CA2271890A1 - Composite laminate automotive structures - Google Patents
Composite laminate automotive structures Download PDFInfo
- Publication number
- CA2271890A1 CA2271890A1 CA002271890A CA2271890A CA2271890A1 CA 2271890 A1 CA2271890 A1 CA 2271890A1 CA 002271890 A CA002271890 A CA 002271890A CA 2271890 A CA2271890 A CA 2271890A CA 2271890 A1 CA2271890 A1 CA 2271890A1
- Authority
- CA
- Canada
- Prior art keywords
- longitudinal
- shell
- door beam
- layer
- inner shell
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A side impact beam (100) for an automotive body construction has an outer structural portion (102) of mild steel or nonheat-treated high-strength steel, and an inner reinforcement stamping (104) of ultrahigh-strength steel separated by a thin layer of structural foam (106) of thermally expandable resin-based material including hollow microspheres. The inner reinforcement (104) is localized at the midpoint of the side impact beam (100). A vehicle bumper (200) for a motor vehicle has an outer structural portion (202) of mild steel or nonheat-treated high-strength steel, and an inner reinforcement stamping (206) of ultrahigh-strength steel separated by a thin layer of structural foam (208) of thermally expandable resin-based material including hollow microspheres. The inner reinforcement (206) is localized at the midpoint of the vehicle bumper (200).
Description
COMPOSITE LAMINATE AUTOMOTIVE STRUCTURES
The present invention relates generally to automotive body structural membcrs and, more specifically, relates to techniques for increasing strength and stiffness of automotive body structural members.
In a number of applications, particularly in the automotive industry, it is important to provide high-strength structural members at the lowest possible mass. A
number of composite materials have been proposed by others in the past for use in forming structural members, including exotic light-weight alloys. In the automotive industry, however, the need for mass reduction without sacrificing strength must be balanced against the cost of the product to the consumer. Thus, there is a need for maintaining or increasing the strength of structural members such as rockers, windshield, pillars, radiator support beams, drive shafts, side impact beams and bumpers without significantly increasing materials and labor costs.
The reinforcement of motor vehicle structural members through the use of composite materials is known. For example, the present inventor has disclosed a number of metallplastic composite structures for use in reinforcing motor vehicles components. In U.S.
Patent No.
4,901,500, entitled "Lightweight Composite Beam," a reinforcing beam for a vehicle door is disclosed which comprises an open channel-shaped metal member having a longitudinal cavity which is filled with a thermoset or thermoplastic resin-based material. In U.S. Patent No. 4,908,930 entitled, "Method of Making a Torsion Bar," a hollow torsion bar reinforced by a mixture of resin with filler is described. The tube is cut to length and. charged with a resin-based material.
The present invention relates generally to automotive body structural membcrs and, more specifically, relates to techniques for increasing strength and stiffness of automotive body structural members.
In a number of applications, particularly in the automotive industry, it is important to provide high-strength structural members at the lowest possible mass. A
number of composite materials have been proposed by others in the past for use in forming structural members, including exotic light-weight alloys. In the automotive industry, however, the need for mass reduction without sacrificing strength must be balanced against the cost of the product to the consumer. Thus, there is a need for maintaining or increasing the strength of structural members such as rockers, windshield, pillars, radiator support beams, drive shafts, side impact beams and bumpers without significantly increasing materials and labor costs.
The reinforcement of motor vehicle structural members through the use of composite materials is known. For example, the present inventor has disclosed a number of metallplastic composite structures for use in reinforcing motor vehicles components. In U.S.
Patent No.
4,901,500, entitled "Lightweight Composite Beam," a reinforcing beam for a vehicle door is disclosed which comprises an open channel-shaped metal member having a longitudinal cavity which is filled with a thermoset or thermoplastic resin-based material. In U.S. Patent No. 4,908,930 entitled, "Method of Making a Torsion Bar," a hollow torsion bar reinforced by a mixture of resin with filler is described. The tube is cut to length and. charged with a resin-based material.
In U.S. PatentNo. 4,7S 1,249, entitled, "Reinforcement Insert for a Structural Member with Method of Making and Using the Same," a precast reinforcement insert for structural members is provided which is formed of a plurality of pellets containing a thermoset resin with a blowing agent. The precast is expanded and cured in place in the structural member. In U.S. Patent No.
4,978, 562, entitled, "Composite Tubular Door Beam Reinforced with a Syntactic Foam Core Localized at the Mid Span of the Tube," a composite door beam is described which has a resin-based core that occupies not more than one-third of the bore of a metal tube.
In addition to the present inventor's own prior work, a number of metal laminates constructions are known in which flat metal plates are bonded together by an intervening layer of resin. It is also known to form a metal laminate sheet for use as a floor panel member which comprises a pair of flat metal sheets having an intervening layer of asphalt or elastic polymer.
Although filling sections with plastic foam does significantly increase section stiffness (at least when high-density foams are utilized), they also increase mass and thus part weight, which, as stated, is an undesirable feature in automotive applications. Moreover, although increasing the metal gauge of a section or adding localized metal reinforcements will increase stiffness, as the metal thickness increases, it is more difficult to form the part due to limitations in metal forming machines. Importantly, in many applications increasing metal gauge will not work effectively because stiffness frequency is proportional to section stiffness divided by section mass:
f = K/m (i.e., frequency is proportional to the square foot of stiffness over mass). Mass and stiffness are increased proportionately, with no resultant change in the dynamic stiffness frequency of the part.
In addition, filling a section entirely with foam creates a large heat sink and requires elaborate sealing operations to close access holes in the stampings. Also, the presence of the foam may interfere with the placement of interior trim panels, wiring harnesses and hinges.
4,978, 562, entitled, "Composite Tubular Door Beam Reinforced with a Syntactic Foam Core Localized at the Mid Span of the Tube," a composite door beam is described which has a resin-based core that occupies not more than one-third of the bore of a metal tube.
In addition to the present inventor's own prior work, a number of metal laminates constructions are known in which flat metal plates are bonded together by an intervening layer of resin. It is also known to form a metal laminate sheet for use as a floor panel member which comprises a pair of flat metal sheets having an intervening layer of asphalt or elastic polymer.
Although filling sections with plastic foam does significantly increase section stiffness (at least when high-density foams are utilized), they also increase mass and thus part weight, which, as stated, is an undesirable feature in automotive applications. Moreover, although increasing the metal gauge of a section or adding localized metal reinforcements will increase stiffness, as the metal thickness increases, it is more difficult to form the part due to limitations in metal forming machines. Importantly, in many applications increasing metal gauge will not work effectively because stiffness frequency is proportional to section stiffness divided by section mass:
f = K/m (i.e., frequency is proportional to the square foot of stiffness over mass). Mass and stiffness are increased proportionately, with no resultant change in the dynamic stiffness frequency of the part.
In addition, filling a section entirely with foam creates a large heat sink and requires elaborate sealing operations to close access holes in the stampings. Also, the presence of the foam may interfere with the placement of interior trim panels, wiring harnesses and hinges.
Accordingly) it would be desirable to provide a low-cost technique for increasing the stiffness of a section without proportionately increasing the mass. The present invention provides sections which have increased stiffness values with no significant increase in mass and without the use of high volumes of expensive resins. In many applications, the present invention reduces vibrations which cause unwanted "shake" of a component.
SUMMARY QF THE INVENTION
In one aspect, the present invention provides a hollow laminate beam characterized by its high-stiffness-to-mass ratio. The beam has an outer portion which is separated from an inner tube by a thin layer of structural foam. The cavity defined by the beam may be open or closed along its length.
