular weight. If the curve exhibits one maximum, the polymer is referred to as "unimodal", whereas if the curve exhibits a very broad maximum or two or more maxima and the polymer consists of two or more fractions, the polymer is referred to as "bimodal", "multimodal" etc. In the following, all poly-mers whose molecular-weight-distribution curve is very broad or has more than one maximum are jointly referred to as "multimodal".
The invention further provides a telesingle wire comprising a conductor surrounded by an insulation, characterised in that the insulation comprises a composi-tion according to any one of claims 1-10.
Still further the invention provides a telecommuni-cation cable comprising a plurality of telesingle wires each comprising a conductor surrounded by an insulation, said plurality of telesingle wires in turn being sur-rounded by a sheath, characterised in that the insulation of the telesingle conductors comprises a composition according to any one of claims 1-10.
Further distinctive features and advantages of the invention will appear from the following description and the appended claims.
Detailed description of the invention In order to facilitate the understanding of the invention a detailed description will be given below with reference to the drawings.
Field of the inrnrention The present: invention relates to an insulating com-position for cornmunication cables which have insulated copper conductors and are used for data, video or voice transmission. More particularly, the present invention relates to an insulating composition for data transmis-sion wires of communication cables such as telesingle wires and coaxial cables.
Backaround of the invention Telecommunication cables are often comprised of a plurality of telesingle wires surrounded by a sheath. The number of telesingle wires may vary from a few in a data transmission cable up to about one thousand in a tele-phone cable. The sheath surrounding the bundle of tele-single wires corisists of at least one layer and may con-sist of two layers, an inner sheath layer and an outer sheath layer. Iri order to further protect and isolate the telesingle wires a filler such as petroleum jelly may in e.g. telephone cables be inserted in the voids between the telesingle wires and the sheath. Each telesingle wire normally consist;s of one solid 0.4-0.5 mm thick copper conductor surrounded by a 0.15-0.25 mm thick insulating layer. The overall thickness of a telesingle wire is thus only about 0. 7-1. 0 mm.
Another type of data transmission cable, is the so-called coaxial cable, where a central copper conduc-tor, typically from 0.5 up to 2 mm thick, is surrounded by an insulating layer up to 2 mm thick, and then by a coaxial metallic: screen which in turn is surrounded by an outer sheath.
The insulat;ing composition of the present invention is intended as the insulating layer of telesingle wires as well as of coaxial cables, but for the sake of simpli-city the invention will be explained and illustrated with reference to telesingle wires only. Generally, the pro-perties required. of a coaxial cable are substantially the same as those of a telesingle wire.
The insulating layer surrounding each telesingle conductor normally comprises a medium to high density polyethylene composition. The insulating layer may be solid, foamed, or a combination thereof such as foamed with an outer skin or foamed with both an inner and an outer skin. The foam is prepared by introducing a gas such as nitrogen, carbon dioxide, or a solid blowing agent such as e.g. azodicarbonamide (dec. temp. about 200 C) into the polymer composition. The skin/foam struc-ture is prepared by coextruding the polymer composition in two or three layers and foaming one of the coextruded layers.
Particularly important characteristics of the in-sulating layer of a telesingle wire are good process-ability, high thermo-oxidative stability, high environ-mental stress cracking resistance (ESCR), and good sur-face finish. The importance of good processability is illustrated by the fact that the copper conductor is coated with the insulating layer in a thickness of only 0.15-0.25 mm at a coating speed of up to about 2500 m/min. In addition the coating must be very even and any exposure of the copper conductor must be avoided because of the risk of short circuiting, overhearing and other signal disturbances. An uneven thickness of the insulating layer also leads to capacitance variations.
Further, the telesingle wires of a telecommunication cable are often exposed to very severe temperature con-ditions and in hot countries the telesingle wires may be exposed to temperatures as high as about 70-90 C. In order to achieve a good thermal resistance various stabilizers like thermooxidation stabilizers and metal deactivators are normally added to the insulating compo-sition, but such stabilisers are expensive and it would be desirable if the use thereof could be reduced or eliminated. Further still, the fillers such as petroleum jelly and the copper conductor often have a deleterious influence on the insulation, particularly when the tele-single wire is exposed to high temperatures. In order to withstand this deleterious influence the insulating com-position should have a high ESCR. Finally, the surface finish of the insulating layer must be high in order to avoid formation of dust when twisting the telesingle wires.
From the above it is evident that the insulating layer of telesinc3le wires is exposed to a number of very disparate conditions and strains and should display a combination of very specific and to a certain extent contradictory characteristics, particularly with regard to processability, thermo-oxidative stability, and ESCR.
An improvement in one or more of these characteristics and a reduction of the amount of stabilisers added would be very desirable and represent an important technical advance.
In this connection it should be mentioned that a bimodal cable-sheathing composition is known through WO
97/03124. This cable-sheathing composition consists of a multimodal olefiri polymer mixture, obtained by polymeri-sation of at least one a-olefin in more than one stage and having a density of about 0.915-0.955 g/cm3 and a melt flow rate of about 0.1-3.0 g/10 min, said olefin polymer mixture comprising at least a first and a second olefin polymer, of which the first has a density and a melt flow rate selected from (a) about 0.930-0.975 g/cm3 and about 50-2000 g/10 min and (b) about 0.88-0.93 g/cm3 and about 0.01-0.8 g/10 min. It should be stressed that this composition is not an insulating composition for telesingle wires, but a cable-sheathing composition, i.e.
a composition for the outer sheathing of a cable, e.g.
the sheathing surrounding a bundle of telesingle wires as mentioned previously. The properties required of a cable-sheathing composition are not the same as those of an insulating composition for a telesingle wire. Thus, high mechanical strength and low shrinkage are particularly important to a cable-sheathing, while processability and surface finish are less critical. On the contrary, thermo-oxidative stability, ESCR, and in particular processability are of decisive importance to the insula-tion of a telesi:ngle wire. These different requirements in properties of a cable-sheathing versus an insulation for a telesingle wire means that a composition optimized for a cable-sheathing would not be useful as an insula-tion for a telesingle wire and vice versa.
