CA1153502A - Flexible absorbent boards - Google Patents
Flexible absorbent boardsInfo
- Publication number
- CA1153502A CA1153502A CA000361534A CA361534A CA1153502A CA 1153502 A CA1153502 A CA 1153502A CA 000361534 A CA000361534 A CA 000361534A CA 361534 A CA361534 A CA 361534A CA 1153502 A CA1153502 A CA 1153502A
- Authority
- CA
- Canada
- Prior art keywords
- board
- dry
- density
- web
- hydrocolloidal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
°
Abstract An absorbent material is provided for body fluid absorbent products which material has relatively high tensile strength, and is extremely flexible and may be incorporated into absorbent products without substantial loss in user's comfort. The material is made by forming a slurry of water wherein the solids comprise celluloslic fibers and hydrocolloidal material. The wet web is formed from the slurry and the web is then dried. The dry web is then compacted to a density of at least 110% and preferably at least 150% based on the density of the dry web. The resulting product has a tensile strength of at least 10 Kg/cm2 and the Gurley Stiffness of less than about 40 gm.
Abstract An absorbent material is provided for body fluid absorbent products which material has relatively high tensile strength, and is extremely flexible and may be incorporated into absorbent products without substantial loss in user's comfort. The material is made by forming a slurry of water wherein the solids comprise celluloslic fibers and hydrocolloidal material. The wet web is formed from the slurry and the web is then dried. The dry web is then compacted to a density of at least 110% and preferably at least 150% based on the density of the dry web. The resulting product has a tensile strength of at least 10 Kg/cm2 and the Gurley Stiffness of less than about 40 gm.
Description
1~535~2 ~LEXIBLE ABSO~B~NT 30ARDS
~AC~G~CUND OF THE INVENTION
This invention concerns methods and products utilizing fiberous absorbent bodies for absorbing fluids.
In particular, the invention concerns products for absorbiny body fluids such as catamenial tampons, dlapers, sanitary napkins and the like, and is specifical!y directed toward fiberous absorbent bodies which are easily handled in processes for manufacturing such products, which bodies exhibit increased absorbency as contrasted with commonly used fiberous bodies.
The vast majority of body fluid absorbent products now in use comprise, at least in their formative stages, pads of loosely associated fiberous and generally cellulosic absorbent materials such as comminuted ~ood pulp fluff, rayon staple, cotton, cotton linter~ and the like. For generations, these mater.als have ?roven ~o be useful and effective in dressings, diapers and sanitary protection devices in that these materials are absorben~, inexpensive and, in the case of absorbent products whlch must be worn by the user for a substantial period of time, these materials are fle.Yible and hence comfortable.
Unfortunately, balanced against such highly desirable properties, is the fact that pads manufactured from the loosely assoclated fiberous materials are relativelv ~eak, have little tensile s'rength and must be handled gingerly throughout any product manufacturing process. Several attempts have been made to increase the structural integrity of these pads ~ut in the main, such attempts have resulted in products which are either less absorbent or less flexible and hence represent only a compromise bet~een the exigencies of manufacturing and the functional l~S353Z
properties of the final product. For example, in U.S.
Patent 4,057,061 issued on November 8, 1977 to Shigemitsu Ishikawa, a thin pad is described which comprises compressed cot~ony pulp fiDers, the compression being 5 ~aught to add to the structural integrity of the pad.
This advantage notwithstanding, the thin pad, by virtue of the compression, is substantially less flexible and hence less comfortable than prior products. A similar approach has been taken in ~.S. Patents 3,065,751 issued to Gunner Gravdahl on December 8, 1970; and 3,017,304 issued to A.
A. Burgeni on January 16, 1962 with similar results.
The manufacturing problems related to absorbent pads have increased to an extent with the development of a series of cellulosic materials which exhibit substantially increased absorptive proper.ies by virtue of chemical modification. Examples of such materials aze the grafted cellulose copolymers described in U.S. Patent 3,!389,678 issued to Pronoy Chatterjee et al. on June 17, 1975; and the crosslinked carboxyalkyl cellulosic materials described in U.S. Patents 3,731,686 and 3,858,585 issued to Pronoy Chatterjee on May 8, 1973 and ~une 7, 1975, and in U.S. Patent 3,589,364 issued to W. L. Dean et al. on June, 1971. These materials are in the for~ of highly swellable, and highly fluid-retentive f.bers. It is desirable to combine these fibers with the more conventional absorbent materials such as rayon, wood pulp, cotton or the like to produce an absor~ent body having increased ~luid retentive properties. Unfortunate~y, when mixing such fiberous materials it is not an easy processins task to get an even distribution and this has added to the burden of producing an absorbent bodv 'or the products of interest herein.
Accordingly, there is need for improvement in the manufacture of absorbent bodies specifically directed toward increasing the integrity o~ the ~odies wi'hout sacrificing flexibility and, particularly ~hen ntroducing 11535~Z.
chemically modified absorbent materials into the absorbent body, S~MMARY OF THE INVENTION
In accordance with this invention, absorbent material is now ~rovided for body fluid absorbent products which material has relatively high tensile strength so that it may be handled during processing far less singerly than prior absorbent materials. This high tensile strength notwithstanding, the material is extremely flexible and may be incorporated into absorbent products without any substantial loss in user's comfort. Further, the material of this invention is substantially ~ore absorbent, i.e., can absorb and retain greater volumes of body 'iu-~, then conventional absorbents.
Specifically, in accordance with the method of this invention, a slurry of water with no more than about 0.1 and preferably no more than about 0.05~ solids ia for~ed wherein the solids comprise cellulosic fibers and particulate hydrocolloidal material. The ratio of ,uch hydrocolloidal material to the cellulosic fibers is at least 0.01 grams per gram and ~referably at leas~
0.1 grams per gram. A wet web is formed from the slurry by such means as by depositing the same onto a screen and drawing the water away with the aid of vacuum. The wet web is then dried, preferably to a water content of less than about 10.0 percent by weight to form a dry, relatively bul`.~y web. In accordance with the teaching of this invention, the dry web is now increased in density bv at least about 10.0~ and preferably at leas~ about 50.0 to form the board like web of this invention. Said in other words, the resulting board has a density of at least 110% and preferably at least 150~ based on the density of the dried bulky web. The increase in densi_y increases the tensile strength of the dried web. Sur~risingly, tnis increase in tensile strength and increase in density is ~535~2 accompanied by a marked and substantial decrease in stiffness. The decrease in stiffness is so great, in fact, that the resulting densified web may be used directly in absorbent products and will not signi~icantly effect the user~s comfort.
Preferably, the densified web will have a tensile strength of at least 10 Kg/cm2. Concomitantly, the Gurley Stiffness will be less than about ~0 gm and preferably less than 12 gm, these latter parameters being more specifically defined herein. Further, a product having the above set out parameters can be pro-duced by forming and densifying webs which, in their densified state, are more than 0.3 millimeters thick and preferably more than O . 6 millimeters thick. The importance of such thickness is that the densified web can be em-ployed as a major, or even as the sole, absorbent element in a body fluid absorbent product and will, by virtue of its thickness, provide substantial absorbent capacity.