In another aspect, the hollow laminate be2un of the present invention is an automotive radiator support beam having an outer metal section anti a generally rectangular inner tube, which may be open on one side. At least tluee sides of the rectangular inner tube are coated with a structural foam which is disposed between the rectangular inner tube and the outer metal section and in contact therewith. A metal cap is welded in place to complete the beam and retain the inner tube.
The diameter of any through holes in the inner tube which are in alignment with through-holes in the outer portion are larger than the outer portion throul;h-holes such that the structural foam does not block the through-hole clearances of either metal thicknesses.
In still another aspect, the laminate beam of the present invention is an automotive windshield pillar. A hollow metal tube is disposed within the pillar and is separated from the outer pillar stampings by a thin layer of structural foam.
In still another aspect, the laminate beam of the present invention is an automotive rocker panel assembly. The rocker panel assembly comprises mating inner and outer panel sections which form a generally rectangular rocker panel wall structure. Positioned within the rocker panel wall structure is a closely fitting inner metal tube which defines a cavity. A
thin layer of structural foam is disposed between the rocker panel wall structure and the inner tube structure.
In still another aspect the beam is a motor vehicle drive shaft. An inner tube is closely received within the outer drive shaft housing, thereby defining an annulus. A layer of foam is disposed in the annulus.
The present invention also provides a method of increasing the stiffness-to-mass ratio of a beam, wherein the beam defines a cavity. The method includes the steps of forming a tube which fits within the cavity defined by the beam; placing a layer of resin on at least a portion of the outer surface of the tube; and inserting the tube in the cavity, with the resin contacts the inner wall of the tube.
In still another aspect, the present invention comprises a C-rail section for use in truck frames. An inner stamped or rolled C-shaped member is separated from the outer C-frame rail by a layer of resin-based material.
In still another aspect, a plurality of plugs made of a foam which disintegrates at high temperatures are used to close through-holes in a part which is subsequently filled with a core material. The part is then passed through an oven which melts or disintegrates the plugs.
In still another aspect, the present invention provides a door beam or side impact beam for a motor vehicle door which provides increased compression resistance at minimal cost and weight. A local reinforcement is provided in the mid-span of a steel shell.
The local reinforcement includes a high-strength, thin steel stamping and a layer of thermally expandable foam. This allows the outer shell to be formed of relatively inexpensive mild steel. The foam is sandwiched between the outer shell and the thin steel stamping.
In one aspect, the outer steel shell and inner steel stamping having mating flanges that are welded together by spot welds.
In still another aspect, a reinforced bumper is provided for a motor vehicle.
A local reinforcement provides a steel-foam-steel laminate high-strength structure.
Figure 1 is a perspective view of the front end of a motor vehicle, with the engine removed and the body shown in phantom.
Figure 2 is an exploded perspective viE;w of a radiator support beam made in accordance with the present invention.
Figure 2A is a fragmentary view of the: oversized through-holes of the present invention.
Figure 3 is a plan view of the radiator support beam of Figure 2.
Figure 4 is a front elevational view of the radiator support beam of the radiator support beam of Figure 2.
Figure 5 is a fragmentary longitudinal cross-section along lines 5-5 of Figure 3.
Figure 6 is a cross-section along lines 6-6 of Figure 3.
Figure 7 is a plan view of another radiator support beam made in accordance with the present invention in another configuration.
Figure 8 is a fragmentary longitudinal cross-section taken along lines 8-8 of Figure 7.
Figure 9 is a cross-section along lines 9-9 of Figure 7.
Figure 10 is a cross-section of a rocker panel made in accordance with the present invention.
Figure 11 is a cross-section of a windshield pillar made in accordance with the present invention.
Figure 12 is a cross-section of a drive shaft made in accordance with the present invention.
Figure 13 is a cross-section of a C-rail section made in accordance with the present invention.
Figure 14 is a cross-section of a radiator support beam made according to another aspect of tile present invention.
Figure 15 is a perspective view of a reinforced door beam in accordance with the present invention.
_7-Figure 16 is a section along lines 16-16 of Figure 15.
Figure 17 is a section along lines 17-17 of Figure 15.
Figure 18 is a cross-section of a reinforced door beam in another configuration.
Figure 19 is a perspective view of a reinforced door beam in accordance with the present invention.
Figure 20 is a section along lines 20-20 of Figure 19.
Figure 21 is a fragmentary perspective view of one end of the beam shown ili Figure 19.
Figure 22 is a perspective view of a reinforced bumper made in accordance with the present invention.
Figure 23 is a cross-section along Iines 23-23 of Figure 22.
DETAILED DESCRIPTION OF THE PRhFERRFD EMBQDIMENTS
Referring now to Figure 1 of the drawings, a motor vehicle 10 is shown with the engine removed and the body illustrated in phantom. Radiator support structure or beam 12 is mounted on the chassis and serves to support the vehicle radiator (not sho~~~n). In Figure 2, radiator support beam 12 is illustrated in exploded view having outer shell or portion 14 which in this embodiment is a steel stamping. An inner tube, here shown as charu~el-shaped tube 16, is provided _g_ having a layer of resin-based material I8 applied to selected surfaces. Cap 20 is seen having a plurality of through-holes 22 and serves to enclose channel-shaped tube 16 within outer shell 14.
More specifically, and referring now of Figures 2 through 6, outer shell 14 defines a cavity or channel 24. A number of through-holes 26 are seen through which electric wiring (not shown) may extend. Outer shell I4 includes a laterally extending mounting bracket or plate portion 28 which is secured to components of the engine assembly.
The benef is of the present invention are provided by inner tube or inner portion 16 which in this case is roll-formed metal, far example thin gauge steel, which is formed so that it may be closely fitted within cavity 24 of outer shell 14. Inner tube 16 in this embodiment closely conforms to the geometry of outer shell 14, including having a lateral plate 30 that mates with mounting bracket 28. By providing a layer of resin-based material I 8 on selected surfaces of inner tube 16 and then assembling inner tube 16 and outer shell 14 to form the tube-in-tube construction shown best in the cross-section of Figure 6, the stiffness of beam 12 is increased significantly without a significant increase in mass. Accordingly, as shown in Figures 2 and 6, a layer of a resin-based material 18 is applied, shown here on three sides of inner tube I
8.
A number of resin-based compositions can be utilized to form resin-based layer in the present inventions. The preferred compositions impart excellent strength and stiffness characteristics to beam 12 while adding only marginally to the weight. With specific reference now to the composition of the resin-based layer, the density of the material should preferably be from about 15 pounds per cubic feet to about 40 pounds per cubic feet to minimize weight. The melting point of resin-based layer 18, heat distortion temperature and the temperature at which chemical breakdown occurs must also be sufficiently high such that layer I8 substantially maintains its structure at high temperatures typically encountered in paint ovens and the like. Therefore, resin-based layer 18 should be able to withstand temperatures in excess of 300 degrees F. and preferably 350 degrees F. for short times. Also, the resin-based layer 18 should be able to withstand heats of about 180 degrees F. to 220 degrees F, for extended periods without exhibiting substantial heat-induced distortion or degradation.
In more detail, resin-based layer I 8 includes a synthetic resin, a cell-forming agent, and a filler. A synthetic resin comprises from about 35.0 ,percent to about 95.0 percent by weight, preferably from about 75.0 percent to about 94.0 percent bar weight, and most preferably from about 78.0 percent to about 90.0 percent by weight of layer 18. As used herein, the term "cell-forming agent" refers generally to agents which produce bubbles;, pores, or cavities in layer 18. That is, resin-based layer 18 has a cellular structure, having numerous cells disposed throughout its mass.