Summary of the invention It has now been found that the above goals may be achieved by a communication cable such as a telesingle wire or a coaxial cable with an insulating layer which, instead of a uniinodal polyethylene plastic as used in conventional insialating layers of telesingle wires, comprises a multimodal olefin polymer mixture having certain specified values of the molecular weight distribution and the environmental stress cracking resistance (ESCR) together with certain specified values of density and melt flow rate, both as regards the poly-mer mixture and as regards the polymer fractions forming part thereof.
The present invention thus provides an insulating composition for communication cables such as telesingle wires and coaxial cables, characterised in that it comprises a mult:imodal olefin polymer mixture, obtained by polymerisation of at least one a-olefin in more than one stage, having a density of about 0.920-0.965 g/cm3, a melt flow rate (MFR2) of about 0.2-5 g/10 min, an FRR21/2 _60, and an environmental stress cracking resistance (ESCR) according to ASTM D 1693 A/10% Igepal, of at least 500 hrs, said olefin polymer mixture comprising at least a first and a second olefin polymer, of which the first is selected from (a) a low molecular weight (MW) olefin polymer with a density of about 0.925-0.975 g/cm3 and a melt flow rate (MFR2) of about 300-20 000 g/10 min, and (b) a high molecular weight (MW) olefin polymer with a density of about. 0.880-0.950 g/cm3 and a melt flow rate 5 (MFR21) of about 0.5-20 g/10 min.
By the "modality" of a polymer is meant the struc-ture of the molecular-weight distribution of the polymer,.
i.e. the appearance of the curve indicating the number of molecules as a function of the molecular weight. If the curve exhibits one maximum, the polymer is referred to as "unimodal", whereas if the curve exhibits a very broad maximum or two or more maxima and the polymer consists of two or more fractions, the polymer is referred to as "bimodal", "multimodal" etc. In the following, all poly-mers whose molecular-weight-distribution curve is very broad or has more than one maximum are jointly referred to as "multimodal".
The invention further provides a telesingle wire comprising a conductor surrounded by an insulation, characterised in that the insulation comprises a composi-tion according to any one of claims 1-10.
Still further the invention provides a telecommuni-cation cable comprising a plurality of telesingle wires each comprising a conductor surrounded by an insulation, said plurality of telesingle wires in turn being sur-rounded by a sheath, characterised in that the insulation of the telesingle conductors comprises a composition according to any one of claims 1-10.
Further distinctive features and advantages of the invention will appear from the following description and the appended claims.
Detailed description of the invention In order to facilitate the understanding of the invention a detailed description will be given below with reference to the drawings.
Brief description of the drawings Fig. 1 shows a schematic cross-section of a tele-communication cable with telesingle wires; and Fig. 2 a-d show schematic cross-sections of diffe-rent types of telesingle wires.
As mentioned above, one aspect of the invention relates to a telecommunication cable and a cross-section of a telecommunication cable is shown in Fig. 1. The telecommunication cable 1 comprises a plurality of tele-single wires 2, surrounded by a two-layered sheath 3 consisting of an inner sheath 4 and an outer sheath S.
The voids between the telesingle wires and the sheath are filled with a filler 6 such as a petroleum jelly. For the sake of simplicity Fig. 1 shows a cable with only a few telesingle wires, but in practice the number of tele-single wires can be much higher and up to about one thousand in a ca:ble.
Fig 2a-2d schematically show different types of telesingle wires. Generally, a telesingle wire consists of a metallic conductor 7, usually a solid copper wire with a diameter of 0.4-0.5 mm. The metallic conductor is surrounded by an insulation 8 which may be solid (Fig.
2a), foamed (Fig. 2b), foamed with an outer skin (Fig.
2c), or foamed with both an outer skin and an inner skin (Fig. 2d). The i:nsulation 8 has a thickness of 0.15-0.25 mm and it should be noted that for the sake of illustra-tion the thickness of the insulation 8 has been exaggerated in Fig. 2.
As indicated in the foregoing, the telesingle in-sulating composition according to the invention is distinguished by the fact that it comprises a multimodal olefin polymer mixture of specified density and melt flow rate together with certain specified values of the mole-cular weight distribution and the ESCR. More particular-ly, the molecular weight distribution, measured as FRR21/2, of the composition according to the invention is at least 60, preferably 70-100, and the ESCR of the composition of the invention is at least 500 hrs, pre-ferably at least 2000 hrs, measured according to ASTM D
1693 A/10% Igepal as explained in more detail below. In addition the insulating composition may include various stabilizers, such as antioxidants, metal deactivators, etc., in amounte required by the particular application.
It is previously known to produce multimodal, in particular bimodal, olefin polymers, preferably multi-modal ethylene plastics, in two or more reactors con-nected in series. As instances of this prior art, men-tion may be made of EP 040 992, EP 041 796, EP 022 376 and WO 92/12182, which are hereby incorporated by way of reference as reqards the production of multimodal poly-mers. According to these references, each and every one of the polymerisation stages can be carried out in liquid phase, slurry or gas phase.
According to the present invention, the main poly-merisation stages are preferably carried out as a combi-nation of slurry polymerisation/gas-phase polymerisation or gas-phase pol.ymerisation/gas-phase polymerisation. The slurry polymerisation is preferably performed in a so-called loop reactor. The use of slurry polymerisation in a stirred-tank reactor is not preferred in the present invention, since: such a method is not sufficiently flex-ible for the production of the inventive composition and involves solubility problems. In order to produce the inventive composition of improved properties, a flexible method is required. For this reason, it is preferred that the composition is produced in two main polymerisation stages in a combination of loop reactor/gas-phase reactor or gas-phase reactor/gas-phase reactor. It is especially preferred that the composition is produced in two main polymerisation stages, in which case the first stage is performed as slurry polymerisation in a loop reactor and the second stage is performed as gas-phase polymerisation in a gas-phase reactor. Optionally, the main polymerisa-tion stages may be preceded by a prepolymerisation, in which case up to 20% by weight, preferably 1-10% by weight, of the total amount of polymers is produced.