At the same time, handling of the web is greatly facili-tated because of its hi~h tensile strength and this is accomplished without sacrificing user comfort.
According to a further broad aspect of the pre-sent invention, there is provided a method for producing an absorbent, relatively thick flexible absorbent board of fibrous material. The method comprises forming a slurry of water with no more than about 0.1% by weight solids. The solids comprise cellulosic fibers and parti-culate hydrocolloidal material in a ratio of at least 0.01 grams of hydrocolloidal material per gram of cellulosic fibers. A wet web is then formed from the slurry The web is dried to a water content of less than 10~/o by weight to form a undensified dry web. The density of the dry web is increased by at least 10%. The densified, dry web has a high tensile strength, and low stiffness relative to the undensified dry web, - 4a ~5356)~
According to a further broad aspect of the present invention, there is provided a flexible, absorbent board having a high tensile strength, The board comprises cellulosic fibers and particulate hydrocolloidal material in a ratio of at least 0,01 gm, of hydrocolloidal material per gram of cellulosic fibers, The board has a tensile strength of at least 10 Kg/cm2, a thickness of at least 0.3 mm, and a Gurley Stiffness of less than 40 gms. The board has been compacted in a dry state to a density of at least ll~/o of the density of the uncompacted dry board.
According to a other broad aspects of the pre-sent invention, there is provided a sanitary napkin and a catamenial tampon comprising the above-described absor-bent element, BRIEF DESCRIPTION OF TH:E D~AWINGS
The invention will be more clearly understood by reference to the description which follows when taken together with the attached drawings in which:
Fig, 1 is a schematic flow diagram of the pro-cess for making the strong, flexible, highly absorbent material of this invention; (this figure appears on the same sheet with figures 4-7) Fig, 2 is a graphical representation of the relationship between Gurley Stiffness, density and hydrocolloidal content for the first embodiment of the material of this invention, 11535~z.
Fig. 3 is a graphical representation of the same parameters as Fig. 3 for the second embodiment of the material of this invention;
Fig. 4 is a prospective view of a first sanitary napkin incorporating material of this invention with parts removed to illustrate the structure thereof;
F ig . S is a transve-se, cross sectional view of the sanitary napkin of Fig. 4; taken along line 5-5;
Fig. 6 is a prospective view of a second sanitary napkin incorporating a material of this invention with parts removed to illustrate the structure thereof;
~ ig. 7 is a transverse, cross-sectional ~liew of the napkin of Fig. 6, taken along line 7-7;
Fig. 8 is a prospective view of a third sanitary napkin incorporating a material of this invention wi~h parts removed to illustrate the structure thereof;
Fig. 9 is a transverse, cross-sectional view of the of Fig. 8, taken along line 10-10;
Fig. 10 is a planar view of a diaper _ncor~oratins the material of this invention;
Fig. ll is a transverse, cross-sectional view of the diaper of Fig. 10 taken along line 13-13;
Fig. 12 is a perspective view of a partially rolled tampon blank incorporating the material of this invention;
and Fig. 13 is a cross-sectional view of the finished tampon made from the blank of Fig. 12.
DETAILED DESCRIPTION OF THE INVENTION
Referring now to Fig. l, shown there is a schematic flow diagram of the process for providing an absorbent material in accordance with the teachings of this invention. A slurry is formed in a slurry forming station 10 from a water supply 12, a cellulosic fiber supply 11 and a hydrocolloidal particle supply 16. ~he cellulos~c ~535¢)~
fiber may be any of the commonly used cellulosic materials available for absorbent products and may include, for example, wood pulp, cotton, grasses, or regenerated cellulose ~ibers and the like. It is generally pre~erred that these fibers lie within the range of about lO0 to about 3000 microns in length. Currently because cf both cost and availability considerations, wood pulp is the cellulosic fiber of choice.
The hydrocolloidal particles from supply 16 may take various physical and chemical forms. With regard to physical form, as used herein, the terms "particles" and "particulate" are meant to refer to material which is made up of discrete units of various shapes such as powders, fibers, or flakes. Generally, these particles consist o~
water insoluble, but water swellable, polymeric substances capable of absorbing water in an amount which is at least ten times the weight of the hydrocolloid particles in the dry form and is preferably about l; to about 30 times the dry weight. Preferably, the hydrocolloid particles are i~
the shape of fibers and may be conveniently obtained by chemically modifying cellulosic fibers.
Such material may be described che.mically as having a backbone of natural or synthetic polymers wi.h hydrophilic groups or polymers containing hydrophilic groups being chemically bonded to the backbone or in intimate admixture therewith. Included in this class of materials are such modified natural and regenerated poly~ers as polysaccharides including, for example, cellulose and starch and regenerated cellulose, which are modi-ied by being carboxyalkylated, phosphonoalkylated, sulphoalkylated, or phosphorylated to render them highly hydrophilic. Such modified polymers may also be crosslinked to enhance their hydrophilicity and render them water insoluble.
~i53502 , These same polysaccharides may also serve, for example, as the backbone onto which other ?olymer moieties may be bonded by gra~t copolymerization techniques. Such grafted polysaccharides and their method of manufac~ure are described in ~.S. Patent No. 4,105,033 iss~ed on August 8, 1978 to P. ~. Chatteree et al. and may be described as oolysaccharide chains having grafted thereon a hydrophilic chain of the general formula 1 (C~2)q - IRl j 1- (C~2)p - IR2 _ l A J L I = ~
wherein A and B are selected from the group consis_ing of -CR3, -C(alkali metal), -OHNH3, -NH2, wherein Rl, R2 and R3 are selected from the group consisting of hydrogen and alkyl having 1 to 4 car~on atoms, wherein r is an integer having a value of 0 to about 5000, s is an integer having a value of 0 to about 20 5000, r plus s is at least 500, p is an integer having a value of zero or 1 and q is an integer having a value of !
to 4. The preferred hydroohilic chains are hydrolyzed polyacrylonitrile chains and copolymers of polyacr-ylamide and sodium polyacrylate.
ln addition to modified natural and regenerated polymers, the hydrocolloid particle component of the densified layer of this invention may comprise whollv synthetic hydrophilic particles. cxamples of those now known in the art are polyacrylonitrile fibers which may be modified by grafting such moieties thereon such as polyvinyl alcohol chains, polyvinyl alcohol itself, hydrophilic polyurethane, poly(alkyl phosphonates) partially hydrolyzed polyacrylamides (e.g., poly(N-N-Dimethyl acrylamide), sulfonated polystyrene, or poly(alkylene oxide). These highly hydrophilic synthetic 1~535~)~
polymers may be modified by other chemical treatments such as crosslinking or hydrolysis.
The cellulosic fibers, the hydrocolloidal particles ~nd the water from supplies 14, 16, and 12, respectively are all combined in the slurry forming station 10 to form a slurry which is then conveyed by means 18 to a web forming station 20. The proportions of the components in the slurry are controlled so that the slurry comprises no more than about 0.1 and preferably no more than about 0.05% solids, e.gO, fibers and particles. 2rererably the slurry comprises about 0.05 to 0.01~ solids with about 0.01~ being the esn~n~rat- of choice. The solids are controlled to be in the ratio of at least 0.01 grams of hydrocolloidal material per gram of cellulosic fibers and 1; preferably at least about 0.1 srams per gram.
