CA2131788A1 - Solventless dimeric cyclic ester distillation process - Google Patents
Solventless dimeric cyclic ester distillation processInfo
- Publication number
- CA2131788A1 CA2131788A1 CA002131788A CA2131788A CA2131788A1 CA 2131788 A1 CA2131788 A1 CA 2131788A1 CA 002131788 A CA002131788 A CA 002131788A CA 2131788 A CA2131788 A CA 2131788A CA 2131788 A1 CA2131788 A1 CA 2131788A1
- Authority
- CA
- Canada
- Prior art keywords
- cyclic ester
- column
- acid
- vapor
- alpha
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A dimeric cyclic ester of an alpha-hydroxycarboxylic acid (lactide) is separated and recovered from a vapor product stream containing the cyclic ester, the corresponding lower-boiling hydroxycarboxylic acid (lactic), higher-boiling oligomeric hydroxycarboxylic acid and water without the use of solvents. More specifically, the vapor stream is condensed to obtain a condensate containing substantially all the cyclic ester, and the condensate is refined by distillation means alone to recover the cyclic ester substantially free of water, the alpha-hydroxycarboxylic acid and the higher-boiling oligomers.
Description
213178~
The vapor product stream invariably contains not only the dimenc cyclic ester but volatile hydrox~ylic impurities, among them water, the monomeric alpha-hydroxyacid, which is generally more volatile than the dimeric ester, and o~en higher boiling oligomers of the alpha-hydroxyacid, all of them undesirable as they are s polymerization chain stoppers.
Further, under the conditions of typical previously known art procedures for the separation and recovery of the cyclic ester from the vapor product stream, such as condensation, scrubbing with a solvent or crystallization from a solvent, thehydroxylic impurities, particularly water and alpha-hydroxycarboxylic acid, are capable 0 of undergoing ring-opening reactions with the cyclic ester, resulting in decrease in cyclic ester yield and increase in the acidity of the cyclic ester product. Such reactions are more prone to occur the higher temperature of the recovery process employed.For examp}e, removal and recovery of a cyclic ester such as lactide from 'the vapor product stream by scrubbing with an alcohol such as isopropyl alcohol, as exemplified in U.S. Patents 4,835,293 and 5,053,522, not only provides a medium for potentiai yield-decreasing reaction of the vapor strearn hydroxylic impurities with the lactide product but entails the ~rther possibility of the hydroxylic solvent itself reacting with the cyclic ester to form yield-decreasing open-ch~in derivatives thereof.
Moreover, reliaDce on a solvent, whether for scrubbing the vapor product stream to recover the cyclic ester or for purifying it by recrystallization, is disadvarita ,eous a. it necessitates facilities for storing the solvent, using it, purif~in, it and preventing it ~rom escapîng into and contaminating the environment, all of which adds significantly to the process investment and operating costs.
: U. S. Patent No. 4,990,222 discloses obtaining glycolide or alkyl 2s ~ substituted glycolides firom low molecular weight polyglycolide by mixing the poiyglycolide with a catalyst and ~eeding the mixture to a twin screw e~truder. The twin screw e~truder has a temperature gradient of about 130C to 280C which a~ects conversion of the polyglycolide to glycolide which is removed firom the twin screw e~ctruder under vacuum near the dowIlstream end of the twin screw extruder. The 30 glyc~lide is se.parated from the other materials removed with it from the twin screw extruder by means of a disbllation apparatus such as a thin film evaporator or falling film evaporator.
.
SUMMARY OF T~ INV~:NTION
In vi~w of the above problems associated with the previously known process, it is an object of this invention to provide a process fot the separation and %~
21 3i 7 - la -recovery of dimeric cyclic esters from vapor product streams containing hydroxylic impurities that effects the separation of the ester from the impurities without the use of a solvent.
It is another object to provide such a separation and recovery process that relies on relative volatilities to effect separation of the cyclis ester ~om the correspondin;, and lower-boiling monomeric alpha-hydroxycarboxvlic acid, the higher-boiling oligomeric hydroxycarboxylic acids and water when present.
. . .
~fi ~ri ~1' ,"s. , ,~ "",A ".~ ,"~' ~ J ,;;~ . ~'~: ~ .. . ,. ~, ,~, . ~, ~ ` ', ' ' ' ,' ' ' ',~. ,.,' : `, ~ ; .
213~88 W~ 93/1~20 PCI /US93/02298 The vapor product stream invariably contains not only the dimeric cyclic ester but volatile hydroxylic impurities, among them water, the monomeric alpha-hydroxyacid, which is generally more volatile than the dimenc ester, and oflcen higher boiling oligomers of ~he alpha-hydroxyacid, all of them undesirable as they are s polymerization chain stoppers.
Further, under the condi~ions of typical previously known art procedures for the sepa~ation and recovery of the cyclic ester from the vapor product stream, such as condensation, scrubbing uith a solvent or crystalli~ation from a solvent, thehydroxylic impurities, particularly water and alpha-Xydroxycarboxylic acid, are capable 10 of undergoing ling-opening reactiorls with the cyclic ester, resulting in decrease in cyclic ester )neld and increase in the acidity of the c3rclic ester product. Such reactions are more prone to occur the higher temperature ofthe recovery process employed.
For example~ removal and recovery of a cyclic ester such as lactide firom the vapor product s~ream by scrubbing with an alcohol such as isopropyl alcohol, as 1~ exemplified in U.S. Patents 4,835,293 and 5,053,522, not only provides a medium for potential yield-decreasing reaction of the vapor stream hydroxylic impurities with the lactide product but e~tails the~ her possibility of the hydroxylic solvent îtself reacting with the cyclic ester to form yield-decreasing open-chain derivatives thereof.
Moreover, reliance on a solvent, whether for scrubbing the vapor 20 product stream to recover:the cyclic ester or ~r pu~ ing it by recrystallization, is disadvantageous as h necessitates facilities for storing the solvent, using it, puri~ing it ~: and preventing it ~om escaping into and contan~inating the environment, all of which adds significantly to the process investment and operating costs.
:
SUMIUARY OF TE~E INVlENTION
In view of the above problems associated with the previously kn~m :: :
process, it is an objeGt :of this invention to provide a process for the separation and rec~very of dimeric cyclic esters from vapor product streams containing hydroxylic impu~ities that ef~ects the eparation of the ester from the impurities without the use of a so~ent.
It is another object to provide such a separation and recovery process : that relics on relative voi~tilities to effect separatisn of the c~iic ester ~om the corresponding and lower-boiling monomeric alpha-hydr~xycarboxylic acid, the :~ 35 higher-boiling oligomenc hydroxycarboxylic acids ~nd water when present.
213178~
93/18020 P~r/us93/o22 Still another object is to provide a solvent-less process which enables the separation and recovery of lactide and other dimeric cyclic esters ~om vapor product streams by distillation means alone.
Thus the present invention provides a process for the separation and s recovery of a dimeric cyclic ester ~rom a vapor product stream containing said ester and rninor amounts of one or more hydroxylic impurities including an alpha-hydroxycarbo~ylic acid more volatile than the cyclic ester and optionally including water arld oligomeric hydroxycarboxylic acid higher-boiling (i.e., less volatile3 than the cyclic ester, which process comprises condensing the vapor stream and 10 ~ctionally distilling the condensate to separate the cyclic ester ~om residual hydroxylic impurities, including lower-boiling monomeric alpha-hydroxycarbo~ylic and, when present, higher-boiling oligomeric hydroxycarboxylic acids, and recovering a dimeric c~rclic ester frac$ion having a substantially lowered acid content.
Preferably, the cyclic ester is a lactide, which may be L-, D-m, meso- or 15 racemic lactide, and the alpha-hydro~ycarbo~ylic acid is L-, D- or racemic lactic acid, and the higher-boiling acid impurity is an oligomer of a lactic acid as above.