This cellular structure provides a Iow-density, high-strength material, which, in beam 12, provides a strong, yet lightweight structure. Cell-forming agents which are compatible with the present invention include reinforcing "hollow" microspheres or microbubbles which may be formed of either glass or plastic. Plastic microspheres may be either thermosetting or thermoplastic and either expanded or unexpended. In one embodiment, unexpended microspheres are used which are then expanded to form resin-based layer 18. The preferred microspheres are from about 1.0 to about 250 and preferably from about 10 to about I80 microns in diameter. The cell-forming agent may also comprise a larger, lightweight material such as macrospheres of greater than 400 microns in diameter. Also, the cell-forming agent may comprise a blowing agent which may be either a chemical blowing agent or a physical blowing agent. Glass microspheres are particularly preferred.
Where the cell-forming agent comprises microspheres or macrospheres, it constitutes from about 1.0 percent to about 60.0 percent by weight, preferably from about 1.0 percent to about 35.0 percent by weight, and most preferably from about 3.0 percent to about 20.0 percent by weight of layer 18.
Where the cell-forming agent comprises a blowing agent, it constitutes from about 1.0 percent to about 10.0 percent by weight, preferably from about 1.0 percent to about S.0 percent by weight, and most preferably from about 3.0 percent to about 5.0 percent by weight of layer 18. Suitable fillers include glass or plastic microspheres, silica fume, calcium carbonate, milled glass fiber, and chopped WO 98l21060 PCT/US97/19981 glass strand. Glass microspheres are particularly preferred. Other materials may be suitable. A
filler comprises from about 1.0 percent to about 55.0 percent by weight, preferably from about 5.0 percent to about 24.0 percent by weight and most preferably from about 7.0 percent to about 19.0 percent by weight of resin-based layer 18.
Preferred synthetic resins for use in the present invention include thermosets such as epoxy resins, vinyl ester resins, ihermoset polyester resins, and urethane resins. It is not intended that the scope of the present invention be limited by molecular weight of the resin. Where the resin component of the liquid filler material is a thermoset resin, various accelerators, such as "EMI-24"
(imidazole accelerator) and "DMP-30," and curing agents, preferably organic peroxides such as "MEK" peroxide and "Percadox," may also be included to enhance the cure rate.
A functional amount of accelerator is typically from about 0.1 percent to about 4.0 percent of the resin weight with corresponding reduction in one of the three components, resin, cell-fornzing agent or filler.
Similarly, the amount of curing agent used is typically from about 12 percent to about 4 percent of the resin weight with a corresponding reduction in one of the three components, resin, cell-forming agent or filler. Effective amounts of processing aids, stabilizers, colorants, UV absorbers and the like may also be included in layer. Thermoplastics may also be suitable.
In the following tables, preferred formulations for resin-based layer 18 are set forth.
It has been found that these formulations provide a layer 18 which results in a beam 12 having a stiffness-to-mass ratio of greater than 1, where 1 is a normalized stiffness-to-mass ratio of a hollow or open C-channel metal beam regardless of mass.
Formulas I and III are preferred for use with clean metal surfaces (i.e., after removing any residue on the contacting metal surfaces such as mill oils and drying compounds). Formula II
does not require extensive pre-cleaning of the metal.
PERCENTAGE PERCENTAGE
]~1GREDIENT ~Y WEIGHT ~Ic~REDIENT BY WEIGHT
FORMULA I FQ$.MULA IIII
Polyester Resin 80.9 EP~ON 828 54.5 ("ARS-137-69") Haloxy 62 7.5 "Percadox 16N" 1.1 De:r 732 6.1 "3 M C I 5" 18 Expancel 551 DU 2.0 SG Micros 8.8 3M: K20 17.7 DI-~CY 3.4 Polyester Resin 48.8 ("ARISTECH 13031") "Percadox 16N" 0.7 "SG Micros" (PA IND) 50.5 As will be appreciated by those skilled in the a.rt, EPON 828 is an epoxy resin, Haloxy 62 is an epoxy diluent, Der 732 is a flexible epoxy, Expancel S51 DU is a blowing agent, SG Micron and 3M K20 are microspheres and DI-CY is a curing agent.
A number of methods of applying layer 1.B to reinforcement tube 16 may be suitable, for example by spraying the resin-based material onto the surface of tube 16.
It may be suitable to fill the space between the inner and outer tubes after tihey are assembled.
Most preferred is the application of the resin-based material using a duck-bill avpplicator which applies a wide, even ribbon of resin on the surfaces of tube 16. In most applications, the thickness (inches) of layer i 8 should be from about .060 to about .50 and more preferably from. about .10 to about .2~, where the preferred foam compositions described herein are utilized.
In those embodiments of the present invention in which outer shell 14 has one or more through-holes 26, for example, for the passage of electrical wiring or the like, it will be necessary to provide matching through-holes 32 in inner tube 16 in register with the through-holes 26 of the outer shell. Since structural foam layer 18 could in some instances block a11 or a portion of through-holes 32, requiring a separate assembly step of clearing the foam material from the hole, In a preferred embodiment of this invention, clearance is obtained by creating over-sized through-holes 32 in alignment with through-holes 26. It is preferred that the diameter of through-holes 32 be at least 20 percent larger than that of through-holes 26, but in some applications equal size through-holes will be sufficient. In this manner, resin or foam which extends from the edges of inner tube 16 into the clearance of through-holes 32 will generally not block wire, clips or screws and the like that are threaded through through-holes 26. This concept is also illustrated in Figure 2A (as viewed looking through hole 32 from the inside) in which a portion of layer 18 extends into the clearance of through-hole 32 during application, but not to the margins of through-hole 26. In the event that layer 18 does obstruct any of the through-holes 32, it may be blown clear using an air jet before layer 18 solidifies.
Refen;ing again to Figures 2 and 5, cap 20 closes radiator support beam I2 as well as cavity or channel 34 defined by inner tube 16. Cavity 34 will generally be clear (i.e., inner tube 16 will be hollow) other than for the presence of wiring. Cap 20 is preferably welded in place. The effective thickness of the reinforced walls of beam 12 is typically four to five times that of shell 14, with very little increase in weight.
Where layer 18 is a thermoset and/or expandable resin-based material, layer 18 may be cured andlor expanded in place from the heat of the B-coat oven. It is preferred that layer 18 bond together shell 14 and tube 16. It should also be noted that the construction of the present invention allows the B-coat to drain, which would not be possible if the entire beam were foam-filled. In addition, the minimal amount of foam which is used does not create a heat sink body as is the case with large, dense foam areas and the minirr~al amount of foam usage reduces materials cost. Also, the need for plugs or the like to allow foam filling of the entire beam is eliminated.
In another embodiment of the present invention, and referring now to Figures 7, 8, and 9, inner tube 16' is shown which has a rectangullar shape and is in the nature of a closed rectangular tube (i.e. closed along its length). As with channel-shaped inner tube 16 rectangular inner tube 16' will generally be hollow. Layer 18 is shown applied to three sides of inner tube 16'.
In general, at least about 25 percent and more preferably at least about 75 percent of the mating area which forms the tube-in-tube region of beam 12 should be covered by layer 18.
Where desired, inner tube 16 at through-holes 32 may be flanged inwardly toward outer shell 14 such that the flange serves as a closure to confine and isolate layer 18. Alternatively, outer shell 14 at through-holes 26 may be flanged inwardly toward inner tube 16 for the same purpose. Also, plugs or grommets in through-holes 26 and/or 32 can be used for this purpose.