The slurry may be formed in several ways known in the art and associated with the wet laying of fibrous webs.
In some instances it may be prudent to form the slurry at a high solids concentration, e.g., about 1.5~ by weight solids and then dilute the slurry wi~h the addition of further water to the desired concentration. It may also be convenient to premix any of the ~i ~ ccS in any other combination prior to forming the final slurry.
Irrespective of how the slurry is formed, it is next passed to the web forming station 20 where a wet ~eb is formed, for example, by depositing the slurry onto a continuous belt and maintaining a pressure differential across the faces of the belt to draw away a oreponcerance of the water and leave a loosely compacted wet web of cellulosic fibers and hydrocolloid particles in intimate mixture. At this point in the process of this invention, it is desirable that the web have a solids content of not more than about 50~ by weight of wet web and not less than about 2~. The wet web is passed by means 24 to a drying station 26 wherein the web is next dried to a water content of less than about 10~ by weight and prererably ~S35i~)2 less than about 5~. Such drying may be accomplished using equipment well ~nown in the art such as by applying heat through means 30 in the form of hot air, electrical resistance coils, steam cans or the like.
S The product leaving drying station 26 is a relatively lofty, thick board-like material which has only moderate tensile strength and is only moderately capable of maintaining its integrity during handling. The dried board-like web is very stiff and, while highly absorbent, cannot be used directly in a sanitary napkin or similar body fluid absorbent product which is to be worn by tne user in that the high degree of stiffness will cause great user discomfort and prevent the product from conrorming to the body, this latter feature causing the resulting product to fail prematurely. Typically, the dry web has a density which ranges from about O.li to 0.3 gm/cc, is about 1.0 to 2.0 mm. thick, has a t_nsile strensth of .rom about 10 to 100 Kg/cm2 and has a Gurley stiffness value of about 25 to 40 gm.
In accordance with this invention, the dry web is now passed via conveyor 32 to a compacting station 3~ wherein the density of the web is increased to a densi_y of at least about 110~ and preferably to at least about 1;0~ of the density prior to compacting. In order to accomplish this high level of compaction and have the increased density be permanent, i.e., have the compacted board ta~e a permanent set, a very high pressure must be ap?lied to the dry web. Generally, a pressure of at leas~ about 30 psi should be applied and more preferably the ?ressure should be at least lS0 psi. While the compacting pressure could be applied by several means such as by passing the dry web through the nips of two or more pressure rollers, it is usually preferred to obta,n the compaction by use or a hydraulic press which is designed to deliver such high 3; pressures.
1~53S~Z
The resulting compacted web has a substantially higher tensile strength as compared to that of the uncompacted dry web and so can be easily handled while still maintaining its structural integrity. For reason not yet understood, the compacting process, in addition to greatly increasing the tensile strength of the board, dramatically reduces the stiffness. When made in accordance with the teachings herein, the compacted board of this invention is so flexible that it may be used directly, without any grinding or commi.nution step, in absorbent products which are to be worn without any substantial user discomfort.
Example 1 A series of samples are prepared having various ratios of hydrocolloidal particles in admixture with wood pulp. ~he hydrocolloidal particles employed are those described in the aforementioned U.S. 2atent 3,889,678 and, specifically, sample number 4, in Table II, of that patent. This material is a cellulose graft copolymer consisting of a cellulose backbone having grafted thereto polymer moieties consisting of co-polymers of sodium acrylate and ethylacrylate in a weight ratio of 19.8 parts by weight cellulose to 33.9 parts by weight of poly(ethylacrylate) to 46.3 parts by weight of poly(sodium acrylate). This hydrocolloid is in fibrous ~orm with the fibers having an arithmetic average fiber length of approximately 0.8 mm. In the case of each of the sample blends, the following procedure is employed:
The hydrocolloid and the wood pulp are dispersed in water to yield a slurry having a consistency of 1.173 by weight solids. One liter of the slurry is placed in a handsheet mold measuring 7 3/4 inches by 7 3/4 inches and manufactured by the Williams Apparatus Company of Watertown, New York. The slurry is than diluted to a ~1535~2 .
consistency of 0.01% by weight solids in accordance with the procedure set out in TAPPI Standard Method T-2050S71.
After mixing thoroughly, the water is allowed to gravity drain, leaving a wet hydrocolloid/wood pul? web having a solids content of about 5%, based on the wet web.
The wet web is blotted with blotter boards and sq~eezed to remove excess water and then dried in an air circulated oven to a water content of abou~ 2.0% water, by weight of the dry material. The resulting stiff, lofty product is compacted to varying densities in a hydraulic press.
Table I below records values of the tensile strength as a function of the hydrocolloid particle content for boards made in accordance with the aDove procedure. The tensile strength to break is determined with an Instron ~niversal Testing ~"achine by setting the jaw distance at 10.2 c~. and pulling at a cross-head s?eed of 5.1 cm/min.
The value~ for tensile strength in Table I are normalized by dividing the tensile strength to break by the cross sectional area of the board (i.e., the section perpendicular to the force applied).
11535~)2 Table I
TENSILE SrRENGr~ VS. ~NSITY
( GRAÇTED OEI~JLOSE ) SNormalized ~Kg/cm2) Jaw Distance 10.2 cm Cross~ead Speed 5.1 cm/min 10Unpressed Sheet ressed Sheet Hydrocolloid Concentration Tensile ~ensity Tensile Density % ~ensity t~ by ~ieight) (Kg/Cm )(g/cm ) ~Kg/cm )(g/cm ) Increased 0 109 0.45 112 0.51 13.3
~AC~G~CUND OF THE INVENTION
This invention concerns methods and products utilizing fiberous absorbent bodies for absorbing fluids.
In particular, the invention concerns products for absorbiny body fluids such as catamenial tampons, dlapers, sanitary napkins and the like, and is specifical!y directed toward fiberous absorbent bodies which are easily handled in processes for manufacturing such products, which bodies exhibit increased absorbency as contrasted with commonly used fiberous bodies.
The vast majority of body fluid absorbent products now in use comprise, at least in their formative stages, pads of loosely associated fiberous and generally cellulosic absorbent materials such as comminuted ~ood pulp fluff, rayon staple, cotton, cotton linter~ and the like. For generations, these mater.als have ?roven ~o be useful and effective in dressings, diapers and sanitary protection devices in that these materials are absorben~, inexpensive and, in the case of absorbent products whlch must be worn by the user for a substantial period of time, these materials are fle.Yible and hence comfortable.
Unfortunately, balanced against such highly desirable properties, is the fact that pads manufactured from the loosely assoclated fiberous materials are relativelv ~eak, have little tensile s'rength and must be handled gingerly throughout any product manufacturing process. Several attempts have been made to increase the structural integrity of these pads ~ut in the main, such attempts have resulted in products which are either less absorbent or less flexible and hence represent only a compromise bet~een the exigencies of manufacturing and the functional l~S353Z
properties of the final product. For example, in U.S.