By "hydroxylic impurities" as used herein it is meant to include hydroxycarboxylic acids such as ~he monomeric alpha~hydroxy acid and low molecular weight oligomenc hydroxycarboxylic acids thereof:as well as water, which is normally 20; produced therewith as volatile impurities in the vapor product s~ream formed on depolyme~izin~/thermolyzing an oligomer of an alpha-hydroxycarboxylic acid such as lacticacid.
:: ~ The invention is:based on the disc~very that impure cyclic ester as ; defined :can b~ separated ~om its impurities and obtained thereby as polymer grade 25 : rnaterial by distillation means alone, more particularly by fractional distillation at temperatures and pressures that rninimize acid-producing side reactions. The : solventless distillation p3~ocess of this invention is surprisingly ef~ective and economic for the intended pulpose In view of the dynamic nature of the water-hydroxycarboxylic acid(s)~cyclic ester system and its propensity to deteriorate in terms of cyclic ester 30 quality under cDnditions oî therrnal stress.
: : ' ;::
7 ~ ~
In general, the invention is applicable to the preparation, recovery and purification of cyclic esters having the formula R2 \ C/ \C//
~,C\ /C~ Rl 0 wherein Rl and R2 are independently hydrogen or an alkyl radical having 1 to 6 carbon atoms. Preferably Rl and R2 are H or methyl, as in glycolide (where;n Rl = R2 = H) and more preferably as in lactide (wherein Rl = H, R2 = methyl).
In general, it has been ~ound the relative order of decreasin~ volatility of the princlpal componen~s of a depolymerization vapor product stream (excluding s carrier gas when such is used to strip the depolyrnerization products from the reaction mass) is water, monomeric alpha-hydroxycarboxylic acid (lactic acid), dimeric cyclic ester (lactide~ and volatile oligomers of the alpha-hydro~ acid. For example, the boiling points of water, lactic acid (LA), lactide (LD) and lactoyllactic acid ~L2A) at atmospheric pressure at 100, 217, 259 ~estimatedl and 359C ~estimated), respectively.
20 The same relative order of volatility holds over a wide range of reduced pressures, although the ratio (or "alpha"~ of the vapor pressur~s exerted by any two components at a given temperature may change with change in pressure. The vapor pressures of each component over a range of tcmperatures are readily determined by trial and the "alphas" of the various component pairs are straight forwardly calculated. It isr ~ ~!3 ~ preferred to operate the fractional distillation process at coordinated temperatures and pressures such that the "alpha" of the alpha-hydroxyacid (lactic) vapor pressure to the c ycllc ester ~lactide) vapor pressure and the "alpha" of ~he cyclic es~er vapor pressure to the H~OCR1,R2CO)2OH (lactoyllactic acid~ vapor pressure are as high as practicable, preferably each "alpha" is at least about 5 at a particular condensation temperature and 30 pressllre.
Since the "alpha" ratio for any given pair of components tends to decrease with increasirlg temperature it is best to operate ~t low temperatures and pressures 50 as to maximize the degree of the separations desired.
In ano~her aspect of the invention, the vapor product s~ream issuing 35 ~om a depolymenzation reactor, which contains ~he major proportion of a dimeric cyclic ester as deISned (lactide~ and minor amounts of one or ~nore hydroxylic impurities including an aipha-hydroxycarboxylic acid more volatile ~han the cyclic ester and T
213~788 93/~8020 PCI/USg3/02~98 In general, the invention is applicable to the preparation, recovery and purification of cyclic esters having the formula Rl R2 ~ C
C C R
O O R~
0 wherein R~ and lR~ are independently hydrogen or an alkyl radical ha~ing 1 ~o 6 carbon atoms. Prefierably Rl and R2 are H or methyl, as in glycolide (wherein Rl = R2 = H) and rnore preferably as in lactide (wherein R1 = H, R2 = methyl).
Ill general, it has been found the relative order of decreasing volatility of the principal components of a depolymerization v~vr product s~ream (excluding 1~ calTier gas when such is used to strip the depolymerization products from the rea~ion mass) is wate~, monomeric alpha-hydroxycarbo~lic acid ~lactic acid), dimeric ~rclic ester (lactide) arld volatile oligomers of the alpha-hydroxy acid. ~or example, the laoiling points of water, lactic acid (LA), lactide (LD~ and lactoyllactic acid ~L2A) ~t atmo~pheric pressure at 100, 217, 259 (estimated) aIld 359C (estima~ed), respectively.
The sam e relative order OI volatility holds over a wide range of reduced pressures, ; alth~ugh ~he ratio (or U~pha") ofthe vapor pres~ures exe~ed by any tw o co m ponen~s at a 8~ven tem perature nnay change Ynth change in pressure. The vapor pressures of each:co m ponent over a range oftemperatures are readily detern~ned by t~al and the : "alphas" o~ the vanous co m ponent pairs are str~ght forvvardly calculated. It is 2s ~prefe~red to opera~e the f~actional distillation process at coordinated tem peratures and -: pressures such tha2the "alpha" ofthe alpha-hydroxyacid ~lactic~ vapor pressure to the cyclic ester (lactide~ vapor pressure and the "alpha" of the cyclic ester vapor pressure to the H(OCRl,R~CO)2OH (lactoyllactic acid) vapor pressure are as high as practicable, prefierably each l'alpha" is atleast about 5 at a pa¢ticular condensation lemperature and pressure.
Since the "alpha" ratio for any given pair of components tends to decrease with increasing t~mperature it is best to operate at low temperatures and pressures so as to maximize the degree of the separations desired.
In another aspect of the invention, the vapor produet stream issui~g 35 ~om a depolymeriza~ion reactor, which contains the major proportiorl of a dime~ic eyclic ester as defined (lactide) and minor amounts of one or more hydroxylic impurities including an alpha-hydroxycarbo~ylic acid more volatile th~n the cyclic ester and .~ .
established and continuously taken off as a vapor sidestream at a point which is below the overhead takeoff and below the condensate feed point to the column, and ~d) a highest boilin~ fraction consisting lar ely of oligomeric acid(s) and some cyclic ester is present at the bottom of the colurnn, which is purged as necessary to rnaintain a s balanced colurnn. The feed rate of the condensate to the column and the take-off rates of the overhead, the cyclic ester fraction and the purge (heel) from the bottom-rnost fraction are coordinated such that a substantially steady state condition can bemaintained in the column. Further, the overhead can be continuously processed toisolate a cyclic ester-rich component which can be recycled to the ~actionating colurnn 0 and the acid-lich remainder recycled to the oligomerization step. Sirnilarly, the purge ~heel) taken from the bottom of the colurnn, which is rich in oligomeric acids and contains some cyclic ester can be recycled to the depolymerization step ~or conversion to additional quantities of cyclic ester.
In the fractional distillation step, best results are ac~lieved at low temperatures and pressures. Low temperatures minimize the possible occurrence ofside reactions between water and/or acid with the cyclic ester that can lead to product loss and deterioration of product quality. For lactide recovery it is preferred the temperature be not greater than 220`C, more preferably not greater than 200`C, and most preferably not greater than 180` C.
~or example, with reference to Fig. 1, cr~de lactide condensate : containing lactic acid, optionally water and higher-boiling oligomers thereof obtained by sondensing the vapor product stream issuing from a depolymerization unit is fed through line 2 to distillation colurnn 1 maintained at a bottoms temperature not great than 180` C and a pressure of 30 rnm Hg, which conditions of temperature and pressure 2s are sufficient to vaporize the feed material substantially completely.