A number of materials can be used to form outer shell 14 and inner tube 16 such as plastic or metal, but steel is preferred. The outer shell metal gauge (inches) will typically be from about .030 to about .090. The inner tube metal gauge will typically be from about .025 to about 050.
A number of additional specific applications of the present invention will be apparent in light of the teachings herein. A few of the preferred applications are set forth hereinafter.
Referring now io Figure 10 of the drawings, metal automotive rocker panel assembly 40 is shown having metal rocker inner panel 42 and metal rocker outer panel 44. Inner tube 46 is provided along with a layer of resin-based material 48 disposed thereon which separates inner tube 46 from the rocker panels 42 and 44. An adhesive bead 45, which may be made of the same material as layer 48, is provided adjacent trim holes 50. The assembly is welded at flanges 52.
In Figure 11, the present invention is shown in use as a windshield pillar 54.
Again, the tube-in-tube construction is employed with windshield pillar outer 56 being separated tom windshield pillar inner tube 58 by resin-based layer 60. The assembly is welded together at flanges 62.
In Figure 12, a cross-section of automotive driveshaft 64 is shown having an outer metal tube 66 separated from an inner metal tube 68 by a layer of structural foam 70.
In Figure 13, C-rail 72 is shown having outer wall section 74 separated from inner tube or channel portion 76 by a layer of structural foam 78.
In still another embodiment, and referring now to Figure 14 of the drawings, the entire cavity of a structural member such as radiator support beam 80 having cap 8 l and shell 83 is filled with a cementatious material or a structural foam 82. In order to prevent material 82 from flowing out of cavity 84 through through-holes 86 and 88, plugs 90 and 92 are provided, preferably formed of a foam material such as StyrofoamTM which will disintegrate at temperatures present in automotive treatment ovens. The plugs are preferably inserted into a11 through-holes except those through which material 82 is injected. In this manner, plugs 88 and 90 are automatically "removed"
so that sufficient clearance is maintained for wiring clips and the like. The preferred material for use in forming material 82 is described in U.S. Patent No. 5,124,186, "Composite Tubular Door Beam Reinforced with a Reacted Core Localized at the Mid-Span of the Tube," dated 3une 23, 1992, the entire disclosure of which is incorporated by reference. Most preferably, the material described beginning at line 41 of column 10 of the aforementioned U. S. Patent No.
5,124,186 is preferred.
In still another embodiment, and referring .now to Figures 15 and 16 of the drawings, a reinforced door beam or side impact beam 100 is seen having an outer structural shell 102 which is preferably formed of mild steel (preferably a yield strength of 2S,000 -35,000 psi) or non-heat treated high-strength steel having a nominal thickness of fiom about .050 inch to about .100 inches.
Structural shell 102 is reinforced locally in accordance with the present invention to provide compression face reinforcement element 104 (shown :in phantom in Figure I S)) In the most preferred embodiment) reinforcement 104 occupies less than about the center one-third of structural shell I02 but preferably more than one-eighth of the lenl;th of structural shell 102.
Referring now also to Figure 17 of the drawings, reinforcement 104 is shown in one embodiment as a three-sided reinforcement with a layer of structural foam l06 disposed along three inner surfaces 108,109 and 110 of structural shell 102. In the illustrated embodiment of Figures 1 S, 16 and 17, foam layer 106 is shown spanning longitudinal gap 112 of structural shell 102, although this orientation is not required. Foam layer 106 is preferably from about .0S0 to about .25 inches thick. Disposed on inner surfaces 108, 109 and 110 of foam layer I06 is inner shell 114 which is preferably formed of thin ultra high-strength steel, preferably having a nominal thickness of from about .025 to about .080 inches. Inner shell 114 is co-extf;nsive with foam layer 106. That is, inner shell 114 has a size and geometry which matches foam Layer 106.
In one mode of fabrication, reinforced door beam 100 is fabricated by extruding a ribbon or sheet of unexpanded resin-based material which is then applied to the surface of inner shell 114 (prefonned to the desired geometry). Inner shell 114 would thus serve the function of a carrier member for the unexpended material that forms foam layer I06. Inner shell 114 with the attached resin can then be inserted into one end of structural shell I 02 and enough pressure applied to bond the resin in place, i.e. to hold the unexpended material that forms foam layer l06 and its attached inner shell 114 in place in the mid portion of outer shell 102. In addition, it may be desirable to add dimples (not shown) in outer shell 102 to hold inner shell 114 and its resin layer in place.
Reinforced door beam 10Q is attached inside a door cavity in any number of configurations such as that shown in U.S. Patent No. 4,978,562 mentioned above, the entire disclosure of which is incorporated herein by reference. The precise attachment means such as end pieces and/or welding is not a critical part of the present invention. Once installed in the vehicle door, reinforced door beam 100 is heated to a temperature sufficient to thermally expand or "foam"
layer 106, such as when the motor vehicle is placed in a paint oven or the like. At the blowing agent activation temperature, the resin that forms layer 106 expands to its final form and solidifies to form a strong bond between inner shell 114 and outer shell 102. Since layer 106 is a structural foam and inner shell 114 is a thin high-strength steel, structural shell 102 is reinforced with a minimum weight increase.
In Figure 18 of the drawings, reinforced door beam 100' is shown having outer structural shell 102', foam layer 106' and inner shell 114'. In this embodiment, foam layer 106' (and inner shell 114') are four-sided in contrast to the three-sided embodiment described in the previous embodiment. In both the three-sided embodiment and the four-sided embodiment, the material used to form the thermally expandable foam layer is that which was previously described in connection with the previous embodiments.
In another embodiment, reinforced door beam or side impact beam 150 is provided with outer shell I52, again a mild to medium strength steel having a thickness of .050 to .100 inch, which includes wide flanges 154 on one side thereof. Flanges 1S4 will typically have a width of from about .43 to about .75 inches. Centrally disposed inner shell 156 has matching flanges 158 and is formed of thin high-strength steel (nominal thickness of from about .025 to about .080 inches).
Inner shell I 56 occupies only about one-third of the length of outer shell l52.
As best seen in Figures 20 and 2I, inner shell 156 is separated from outer shell 152 by a layer I 60 of thermally expanded resin-based material. As expanded, layer l60 has a preferred thickness of from about .060 to about .2S inches. In this embodiment, structural foam layer 160 does not reside between flanges 1 S4 and flanges 1 S8. Instead, flanges 1 S4 and flanges 1 S8 are spot-welded together. Thus, the invention provides localized reinforcement to force in the direction of arrow "A" at minimal additional cost and weight.
Referring now to Figure 22 of the drawings, in one embodiment the present invention provides a reinforced bumper 200 for a motor vehicle. Th.e design of bumper 200 is similar to that of door beam 100 (of Figure 1 S) in some respects. Accordiingly, outer bumper shell 202 is provided which is in the nature of a C-section having flange portions 204. Located in the mid-span of shell 202 preferably the central one-third portion (and preferably at least more than about the middle one-eighth of said shell 202), reinforcement 206 is shovrn having a layer of structural foam 208 disposed between the inner surface 210 of bumper shell 202 and thin, ultra high-strength inner shell 210. Bumper shell 202 will typically be formed of steel (rruld steel or non-heat treated high-strength steel) having a thickness of from about .0S0 to .080 inches. Foam layer 208 will be one of the prefen ed resin-based thermally expanded materials previously described and will have a thickness of from about .060 to about .2S inches. Inner shell 210 wi:Il have a thickness of from about .030 to about .080 inches and will be made from high-strength steel.