Generally, this technique results in a multimodal polymer mixture through polymerisation with the aid of a chro-mium, metallocene or Ziegler-Natta catalyst in several successive polymerisation reactors. In the production of, say, a bimodal ethylene plastic, which according to the invention is the preferred polymer, a first ethylene polymer is produced in a first reactor under certain con-ditions with respect to monomer composition, hydrogen-gas pressure, temperature, pressure, and so forth. After the polymerisation in the first reactor, the reaction mixture including the polymer produced is fed to a second reac-tor, where further polymerisation takes place under other conditions. Usually, a first polymer of high melt flow rate (low molecular weight) and with a moderate or small addition of comonomer, or no such addition at all, is produced in the first reactor, whereas a second polymer of low melt flow rate (high molecular weight) and with a greater addition of comonomer is produced in the second reactor. As comonomer, use is commonly made of other olefins having up to 12 carbon atoms, such as a-olefins having 3-12 carbon atoms, e.g. propene, butene, 4-methyl-1-pentene, hexene, octene, decene, etc., in the copoly-merisation of ethylene. The resulting end product con-sists of an intirnate mixture of the polymers from the two reactors, the different molecular-weight-distribution curves of these polymers together forming a molecular-weight-distribution curve having a broad maximum or two maxima, i.e. the end product is a bimodal polymer mix-ture. Since mult:Lmodal, and especially bimodal, polymers, preferably ethylene polymers, and the production thereof belong to the prior art, no detailed description is call-ed for here, but reference is had to the above specifica-tions.
It should be pointed out that, in the production of two or more polyrner components in a corresponding number of reactors connected in series, it is only in the case of the component; produced in the first reactor stage and in the case of t:he end product that the melt flow rate, the density and the other properties can be measured directly on the material removed. The corresponding properties of the polymer components produced in reactor stages followincl the first stage can only be indirectly determined on the basis of the corresponding values of the materials introduced into and discharged from the respective reactor stages.
Even though multimodal polymers and their production are known per se, it is not, however, previously known to use such multimodal polymer mixtures in telesingle in-sulating compositions. Above all, it is not previously known to use in this context multimodal polymer mixtures having the specific values of density, melt flow rate, molecular weight distribution and ESCR as are required in the present invention.
As hinted at above, it is preferred that the multi-modal olefin polymer mixture in the cable-sheathing com-position according to the invention is a bimodal polymer mixture. It is also preferred that this bimodal polymer mixture has been produced by polymerisation as above under different :polymerisation conditions in two or more polymerisation reactors connected in series. Owing to the flexibility with respect to reaction conditions thus ob-tained, it is most preferred that the polymerisation is carried out in a loop reactor/a gas-phase reactor, a gas-phase reactor/a gas-phase reactor or a loop reactor/a loop reactor as the polymerisation of one, two or more olefin monomers, the different polymerisation stages hav-ing varying comonomer contents. Preferably, the polymeri-sation conditions in the preferred two-stage method are so chosen that a comparatively low-molecular polymer hav-ing a moderate, :Low or, which is preferred, no content of comonomer is produced in one stage, e.g. the first stage, owing to a high content of chain-transfer agent (hydrogen -- ----- ------gas), whereas a high-molecular polymer having a higher content of comonomer is produced in another stage, e.g.
the second stage. The order of these stages may, however, equally well be reversed.
5 Preferably, the multimodal olefin polymer mixture in accordance with the invention is a mixture of propy-lene plastics or, which is most preferred, ethylene plas-tics. The comonomer or comonomers in the present inven-tion are chosen from the group consisting of a-olefins 10 having up to 12 carbon atoms, which in the case of ethy-lene plastic means that the comonomer or comonomers are chosen from a-olefins having 3-12 carbon atoms. Especial-ly preferred comonomers are butene, 4-methyl-l-pentene, 1-hexene and 1-octene.
By the term "ethylene plastic" is meant a plastic based on polyethylene or on copolymers of ethylene, the ethylene monomer making up most of the mass.
By the term "propylene plastic" is meant a plastic based on polypropylene or on copolymers of propylene, the propylene monomer making up most of the mass.
In view of the above, a preferred ethylene-plastic mixture according to the invention consists of a low-molecular ethylene homopolymer mixed with a high-mole-cular copolymer of ethylene and butene, 4-methyl-i-pen-tene, 1-hexene or 1-octene.
The properties of the individual polymers in the olefin polymer mixture according to the invention should be so chosen that the final olefin polymer mixture has a density of about 0.920-0.965 g/cm3, preferably about 0.925-0.955 g/cm3, and a melt flow rate, MFR2, of about 0.2-5.0 g/10 min, preferably about 0.5-2.0 g/10 min.
According to the invention, this may be achieved by the olefin polymer mixture comprising a first olefin polymer having a density of about 0.925-0.975 g/cm3, preferably about 0.935-0.975 g/cm3, and a melt flow rate of about 300-20000 g/10 min, preferably about 300-2000 g/10 min, and most preferred about 300-1500 g/10 min, and at least a second olefin polymer having such a density and such a melt flow rate that the olefin polymer mixture obtains the density and the melt flow rate indicated above.
If the mult.imodal olefin polymer mixture is bimodal, i.e. is a mixture of two olefin polymers (a first olefin polymer and a second olefin polymer), the first olefin polymer being produced in the first reactor and having the density and the melt flow rate indicated above, the density and the melt flow rate of the second olefin poly-mer, which is produced in the second reactor stage, may, as indicated in the foregoing, be indirectly determined on the basis of the values of the materials supplied to and discharged from the second reactor stage.
In the event that the olefin polymer mixture and the first olefin polymer have the above values of density and melt flow rate, a calculation indicates that the second olefin polymer produced in the second stage should have a density in the order of about 0.880-0.950 g/cm3, pre-ferably 0.910-0.950 g/cm3, and a melt flow rate (MFR21) in the order of about 0.5-20 g/10 min, preferably about 0.7-10 g/10 min.