A w~ter and lactic acid vapor fraction containing some lactide is taken o verhead via line 3j a }actide-rich ~action, largely free of water, lactic acid and higher-boiling oligomeric lactic acids is removed firom the column as a vapor side stream through line 4 and is condensed to liquid in condenser 5 maintained at a temperature (about 100` C) just above the melting point of the lactide.
A higher boiling bottoms stream sonsisting largely of oligomers and lactide is removed via line 6. The molten lactide conde~sed in S can be fi~rther refined, if desired, to provide still lowe~asid content material by feeding the condensate ~om S
~ ~ through line 7 to a second ~actionating column 8 also maintained at a bottom 180C
:;; ~ 35 and 30 rnm Hg. The vapor overhead ~om 8 is removed throu~h ~, the refined lactide ~: vapor stream through 10 and the high-bo~lers through 11. The lactide Srapor stream passes through sondenser lZ where it is liquefied and advantageously emerges as a 21 3~78~
polymer-orade molten stream via e,~cit line 13. This stream, if desired, can be fed directly in the molten state to a polymerizer for the production of hioh molecular weight polylactic acid. Should the molten stream exiting 13 perchance have a higher acid content than desired, it can be fed to a third fractionating column and thedistillative refining process repeated.
The overhead stream exiting line 3, which is rich in water and lactic acid and may contain lactide can be dehydrated if necessary and fed to an oligomerization reactor (not shown) for conversion to a depolymerizable lactic acid oligomer as is known in the art.
o Referring to Fig. 2, overhead lactide stream 9 containing lactic acid is combined with bottoms streams 6, both containing lactide and higher-boiling oligomers.
: ~ The combined 6-9 strearn is passed via line 15 to flash still 16, maintained at 125'C and 10 mm Hg, from which is flashed residual lactic acid and the bulk of the lactide content -o~ the combined stream as a vapor stream. The vapor stream exits 16 via line 17, 3 passes through condenser 18, emerges as crude liquid composition lactide composition and joins incoming crude lactide condensate ~om a depolymerization reactor ~not shown) at line 2.
High-boiling oligomeric residue is removed from 16 through line ~0. Its :
lactic acid values can be recovered, if desired, by hydrolysis; the hydrolysate can be concentra~ed and the concentrate fed to an oligomerization reactor (not shown) for co~lversion to a depolymerizable lactic acid oligomer as described above for theaqueous lactide stream exiting line 3.
~` ~ The following examples are presented to fi~rther illustrate specific embodiments of the present invention and as such are not to be interpreted as being 2~ unduly lirniting ~ Temperatures are in degrees Celsius and percenta ,es in percent by weight unless otherwise.stated.
E~ IPLE 1 This Example illustrates the crackingldepolymerization of an oligomer of L-lact,lc acid to form an impure L-lactide vapor stream and partial condensation of the ~' ~ vapor stream to obtain a high lactide content condensate, followed by fractional distillation of the condensate to recover low acid content L-lactide.
: ~ An oligomer of L-lactic acid was prepared by heating 88% L-lactic acid eontair~ing 0.3 percent stannous octoate at temperatures up to 180` wîth removal of water until the product had a degree of polymerization of about 10. The still molten (150`) oligomer was continuously craclced by feeding it ~o the top of a 7.62 cm ~' WO 93/18020 P~JUS93/02298 polymer-grade molten s~ream via exit line 14. This stream, if desired, can be ~ed directly in the molten state to a polymerizer for the production of high molecular weight polylactic acid. Should the molten stream exiting 14 perchance have a higher acid content than desired, it can be fed to a third fractionating column and thedistillative refining process repeated.
The overhead stream ~xiting line 3, which is rich in water and lactic acid and may contain lactide can be dehydrated if necessaly and fed to an oligomerization reactor (not shown) ~or conversion to a depolymerizable lactic acid oligomer as is known in the art.
0 Referring to Fig. 2, overhead lactide stream 2 containing lactic acid is combined with bvttoms streams 6, both containing lactide and higher-boiling oligomers.
The combined 6-9 stream is passed via line 15 to flash still 16, maintained at 125`C and 10 mm Hg, from which is flashed residual lactic acid and the buik of the lactide content of` the combined stream as a vapor stream. The vapor stream exits 16 vla line 17, passes through condenser 18, emerges as crude liquid composition lactide composition and joins incoming cmde lactide condensate ~om a depolymerLzation reactor (not shown) at line 2.
High-boilirlg o}igomeric residue is removed from 16 through line 20. Its lactic acid values can be ~recovered, if desired, by hydrolysis; the hydrolysate call be 2û concentrated and the conce~rate fed to an oligomerization reactor (not shown) fior cQnversion to a~depolymerizable lactic acid oligc,mer as described above for thea~ueous lactide stream exi~ing line 3.
The following examples are presented to fi~rther illustr~te specific embodiments of the present invention and as such are not to be interpreted as being unduly limiting. Temperatures are in degrees Celsius and percentages in percent by weight unless ot}lerwise stated.
:
EXAMPLE I
T~is Example illustrates the crackin~/depolymerization of an oligomer of L-lactic acid to form an impure L-lactide vapor stream and partial condensation of the vapor stream to obtain a high lactide content condensate, followed by ~ctional distillation of the con~ensate to recover low acid content L~lactide.
An oligomer of L-lactic acid was prepared by he~ting 88% L-}actic acid containing 0.3 percent stannous oc~oate at temperatures up to 180` with removal o~
3S water Imtil the product had a degree o~polyJTIe~ization of about 10. The still molteq~
(150`) oligomer was continuously cracked by fieeding it to the top of a 7.62 em ~O 93/18û20 21317 8 ~ PCr/VS93J02298 diameter 5-sieve tray glass Oldershaw column heated to 210` and maintained at a reduced pressure of 10 mm Hg.
About 1,437 gms of the oligomer was fed to the cracking column over a 2.5 hour period, during which time about 71% of the oligomer was cracked to 5 vaporized products. Partial condensation of the vapor product s~ream at 132` and 11 mm Hg pressure gave an acid-rich vapor (about 172 gms) and 843 grams of lactide-rich condensate containing 300 meg/kg of acidity corresponding to 253 meg of acidity. The condensate was immediately solidified by cooling at -10` for oven~ight storage.
The 843 gms of frozen condensate was liquefied by microwave he~ting 0 and then batch-distilled in a 5.1 cm diameter 20 plate Oldershaw column at 5 mm Hg~ a 4:1 to 6:1 reflux ratio, a bottoms temperature of 155-1~7`, and a head temperature of 119-124` over a 2.5 hour period. FiYe overhead cuts were taken as follows:
~_ ~
I C~UT: WEIG~IT ACll)lTY
~ e, ... ......... ,.. . ~
I 1 661 gms 674.8 meg/kg .. ... . .,, _ l 2 60.1 240 ::
l 3 8S. 1 69 I 4 746 27.4 _ .. ....... ~... .
~: l ~ 174.7 7.4 _ ~
Elel 21114 5'~9 The procedure of Example 1 was repeated with a lactic acid oligomer containing 16 lactyl i.e. -OCH(CH33CO- units. Approximately 1,437 gms of the oligomer at a temperature of 170` was fed over a 3 hour penod at a rate of about 8 fmin to the depolymerizer maintained at 210`. The vapor product strearn from the2o ~depolymerizer~was partially condensed as before a~ 132` and 10 rnm Hg to ~rield ~
water-acid ~action ~208 gms~ and a crude liquid lactide condensate ~733 gms) ha~ng an acidity content of 324 meq/kg. The residue in the depolymserizer arnounted to 484 gms.