Patent 4,057,061 issued on November 8, 1977 to Shigemitsu Ishikawa, a thin pad is described which comprises compressed cot~ony pulp fiDers, the compression being 5 ~aught to add to the structural integrity of the pad.
This advantage notwithstanding, the thin pad, by virtue of the compression, is substantially less flexible and hence less comfortable than prior products. A similar approach has been taken in ~.S. Patents 3,065,751 issued to Gunner Gravdahl on December 8, 1970; and 3,017,304 issued to A.
A. Burgeni on January 16, 1962 with similar results.
The manufacturing problems related to absorbent pads have increased to an extent with the development of a series of cellulosic materials which exhibit substantially increased absorptive proper.ies by virtue of chemical modification. Examples of such materials aze the grafted cellulose copolymers described in U.S. Patent 3,!389,678 issued to Pronoy Chatterjee et al. on June 17, 1975; and the crosslinked carboxyalkyl cellulosic materials described in U.S. Patents 3,731,686 and 3,858,585 issued to Pronoy Chatterjee on May 8, 1973 and ~une 7, 1975, and in U.S. Patent 3,589,364 issued to W. L. Dean et al. on June, 1971. These materials are in the for~ of highly swellable, and highly fluid-retentive f.bers. It is desirable to combine these fibers with the more conventional absorbent materials such as rayon, wood pulp, cotton or the like to produce an absor~ent body having increased ~luid retentive properties. Unfortunate~y, when mixing such fiberous materials it is not an easy processins task to get an even distribution and this has added to the burden of producing an absorbent bodv 'or the products of interest herein.
Accordingly, there is need for improvement in the manufacture of absorbent bodies specifically directed toward increasing the integrity o~ the ~odies wi'hout sacrificing flexibility and, particularly ~hen ntroducing 11535~Z.
chemically modified absorbent materials into the absorbent body, S~MMARY OF THE INVENTION
In accordance with this invention, absorbent material is now ~rovided for body fluid absorbent products which material has relatively high tensile strength so that it may be handled during processing far less singerly than prior absorbent materials. This high tensile strength notwithstanding, the material is extremely flexible and may be incorporated into absorbent products without any substantial loss in user's comfort. Further, the material of this invention is substantially ~ore absorbent, i.e., can absorb and retain greater volumes of body 'iu-~, then conventional absorbents.
Specifically, in accordance with the method of this invention, a slurry of water with no more than about 0.1 and preferably no more than about 0.05~ solids ia for~ed wherein the solids comprise cellulosic fibers and particulate hydrocolloidal material. The ratio of ,uch hydrocolloidal material to the cellulosic fibers is at least 0.01 grams per gram and ~referably at leas~
0.1 grams per gram. A wet web is formed from the slurry by such means as by depositing the same onto a screen and drawing the water away with the aid of vacuum. The wet web is then dried, preferably to a water content of less than about 10.0 percent by weight to form a dry, relatively bul`.~y web. In accordance with the teaching of this invention, the dry web is now increased in density bv at least about 10.0~ and preferably at leas~ about 50.0 to form the board like web of this invention. Said in other words, the resulting board has a density of at least 110% and preferably at least 150~ based on the density of the dried bulky web. The increase in densi_y increases the tensile strength of the dried web. Sur~risingly, tnis increase in tensile strength and increase in density is ~535~2 accompanied by a marked and substantial decrease in stiffness. The decrease in stiffness is so great, in fact, that the resulting densified web may be used directly in absorbent products and will not signi~icantly effect the user~s comfort.
Preferably, the densified web will have a tensile strength of at least 10 Kg/cm2. Concomitantly, the Gurley Stiffness will be less than about ~0 gm and preferably less than 12 gm, these latter parameters being more specifically defined herein. Further, a product having the above set out parameters can be pro-duced by forming and densifying webs which, in their densified state, are more than 0.3 millimeters thick and preferably more than O . 6 millimeters thick. The importance of such thickness is that the densified web can be em-ployed as a major, or even as the sole, absorbent element in a body fluid absorbent product and will, by virtue of its thickness, provide substantial absorbent capacity.
At the same time, handling of the web is greatly facili-tated because of its hi~h tensile strength and this is accomplished without sacrificing user comfort.
According to a further broad aspect of the pre-sent invention, there is provided a method for producing an absorbent, relatively thick flexible absorbent board of fibrous material. The method comprises forming a slurry of water with no more than about 0.1% by weight solids. The solids comprise cellulosic fibers and parti-culate hydrocolloidal material in a ratio of at least 0.01 grams of hydrocolloidal material per gram of cellulosic fibers. A wet web is then formed from the slurry The web is dried to a water content of less than 10~/o by weight to form a undensified dry web. The density of the dry web is increased by at least 10%. The densified, dry web has a high tensile strength, and low stiffness relative to the undensified dry web, - 4a ~5356)~
According to a further broad aspect of the present invention, there is provided a flexible, absorbent board having a high tensile strength, The board comprises cellulosic fibers and particulate hydrocolloidal material in a ratio of at least 0,01 gm, of hydrocolloidal material per gram of cellulosic fibers, The board has a tensile strength of at least 10 Kg/cm2, a thickness of at least 0.3 mm, and a Gurley Stiffness of less than 40 gms. The board has been compacted in a dry state to a density of at least ll~/o of the density of the uncompacted dry board.
According to a other broad aspects of the pre-sent invention, there is provided a sanitary napkin and a catamenial tampon comprising the above-described absor-bent element, BRIEF DESCRIPTION OF TH:E D~AWINGS
The invention will be more clearly understood by reference to the description which follows when taken together with the attached drawings in which:
Fig, 1 is a schematic flow diagram of the pro-cess for making the strong, flexible, highly absorbent material of this invention; (this figure appears on the same sheet with figures 4-7) Fig, 2 is a graphical representation of the relationship between Gurley Stiffness, density and hydrocolloidal content for the first embodiment of the material of this invention, 11535~z.
Fig. 3 is a graphical representation of the same parameters as Fig. 3 for the second embodiment of the material of this invention;
Fig. 4 is a prospective view of a first sanitary napkin incorporating material of this invention with parts removed to illustrate the structure thereof;
F ig . S is a transve-se, cross sectional view of the sanitary napkin of Fig. 4; taken along line 5-5;
Fig. 6 is a prospective view of a second sanitary napkin incorporating a material of this invention with parts removed to illustrate the structure thereof;
~ ig. 7 is a transverse, cross-sectional ~liew of the napkin of Fig. 6, taken along line 7-7;
Fig. 8 is a prospective view of a third sanitary napkin incorporating a material of this invention wi~h parts removed to illustrate the structure thereof;
Fig. 9 is a transverse, cross-sectional view of the of Fig. 8, taken along line 10-10;
Fig. 10 is a planar view of a diaper _ncor~oratins the material of this invention;
Fig. ll is a transverse, cross-sectional view of the diaper of Fig. 10 taken along line 13-13;
Fig. 12 is a perspective view of a partially rolled tampon blank incorporating the material of this invention;
and Fig. 13 is a cross-sectional view of the finished tampon made from the blank of Fig. 12.