As indicated in the foregoing, the order of the stages may be reversed, which would mean that, if the final olefin polymer mixture has a density of about 0.920-0.965 g/cm3, preferably about 0.925-0.955 g/cm3, and a melt flow rate of about 0.2-5.0 g/10 min, prefer-ably about 0.5-2.0 g/l0 min, and the first olefin poly-mer produced in the first stage has a density of about 0.880-0.950 g/cm3, preferably about 0.910-0.950 g/cm3, and a melt flow rate (MFR21) of 0.5-20 g/10 min, pre-ferably about 0.7-10 g/10 min, then the second olefin polymer produced in the second stage of a two-stage method should, according to calculations as above, have a density in the order of about 0.925-0.975 g/cm3, prefer-ably about 0.935-0.975 g/cm3, and a melt flow rate of 300-20000 g/l0 min, preferably about 300-2000 g/10 min, and most preferred about 300-1500 g/10 min.
As mentioned above, one aspect of the invention relates to a telecommunication cable and a cross-section of a telecommunication cable is shown in Fig. 1. The telecommunication cable 1 comprises a plurality of tele-single wires 2, surrounded by a two-layered sheath 3 consisting of an inner sheath 4 and an outer sheath S.
The voids between the telesingle wires and the sheath are filled with a filler 6 such as a petroleum jelly. For the sake of simplicity Fig. 1 shows a cable with only a few telesingle wires, but in practice the number of tele-single wires can be much higher and up to about one thousand in a ca:ble.
Fig 2a-2d schematically show different types of telesingle wires. Generally, a telesingle wire consists of a metallic conductor 7, usually a solid copper wire with a diameter of 0.4-0.5 mm. The metallic conductor is surrounded by an insulation 8 which may be solid (Fig.
2a), foamed (Fig. 2b), foamed with an outer skin (Fig.
2c), or foamed with both an outer skin and an inner skin (Fig. 2d). The i:nsulation 8 has a thickness of 0.15-0.25 mm and it should be noted that for the sake of illustra-tion the thickness of the insulation 8 has been exaggerated in Fig. 2.
As indicated in the foregoing, the telesingle in-sulating composition according to the invention is distinguished by the fact that it comprises a multimodal olefin polymer mixture of specified density and melt flow rate together with certain specified values of the mole-cular weight distribution and the ESCR. More particular-ly, the molecular weight distribution, measured as FRR21/2, of the composition according to the invention is at least 60, preferably 70-100, and the ESCR of the composition of the invention is at least 500 hrs, pre-ferably at least 2000 hrs, measured according to ASTM D
1693 A/10% Igepal as explained in more detail below. In addition the insulating composition may include various stabilizers, such as antioxidants, metal deactivators, etc., in amounte required by the particular application.
It is previously known to produce multimodal, in particular bimodal, olefin polymers, preferably multi-modal ethylene plastics, in two or more reactors con-nected in series. As instances of this prior art, men-tion may be made of EP 040 992, EP 041 796, EP 022 376 and WO 92/12182, which are hereby incorporated by way of reference as reqards the production of multimodal poly-mers. According to these references, each and every one of the polymerisation stages can be carried out in liquid phase, slurry or gas phase.
According to the present invention, the main poly-merisation stages are preferably carried out as a combi-nation of slurry polymerisation/gas-phase polymerisation or gas-phase pol.ymerisation/gas-phase polymerisation. The slurry polymerisation is preferably performed in a so-called loop reactor. The use of slurry polymerisation in a stirred-tank reactor is not preferred in the present invention, since: such a method is not sufficiently flex-ible for the production of the inventive composition and involves solubility problems. In order to produce the inventive composition of improved properties, a flexible method is required. For this reason, it is preferred that the composition is produced in two main polymerisation stages in a combination of loop reactor/gas-phase reactor or gas-phase reactor/gas-phase reactor. It is especially preferred that the composition is produced in two main polymerisation stages, in which case the first stage is performed as slurry polymerisation in a loop reactor and the second stage is performed as gas-phase polymerisation in a gas-phase reactor. Optionally, the main polymerisa-tion stages may be preceded by a prepolymerisation, in which case up to 20% by weight, preferably 1-10% by weight, of the total amount of polymers is produced.
Generally, this technique results in a multimodal polymer mixture through polymerisation with the aid of a chro-mium, metallocene or Ziegler-Natta catalyst in several successive polymerisation reactors. In the production of, say, a bimodal ethylene plastic, which according to the invention is the preferred polymer, a first ethylene polymer is produced in a first reactor under certain con-ditions with respect to monomer composition, hydrogen-gas pressure, temperature, pressure, and so forth. After the polymerisation in the first reactor, the reaction mixture including the polymer produced is fed to a second reac-tor, where further polymerisation takes place under other conditions. Usually, a first polymer of high melt flow rate (low molecular weight) and with a moderate or small addition of comonomer, or no such addition at all, is produced in the first reactor, whereas a second polymer of low melt flow rate (high molecular weight) and with a greater addition of comonomer is produced in the second reactor. As comonomer, use is commonly made of other olefins having up to 12 carbon atoms, such as a-olefins having 3-12 carbon atoms, e.g. propene, butene, 4-methyl-1-pentene, hexene, octene, decene, etc., in the copoly-merisation of ethylene. The resulting end product con-sists of an intirnate mixture of the polymers from the two reactors, the different molecular-weight-distribution curves of these polymers together forming a molecular-weight-distribution curve having a broad maximum or two maxima, i.e. the end product is a bimodal polymer mix-ture. Since mult:Lmodal, and especially bimodal, polymers, preferably ethylene polymers, and the production thereof belong to the prior art, no detailed description is call-ed for here, but reference is had to the above specifica-tions.
It should be pointed out that, in the production of two or more polyrner components in a corresponding number of reactors connected in series, it is only in the case of the component; produced in the first reactor stage and in the case of t:he end product that the melt flow rate, the density and the other properties can be measured directly on the material removed. The corresponding properties of the polymer components produced in reactor stages followincl the first stage can only be indirectly determined on the basis of the corresponding values of the materials introduced into and discharged from the respective reactor stages.