The crude lactide condensate was stored for 14 days at 0` and r~melted 2S by microwave heatillg. Its acidity was redetermined and ~ound to have increased to 544 meq/kg 721 gms of the crude lactide was then ~actionally distilled ~ 30 mm Hg, a head temperature o~l50-155` and a reflux of 4:1 to 6:1. Five cuts were taken:
WO 93/18020 ~ 1 ~17 g ~ PCr/US93/02' ~ O
, CUT WEIG~IT ACIDITY
, 1 _ 41.8 _ 2940 2__ _ 79.3 96 _ _ 3_ _ 163.7 _ 54_ _ ~ 143.3 37 99.4 133 I ~_ , _ _ ... .
il= I _ 101.4 9~0 Practions of previously r~fined (distilled) lactide having acidities of less than about 100 meq~cg were combined and melted to provide 1,017 gms havin~ an s initial acidity of 59 meq/kg, which increased to 7~ me~/kg a~er storage overnight at 2~` and then remelted at 100`.
1,013 ~pns of the lactide composition was ~actionally distilled as described in Examples 4 and 5. the pressure was 30 mm Hg, the head temperature 134 to 156`, and the opçrating reflux ratio was about 4:1.
10 Acidity, meql~g ~ . . ___ CIJT WT. gmsINITIAL After 20 hrs at 25 ~ 1 ;79.~ 484 513 : ~ 2 _ ~ _ 90.6 ~.~ 21 3 ~ 104.6 1 g : ~ : ~ . _ . .. . .
`~:: : ~ 4 ~ : 95.6 2 10 _ . _ _ ~
; 1iO.2 _ 3 8 ~ ~ 6 ~ __108.4 _ _ __3 : ~ 7 ~110.3 5 8 . . . . .. - .... __ _ ~ : 8 : ~ 107.9 not. det. 22 , ._ . . .. ~ __ ~ _ : 9 _ ~ 53.2 not. det. _ 22 _ Heel 11_8 not. det _ l;l __ , : ~ These results show that the invention process is capaUe OI produci~
low acid content lactide even under batch distillation conditions. They also show that 1S the acid-lactide~ s3rstem is: a dynamic one with the: acid content tending to increase an s$anding, even at annbient tem peratures unless precautions are t ~ en to exclude m oisture.
wo 93~8020 2 1 ~ 1 7 ~ 8 Pcr/US93/02298 The distillation results also suggest that low, substantially nil, acid conterlt lactide and other dimeric cyclic esters at alpha-hydroxycarboxylic acids could be obtained in high yields under continuous distil~ation conditions, thereby completely obviating the need for solvent treatments to obtain such high qualitys pol~ner-grade m~tenal.
The procedure of Example 1 was carried out with 2 kg of 88% lactic acid con~aining 6 gms of stannous octoate, which was dehydrated and oligomenzed by 0 heating a$ 120 to 180` with removal of 407 gms of water. The resulting oligomer con~ained on the average 10 lactyl units. Approximately 1,437 gms ofthe molten (150 - ~6û`) oligomer was fed at a rate of about 9.6 gms/min to the depolymerizer maintained at 220`C and 10 mm Hg pressure. The vapor product stream issuing firom the depolymerizer was partially condensed in the flash chamber at 100-103` and 2 mm 15 Hg pressure. The condensate, about 890 gms, contained 755 meq/lcg of acidity.The above condensate was batch distilled as described in Example 5.
The pres~e was 30 mm Hg, the head temperature ranged ~rom an initial 117` to 135`
and finally ~t 155` for a first cut and at 155` for 5 additional cuts, and the reflux ratio ranged f~om 12:1 to 1:1 fior cuts 3-6. The 6 cuts were as follows:
~ut _ _Wt. gms Acidity? ~eq/kg 104.4 ~825 2 123. 1 41 - .. .. .... ~ . . ...... . . . I
--- _3 ~ 114.5 : 24_ __ 4 ~ 10~.7 26 ~. ~ ~ . . ~ l _ 5 ~ _ 130.9 !90.
~; ~ 6 2~Z.9 343 :
:
1 :XAMPLE 5 The procedure of Example 1 was repeated. The lactic acid oligomer contained 11.3 la~tyl units. AQproximately 1,437 gms of the molten (150`) oligomer was fed ~o the depolymerizer over a 165 minute penod, and the vapor product streZ~n om the depolyme~izer was ~ed to the pa~tiZal condensation chamber rnailltained at 100`
~; and 2 mm Hg.
The overhead ~om the partial condenser, collected in two cold traps, weighed 69.7 gms, the crude lac~ide remZaininglJ in the condensing cha;nber weighed 1,351 gms and had ~1 } meq/kg of acidity.
WO 93/18020 2 1 3 17 8 8 P~/US93/02.
~ 2 The crude lactide was fractionally distilled batchwise as before, and 7 cuts were taken:
Cut Wt. gms Acidity, meq/kg 1 129.4 2529 _ 3 161 5 36 4 145.8 24 L~ ~ ~
Comparison of the batch distillation results of Examples 2, 4 and 5 o~ained at 30 mm Hg with those of Example 1 obtained at ~ mm Hg shows that better results are obtained at the lower pressure. This can be attributed to a lesser tendency for the distillation m~ss to produce acidic species at the lower temperatures pertaining at the lower pressure.:
` ~ :
Distillation ClltS 2, 3, 4 and 5 from Example 4 were combined with distillation cuts 3, 4, 5, 6 and 7 ~om Example S. 1167 gms of the composite having 59 meq/kg of acidity was batcbwise ~actionally distilled as in Example 1 except that the dis~illation pressure was 30 rnm Hg, and the temperature was l55` at the head and 160-163` at the ~ase of the column. The reflux ratio was 4:1 throughout. Seven distlllation cuts were talcen:
:;: :
WO93/180~0 21~1788 Pcr/uss3/02298 Cut Wt. gms. Acidity, meq/kg --~ 3 - 130.3 17 _ 165.7 14 152.2 9 ~ L ~
:
Having thus described and exemplified the invention with a cert~in degree of particulality, it should be appreciated that the following claims are not to be so lin~ited 5 but are to be affor~ed a scope commensurate u~th the wording of each element of the claim and equivalents thereo ,~
:: :: :
. : :
The vapor product stream invariably contains not only the dimenc cyclic ester but volatile hydrox~ylic impurities, among them water, the monomeric alpha-hydroxyacid, which is generally more volatile than the dimeric ester, and o~en higher boiling oligomers of the alpha-hydroxyacid, all of them undesirable as they are s polymerization chain stoppers.
Further, under the conditions of typical previously known art procedures for the separation and recovery of the cyclic ester from the vapor product stream, such as condensation, scrubbing with a solvent or crystallization from a solvent, thehydroxylic impurities, particularly water and alpha-hydroxycarboxylic acid, are capable 0 of undergoing ring-opening reactions with the cyclic ester, resulting in decrease in cyclic ester yield and increase in the acidity of the cyclic ester product. Such reactions are more prone to occur the higher temperature of the recovery process employed.For examp}e, removal and recovery of a cyclic ester such as lactide from 'the vapor product stream by scrubbing with an alcohol such as isopropyl alcohol, as exemplified in U.S. Patents 4,835,293 and 5,053,522, not only provides a medium for potentiai yield-decreasing reaction of the vapor strearn hydroxylic impurities with the lactide product but entails the ~rther possibility of the hydroxylic solvent itself reacting with the cyclic ester to form yield-decreasing open-ch~in derivatives thereof.
Moreover, reliaDce on a solvent, whether for scrubbing the vapor product stream to recover the cyclic ester or for purifying it by recrystallization, is disadvarita ,eous a. it necessitates facilities for storing the solvent, using it, purif~in, it and preventing it ~rom escapîng into and contaminating the environment, all of which adds significantly to the process investment and operating costs.