As with the reinforced door beam previously described, the thermally expandable resin layer may be extruded, cut to length, and placed on i~Zner shell 210 as a carrier. It may then be inserted in place in bumper shell 202. Preferably after assembly of the vehicle, the resin is thermally expanded to form a light-weight foam layer having a high-strength inner shell.
It will be appreciated, then, that the side impact beams and bumpers shown in Figures 15-23 derive unexpected cost savings and quality by (1) using mild steel or non-heat treated steel as the outer shell (which has the greatest mass) and only a small amount of high-strength steel as the localized inner shell and (2) by minimizing the amount of resin which is used.
It will be understood that the mild strength steel holds its geometric shape after forming (does not exhibit spring back) much better than heat treated steel.
SUMMARY QF THE INVENTION
In one aspect, the present invention provides a hollow laminate beam characterized by its high-stiffness-to-mass ratio. The beam has an outer portion which is separated from an inner tube by a thin layer of structural foam. The cavity defined by the beam may be open or closed along its length.
In another aspect, the hollow laminate be2un of the present invention is an automotive radiator support beam having an outer metal section anti a generally rectangular inner tube, which may be open on one side. At least tluee sides of the rectangular inner tube are coated with a structural foam which is disposed between the rectangular inner tube and the outer metal section and in contact therewith. A metal cap is welded in place to complete the beam and retain the inner tube.
The diameter of any through holes in the inner tube which are in alignment with through-holes in the outer portion are larger than the outer portion throul;h-holes such that the structural foam does not block the through-hole clearances of either metal thicknesses.
In still another aspect, the laminate beam of the present invention is an automotive windshield pillar. A hollow metal tube is disposed within the pillar and is separated from the outer pillar stampings by a thin layer of structural foam.
In still another aspect, the laminate beam of the present invention is an automotive rocker panel assembly. The rocker panel assembly comprises mating inner and outer panel sections which form a generally rectangular rocker panel wall structure. Positioned within the rocker panel wall structure is a closely fitting inner metal tube which defines a cavity. A
thin layer of structural foam is disposed between the rocker panel wall structure and the inner tube structure.
In still another aspect the beam is a motor vehicle drive shaft. An inner tube is closely received within the outer drive shaft housing, thereby defining an annulus. A layer of foam is disposed in the annulus.
The present invention also provides a method of increasing the stiffness-to-mass ratio of a beam, wherein the beam defines a cavity. The method includes the steps of forming a tube which fits within the cavity defined by the beam; placing a layer of resin on at least a portion of the outer surface of the tube; and inserting the tube in the cavity, with the resin contacts the inner wall of the tube.
In still another aspect, the present invention comprises a C-rail section for use in truck frames. An inner stamped or rolled C-shaped member is separated from the outer C-frame rail by a layer of resin-based material.
In still another aspect, a plurality of plugs made of a foam which disintegrates at high temperatures are used to close through-holes in a part which is subsequently filled with a core material. The part is then passed through an oven which melts or disintegrates the plugs.
In still another aspect, the present invention provides a door beam or side impact beam for a motor vehicle door which provides increased compression resistance at minimal cost and weight. A local reinforcement is provided in the mid-span of a steel shell.
The local reinforcement includes a high-strength, thin steel stamping and a layer of thermally expandable foam. This allows the outer shell to be formed of relatively inexpensive mild steel. The foam is sandwiched between the outer shell and the thin steel stamping.
In one aspect, the outer steel shell and inner steel stamping having mating flanges that are welded together by spot welds.
In still another aspect, a reinforced bumper is provided for a motor vehicle.
A local reinforcement provides a steel-foam-steel laminate high-strength structure.
Figure 1 is a perspective view of the front end of a motor vehicle, with the engine removed and the body shown in phantom.
Figure 2 is an exploded perspective viE;w of a radiator support beam made in accordance with the present invention.
Figure 2A is a fragmentary view of the: oversized through-holes of the present invention.
Figure 3 is a plan view of the radiator support beam of Figure 2.
Figure 4 is a front elevational view of the radiator support beam of the radiator support beam of Figure 2.
Figure 5 is a fragmentary longitudinal cross-section along lines 5-5 of Figure 3.
Figure 6 is a cross-section along lines 6-6 of Figure 3.
Figure 7 is a plan view of another radiator support beam made in accordance with the present invention in another configuration.
Figure 8 is a fragmentary longitudinal cross-section taken along lines 8-8 of Figure 7.
Figure 9 is a cross-section along lines 9-9 of Figure 7.
Figure 10 is a cross-section of a rocker panel made in accordance with the present invention.
Figure 11 is a cross-section of a windshield pillar made in accordance with the present invention.
Figure 12 is a cross-section of a drive shaft made in accordance with the present invention.
Figure 13 is a cross-section of a C-rail section made in accordance with the present invention.
Figure 14 is a cross-section of a radiator support beam made according to another aspect of tile present invention.
Figure 15 is a perspective view of a reinforced door beam in accordance with the present invention.
_7-Figure 16 is a section along lines 16-16 of Figure 15.
Figure 17 is a section along lines 17-17 of Figure 15.
Figure 18 is a cross-section of a reinforced door beam in another configuration.
Figure 19 is a perspective view of a reinforced door beam in accordance with the present invention.
Figure 20 is a section along lines 20-20 of Figure 19.
Figure 21 is a fragmentary perspective view of one end of the beam shown ili Figure 19.
Figure 22 is a perspective view of a reinforced bumper made in accordance with the present invention.
Figure 23 is a cross-section along Iines 23-23 of Figure 22.
DETAILED DESCRIPTION OF THE PRhFERRFD EMBQDIMENTS
Referring now to Figure 1 of the drawings, a motor vehicle 10 is shown with the engine removed and the body illustrated in phantom. Radiator support structure or beam 12 is mounted on the chassis and serves to support the vehicle radiator (not sho~~~n). In Figure 2, radiator support beam 12 is illustrated in exploded view having outer shell or portion 14 which in this embodiment is a steel stamping. An inner tube, here shown as charu~el-shaped tube 16, is provided _g_ having a layer of resin-based material I8 applied to selected surfaces. Cap 20 is seen having a plurality of through-holes 22 and serves to enclose channel-shaped tube 16 within outer shell 14.
More specifically, and referring now of Figures 2 through 6, outer shell 14 defines a cavity or channel 24. A number of through-holes 26 are seen through which electric wiring (not shown) may extend. Outer shell I4 includes a laterally extending mounting bracket or plate portion 28 which is secured to components of the engine assembly.
The benef is of the present invention are provided by inner tube or inner portion 16 which in this case is roll-formed metal, far example thin gauge steel, which is formed so that it may be closely fitted within cavity 24 of outer shell 14. Inner tube 16 in this embodiment closely conforms to the geometry of outer shell 14, including having a lateral plate 30 that mates with mounting bracket 28. By providing a layer of resin-based material I 8 on selected surfaces of inner tube 16 and then assembling inner tube 16 and outer shell 14 to form the tube-in-tube construction shown best in the cross-section of Figure 6, the stiffness of beam 12 is increased significantly without a significant increase in mass. Accordingly, as shown in Figures 2 and 6, a layer of a resin-based material 18 is applied, shown here on three sides of inner tube I
8.
A number of resin-based compositions can be utilized to form resin-based layer in the present inventions. The preferred compositions impart excellent strength and stiffness characteristics to beam 12 while adding only marginally to the weight. With specific reference now to the composition of the resin-based layer, the density of the material should preferably be from about 15 pounds per cubic feet to about 40 pounds per cubic feet to minimize weight. The melting point of resin-based layer 18, heat distortion temperature and the temperature at which chemical breakdown occurs must also be sufficiently high such that layer I8 substantially maintains its structure at high temperatures typically encountered in paint ovens and the like. Therefore, resin-based layer 18 should be able to withstand temperatures in excess of 300 degrees F. and preferably 350 degrees F. for short times. Also, the resin-based layer 18 should be able to withstand heats of about 180 degrees F. to 220 degrees F, for extended periods without exhibiting substantial heat-induced distortion or degradation.