Even though multimodal polymers and their production are known per se, it is not, however, previously known to use such multimodal polymer mixtures in telesingle in-sulating compositions. Above all, it is not previously known to use in this context multimodal polymer mixtures having the specific values of density, melt flow rate, molecular weight distribution and ESCR as are required in the present invention.
As hinted at above, it is preferred that the multi-modal olefin polymer mixture in the cable-sheathing com-position according to the invention is a bimodal polymer mixture. It is also preferred that this bimodal polymer mixture has been produced by polymerisation as above under different :polymerisation conditions in two or more polymerisation reactors connected in series. Owing to the flexibility with respect to reaction conditions thus ob-tained, it is most preferred that the polymerisation is carried out in a loop reactor/a gas-phase reactor, a gas-phase reactor/a gas-phase reactor or a loop reactor/a loop reactor as the polymerisation of one, two or more olefin monomers, the different polymerisation stages hav-ing varying comonomer contents. Preferably, the polymeri-sation conditions in the preferred two-stage method are so chosen that a comparatively low-molecular polymer hav-ing a moderate, :Low or, which is preferred, no content of comonomer is produced in one stage, e.g. the first stage, owing to a high content of chain-transfer agent (hydrogen -- ----- ------gas), whereas a high-molecular polymer having a higher content of comonomer is produced in another stage, e.g.
the second stage. The order of these stages may, however, equally well be reversed.
5 Preferably, the multimodal olefin polymer mixture in accordance with the invention is a mixture of propy-lene plastics or, which is most preferred, ethylene plas-tics. The comonomer or comonomers in the present inven-tion are chosen from the group consisting of a-olefins 10 having up to 12 carbon atoms, which in the case of ethy-lene plastic means that the comonomer or comonomers are chosen from a-olefins having 3-12 carbon atoms. Especial-ly preferred comonomers are butene, 4-methyl-l-pentene, 1-hexene and 1-octene.
By the term "ethylene plastic" is meant a plastic based on polyethylene or on copolymers of ethylene, the ethylene monomer making up most of the mass.
By the term "propylene plastic" is meant a plastic based on polypropylene or on copolymers of propylene, the propylene monomer making up most of the mass.
In view of the above, a preferred ethylene-plastic mixture according to the invention consists of a low-molecular ethylene homopolymer mixed with a high-mole-cular copolymer of ethylene and butene, 4-methyl-i-pen-tene, 1-hexene or 1-octene.
The properties of the individual polymers in the olefin polymer mixture according to the invention should be so chosen that the final olefin polymer mixture has a density of about 0.920-0.965 g/cm3, preferably about 0.925-0.955 g/cm3, and a melt flow rate, MFR2, of about 0.2-5.0 g/10 min, preferably about 0.5-2.0 g/10 min.
According to the invention, this may be achieved by the olefin polymer mixture comprising a first olefin polymer having a density of about 0.925-0.975 g/cm3, preferably about 0.935-0.975 g/cm3, and a melt flow rate of about 300-20000 g/10 min, preferably about 300-2000 g/10 min, and most preferred about 300-1500 g/10 min, and at least a second olefin polymer having such a density and such a melt flow rate that the olefin polymer mixture obtains the density and the melt flow rate indicated above.
If the mult.imodal olefin polymer mixture is bimodal, i.e. is a mixture of two olefin polymers (a first olefin polymer and a second olefin polymer), the first olefin polymer being produced in the first reactor and having the density and the melt flow rate indicated above, the density and the melt flow rate of the second olefin poly-mer, which is produced in the second reactor stage, may, as indicated in the foregoing, be indirectly determined on the basis of the values of the materials supplied to and discharged from the second reactor stage.
In the event that the olefin polymer mixture and the first olefin polymer have the above values of density and melt flow rate, a calculation indicates that the second olefin polymer produced in the second stage should have a density in the order of about 0.880-0.950 g/cm3, pre-ferably 0.910-0.950 g/cm3, and a melt flow rate (MFR21) in the order of about 0.5-20 g/10 min, preferably about 0.7-10 g/10 min.
As indicated in the foregoing, the order of the stages may be reversed, which would mean that, if the final olefin polymer mixture has a density of about 0.920-0.965 g/cm3, preferably about 0.925-0.955 g/cm3, and a melt flow rate of about 0.2-5.0 g/10 min, prefer-ably about 0.5-2.0 g/l0 min, and the first olefin poly-mer produced in the first stage has a density of about 0.880-0.950 g/cm3, preferably about 0.910-0.950 g/cm3, and a melt flow rate (MFR21) of 0.5-20 g/10 min, pre-ferably about 0.7-10 g/10 min, then the second olefin polymer produced in the second stage of a two-stage method should, according to calculations as above, have a density in the order of about 0.925-0.975 g/cm3, prefer-ably about 0.935-0.975 g/cm3, and a melt flow rate of 300-20000 g/l0 min, preferably about 300-2000 g/10 min, and most preferred about 300-1500 g/10 min.
In order to optimise the properties of the tele-single insulatirig composition according to the invention, the individual polymers in the olefin polymer mixture should be preser.it in such a weight ratio that the aimed-at properties contributed by the individual polymers are also achieved in the final olefin polymer mixture. As a result, the individual polymers should not be present in.
such small amounts, such as about 10% by weight or below, that they do not affect the properties of the olefin polymer mixture. To be more specific, it is preferred that the amount of olefin polymer having a high melt flow rate (low-molecular weight) makes up at least 25% by weight but no more than 75% by weight of the total poly-mer, preferably 35-55% by weight of the total polymer, thereby to optimise the properties of the end product.
Preferably, the properties of the first and second polymers of the composition according to the invention are chosen so that the first and second polymers comprise a low molecular weight polymer and a high molecular weight polymer, respectively, the low molecular weight polymer having a density that is equal to or higher than, more preferably at most 0.05 g/cm3 higher than that of the high molecular weight polymer.
As mentioned earlier, processability, thermo-oxida-tive stability, and ESCR are particularly important properties of the insulating composition of the inven-tion.