DETAILED DESCRIPTION OF THE INVENTION
Referring now to Fig. l, shown there is a schematic flow diagram of the process for providing an absorbent material in accordance with the teachings of this invention. A slurry is formed in a slurry forming station 10 from a water supply 12, a cellulosic fiber supply 11 and a hydrocolloidal particle supply 16. ~he cellulos~c ~535¢)~
fiber may be any of the commonly used cellulosic materials available for absorbent products and may include, for example, wood pulp, cotton, grasses, or regenerated cellulose ~ibers and the like. It is generally pre~erred that these fibers lie within the range of about lO0 to about 3000 microns in length. Currently because cf both cost and availability considerations, wood pulp is the cellulosic fiber of choice.
The hydrocolloidal particles from supply 16 may take various physical and chemical forms. With regard to physical form, as used herein, the terms "particles" and "particulate" are meant to refer to material which is made up of discrete units of various shapes such as powders, fibers, or flakes. Generally, these particles consist o~
water insoluble, but water swellable, polymeric substances capable of absorbing water in an amount which is at least ten times the weight of the hydrocolloid particles in the dry form and is preferably about l; to about 30 times the dry weight. Preferably, the hydrocolloid particles are i~
the shape of fibers and may be conveniently obtained by chemically modifying cellulosic fibers.
Such material may be described che.mically as having a backbone of natural or synthetic polymers wi.h hydrophilic groups or polymers containing hydrophilic groups being chemically bonded to the backbone or in intimate admixture therewith. Included in this class of materials are such modified natural and regenerated poly~ers as polysaccharides including, for example, cellulose and starch and regenerated cellulose, which are modi-ied by being carboxyalkylated, phosphonoalkylated, sulphoalkylated, or phosphorylated to render them highly hydrophilic. Such modified polymers may also be crosslinked to enhance their hydrophilicity and render them water insoluble.
~i53502 , These same polysaccharides may also serve, for example, as the backbone onto which other ?olymer moieties may be bonded by gra~t copolymerization techniques. Such grafted polysaccharides and their method of manufac~ure are described in ~.S. Patent No. 4,105,033 iss~ed on August 8, 1978 to P. ~. Chatteree et al. and may be described as oolysaccharide chains having grafted thereon a hydrophilic chain of the general formula 1 (C~2)q - IRl j 1- (C~2)p - IR2 _ l A J L I = ~
wherein A and B are selected from the group consis_ing of -CR3, -C(alkali metal), -OHNH3, -NH2, wherein Rl, R2 and R3 are selected from the group consisting of hydrogen and alkyl having 1 to 4 car~on atoms, wherein r is an integer having a value of 0 to about 5000, s is an integer having a value of 0 to about 20 5000, r plus s is at least 500, p is an integer having a value of zero or 1 and q is an integer having a value of !
to 4. The preferred hydroohilic chains are hydrolyzed polyacrylonitrile chains and copolymers of polyacr-ylamide and sodium polyacrylate.
ln addition to modified natural and regenerated polymers, the hydrocolloid particle component of the densified layer of this invention may comprise whollv synthetic hydrophilic particles. cxamples of those now known in the art are polyacrylonitrile fibers which may be modified by grafting such moieties thereon such as polyvinyl alcohol chains, polyvinyl alcohol itself, hydrophilic polyurethane, poly(alkyl phosphonates) partially hydrolyzed polyacrylamides (e.g., poly(N-N-Dimethyl acrylamide), sulfonated polystyrene, or poly(alkylene oxide). These highly hydrophilic synthetic 1~535~)~
polymers may be modified by other chemical treatments such as crosslinking or hydrolysis.
The cellulosic fibers, the hydrocolloidal particles ~nd the water from supplies 14, 16, and 12, respectively are all combined in the slurry forming station 10 to form a slurry which is then conveyed by means 18 to a web forming station 20. The proportions of the components in the slurry are controlled so that the slurry comprises no more than about 0.1 and preferably no more than about 0.05% solids, e.gO, fibers and particles. 2rererably the slurry comprises about 0.05 to 0.01~ solids with about 0.01~ being the esn~n~rat- of choice. The solids are controlled to be in the ratio of at least 0.01 grams of hydrocolloidal material per gram of cellulosic fibers and 1; preferably at least about 0.1 srams per gram.
The slurry may be formed in several ways known in the art and associated with the wet laying of fibrous webs.
In some instances it may be prudent to form the slurry at a high solids concentration, e.g., about 1.5~ by weight solids and then dilute the slurry wi~h the addition of further water to the desired concentration. It may also be convenient to premix any of the ~i ~ ccS in any other combination prior to forming the final slurry.
Irrespective of how the slurry is formed, it is next passed to the web forming station 20 where a wet ~eb is formed, for example, by depositing the slurry onto a continuous belt and maintaining a pressure differential across the faces of the belt to draw away a oreponcerance of the water and leave a loosely compacted wet web of cellulosic fibers and hydrocolloid particles in intimate mixture. At this point in the process of this invention, it is desirable that the web have a solids content of not more than about 50~ by weight of wet web and not less than about 2~. The wet web is passed by means 24 to a drying station 26 wherein the web is next dried to a water content of less than about 10~ by weight and prererably ~S35i~)2 less than about 5~. Such drying may be accomplished using equipment well ~nown in the art such as by applying heat through means 30 in the form of hot air, electrical resistance coils, steam cans or the like.
S The product leaving drying station 26 is a relatively lofty, thick board-like material which has only moderate tensile strength and is only moderately capable of maintaining its integrity during handling. The dried board-like web is very stiff and, while highly absorbent, cannot be used directly in a sanitary napkin or similar body fluid absorbent product which is to be worn by tne user in that the high degree of stiffness will cause great user discomfort and prevent the product from conrorming to the body, this latter feature causing the resulting product to fail prematurely. Typically, the dry web has a density which ranges from about O.li to 0.3 gm/cc, is about 1.0 to 2.0 mm. thick, has a t_nsile strensth of .rom about 10 to 100 Kg/cm2 and has a Gurley stiffness value of about 25 to 40 gm.
In accordance with this invention, the dry web is now passed via conveyor 32 to a compacting station 3~ wherein the density of the web is increased to a densi_y of at least about 110~ and preferably to at least about 1;0~ of the density prior to compacting. In order to accomplish this high level of compaction and have the increased density be permanent, i.e., have the compacted board ta~e a permanent set, a very high pressure must be ap?lied to the dry web. Generally, a pressure of at leas~ about 30 psi should be applied and more preferably the ?ressure should be at least lS0 psi. While the compacting pressure could be applied by several means such as by passing the dry web through the nips of two or more pressure rollers, it is usually preferred to obta,n the compaction by use or a hydraulic press which is designed to deliver such high 3; pressures.