: U. S. Patent No. 4,990,222 discloses obtaining glycolide or alkyl 2s ~ substituted glycolides firom low molecular weight polyglycolide by mixing the poiyglycolide with a catalyst and ~eeding the mixture to a twin screw e~truder. The twin screw e~truder has a temperature gradient of about 130C to 280C which a~ects conversion of the polyglycolide to glycolide which is removed firom the twin screw e~ctruder under vacuum near the dowIlstream end of the twin screw extruder. The 30 glyc~lide is se.parated from the other materials removed with it from the twin screw extruder by means of a disbllation apparatus such as a thin film evaporator or falling film evaporator.
.
SUMMARY OF T~ INV~:NTION
In vi~w of the above problems associated with the previously known process, it is an object of this invention to provide a process fot the separation and %~
21 3i 7 - la -recovery of dimeric cyclic esters from vapor product streams containing hydroxylic impurities that effects the separation of the ester from the impurities without the use of a solvent.
It is another object to provide such a separation and recovery process that relies on relative volatilities to effect separation of the cyclis ester ~om the correspondin;, and lower-boiling monomeric alpha-hydroxycarboxvlic acid, the higher-boiling oligomeric hydroxycarboxylic acids and water when present.
. . .
~fi ~ri ~1' ,"s. , ,~ "",A ".~ ,"~' ~ J ,;;~ . ~'~: ~ .. . ,. ~, ,~, . ~, ~ ` ', ' ' ' ,' ' ' ',~. ,.,' : `, ~ ; .
213~88 W~ 93/1~20 PCI /US93/02298 The vapor product stream invariably contains not only the dimeric cyclic ester but volatile hydroxylic impurities, among them water, the monomeric alpha-hydroxyacid, which is generally more volatile than the dimenc ester, and oflcen higher boiling oligomers of ~he alpha-hydroxyacid, all of them undesirable as they are s polymerization chain stoppers.
Further, under the condi~ions of typical previously known art procedures for the sepa~ation and recovery of the cyclic ester from the vapor product stream, such as condensation, scrubbing uith a solvent or crystalli~ation from a solvent, thehydroxylic impurities, particularly water and alpha-Xydroxycarboxylic acid, are capable 10 of undergoing ling-opening reactiorls with the cyclic ester, resulting in decrease in cyclic ester )neld and increase in the acidity of the c3rclic ester product. Such reactions are more prone to occur the higher temperature ofthe recovery process employed.
For example~ removal and recovery of a cyclic ester such as lactide firom the vapor product s~ream by scrubbing with an alcohol such as isopropyl alcohol, as 1~ exemplified in U.S. Patents 4,835,293 and 5,053,522, not only provides a medium for potential yield-decreasing reaction of the vapor stream hydroxylic impurities with the lactide product but e~tails the~ her possibility of the hydroxylic solvent îtself reacting with the cyclic ester to form yield-decreasing open-chain derivatives thereof.
Moreover, reliance on a solvent, whether for scrubbing the vapor 20 product stream to recover:the cyclic ester or ~r pu~ ing it by recrystallization, is disadvantageous as h necessitates facilities for storing the solvent, using it, puri~ing it ~: and preventing it ~om escaping into and contan~inating the environment, all of which adds significantly to the process investment and operating costs.
:
SUMIUARY OF TE~E INVlENTION
In view of the above problems associated with the previously kn~m :: :
process, it is an objeGt :of this invention to provide a process for the separation and rec~very of dimeric cyclic esters from vapor product streams containing hydroxylic impu~ities that ef~ects the eparation of the ester from the impurities without the use of a so~ent.
It is another object to provide such a separation and recovery process : that relics on relative voi~tilities to effect separatisn of the c~iic ester ~om the corresponding and lower-boiling monomeric alpha-hydr~xycarboxylic acid, the :~ 35 higher-boiling oligomenc hydroxycarboxylic acids ~nd water when present.
213178~
93/18020 P~r/us93/o22 Still another object is to provide a solvent-less process which enables the separation and recovery of lactide and other dimeric cyclic esters ~om vapor product streams by distillation means alone.
Thus the present invention provides a process for the separation and s recovery of a dimeric cyclic ester ~rom a vapor product stream containing said ester and rninor amounts of one or more hydroxylic impurities including an alpha-hydroxycarbo~ylic acid more volatile than the cyclic ester and optionally including water arld oligomeric hydroxycarboxylic acid higher-boiling (i.e., less volatile3 than the cyclic ester, which process comprises condensing the vapor stream and 10 ~ctionally distilling the condensate to separate the cyclic ester ~om residual hydroxylic impurities, including lower-boiling monomeric alpha-hydroxycarbo~ylic and, when present, higher-boiling oligomeric hydroxycarboxylic acids, and recovering a dimeric c~rclic ester frac$ion having a substantially lowered acid content.
Preferably, the cyclic ester is a lactide, which may be L-, D-m, meso- or 15 racemic lactide, and the alpha-hydro~ycarbo~ylic acid is L-, D- or racemic lactic acid, and the higher-boiling acid impurity is an oligomer of a lactic acid as above.
By "hydroxylic impurities" as used herein it is meant to include hydroxycarboxylic acids such as ~he monomeric alpha~hydroxy acid and low molecular weight oligomenc hydroxycarboxylic acids thereof:as well as water, which is normally 20; produced therewith as volatile impurities in the vapor product s~ream formed on depolyme~izin~/thermolyzing an oligomer of an alpha-hydroxycarboxylic acid such as lacticacid.
:: ~ The invention is:based on the disc~very that impure cyclic ester as ; defined :can b~ separated ~om its impurities and obtained thereby as polymer grade 25 : rnaterial by distillation means alone, more particularly by fractional distillation at temperatures and pressures that rninimize acid-producing side reactions. The : solventless distillation p3~ocess of this invention is surprisingly ef~ective and economic for the intended pulpose In view of the dynamic nature of the water-hydroxycarboxylic acid(s)~cyclic ester system and its propensity to deteriorate in terms of cyclic ester 30 quality under cDnditions oî therrnal stress.
: : ' ;::
7 ~ ~
In general, the invention is applicable to the preparation, recovery and purification of cyclic esters having the formula R2 \ C/ \C//
~,C\ /C~ Rl 0 wherein Rl and R2 are independently hydrogen or an alkyl radical having 1 to 6 carbon atoms. Preferably Rl and R2 are H or methyl, as in glycolide (where;n Rl = R2 = H) and more preferably as in lactide (wherein Rl = H, R2 = methyl).
In general, it has been ~ound the relative order of decreasin~ volatility of the princlpal componen~s of a depolymerization vapor product stream (excluding s carrier gas when such is used to strip the depolyrnerization products from the reaction mass) is water, monomeric alpha-hydroxycarboxylic acid (lactic acid), dimeric cyclic ester (lactide~ and volatile oligomers of the alpha-hydro~ acid. For example, the boiling points of water, lactic acid (LA), lactide (LD) and lactoyllactic acid ~L2A) at atmospheric pressure at 100, 217, 259 ~estimatedl and 359C ~estimated), respectively.
20 The same relative order of volatility holds over a wide range of reduced pressures, although the ratio (or "alpha"~ of the vapor pressur~s exerted by any two components at a given temperature may change with change in pressure. The vapor pressures of each component over a range of tcmperatures are readily determined by trial and the "alphas" of the various component pairs are straight forwardly calculated. It isr ~ ~!3 ~ preferred to operate the fractional distillation process at coordinated temperatures and pressures such that the "alpha" of the alpha-hydroxyacid (lactic) vapor pressure to the c ycllc ester ~lactide) vapor pressure and the "alpha" of ~he cyclic es~er vapor pressure to the H~OCR1,R2CO)2OH (lactoyllactic acid~ vapor pressure are as high as practicable, preferably each "alpha" is at least about 5 at a particular condensation temperature and 30 pressllre.