The processability is defined herein in terms of the extruder speed in rpm at a given output in kg/h. It is always an advantage if the extruder screw speed in rpm at a given output is as low as possible (the extruder used in the examples is a single screw one of type Nokia--Maillefer with an L/D ratio of 24/1 and diameter 60 mm, run at 240 C and covering an 0.5 mm thick solid copper wire at a line speed of 510 m/min with an insulating composition in the form of an 0.24 mm thick insulation at the given output of 16 kg/h). For a satisfactory process-ability it is further important that the extruded tele-single insulation has an even thickness. This property is measured in terms of.the diameter variation or capa-citance variation of the telesingle wire and/or the pressure variation of the extruder during a production run of the telesingle wire. These variations should be as small as possible and the diameter/capacitance variations should be at most about 3%, preferably at most about 2%, most preferably at most about 1%, while the pressure variation of the extruder should be at most about 2%, preferably at most about 1%, most preferably 0.5%.
The thermo-oxidative stability is measured by means of a DSC-instrument in terms of Oxygen Induction Time (OIT) in minutes in an aluminium cup at 200 C at an 02 throughput of 80 ml/min. All samples compared have the same content of additives.
The Environtnental Stress Cracking Resistance (ESCR), i.e. the resistance of the polymer to crack formation under the action of mechanical stress and a reagent in the form of a su:rfactant, is determined in accordance with ASTM D 1693 A, the reagent employed being 10% Igepal CO-630. The results are indicated as the percentage of cracked sample rods after a given time in hours. F20 means e.g. that :20% of the sample rods were cracked after the time indicated. The present invention requires an ESCR of at least 500 hrs, preferably at least 2000 hrs, i.e. 0/500, preferably 0/2000.
The "melt flow rate" (MFR) is determined in accord-ance with ISO 1133 and is equivalent to the term "melt index" previously used. The melt flow rate, which is indicated in g/10 min, is an indication of the flow-ability, and hence the processability, of the polymer.
The higher the melt flow rate, the lower the viscosity of the polymer. The melt flow rate is determined at 190 C
and at different loadings such as 2,1 kg (MFR2; ISO 1133, condition D) or 21 kg (MFR21; ISO 1133, condition G) . The flow rate ratio is the ratio between MFR21 and MFR2 and is ------------- - ------ -represented as F'RR21/2. The flow rate ratio FRR21/2 which is indicative of the molecular weight distribution of the composition is at least 60, preferably 70-100 at the present invention.
To further facilitate the understanding of the invention some illustrating, non-limiting examples are given below.
Exam-ple 1 In a polymerisation plant consisting of two gas--phase reactors connected in series and using a Ziegler-Natta catalyst, two different bimodal ethylene plastics were polymerised (below referred to as Polymer A and Polymer B, respectively). The polymerisations were carried out so that the high molecular weight polymer fraction was produced in the first reactor (RZ) and the low molecular weight polymer fraction was produced in the second reactor (R2). As a reference a conventional uni-modal ethylene plastic (Ref.) for telesingle wire insula-tion was used.
Material data such as melt flow, density, thermo-oxidative stability and ESCR were determined for Polymer A, B and Ref. The results are given in Table 1.
Table 1 Polymer A Polymer B Ref.
MFR2, final polymer 0.54 0.95 0.72 (g/10 min) Density, final polymer 0.946 0.945 0.946 (g/C1T13) FRR21/2, final polymer 62 68 86 MFR21, R1* (g/10 min) 5 5 -Density, R1* (g/cm3) 0.926 0.921 -% R1** 65 55 ESCR >2000 h >2000 h F20=109 h OIT (min) 161 142 92 * value of polymer from the first reactor ** percentage of polymer from the first reactor based on 5 the final polymer (also called "split") From the results in Table 1 it is evident that the telesingle insulating composition of the invention (Poly-mer A and B) has a greatly improved environmental stress crack resistancE: as well as thermo-oxidative resistance.
10 Example 2 The processabilities of the polymers in Example 1 (Polymer A, B and Ref.) were determined as described earlier by measuring the extruder speed (in rpm), the pressure variation of the extruder, and the diameter 15 variation of the produced telesingle wire. The telesingle wire had a solid 0.5 mm copper conductor and the outer diameter of the telesingle wire was 0.98 mm. The line speed was 510 m/min and the temperature 240 C. The results are shown in Table 2.
Table 2 Polymer A Polymer B Ref.
Extruder speed, rpm 19.5 19.1 23.7 (output 1 kg/miri) Pressure variation, % 0.2 0.2 0.9 Diameter variation, % 0.0 0.0 2 From the results in Table 2 it is evident that the telesingle wire insulation of the invention has an about 20% improved processability with regard to the extruder speed, that the pressure variation is considerably less, and that the diameter variation is outstanding compared to the unimodal reference composition. The absence of diameter variations is an important improvement and means that the telesingle wire will not exhibit any undesired capacitance variations due to uneven insulation.
Example 3 The mechanical properties of Polymer B in Example 1 and the Reference polymer (Ref.) of Example 1 were measured on dumbbells according to ISO 527-2, 1993/5A.
The dumbbells were compression moulded from pellets of the materials in question. The dumbbells were aged in an oven, according to IEC 811-1-2, at 115 C for different periods of time. The results are shown in Table 3.
Table 3 Tensile strength at break (MPa) Unaged Aged 2 months 4 months 6 months Polymer B 33.4 27.9 30.7 33 Ref. 14 16.4 17.4 16.2 Elonqation at break (%) Unaged Aged 2 months 4 months 6 months Polymer B 1100 841 951 854 Ref. 456 729 710 483 OIT min Unaged Aged 2 months 4 months 6 months Polymer B 152 138 101 94 Ref. 107 91 49 34 It is evident from Table 3 that Polymer B of the present invention has substantially better mechanical properties compared to the Reference polymer, both initially (unaged) and after different times of ageing.
Telesingle wires were also made in accordance with Example 2 with Polymer B and the Reference polymer (Ref.) as the insulation layer. Thus, the telesingle wires had a solid 0.5 copper conductor surrounded by a 0.24 mm thick insulation of Polymer B and Ref., respecitively. The mechanical properties tensile strength at break and elongation at break were measured initially (unaged) and after 2 months of ageing at 110 C. The OIT was measured initially (unaged) and after 6 months of ageing at 110 C.