1~53S~Z
The resulting compacted web has a substantially higher tensile strength as compared to that of the uncompacted dry web and so can be easily handled while still maintaining its structural integrity. For reason not yet understood, the compacting process, in addition to greatly increasing the tensile strength of the board, dramatically reduces the stiffness. When made in accordance with the teachings herein, the compacted board of this invention is so flexible that it may be used directly, without any grinding or commi.nution step, in absorbent products which are to be worn without any substantial user discomfort.
Example 1 A series of samples are prepared having various ratios of hydrocolloidal particles in admixture with wood pulp. ~he hydrocolloidal particles employed are those described in the aforementioned U.S. 2atent 3,889,678 and, specifically, sample number 4, in Table II, of that patent. This material is a cellulose graft copolymer consisting of a cellulose backbone having grafted thereto polymer moieties consisting of co-polymers of sodium acrylate and ethylacrylate in a weight ratio of 19.8 parts by weight cellulose to 33.9 parts by weight of poly(ethylacrylate) to 46.3 parts by weight of poly(sodium acrylate). This hydrocolloid is in fibrous ~orm with the fibers having an arithmetic average fiber length of approximately 0.8 mm. In the case of each of the sample blends, the following procedure is employed:
The hydrocolloid and the wood pulp are dispersed in water to yield a slurry having a consistency of 1.173 by weight solids. One liter of the slurry is placed in a handsheet mold measuring 7 3/4 inches by 7 3/4 inches and manufactured by the Williams Apparatus Company of Watertown, New York. The slurry is than diluted to a ~1535~2 .
consistency of 0.01% by weight solids in accordance with the procedure set out in TAPPI Standard Method T-2050S71.
After mixing thoroughly, the water is allowed to gravity drain, leaving a wet hydrocolloid/wood pul? web having a solids content of about 5%, based on the wet web.
The wet web is blotted with blotter boards and sq~eezed to remove excess water and then dried in an air circulated oven to a water content of abou~ 2.0% water, by weight of the dry material. The resulting stiff, lofty product is compacted to varying densities in a hydraulic press.
Table I below records values of the tensile strength as a function of the hydrocolloid particle content for boards made in accordance with the aDove procedure. The tensile strength to break is determined with an Instron ~niversal Testing ~"achine by setting the jaw distance at 10.2 c~. and pulling at a cross-head s?eed of 5.1 cm/min.
The value~ for tensile strength in Table I are normalized by dividing the tensile strength to break by the cross sectional area of the board (i.e., the section perpendicular to the force applied).
11535~)2 Table I
TENSILE SrRENGr~ VS. ~NSITY
( GRAÇTED OEI~JLOSE ) SNormalized ~Kg/cm2) Jaw Distance 10.2 cm Cross~ead Speed 5.1 cm/min 10Unpressed Sheet ressed Sheet Hydrocolloid Concentration Tensile ~ensity Tensile Density % ~ensity t~ by ~ieight) (Kg/Cm )(g/cm ) ~Kg/cm )(g/cm ) Increased 0 109 0.45 112 0.51 13.3
2~ 35 0.22 75 0.50 127.3 0.20 53 0.40 100.0 0.19 38 0.31 63.2 2S 0.18 38 0.28 5~.5 20 60 22 0.17 28 0.29 70.6 0.18 24 0.30 66.7 12 0.15 13 0.29 93.3 12 O.lS 10 0.28 86.7 As can be seen from the above Table, the boards made with the hydrocolloidal particles exhibit a relatively low density of from 0.15 to 0.22 gm/cm3 when dried and uncompacted. In contrast, the 100~ pulp board has a dGnsity of 0.45. Concomitantly, the tensile s;rength of the uncompacted board is low, varying for these samples between 12 to 35 Xg/cm2 as contrasted to 109 Kg/cm2 for 100% wood pulp board. Upon compacting and increasing the density by from 55.5 to 127.3~ based on the original density, the tensile strength has generally 35 increased and, in the case of low proportions of hydrocolloidal materlal and high compaction (e.g., 20 1153S~)2 hydrocolloid and 127.33 compaction), the tensile strength approaches that of 100~ wood pulp board.
Exam~le 2 . .
A series of samples are prepared having various ratios of hydrocolloidal particles in admixture with wood pulp. The samples are made and tested rollowing the procedures of the preceeding example with the exception that the hydrocolloid employed consists of cellulose fibers having been carboxymethylated to a degree of substitution of about 0.7 carboxymethyl groups per anhydrous glucose unit and having been insolubilized by crosslinking. The hydrocolloidal material was obtained from the Hercules Company of Wilmington, Delaware, and is l; sold by them under the trademar~c, Aqualon C. Table II
summarizes the results of the testing of these samples.
Table II
TENSILE STREN~H VS. E2~SI'IY
( CA~?BOXY~HYL CELLU~iSE ) Normalized (Kg/an2 ) Jaw Distance 10.2 cm Cross Head Speed 5.1 an~min Unpressed Sheet Pressed Shee~
Hydrocolloid Concentration Tensile Density Tensile Density ~ Density (9~eight) (~g/cm )(g/cm ) (Kg/cm )(g/cm ) Increased 0 109 0~45 111 0.51 13.3 33 0.21 22 0.36 71.4 34 0.21 49 0.32 52.4 38 0. 22 56 0.28 27. 3 62 0.27 72 0.32 18.5 67 0.29 70 0.32 10.3 ~S3S~)Z
As is shown in Table II, again the hydrocolloid containing board in the uncompacted state has a substantially lower density than a pure wood pulp ~oard and a substantially lower tensile strength. By compacting the hydrocolloid containing board, even to a relatively moderate degree, the tensile strengths are generally significantly improved. This is most pronounced in the range of less than about 60~ by weight of hydrocolloidal particles i.e., less than 1.5 gms of hydrocolloid particles per gram of wood pulp.
Examole 3 -Uncompacted boards having varying concentrations of grafted cellulose hydrocolloidal particles are prepared in 1~ accordance with ~xample l and are compacted under the influence of various degrees of pressure in a hydraulic press. The Gurley Stiffness Value of the resulting ~oa~d is measured using a Gurley Stiffness Testor, (motor operated model) manufactured by ~. & L. E. Gurley of mrOy, New York. In essence, this instrument measures the externally applied moment required to produce a given deflection of a strip of material of specific dimenslons fixed at one end and having a concentrated load applied to the other end. The results are obtained as "Gurley Stiffness" values in units of grams. As used herein, each strip of board tested was 3.5 inches by one inch. Table III summarizes the results of these tests ard these data are further illustrated graphically in Fig. 2.