Since the "alpha" ratio for any given pair of components tends to decrease with increasirlg temperature it is best to operate ~t low temperatures and pressures 50 as to maximize the degree of the separations desired.
In ano~her aspect of the invention, the vapor product s~ream issuing 35 ~om a depolymenzation reactor, which contains ~he major proportion of a dimeric cyclic ester as deISned (lactide~ and minor amounts of one or ~nore hydroxylic impurities including an aipha-hydroxycarboxylic acid more volatile ~han the cyclic ester and T
213~788 93/~8020 PCI/USg3/02~98 In general, the invention is applicable to the preparation, recovery and purification of cyclic esters having the formula Rl R2 ~ C
C C R
O O R~
0 wherein R~ and lR~ are independently hydrogen or an alkyl radical ha~ing 1 ~o 6 carbon atoms. Prefierably Rl and R2 are H or methyl, as in glycolide (wherein Rl = R2 = H) and rnore preferably as in lactide (wherein R1 = H, R2 = methyl).
Ill general, it has been found the relative order of decreasing volatility of the principal components of a depolymerization v~vr product s~ream (excluding 1~ calTier gas when such is used to strip the depolymerization products from the rea~ion mass) is wate~, monomeric alpha-hydroxycarbo~lic acid ~lactic acid), dimeric ~rclic ester (lactide) arld volatile oligomers of the alpha-hydroxy acid. ~or example, the laoiling points of water, lactic acid (LA), lactide (LD~ and lactoyllactic acid ~L2A) ~t atmo~pheric pressure at 100, 217, 259 (estimated) aIld 359C (estima~ed), respectively.
The sam e relative order OI volatility holds over a wide range of reduced pressures, ; alth~ugh ~he ratio (or U~pha") ofthe vapor pres~ures exe~ed by any tw o co m ponen~s at a 8~ven tem perature nnay change Ynth change in pressure. The vapor pressures of each:co m ponent over a range oftemperatures are readily detern~ned by t~al and the : "alphas" o~ the vanous co m ponent pairs are str~ght forvvardly calculated. It is 2s ~prefe~red to opera~e the f~actional distillation process at coordinated tem peratures and -: pressures such tha2the "alpha" ofthe alpha-hydroxyacid ~lactic~ vapor pressure to the cyclic ester (lactide~ vapor pressure and the "alpha" of the cyclic ester vapor pressure to the H(OCRl,R~CO)2OH (lactoyllactic acid) vapor pressure are as high as practicable, prefierably each l'alpha" is atleast about 5 at a pa¢ticular condensation lemperature and pressure.
Since the "alpha" ratio for any given pair of components tends to decrease with increasing t~mperature it is best to operate at low temperatures and pressures so as to maximize the degree of the separations desired.
In another aspect of the invention, the vapor produet stream issui~g 35 ~om a depolymeriza~ion reactor, which contains the major proportiorl of a dime~ic eyclic ester as defined (lactide) and minor amounts of one or more hydroxylic impurities including an alpha-hydroxycarbo~ylic acid more volatile th~n the cyclic ester and .~ .
established and continuously taken off as a vapor sidestream at a point which is below the overhead takeoff and below the condensate feed point to the column, and ~d) a highest boilin~ fraction consisting lar ely of oligomeric acid(s) and some cyclic ester is present at the bottom of the colurnn, which is purged as necessary to rnaintain a s balanced colurnn. The feed rate of the condensate to the column and the take-off rates of the overhead, the cyclic ester fraction and the purge (heel) from the bottom-rnost fraction are coordinated such that a substantially steady state condition can bemaintained in the column. Further, the overhead can be continuously processed toisolate a cyclic ester-rich component which can be recycled to the ~actionating colurnn 0 and the acid-lich remainder recycled to the oligomerization step. Sirnilarly, the purge ~heel) taken from the bottom of the colurnn, which is rich in oligomeric acids and contains some cyclic ester can be recycled to the depolymerization step ~or conversion to additional quantities of cyclic ester.
In the fractional distillation step, best results are ac~lieved at low temperatures and pressures. Low temperatures minimize the possible occurrence ofside reactions between water and/or acid with the cyclic ester that can lead to product loss and deterioration of product quality. For lactide recovery it is preferred the temperature be not greater than 220`C, more preferably not greater than 200`C, and most preferably not greater than 180` C.
~or example, with reference to Fig. 1, cr~de lactide condensate : containing lactic acid, optionally water and higher-boiling oligomers thereof obtained by sondensing the vapor product stream issuing from a depolymerization unit is fed through line 2 to distillation colurnn 1 maintained at a bottoms temperature not great than 180` C and a pressure of 30 rnm Hg, which conditions of temperature and pressure 2s are sufficient to vaporize the feed material substantially completely.
A w~ter and lactic acid vapor fraction containing some lactide is taken o verhead via line 3j a }actide-rich ~action, largely free of water, lactic acid and higher-boiling oligomeric lactic acids is removed firom the column as a vapor side stream through line 4 and is condensed to liquid in condenser 5 maintained at a temperature (about 100` C) just above the melting point of the lactide.
A higher boiling bottoms stream sonsisting largely of oligomers and lactide is removed via line 6. The molten lactide conde~sed in S can be fi~rther refined, if desired, to provide still lowe~asid content material by feeding the condensate ~om S
~ ~ through line 7 to a second ~actionating column 8 also maintained at a bottom 180C
:;; ~ 35 and 30 rnm Hg. The vapor overhead ~om 8 is removed throu~h ~, the refined lactide ~: vapor stream through 10 and the high-bo~lers through 11. The lactide Srapor stream passes through sondenser lZ where it is liquefied and advantageously emerges as a 21 3~78~
polymer-orade molten stream via e,~cit line 13. This stream, if desired, can be fed directly in the molten state to a polymerizer for the production of hioh molecular weight polylactic acid. Should the molten stream exiting 13 perchance have a higher acid content than desired, it can be fed to a third fractionating column and thedistillative refining process repeated.
The overhead stream exiting line 3, which is rich in water and lactic acid and may contain lactide can be dehydrated if necessary and fed to an oligomerization reactor (not shown) for conversion to a depolymerizable lactic acid oligomer as is known in the art.
o Referring to Fig. 2, overhead lactide stream 9 containing lactic acid is combined with bottoms streams 6, both containing lactide and higher-boiling oligomers.
: ~ The combined 6-9 strearn is passed via line 15 to flash still 16, maintained at 125'C and 10 mm Hg, from which is flashed residual lactic acid and the bulk of the lactide content -o~ the combined stream as a vapor stream. The vapor stream exits 16 via line 17, 3 passes through condenser 18, emerges as crude liquid composition lactide composition and joins incoming crude lactide condensate ~om a depolymerization reactor ~not shown) at line 2.
High-boiling oligomeric residue is removed from 16 through line ~0. Its :
lactic acid values can be recovered, if desired, by hydrolysis; the hydrolysate can be concentra~ed and the concentrate fed to an oligomerization reactor (not shown) for co~lversion to a depolymerizable lactic acid oligomer as described above for theaqueous lactide stream exiting line 3.
~` ~ The following examples are presented to fi~rther illustrate specific embodiments of the present invention and as such are not to be interpreted as being 2~ unduly lirniting ~ Temperatures are in degrees Celsius and percenta ,es in percent by weight unless otherwise.stated.
E~ IPLE 1 This Example illustrates the crackingldepolymerization of an oligomer of L-lact,lc acid to form an impure L-lactide vapor stream and partial condensation of the ~' ~ vapor stream to obtain a high lactide content condensate, followed by fractional distillation of the condensate to recover low acid content L-lactide.