In more detail, resin-based layer I 8 includes a synthetic resin, a cell-forming agent, and a filler. A synthetic resin comprises from about 35.0 ,percent to about 95.0 percent by weight, preferably from about 75.0 percent to about 94.0 percent bar weight, and most preferably from about 78.0 percent to about 90.0 percent by weight of layer 18. As used herein, the term "cell-forming agent" refers generally to agents which produce bubbles;, pores, or cavities in layer 18. That is, resin-based layer 18 has a cellular structure, having numerous cells disposed throughout its mass.
This cellular structure provides a Iow-density, high-strength material, which, in beam 12, provides a strong, yet lightweight structure. Cell-forming agents which are compatible with the present invention include reinforcing "hollow" microspheres or microbubbles which may be formed of either glass or plastic. Plastic microspheres may be either thermosetting or thermoplastic and either expanded or unexpended. In one embodiment, unexpended microspheres are used which are then expanded to form resin-based layer 18. The preferred microspheres are from about 1.0 to about 250 and preferably from about 10 to about I80 microns in diameter. The cell-forming agent may also comprise a larger, lightweight material such as macrospheres of greater than 400 microns in diameter. Also, the cell-forming agent may comprise a blowing agent which may be either a chemical blowing agent or a physical blowing agent. Glass microspheres are particularly preferred.
Where the cell-forming agent comprises microspheres or macrospheres, it constitutes from about 1.0 percent to about 60.0 percent by weight, preferably from about 1.0 percent to about 35.0 percent by weight, and most preferably from about 3.0 percent to about 20.0 percent by weight of layer 18.
Where the cell-forming agent comprises a blowing agent, it constitutes from about 1.0 percent to about 10.0 percent by weight, preferably from about 1.0 percent to about S.0 percent by weight, and most preferably from about 3.0 percent to about 5.0 percent by weight of layer 18. Suitable fillers include glass or plastic microspheres, silica fume, calcium carbonate, milled glass fiber, and chopped WO 98l21060 PCT/US97/19981 glass strand. Glass microspheres are particularly preferred. Other materials may be suitable. A
filler comprises from about 1.0 percent to about 55.0 percent by weight, preferably from about 5.0 percent to about 24.0 percent by weight and most preferably from about 7.0 percent to about 19.0 percent by weight of resin-based layer 18.
Preferred synthetic resins for use in the present invention include thermosets such as epoxy resins, vinyl ester resins, ihermoset polyester resins, and urethane resins. It is not intended that the scope of the present invention be limited by molecular weight of the resin. Where the resin component of the liquid filler material is a thermoset resin, various accelerators, such as "EMI-24"
(imidazole accelerator) and "DMP-30," and curing agents, preferably organic peroxides such as "MEK" peroxide and "Percadox," may also be included to enhance the cure rate.
A functional amount of accelerator is typically from about 0.1 percent to about 4.0 percent of the resin weight with corresponding reduction in one of the three components, resin, cell-fornzing agent or filler.
Similarly, the amount of curing agent used is typically from about 12 percent to about 4 percent of the resin weight with a corresponding reduction in one of the three components, resin, cell-forming agent or filler. Effective amounts of processing aids, stabilizers, colorants, UV absorbers and the like may also be included in layer. Thermoplastics may also be suitable.
In the following tables, preferred formulations for resin-based layer 18 are set forth.
It has been found that these formulations provide a layer 18 which results in a beam 12 having a stiffness-to-mass ratio of greater than 1, where 1 is a normalized stiffness-to-mass ratio of a hollow or open C-channel metal beam regardless of mass.
Formulas I and III are preferred for use with clean metal surfaces (i.e., after removing any residue on the contacting metal surfaces such as mill oils and drying compounds). Formula II
does not require extensive pre-cleaning of the metal.
PERCENTAGE PERCENTAGE
]~1GREDIENT ~Y WEIGHT ~Ic~REDIENT BY WEIGHT
FORMULA I FQ$.MULA IIII
Polyester Resin 80.9 EP~ON 828 54.5 ("ARS-137-69") Haloxy 62 7.5 "Percadox 16N" 1.1 De:r 732 6.1 "3 M C I 5" 18 Expancel 551 DU 2.0 SG Micros 8.8 3M: K20 17.7 DI-~CY 3.4 Polyester Resin 48.8 ("ARISTECH 13031") "Percadox 16N" 0.7 "SG Micros" (PA IND) 50.5 As will be appreciated by those skilled in the a.rt, EPON 828 is an epoxy resin, Haloxy 62 is an epoxy diluent, Der 732 is a flexible epoxy, Expancel S51 DU is a blowing agent, SG Micron and 3M K20 are microspheres and DI-CY is a curing agent.
A number of methods of applying layer 1.B to reinforcement tube 16 may be suitable, for example by spraying the resin-based material onto the surface of tube 16.
It may be suitable to fill the space between the inner and outer tubes after tihey are assembled.
Most preferred is the application of the resin-based material using a duck-bill avpplicator which applies a wide, even ribbon of resin on the surfaces of tube 16. In most applications, the thickness (inches) of layer i 8 should be from about .060 to about .50 and more preferably from. about .10 to about .2~, where the preferred foam compositions described herein are utilized.
In those embodiments of the present invention in which outer shell 14 has one or more through-holes 26, for example, for the passage of electrical wiring or the like, it will be necessary to provide matching through-holes 32 in inner tube 16 in register with the through-holes 26 of the outer shell. Since structural foam layer 18 could in some instances block a11 or a portion of through-holes 32, requiring a separate assembly step of clearing the foam material from the hole, In a preferred embodiment of this invention, clearance is obtained by creating over-sized through-holes 32 in alignment with through-holes 26. It is preferred that the diameter of through-holes 32 be at least 20 percent larger than that of through-holes 26, but in some applications equal size through-holes will be sufficient. In this manner, resin or foam which extends from the edges of inner tube 16 into the clearance of through-holes 32 will generally not block wire, clips or screws and the like that are threaded through through-holes 26. This concept is also illustrated in Figure 2A (as viewed looking through hole 32 from the inside) in which a portion of layer 18 extends into the clearance of through-hole 32 during application, but not to the margins of through-hole 26. In the event that layer 18 does obstruct any of the through-holes 32, it may be blown clear using an air jet before layer 18 solidifies.
Refen;ing again to Figures 2 and 5, cap 20 closes radiator support beam I2 as well as cavity or channel 34 defined by inner tube 16. Cavity 34 will generally be clear (i.e., inner tube 16 will be hollow) other than for the presence of wiring. Cap 20 is preferably welded in place. The effective thickness of the reinforced walls of beam 12 is typically four to five times that of shell 14, with very little increase in weight.
Where layer 18 is a thermoset and/or expandable resin-based material, layer 18 may be cured andlor expanded in place from the heat of the B-coat oven. It is preferred that layer 18 bond together shell 14 and tube 16. It should also be noted that the construction of the present invention allows the B-coat to drain, which would not be possible if the entire beam were foam-filled. In addition, the minimal amount of foam which is used does not create a heat sink body as is the case with large, dense foam areas and the minirr~al amount of foam usage reduces materials cost. Also, the need for plugs or the like to allow foam filling of the entire beam is eliminated.