1153S~Z
Table III
EFFECT OF E~SITY CN GU ~ Y ~IF~S
. (GR~D OE ~ L~SE) Hydrocolloid Pressure Concentration (psi)_ % ~v Weight: 20 40 60 80 90 0.0 Gurlev (gm) 38.6 33.4 31.4 25.6- ~.3 Density (g/cc) 0.22 0.19 0.17 0.15 0.15 % Increase 0 0 0 0 0 35.7 Guriey (gm) 17.5 11.7 11.8 7.3 6.5 Censity (g/cc) 0.32 0.30 0.27 0.31 0.27 % Increase 45.5 57.9 58.8 106.7 80.0 107.14 Gurley (gm) 12.5 9.7 8.1 4.2 4.3 Density (g/cc) 0.36 0.39 0.38 0.36 0.35 % Increase 63.6 105.3 123.5 140.0 133.3 178.5 Gurley (gm) 8.8 7.7 5.6 3.1 2.2 Density (g/cc) 0.46 0.44 0.42 0.42 0.43 % Increase 109.1 131.6 147.1 180.0 186.7 249.9 Gurley (gm) 8.4 5.4 4.1 2.1 2.3 Density (g/cc) 0.51 0.52 0.50 0.48 0.48 % Increase 131.8 173.7 194.1 220.0 220.0 357.0 Gurley (gm) 7.2 5.2 3.5 2.5 1.9 Censity (g/cc) 0.56 0.59 0.57 0.S6 0.56 % Increase 154.5 210.5 235.3 273.3 273.3 535.5 Gurley (gm) 6.9 4.9 3.2 2.0 1.8 Density (g/cc) 0.62 0.67 0.66 0.65 0.6 % Increase 181.8 252.6 28~.2 333.3 340.0 As can be seen from these data, the uncom?acted boards exhibit Gurley Stiffness values of over 25 gm and in some cases over 30 gm, these values representing board which is relatively stiff and which cannot be used directly in an absorbent product. However, when in accordance with the teachings of this invention, the densities of the board are increased by compaction under pressure by values of from 45.5 to 340% increase, based on the uncompacted density, the Gurley Stiffness surprisingly decreases to values ranglng from 17.5 gm to as low as 1~535~Z
1.8 gm. At these values the board is quite fle:~ible and may be used directly in absorbent products. It will be ~`~ noted that the decrease in Gurley Stiffness ~
d ~ t ~
1hh4K~ alth'ough not proportionately, with the increase in density.
Example 4 Uncompacted boards having varying proportions of carboxymethyl cellulose hydrocolloidal particles are prepared in accordance with 2xample 2 and are compacted and tested for Gurley Stiffness Values using the procedure set out in Example 3. Table 4 summarizes the results of these tests and these are further illustrated graphically in r ig. 3.
1~535~2 Table IV
EFFECT OF OENSITY CN G~RLEY STIFFNESS
(CAR~OXYMEIffYL C~LLUL~Sc) Hydrocolloid Pressure Concentration (psi) ~_bv ~eight: 20% 40~ 60~ 80~ 90~
0 Gurley (gm) 33.6 30.0 29.1 30.8 34.2 Density (g/cc) 0.21 0.21 0.22 0.2/ 0.29 % Increase _0 0 0 0 0 3i.7 Gurley (gm) 13.0 11.9 14.2 23.4 22.7 Density (g/cc) 0.32 0.33 0.32 0.31 0.34 ~ Increase _ 47 6 57 1 45.5 14.8 17.2 107.14 Gurley tgm) 9.9 11 0 11.2 18.2 16.4 Density (g/cc) 0.42 0.41 0.36 0.38 0.41 % Increase 100.0 95 2 63.6 40.7 41.4 178.5 Gurley (gm) 8.1 8.5 7.3 11.7 13.0 Censi'.y (g/cc) 0.50 0.47 0.48 0.44 0.45 ~ Incre~se 138.1 123.8 118.2 63.0 55.2 249.9 Gurley (gm) 6.3 6.8 7.9 8.7 16.2 Density (g/cc) 0.54 0.51 0.52 0.50 0.53 ~ Increase 157.1 142.8 136.4 85.2 82.8 357.0 Guriey (gm) 5.9 6.3 6.9 8.9 9.7 Density (g/cc) 0.62 0.61 0.61 0.54 0.55 ~ Increase 19;.2 100.5 177.3 100.0 89.7 535.5 Gurley (gm) 6.6 6.2 5,9 6.1 6.3 Censity (g/cc) 0.70 0.67 0.68 0.61 0.64 ~ Increase 233.3 219.1 209.1 125.9 120 As in the foregoing example, it can be seen from these data that the uncompacted boards exhibit Gurley Stiffness Values over 25 gm and in most cases over 30 gm, i.e., the board is extremely stiff. Again, when these boards are compacted in accordance with the teac~ings ~53S~)Z
of this invention, the density of the boards are increased by values of from 14.8 to 233.3%, based on the uncompacted den ity. The Gurley Stiffness Values for these compacted boards then ranges from 23.4 gm to a low of 5.9 gm and the compacted boards are generally flexible and usable in absorbent products. It should be noted that even at the moderate increase in density of 14.8%, the Gurley Stiffnes~ Value was reduced from 30.8 gm to 23.4 gm, reduction of about 25~.
Referring now to the drawings, Figs. 4 and 5 illustrate in perspective and traverse cross sectional views, respectively, a first sanitary napkin 40 incorporating the flexible board material of this invention. The napkin 40 comprises an absorbent pad 42 which may be composed of various absorbent materials such as wood pulp, rayon or any of the other commonlv used absorbents. Overlying the face of the pad 42 which is to be worn away from the body is a mens~rual fluid impervious barrier sheet 44 provided to protect the user's clothing from striXe through of body fluids absorbed by the na?kin.
Polyethylene or some other film forming polymer is the material of choice. The entire assembly of pad and barrier sheet are overwrapped with a menstrual fluid pervious cover 46 which may be either a woven or nonwoven material and is commonly comprised of fibers of rayon, polyester, cotton or the like. The napkin 40 is to be placed into the crotch portion of an undergarment and held there by use of a pressure-sensitive adhesive ele~ent 4a which extends longitudinally and centrally on the garment facing side of the napkin. A protective release strip 50 is provided overlying the adhesive element 43 to protect the adhesive element from dirt and unintended attachment prior to use.
In accordance with this invention, a sheet 52 of the flexible hydrocolloidal particle containing board of this invention is placed between the barrier sheet 44 and the :~lS35~)Z
pad 42. Preferably the sheet is smaller in both longitudinal and transverse dimensions than the pad or barrier and is centrally placed therebetween.
~ecause of the highly flexible nature of the board of this invention the sanitary napkin 40 is flexible and comfortable to use. By virtue of the hydrocolloidal particles contained in the boa-d and their high degree o hydrophilicity, the napkin exhibits increased absorption capacity.
Referring now to Figures 6 and 7, shown therein is another embodiment of this inven.ion. As in the previous embodiment, napkin 54 is provided with an absorbent pad 56, a barrier sheet 58 overlying the garment facing side of the pad and a cover material 60 enveloping the barrier and pad asse~bly. Again, an adhesive element 62 and a protective strip 64 for the adhesive element 62 are provided. In this specific embodiment a board 66 is provided but in this instance the board is pcsitioned centrally within pad 56. This may be accomplished by choosing a sliver of material comprising pad 56 which has a width of approximately t~ice the desired width of the napkin, lying the board on one half of this width and folding the pad in half so that the board will be centrally located therein. Again as in the previous embodiment by virtue of the nature of the board of this invention the napkin 54 is both flexible and comfortable in use and has increased absorptive capacity.