: ~ An oligomer of L-lactic acid was prepared by heating 88% L-lactic acid eontair~ing 0.3 percent stannous octoate at temperatures up to 180` wîth removal of water until the product had a degree of polymerization of about 10. The still molten (150`) oligomer was continuously craclced by feeding it ~o the top of a 7.62 cm ~' WO 93/18020 P~JUS93/02298 polymer-grade molten s~ream via exit line 14. This stream, if desired, can be ~ed directly in the molten state to a polymerizer for the production of high molecular weight polylactic acid. Should the molten stream exiting 14 perchance have a higher acid content than desired, it can be fed to a third fractionating column and thedistillative refining process repeated.
The overhead stream ~xiting line 3, which is rich in water and lactic acid and may contain lactide can be dehydrated if necessaly and fed to an oligomerization reactor (not shown) ~or conversion to a depolymerizable lactic acid oligomer as is known in the art.
0 Referring to Fig. 2, overhead lactide stream 2 containing lactic acid is combined with bvttoms streams 6, both containing lactide and higher-boiling oligomers.
The combined 6-9 stream is passed via line 15 to flash still 16, maintained at 125`C and 10 mm Hg, from which is flashed residual lactic acid and the buik of the lactide content of` the combined stream as a vapor stream. The vapor stream exits 16 vla line 17, passes through condenser 18, emerges as crude liquid composition lactide composition and joins incoming cmde lactide condensate ~om a depolymerLzation reactor (not shown) at line 2.
High-boilirlg o}igomeric residue is removed from 16 through line 20. Its lactic acid values can be ~recovered, if desired, by hydrolysis; the hydrolysate call be 2û concentrated and the conce~rate fed to an oligomerization reactor (not shown) fior cQnversion to a~depolymerizable lactic acid oligc,mer as described above for thea~ueous lactide stream exi~ing line 3.
The following examples are presented to fi~rther illustr~te specific embodiments of the present invention and as such are not to be interpreted as being unduly limiting. Temperatures are in degrees Celsius and percentages in percent by weight unless ot}lerwise stated.
:
EXAMPLE I
T~is Example illustrates the crackin~/depolymerization of an oligomer of L-lactic acid to form an impure L-lactide vapor stream and partial condensation of the vapor stream to obtain a high lactide content condensate, followed by ~ctional distillation of the con~ensate to recover low acid content L~lactide.
An oligomer of L-lactic acid was prepared by he~ting 88% L-}actic acid containing 0.3 percent stannous oc~oate at temperatures up to 180` with removal o~
3S water Imtil the product had a degree o~polyJTIe~ization of about 10. The still molteq~
(150`) oligomer was continuously cracked by fieeding it to the top of a 7.62 em ~O 93/18û20 21317 8 ~ PCr/VS93J02298 diameter 5-sieve tray glass Oldershaw column heated to 210` and maintained at a reduced pressure of 10 mm Hg.
About 1,437 gms of the oligomer was fed to the cracking column over a 2.5 hour period, during which time about 71% of the oligomer was cracked to 5 vaporized products. Partial condensation of the vapor product s~ream at 132` and 11 mm Hg pressure gave an acid-rich vapor (about 172 gms) and 843 grams of lactide-rich condensate containing 300 meg/kg of acidity corresponding to 253 meg of acidity. The condensate was immediately solidified by cooling at -10` for oven~ight storage.
The 843 gms of frozen condensate was liquefied by microwave he~ting 0 and then batch-distilled in a 5.1 cm diameter 20 plate Oldershaw column at 5 mm Hg~ a 4:1 to 6:1 reflux ratio, a bottoms temperature of 155-1~7`, and a head temperature of 119-124` over a 2.5 hour period. FiYe overhead cuts were taken as follows:
~_ ~
I C~UT: WEIG~IT ACll)lTY
~ e, ... ......... ,.. . ~
I 1 661 gms 674.8 meg/kg .. ... . .,, _ l 2 60.1 240 ::
l 3 8S. 1 69 I 4 746 27.4 _ .. ....... ~... .
~: l ~ 174.7 7.4 _ ~
Elel 21114 5'~9 The procedure of Example 1 was repeated with a lactic acid oligomer containing 16 lactyl i.e. -OCH(CH33CO- units. Approximately 1,437 gms of the oligomer at a temperature of 170` was fed over a 3 hour penod at a rate of about 8 fmin to the depolymerizer maintained at 210`. The vapor product strearn from the2o ~depolymerizer~was partially condensed as before a~ 132` and 10 rnm Hg to ~rield ~
water-acid ~action ~208 gms~ and a crude liquid lactide condensate ~733 gms) ha~ng an acidity content of 324 meq/kg. The residue in the depolymserizer arnounted to 484 gms.
The crude lactide condensate was stored for 14 days at 0` and r~melted 2S by microwave heatillg. Its acidity was redetermined and ~ound to have increased to 544 meq/kg 721 gms of the crude lactide was then ~actionally distilled ~ 30 mm Hg, a head temperature o~l50-155` and a reflux of 4:1 to 6:1. Five cuts were taken:
WO 93/18020 ~ 1 ~17 g ~ PCr/US93/02' ~ O
, CUT WEIG~IT ACIDITY
, 1 _ 41.8 _ 2940 2__ _ 79.3 96 _ _ 3_ _ 163.7 _ 54_ _ ~ 143.3 37 99.4 133 I ~_ , _ _ ... .
il= I _ 101.4 9~0 Practions of previously r~fined (distilled) lactide having acidities of less than about 100 meq~cg were combined and melted to provide 1,017 gms havin~ an s initial acidity of 59 meq/kg, which increased to 7~ me~/kg a~er storage overnight at 2~` and then remelted at 100`.
1,013 ~pns of the lactide composition was ~actionally distilled as described in Examples 4 and 5. the pressure was 30 mm Hg, the head temperature 134 to 156`, and the opçrating reflux ratio was about 4:1.
10 Acidity, meql~g ~ . . ___ CIJT WT. gmsINITIAL After 20 hrs at 25 ~ 1 ;79.~ 484 513 : ~ 2 _ ~ _ 90.6 ~.~ 21 3 ~ 104.6 1 g : ~ : ~ . _ . .. . .
`~:: : ~ 4 ~ : 95.6 2 10 _ . _ _ ~
; 1iO.2 _ 3 8 ~ ~ 6 ~ __108.4 _ _ __3 : ~ 7 ~110.3 5 8 . . . . .. - .... __ _ ~ : 8 : ~ 107.9 not. det. 22 , ._ . . .. ~ __ ~ _ : 9 _ ~ 53.2 not. det. _ 22 _ Heel 11_8 not. det _ l;l __ , : ~ These results show that the invention process is capaUe OI produci~
low acid content lactide even under batch distillation conditions. They also show that 1S the acid-lactide~ s3rstem is: a dynamic one with the: acid content tending to increase an s$anding, even at annbient tem peratures unless precautions are t ~ en to exclude m oisture.
wo 93~8020 2 1 ~ 1 7 ~ 8 Pcr/US93/02298 The distillation results also suggest that low, substantially nil, acid conterlt lactide and other dimeric cyclic esters at alpha-hydroxycarboxylic acids could be obtained in high yields under continuous distil~ation conditions, thereby completely obviating the need for solvent treatments to obtain such high qualitys pol~ner-grade m~tenal.
The procedure of Example 1 was carried out with 2 kg of 88% lactic acid con~aining 6 gms of stannous octoate, which was dehydrated and oligomenzed by 0 heating a$ 120 to 180` with removal of 407 gms of water. The resulting oligomer con~ained on the average 10 lactyl units. Approximately 1,437 gms ofthe molten (150 - ~6û`) oligomer was fed at a rate of about 9.6 gms/min to the depolymerizer maintained at 220`C and 10 mm Hg pressure. The vapor product stream issuing firom the depolymerizer was partially condensed in the flash chamber at 100-103` and 2 mm 15 Hg pressure. The condensate, about 890 gms, contained 755 meq/lcg of acidity.The above condensate was batch distilled as described in Example 5.