In another embodiment of the present invention, and referring now to Figures 7, 8, and 9, inner tube 16' is shown which has a rectangullar shape and is in the nature of a closed rectangular tube (i.e. closed along its length). As with channel-shaped inner tube 16 rectangular inner tube 16' will generally be hollow. Layer 18 is shown applied to three sides of inner tube 16'.
In general, at least about 25 percent and more preferably at least about 75 percent of the mating area which forms the tube-in-tube region of beam 12 should be covered by layer 18.
Where desired, inner tube 16 at through-holes 32 may be flanged inwardly toward outer shell 14 such that the flange serves as a closure to confine and isolate layer 18. Alternatively, outer shell 14 at through-holes 26 may be flanged inwardly toward inner tube 16 for the same purpose. Also, plugs or grommets in through-holes 26 and/or 32 can be used for this purpose.
A number of materials can be used to form outer shell 14 and inner tube 16 such as plastic or metal, but steel is preferred. The outer shell metal gauge (inches) will typically be from about .030 to about .090. The inner tube metal gauge will typically be from about .025 to about 050.
A number of additional specific applications of the present invention will be apparent in light of the teachings herein. A few of the preferred applications are set forth hereinafter.
Referring now io Figure 10 of the drawings, metal automotive rocker panel assembly 40 is shown having metal rocker inner panel 42 and metal rocker outer panel 44. Inner tube 46 is provided along with a layer of resin-based material 48 disposed thereon which separates inner tube 46 from the rocker panels 42 and 44. An adhesive bead 45, which may be made of the same material as layer 48, is provided adjacent trim holes 50. The assembly is welded at flanges 52.
In Figure 11, the present invention is shown in use as a windshield pillar 54.
Again, the tube-in-tube construction is employed with windshield pillar outer 56 being separated tom windshield pillar inner tube 58 by resin-based layer 60. The assembly is welded together at flanges 62.
In Figure 12, a cross-section of automotive driveshaft 64 is shown having an outer metal tube 66 separated from an inner metal tube 68 by a layer of structural foam 70.
In Figure 13, C-rail 72 is shown having outer wall section 74 separated from inner tube or channel portion 76 by a layer of structural foam 78.
In still another embodiment, and referring now to Figure 14 of the drawings, the entire cavity of a structural member such as radiator support beam 80 having cap 8 l and shell 83 is filled with a cementatious material or a structural foam 82. In order to prevent material 82 from flowing out of cavity 84 through through-holes 86 and 88, plugs 90 and 92 are provided, preferably formed of a foam material such as StyrofoamTM which will disintegrate at temperatures present in automotive treatment ovens. The plugs are preferably inserted into a11 through-holes except those through which material 82 is injected. In this manner, plugs 88 and 90 are automatically "removed"
so that sufficient clearance is maintained for wiring clips and the like. The preferred material for use in forming material 82 is described in U.S. Patent No. 5,124,186, "Composite Tubular Door Beam Reinforced with a Reacted Core Localized at the Mid-Span of the Tube," dated 3une 23, 1992, the entire disclosure of which is incorporated by reference. Most preferably, the material described beginning at line 41 of column 10 of the aforementioned U. S. Patent No.
5,124,186 is preferred.
In still another embodiment, and referring .now to Figures 15 and 16 of the drawings, a reinforced door beam or side impact beam 100 is seen having an outer structural shell 102 which is preferably formed of mild steel (preferably a yield strength of 2S,000 -35,000 psi) or non-heat treated high-strength steel having a nominal thickness of fiom about .050 inch to about .100 inches.
Structural shell 102 is reinforced locally in accordance with the present invention to provide compression face reinforcement element 104 (shown :in phantom in Figure I S)) In the most preferred embodiment) reinforcement 104 occupies less than about the center one-third of structural shell I02 but preferably more than one-eighth of the lenl;th of structural shell 102.
Referring now also to Figure 17 of the drawings, reinforcement 104 is shown in one embodiment as a three-sided reinforcement with a layer of structural foam l06 disposed along three inner surfaces 108,109 and 110 of structural shell 102. In the illustrated embodiment of Figures 1 S, 16 and 17, foam layer 106 is shown spanning longitudinal gap 112 of structural shell 102, although this orientation is not required. Foam layer 106 is preferably from about .0S0 to about .25 inches thick. Disposed on inner surfaces 108, 109 and 110 of foam layer I06 is inner shell 114 which is preferably formed of thin ultra high-strength steel, preferably having a nominal thickness of from about .025 to about .080 inches. Inner shell 114 is co-extf;nsive with foam layer 106. That is, inner shell 114 has a size and geometry which matches foam Layer 106.
In one mode of fabrication, reinforced door beam 100 is fabricated by extruding a ribbon or sheet of unexpanded resin-based material which is then applied to the surface of inner shell 114 (prefonned to the desired geometry). Inner shell 114 would thus serve the function of a carrier member for the unexpended material that forms foam layer I06. Inner shell 114 with the attached resin can then be inserted into one end of structural shell I 02 and enough pressure applied to bond the resin in place, i.e. to hold the unexpended material that forms foam layer l06 and its attached inner shell 114 in place in the mid portion of outer shell 102. In addition, it may be desirable to add dimples (not shown) in outer shell 102 to hold inner shell 114 and its resin layer in place.
Reinforced door beam 10Q is attached inside a door cavity in any number of configurations such as that shown in U.S. Patent No. 4,978,562 mentioned above, the entire disclosure of which is incorporated herein by reference. The precise attachment means such as end pieces and/or welding is not a critical part of the present invention. Once installed in the vehicle door, reinforced door beam 100 is heated to a temperature sufficient to thermally expand or "foam"
layer 106, such as when the motor vehicle is placed in a paint oven or the like. At the blowing agent activation temperature, the resin that forms layer 106 expands to its final form and solidifies to form a strong bond between inner shell 114 and outer shell 102. Since layer 106 is a structural foam and inner shell 114 is a thin high-strength steel, structural shell 102 is reinforced with a minimum weight increase.
In Figure 18 of the drawings, reinforced door beam 100' is shown having outer structural shell 102', foam layer 106' and inner shell 114'. In this embodiment, foam layer 106' (and inner shell 114') are four-sided in contrast to the three-sided embodiment described in the previous embodiment. In both the three-sided embodiment and the four-sided embodiment, the material used to form the thermally expandable foam layer is that which was previously described in connection with the previous embodiments.
In another embodiment, reinforced door beam or side impact beam 150 is provided with outer shell I52, again a mild to medium strength steel having a thickness of .050 to .100 inch, which includes wide flanges 154 on one side thereof. Flanges 1S4 will typically have a width of from about .43 to about .75 inches. Centrally disposed inner shell 156 has matching flanges 158 and is formed of thin high-strength steel (nominal thickness of from about .025 to about .080 inches).
Inner shell I 56 occupies only about one-third of the length of outer shell l52.
As best seen in Figures 20 and 2I, inner shell 156 is separated from outer shell 152 by a layer I 60 of thermally expanded resin-based material. As expanded, layer l60 has a preferred thickness of from about .060 to about .2S inches. In this embodiment, structural foam layer 160 does not reside between flanges 1 S4 and flanges 1 S8. Instead, flanges 1 S4 and flanges 1 S8 are spot-welded together. Thus, the invention provides localized reinforcement to force in the direction of arrow "A" at minimal additional cost and weight.