Immediately before measuring the properties the copper conductor was removed from the telesingle wires and the properties measured on the remaining insulation. The results are shown in Table 4.
Table 4 Tensile strength at break (MPa) Unaged Aged 2 months Polymer B 32.9 31.7 Ref. 29.3 31.2 Elongation break (%) Unaged Aged 2 months Polymer B 925 1016 Ref. 808 983 OIT (min) Unaged Aged 6 months Polymer B 174 60 Ref. 108 38 It is evident from Table 4 that when used as a tele-single insulation Polymer B of the present invention has substantially better properties compared to the Reference polymer, both initially (unaged) and after ageing. As is seen from Table 4 compared to Table 3, the values of tensile strength at break and of elongation at break are increased for the Reference polymer when it is used as a telesingle insulation. This may be explained by the fact that when the polymer is used as a telesingle insulation it is oriented during the extrusion and this orientation.
of the polymer entails enhanced tensile strength at break and elongation at break.
such small amounts, such as about 10% by weight or below, that they do not affect the properties of the olefin polymer mixture. To be more specific, it is preferred that the amount of olefin polymer having a high melt flow rate (low-molecular weight) makes up at least 25% by weight but no more than 75% by weight of the total poly-mer, preferably 35-55% by weight of the total polymer, thereby to optimise the properties of the end product.
Preferably, the properties of the first and second polymers of the composition according to the invention are chosen so that the first and second polymers comprise a low molecular weight polymer and a high molecular weight polymer, respectively, the low molecular weight polymer having a density that is equal to or higher than, more preferably at most 0.05 g/cm3 higher than that of the high molecular weight polymer.
As mentioned earlier, processability, thermo-oxida-tive stability, and ESCR are particularly important properties of the insulating composition of the inven-tion.
The processability is defined herein in terms of the extruder speed in rpm at a given output in kg/h. It is always an advantage if the extruder screw speed in rpm at a given output is as low as possible (the extruder used in the examples is a single screw one of type Nokia--Maillefer with an L/D ratio of 24/1 and diameter 60 mm, run at 240 C and covering an 0.5 mm thick solid copper wire at a line speed of 510 m/min with an insulating composition in the form of an 0.24 mm thick insulation at the given output of 16 kg/h). For a satisfactory process-ability it is further important that the extruded tele-single insulation has an even thickness. This property is measured in terms of.the diameter variation or capa-citance variation of the telesingle wire and/or the pressure variation of the extruder during a production run of the telesingle wire. These variations should be as small as possible and the diameter/capacitance variations should be at most about 3%, preferably at most about 2%, most preferably at most about 1%, while the pressure variation of the extruder should be at most about 2%, preferably at most about 1%, most preferably 0.5%.
The thermo-oxidative stability is measured by means of a DSC-instrument in terms of Oxygen Induction Time (OIT) in minutes in an aluminium cup at 200 C at an 02 throughput of 80 ml/min. All samples compared have the same content of additives.
The Environtnental Stress Cracking Resistance (ESCR), i.e. the resistance of the polymer to crack formation under the action of mechanical stress and a reagent in the form of a su:rfactant, is determined in accordance with ASTM D 1693 A, the reagent employed being 10% Igepal CO-630. The results are indicated as the percentage of cracked sample rods after a given time in hours. F20 means e.g. that :20% of the sample rods were cracked after the time indicated. The present invention requires an ESCR of at least 500 hrs, preferably at least 2000 hrs, i.e. 0/500, preferably 0/2000.
The "melt flow rate" (MFR) is determined in accord-ance with ISO 1133 and is equivalent to the term "melt index" previously used. The melt flow rate, which is indicated in g/10 min, is an indication of the flow-ability, and hence the processability, of the polymer.
The higher the melt flow rate, the lower the viscosity of the polymer. The melt flow rate is determined at 190 C
and at different loadings such as 2,1 kg (MFR2; ISO 1133, condition D) or 21 kg (MFR21; ISO 1133, condition G) . The flow rate ratio is the ratio between MFR21 and MFR2 and is ------------- - ------ -represented as F'RR21/2. The flow rate ratio FRR21/2 which is indicative of the molecular weight distribution of the composition is at least 60, preferably 70-100 at the present invention.
To further facilitate the understanding of the invention some illustrating, non-limiting examples are given below.
Exam-ple 1 In a polymerisation plant consisting of two gas--phase reactors connected in series and using a Ziegler-Natta catalyst, two different bimodal ethylene plastics were polymerised (below referred to as Polymer A and Polymer B, respectively). The polymerisations were carried out so that the high molecular weight polymer fraction was produced in the first reactor (RZ) and the low molecular weight polymer fraction was produced in the second reactor (R2). As a reference a conventional uni-modal ethylene plastic (Ref.) for telesingle wire insula-tion was used.
Material data such as melt flow, density, thermo-oxidative stability and ESCR were determined for Polymer A, B and Ref. The results are given in Table 1.
Table 1 Polymer A Polymer B Ref.
MFR2, final polymer 0.54 0.95 0.72 (g/10 min) Density, final polymer 0.946 0.945 0.946 (g/C1T13) FRR21/2, final polymer 62 68 86 MFR21, R1* (g/10 min) 5 5 -Density, R1* (g/cm3) 0.926 0.921 -% R1** 65 55 ESCR >2000 h >2000 h F20=109 h OIT (min) 161 142 92 * value of polymer from the first reactor ** percentage of polymer from the first reactor based on 5 the final polymer (also called "split") From the results in Table 1 it is evident that the telesingle insulating composition of the invention (Poly-mer A and B) has a greatly improved environmental stress crack resistancE: as well as thermo-oxidative resistance.
10 Example 2 The processabilities of the polymers in Example 1 (Polymer A, B and Ref.) were determined as described earlier by measuring the extruder speed (in rpm), the pressure variation of the extruder, and the diameter 15 variation of the produced telesingle wire. The telesingle wire had a solid 0.5 mm copper conductor and the outer diameter of the telesingle wire was 0.98 mm. The line speed was 510 m/min and the temperature 240 C. The results are shown in Table 2.