The pres~e was 30 mm Hg, the head temperature ranged ~rom an initial 117` to 135`
and finally ~t 155` for a first cut and at 155` for 5 additional cuts, and the reflux ratio ranged f~om 12:1 to 1:1 fior cuts 3-6. The 6 cuts were as follows:
~ut _ _Wt. gms Acidity? ~eq/kg 104.4 ~825 2 123. 1 41 - .. .. .... ~ . . ...... . . . I
--- _3 ~ 114.5 : 24_ __ 4 ~ 10~.7 26 ~. ~ ~ . . ~ l _ 5 ~ _ 130.9 !90.
~; ~ 6 2~Z.9 343 :
:
1 :XAMPLE 5 The procedure of Example 1 was repeated. The lactic acid oligomer contained 11.3 la~tyl units. AQproximately 1,437 gms of the molten (150`) oligomer was fed ~o the depolymerizer over a 165 minute penod, and the vapor product streZ~n om the depolyme~izer was ~ed to the pa~tiZal condensation chamber rnailltained at 100`
~; and 2 mm Hg.
The overhead ~om the partial condenser, collected in two cold traps, weighed 69.7 gms, the crude lac~ide remZaininglJ in the condensing cha;nber weighed 1,351 gms and had ~1 } meq/kg of acidity.
WO 93/18020 2 1 3 17 8 8 P~/US93/02.
~ 2 The crude lactide was fractionally distilled batchwise as before, and 7 cuts were taken:
Cut Wt. gms Acidity, meq/kg 1 129.4 2529 _ 3 161 5 36 4 145.8 24 L~ ~ ~
Comparison of the batch distillation results of Examples 2, 4 and 5 o~ained at 30 mm Hg with those of Example 1 obtained at ~ mm Hg shows that better results are obtained at the lower pressure. This can be attributed to a lesser tendency for the distillation m~ss to produce acidic species at the lower temperatures pertaining at the lower pressure.:
` ~ :
Distillation ClltS 2, 3, 4 and 5 from Example 4 were combined with distillation cuts 3, 4, 5, 6 and 7 ~om Example S. 1167 gms of the composite having 59 meq/kg of acidity was batcbwise ~actionally distilled as in Example 1 except that the dis~illation pressure was 30 rnm Hg, and the temperature was l55` at the head and 160-163` at the ~ase of the column. The reflux ratio was 4:1 throughout. Seven distlllation cuts were talcen:
:;: :
WO93/180~0 21~1788 Pcr/uss3/02298 Cut Wt. gms. Acidity, meq/kg --~ 3 - 130.3 17 _ 165.7 14 152.2 9 ~ L ~
:
Having thus described and exemplified the invention with a cert~in degree of particulality, it should be appreciated that the following claims are not to be so lin~ited 5 but are to be affor~ed a scope commensurate u~th the wording of each element of the claim and equivalents thereo ,~
:: :: :
. : :
Claims (7)
1. A solventless process for the separation and recovery of a dimeric cyclic ester under reduced pressure from a vapor product stream containing said ester and minor amounts of one or more hydroxylic impurities including an alpha-hydroxycarboxylic acid more volatile than the cyclic ester, water and oligomerichydroxycarboxylic acid higher-boiling than the cyclic ester, which process comprises condensing the vapor stream to form a dimeric cyclic ester condensate, fractionally distilling the resulting condensate and recovering a dimeric cyclic ester fraction having a substantially lowered content of water alpha-hydroxy acid, and oligomeric acid wherein the fractional distillation is conducted continuously and comprises the steps of:
(a) providing a multi-stage distillation column having a feed inlet at a midpoint of the column, an overhead vapor takeoff at the upper end of the column, a vapor sidestream takeoff at a point below the midpoint feed inlet and a high-boiler take off at the lower end of the column.
(b) feeding the cyclic ester condensate to the midpoint of the column (c) establishing in the column (i) an overhead vapor fraction consisting essentially of water, when present, alpha-hydoxycarboxylic acid more volitile than the cyclic ester and litte or no cyclic ester, (ii) a cyclic esterfraction takeoff below the midpoint feed inlet that is substantially free of water, lower-boiling acid and higher-boiling acid and (iii) a high-boiling fraction consisting largely of cyclic ester and higher-boiling oligomeric acids at the lower end of the column, (d) removing the overhead fraction from the upper end of the column, (e) removing the cyclic ester vapor fraction through the vapor sidestream takeoff and (f) removing the higher-boiling fraction at the lower end of the column.
(a) providing a multi-stage distillation column having a feed inlet at a midpoint of the column, an overhead vapor takeoff at the upper end of the column, a vapor sidestream takeoff at a point below the midpoint feed inlet and a high-boiler take off at the lower end of the column.
(b) feeding the cyclic ester condensate to the midpoint of the column (c) establishing in the column (i) an overhead vapor fraction consisting essentially of water, when present, alpha-hydoxycarboxylic acid more volitile than the cyclic ester and litte or no cyclic ester, (ii) a cyclic esterfraction takeoff below the midpoint feed inlet that is substantially free of water, lower-boiling acid and higher-boiling acid and (iii) a high-boiling fraction consisting largely of cyclic ester and higher-boiling oligomeric acids at the lower end of the column, (d) removing the overhead fraction from the upper end of the column, (e) removing the cyclic ester vapor fraction through the vapor sidestream takeoff and (f) removing the higher-boiling fraction at the lower end of the column.
2. The process of Claim 1 wherein the feed rate of the condensate to the column, the removal rate of the vapor overhead from the column, the removal rate of the cyclic ester fraction from the column and the removal rate of the high boiling fraction from the column are coordinated so as to establish a substantially steady state in the column.
3. The process of Claim 1 wherein the cyclic ester is a lactide, the hydroxycarboxylic acid is lactic acid and the oligomeric hydroxy acid is an oligomer of lactic acid.
4. A method for the solventless separation of alpha hydroxyl dimeric cyclic ester under reduced pressure from a vaporous effluent from the depolymerization of alpha hydroxylic oligomer containing water, minor amounts ofhydroxycarboxylic acid alpha hydroxyl dimeric cyclic ester and alpha hydroxylic oligomer without the addition of solvent by (1) partially condensing the vaporous effluent stream to remove water therefrom;
(2) feeding the condensate through a feed inlet to an intermediate point within a continuous fractionation column operating at a temperature no higher than 220°C to effect vaporization of the hydroxycarboxylic acid and the dimeric cyclic ester;
(3) removing from the top of the column a first vapor stream containing a major amount of alpha hydroxylic carboxylic acid and condensing the first stream;
(4) from a point below the condensate feed inlet removing a second vapor stream containing a major amount of dimeric cyclic ester and condensing the second stream; and (5) removing a liquid fraction from the lower end of the column containing a major amount of alpha hydroxylic oligomer
(2) feeding the condensate through a feed inlet to an intermediate point within a continuous fractionation column operating at a temperature no higher than 220°C to effect vaporization of the hydroxycarboxylic acid and the dimeric cyclic ester;
(3) removing from the top of the column a first vapor stream containing a major amount of alpha hydroxylic carboxylic acid and condensing the first stream;
(4) from a point below the condensate feed inlet removing a second vapor stream containing a major amount of dimeric cyclic ester and condensing the second stream; and (5) removing a liquid fraction from the lower end of the column containing a major amount of alpha hydroxylic oligomer
5. The process of Claim 7 wherein the depolymerizable oligomer is an oligomer of L-lactic acid and the lactide product is L-lactide.
6. The process of Claim 7 wherein the distillation temperature is below about 200°C.
7. The process of Claim 7 wherein the distillation is conducted below about 180°C.