Referring now to Figure 22 of the drawings, in one embodiment the present invention provides a reinforced bumper 200 for a motor vehicle. Th.e design of bumper 200 is similar to that of door beam 100 (of Figure 1 S) in some respects. Accordiingly, outer bumper shell 202 is provided which is in the nature of a C-section having flange portions 204. Located in the mid-span of shell 202 preferably the central one-third portion (and preferably at least more than about the middle one-eighth of said shell 202), reinforcement 206 is shovrn having a layer of structural foam 208 disposed between the inner surface 210 of bumper shell 202 and thin, ultra high-strength inner shell 210. Bumper shell 202 will typically be formed of steel (rruld steel or non-heat treated high-strength steel) having a thickness of from about .0S0 to .080 inches. Foam layer 208 will be one of the prefen ed resin-based thermally expanded materials previously described and will have a thickness of from about .060 to about .2S inches. Inner shell 210 wi:Il have a thickness of from about .030 to about .080 inches and will be made from high-strength steel.
As with the reinforced door beam previously described, the thermally expandable resin layer may be extruded, cut to length, and placed on i~Zner shell 210 as a carrier. It may then be inserted in place in bumper shell 202. Preferably after assembly of the vehicle, the resin is thermally expanded to form a light-weight foam layer having a high-strength inner shell.
It will be appreciated, then, that the side impact beams and bumpers shown in Figures 15-23 derive unexpected cost savings and quality by (1) using mild steel or non-heat treated steel as the outer shell (which has the greatest mass) and only a small amount of high-strength steel as the localized inner shell and (2) by minimizing the amount of resin which is used.
It will be understood that the mild strength steel holds its geometric shape after forming (does not exhibit spring back) much better than heat treated steel.
Claims (12)
1. A reinforced door beam, comprising:
a longitudinal hollow door beam shell formed of steel, having first and second ends;
a longitudinal local reinforcement disposed in said hollow door beam shell;
said local reinforcement having a length which is less than about one-third of the length of said longitudinal hollow door beam shell;
said local reinforcement being disposed in said longitudinal hollow door beam shell at approximately midway between said first and second ends of said longitudinal hollow door beam shell;
said local reinforcement having a layer of thermally expanded resin-based material and an inner shell;
said inner shell being formed of thin high-strength steel; and said layer of thermally expanded resin-based material being disposed between an inner surface of said longitudinal hollow door beam shell and said inner shell and being rigidly bonded to said longitudinal hollow door beam shell and to said inner shell.
a longitudinal hollow door beam shell formed of steel, having first and second ends;
a longitudinal local reinforcement disposed in said hollow door beam shell;
said local reinforcement having a length which is less than about one-third of the length of said longitudinal hollow door beam shell;
said local reinforcement being disposed in said longitudinal hollow door beam shell at approximately midway between said first and second ends of said longitudinal hollow door beam shell;
said local reinforcement having a layer of thermally expanded resin-based material and an inner shell;
said inner shell being formed of thin high-strength steel; and said layer of thermally expanded resin-based material being disposed between an inner surface of said longitudinal hollow door beam shell and said inner shell and being rigidly bonded to said longitudinal hollow door beam shell and to said inner shell.
2. The invention recited in claim 1, wherein said thermally expanded resin-based material contains microspheres.
3. The invention recited in claim 1, wherein said longitudinal hollow door beam shell has a rectangular cross-section with four inner sides and wherein said local reinforcement has a C-section cross-section such that said thermally expanded resin-based material is bonded to only three of said four inner sides.
4. The invention recited in claim 1, wherein said longitudinal hollow door beam shell has a rectangular cross-section with four inner sides and wherein said local reinforcement has a rectangular cross-section such that said thermally expanded resin-based material is bonded to all four of said four inner sides.
5. A reinforced door beam, comprising:
a longitudinal door beam shell having first and second ends defining a channel) said longitudinal door beam shell having a pair of lateral flanges and a pair of opposed sidewalk, said lateral flanges of said longitudinal door beam shell extending away from said sidewalls of said longitudinal door beam shell at approximately ninety degrees;
a longitudinal inner shell defining a channel, said longitudinal inner shell having a pair of lateral flanges and a pair of opposed sidewalls, said lateral flanges of said longitudinal inner shell extending away from said sidewalls of said longitudinal inner shell at approximately ninety degrees;
said longitudinal inner shell being disposed approximately midway between said first and second ends and occupying less than about one-third the length of said longitudinal door beam shell;
a layer of thermally expanded resin disposed between said longitudinal door beam shell and said longitudinal inner shell and bonded rigidly to an inner surface of said longitudinal door beam shell and to said longitudinal inner shell; and wherein said longitudinal inner shell is nested in said channel of said longitudinal door beam shell and wherein said flanges of said longitudinal inner shell are welded to said flanges of said longitudinal door beam shell.
a longitudinal door beam shell having first and second ends defining a channel) said longitudinal door beam shell having a pair of lateral flanges and a pair of opposed sidewalk, said lateral flanges of said longitudinal door beam shell extending away from said sidewalls of said longitudinal door beam shell at approximately ninety degrees;
a longitudinal inner shell defining a channel, said longitudinal inner shell having a pair of lateral flanges and a pair of opposed sidewalls, said lateral flanges of said longitudinal inner shell extending away from said sidewalls of said longitudinal inner shell at approximately ninety degrees;
said longitudinal inner shell being disposed approximately midway between said first and second ends and occupying less than about one-third the length of said longitudinal door beam shell;
a layer of thermally expanded resin disposed between said longitudinal door beam shell and said longitudinal inner shell and bonded rigidly to an inner surface of said longitudinal door beam shell and to said longitudinal inner shell; and wherein said longitudinal inner shell is nested in said channel of said longitudinal door beam shell and wherein said flanges of said longitudinal inner shell are welded to said flanges of said longitudinal door beam shell.
6. The invention recited in claim 5, wherein said thermally expanded resin includes hollow microspheres.
7. The invention recited in claim 5, wherein said longitudinal inner shell is formed of high-strength steel.
8. The invention recited in claim 7, wherein said high-strength steel has a thickness of from about .025 to about .080 inches.
9. A reinforced motor vehicle bumper, comprising:
a longitudinal bumper shell defining a cavity and having first and second ends;
a longitudinal local reinforcement disposed in said cavity;
said longitudinal local reinforcement having a length which is less than about one-third of the length of said longitudinal bumper shell;
said longitudinal local reinforcement being; disposed in said longitudinal bumper shell at approximately midway between said first and second ends of said longitudinal bumper shell;
said longitudinal local reinforcement :having a layer of thermally expanded resin-based material and an inner shell;
said inner shell being formed of thin high-strength steel; and said layer of thermally expanded resin-based material being disposed between an inner surface of said longitudinal bumper shell and said inner shell and being rigidly bonded to said longitudinal bumper shell and to said inner shell.
a longitudinal bumper shell defining a cavity and having first and second ends;
a longitudinal local reinforcement disposed in said cavity;
said longitudinal local reinforcement having a length which is less than about one-third of the length of said longitudinal bumper shell;
said longitudinal local reinforcement being; disposed in said longitudinal bumper shell at approximately midway between said first and second ends of said longitudinal bumper shell;
said longitudinal local reinforcement :having a layer of thermally expanded resin-based material and an inner shell;
said inner shell being formed of thin high-strength steel; and said layer of thermally expanded resin-based material being disposed between an inner surface of said longitudinal bumper shell and said inner shell and being rigidly bonded to said longitudinal bumper shell and to said inner shell.
10. The invention recited in claim 1, wherein said thermally expanded resin-based material contains microspheres.
11. The invention recited in claim 9, wherein said resin-based layer has a thickness of from about .060 to about .25 inches.
12. The invention recited in claim 9, wherein said inner shell has a thickness of from about .025 to about .080 inches.