Table 2 Polymer A Polymer B Ref.
Extruder speed, rpm 19.5 19.1 23.7 (output 1 kg/miri) Pressure variation, % 0.2 0.2 0.9 Diameter variation, % 0.0 0.0 2 From the results in Table 2 it is evident that the telesingle wire insulation of the invention has an about 20% improved processability with regard to the extruder speed, that the pressure variation is considerably less, and that the diameter variation is outstanding compared to the unimodal reference composition. The absence of diameter variations is an important improvement and means that the telesingle wire will not exhibit any undesired capacitance variations due to uneven insulation.
Example 3 The mechanical properties of Polymer B in Example 1 and the Reference polymer (Ref.) of Example 1 were measured on dumbbells according to ISO 527-2, 1993/5A.
The dumbbells were compression moulded from pellets of the materials in question. The dumbbells were aged in an oven, according to IEC 811-1-2, at 115 C for different periods of time. The results are shown in Table 3.
Table 3 Tensile strength at break (MPa) Unaged Aged 2 months 4 months 6 months Polymer B 33.4 27.9 30.7 33 Ref. 14 16.4 17.4 16.2 Elonqation at break (%) Unaged Aged 2 months 4 months 6 months Polymer B 1100 841 951 854 Ref. 456 729 710 483 OIT min Unaged Aged 2 months 4 months 6 months Polymer B 152 138 101 94 Ref. 107 91 49 34 It is evident from Table 3 that Polymer B of the present invention has substantially better mechanical properties compared to the Reference polymer, both initially (unaged) and after different times of ageing.
Telesingle wires were also made in accordance with Example 2 with Polymer B and the Reference polymer (Ref.) as the insulation layer. Thus, the telesingle wires had a solid 0.5 copper conductor surrounded by a 0.24 mm thick insulation of Polymer B and Ref., respecitively. The mechanical properties tensile strength at break and elongation at break were measured initially (unaged) and after 2 months of ageing at 110 C. The OIT was measured initially (unaged) and after 6 months of ageing at 110 C.
Immediately before measuring the properties the copper conductor was removed from the telesingle wires and the properties measured on the remaining insulation. The results are shown in Table 4.
Table 4 Tensile strength at break (MPa) Unaged Aged 2 months Polymer B 32.9 31.7 Ref. 29.3 31.2 Elongation break (%) Unaged Aged 2 months Polymer B 925 1016 Ref. 808 983 OIT (min) Unaged Aged 6 months Polymer B 174 60 Ref. 108 38 It is evident from Table 4 that when used as a tele-single insulation Polymer B of the present invention has substantially better properties compared to the Reference polymer, both initially (unaged) and after ageing. As is seen from Table 4 compared to Table 3, the values of tensile strength at break and of elongation at break are increased for the Reference polymer when it is used as a telesingle insulation. This may be explained by the fact that when the polymer is used as a telesingle insulation it is oriented during the extrusion and this orientation.
of the polymer entails enhanced tensile strength at break and elongation at break.
Claims (12)
1. An insulating composition for communication cables such as telesingle wires and coaxial cables, characterised in that it comprises a multi-modal olefin polymer mixture, obtained by polymerisation of at least one .alpha.-olefin in more than one stage, having a density of about 0.920-0.965 g/cm3, a melt flow rate (MFR2) of about 0.2-5 g/10 min, an FRR27,02 >=60, and an environmental stress cracking resistance (ESCR) according to ASTM D 1693 A/10% Igepal, of at least 500 hrs, said olefin polymer mixture comprising at least a first and a second olefin polymer, of which the first is selected from (a) a low molecular weight (MW) olefin polymer with a density of about 0.925-0.975 g/cm3 and a melt flow rate (MFR2) of about 300-20 000 g/10 min, and (b) a high mole-cular weight (MW) olefin polymer with a density of about 0.880-0.950 g/cm3 and a melt flow rate (MFR21) of about 0.5-20 g/10 min.
2. A composition as claimed in claim 1, wherein the multimodal olefin polymer mixture has a density of about 0.925-0.955 g/cm3, and an MFR2 of about 0.5-2 g/10 min.
3. A composition as claimed in claim 1 or 2, wherein the low MW olefin polymer has a density of about 0.935-0.975 g/cm3 and an MFR2 of about 300-2000 g/10 min.
4. A composition as claimed in claim 1 or 2, wherein the high MW olefin polymer has a density of about 0.910-0.950 g/cm3 and an MFR21 of about 0.7-10 g/10 min.
5. A composition as claimed in any one of claims 1-4, wherein the olefin polymer mixture is a mixture of ethylene plastics.
6. A composition as claimed in claim 5, wherein the composition has been obtained by coordination-catalysed polymerisation in at least two stages of ethylene and, in at least one stage, an .alpha.-olefin comonomer having 3-12 carbon atoms.
7. A composition as claimed in claim 6, wherein the polymerisation stages have been carried out as slurry polymerisation, gas-phase polymerisation or a combination thereof.
8. A composition as claimed in claim 7, wherein the slurry polymerisation has been carried out in a loop reactor.
9. A composition as claimed in claim 8, wherein the polymerisation has been carried out in a loop-reactor/-gas-phase-reactor process in at least one loop reactor followed by at least one gas-phase reactor.
10. A composition as claimed in any one of claims 1-9, wherein the density of the low MW
polymer is at most 0.05 g/cm3 higher than that of the high MW polymer.
polymer is at most 0.05 g/cm3 higher than that of the high MW polymer.
11. A telesingle wire comprising a conductor sur-rounded by an insulation, characterised in that the insulation comprises a composition according to any one of claims 1-10.
12. A telecommunication cable comprising a plurality of telesingle wires each comprising a conductor surround-ed by an insulation, said plurality of telesingle wires in turn being surrounded by a sheath, character-ised in that the insulation of the telesingle wires comprises a composition according to any one of claims 1-10.