Figures 8 and 9 illustrate still another sanitary napkin embodying the invention taught herein. Shcwn there is napkin 68 which comprises an absorbent material 70 folded into a generally C shape whose ends abut on the gar~ent facing side of the napkin. Overlying this surface of the napkin is a barrier sheet 72. Within the folds of the C folded material 70 is placed a board of the material of this invention. Again because of the unique character-~L~5350Z
istics of this board, the napkin 68 is soft, flexible, and highly absorbent.
Figures 10 and ll illustrate still another embodiment of this invention, in this case the board of this inven-S tion being employed in a disposable diaper 76. The diaper76 comprises a fluid pervious spacing material 78 which may be made Gf the same woven or non woven materials employed in connection with the sanitary napkins described above. A rectangular pad 80 made of absorbent fibrous material is disposed beneath the facing material and a impervious barrier sheet 84 is used as a backing and generally sealed about its periphery to the facing material 78. As shown in the drawings, sandwiched between the barrier sheet 84 and the pad 80 is a board comprising lS the material of this invention. Once more because of the flexible and absorbent nature of the board, the diaper is comfortable and highly absorbent in use.
Figures 12 and 13 illustrate the flexible board of this invention being employed for use in a catamenial tampon. Illustrated in Figure 86 is a partially rolled tampon blank prior to being compressed into a completed tampon. The blank comprises two rectangular sheets; sheet 88 being an absorbent fibrous material and sheet 90 being the absorbent flexible board of this invention. The two superimposed sheets are rolled into the blank 86 so that alternating layers of the material of sheet 90 and the material of sheet 88 result. The blank is then compressed into the finished tampon shown in Figure 13. The tampon 92 is provided with the usual withdrawal string 9~. In this manner, hydrocolloidal material may be easily distributed, relatively uniformly, throughout the tampon without the need for handling finely divided materials.
Exam~le 2 . .
A series of samples are prepared having various ratios of hydrocolloidal particles in admixture with wood pulp. The samples are made and tested rollowing the procedures of the preceeding example with the exception that the hydrocolloid employed consists of cellulose fibers having been carboxymethylated to a degree of substitution of about 0.7 carboxymethyl groups per anhydrous glucose unit and having been insolubilized by crosslinking. The hydrocolloidal material was obtained from the Hercules Company of Wilmington, Delaware, and is l; sold by them under the trademar~c, Aqualon C. Table II
summarizes the results of the testing of these samples.
Table II
TENSILE STREN~H VS. E2~SI'IY
( CA~?BOXY~HYL CELLU~iSE ) Normalized (Kg/an2 ) Jaw Distance 10.2 cm Cross Head Speed 5.1 an~min Unpressed Sheet Pressed Shee~
Hydrocolloid Concentration Tensile Density Tensile Density ~ Density (9~eight) (~g/cm )(g/cm ) (Kg/cm )(g/cm ) Increased 0 109 0~45 111 0.51 13.3 33 0.21 22 0.36 71.4 34 0.21 49 0.32 52.4 38 0. 22 56 0.28 27. 3 62 0.27 72 0.32 18.5 67 0.29 70 0.32 10.3 ~S3S~)Z
As is shown in Table II, again the hydrocolloid containing board in the uncompacted state has a substantially lower density than a pure wood pulp ~oard and a substantially lower tensile strength. By compacting the hydrocolloid containing board, even to a relatively moderate degree, the tensile strengths are generally significantly improved. This is most pronounced in the range of less than about 60~ by weight of hydrocolloidal particles i.e., less than 1.5 gms of hydrocolloid particles per gram of wood pulp.
Examole 3 -Uncompacted boards having varying concentrations of grafted cellulose hydrocolloidal particles are prepared in 1~ accordance with ~xample l and are compacted under the influence of various degrees of pressure in a hydraulic press. The Gurley Stiffness Value of the resulting ~oa~d is measured using a Gurley Stiffness Testor, (motor operated model) manufactured by ~. & L. E. Gurley of mrOy, New York. In essence, this instrument measures the externally applied moment required to produce a given deflection of a strip of material of specific dimenslons fixed at one end and having a concentrated load applied to the other end. The results are obtained as "Gurley Stiffness" values in units of grams. As used herein, each strip of board tested was 3.5 inches by one inch. Table III summarizes the results of these tests ard these data are further illustrated graphically in Fig. 2.
1153S~Z
Table III
EFFECT OF E~SITY CN GU ~ Y ~IF~S
. (GR~D OE ~ L~SE) Hydrocolloid Pressure Concentration (psi)_ % ~v Weight: 20 40 60 80 90 0.0 Gurlev (gm) 38.6 33.4 31.4 25.6- ~.3 Density (g/cc) 0.22 0.19 0.17 0.15 0.15 % Increase 0 0 0 0 0 35.7 Guriey (gm) 17.5 11.7 11.8 7.3 6.5 Censity (g/cc) 0.32 0.30 0.27 0.31 0.27 % Increase 45.5 57.9 58.8 106.7 80.0 107.14 Gurley (gm) 12.5 9.7 8.1 4.2 4.3 Density (g/cc) 0.36 0.39 0.38 0.36 0.35 % Increase 63.6 105.3 123.5 140.0 133.3 178.5 Gurley (gm) 8.8 7.7 5.6 3.1 2.2 Density (g/cc) 0.46 0.44 0.42 0.42 0.43 % Increase 109.1 131.6 147.1 180.0 186.7 249.9 Gurley (gm) 8.4 5.4 4.1 2.1 2.3 Density (g/cc) 0.51 0.52 0.50 0.48 0.48 % Increase 131.8 173.7 194.1 220.0 220.0 357.0 Gurley (gm) 7.2 5.2 3.5 2.5 1.9 Censity (g/cc) 0.56 0.59 0.57 0.S6 0.56 % Increase 154.5 210.5 235.3 273.3 273.3 535.5 Gurley (gm) 6.9 4.9 3.2 2.0 1.8 Density (g/cc) 0.62 0.67 0.66 0.65 0.6 % Increase 181.8 252.6 28~.2 333.3 340.0 As can be seen from these data, the uncom?acted boards exhibit Gurley Stiffness values of over 25 gm and in some cases over 30 gm, these values representing board which is relatively stiff and which cannot be used directly in an absorbent product. However, when in accordance with the teachings of this invention, the densities of the board are increased by compaction under pressure by values of from 45.5 to 340% increase, based on the uncompacted density, the Gurley Stiffness surprisingly decreases to values ranglng from 17.5 gm to as low as 1~535~Z
1.8 gm. At these values the board is quite fle:~ible and may be used directly in absorbent products. It will be ~`~ noted that the decrease in Gurley Stiffness ~
d ~ t ~
1hh4K~ alth'ough not proportionately, with the increase in density.
Example 4 Uncompacted boards having varying proportions of carboxymethyl cellulose hydrocolloidal particles are prepared in accordance with 2xample 2 and are compacted and tested for Gurley Stiffness Values using the procedure set out in Example 3. Table 4 summarizes the results of these tests and these are further illustrated graphically in r ig. 3.
1~535~2 Table IV
EFFECT OF OENSITY CN G~RLEY STIFFNESS
(CAR~OXYMEIffYL C~LLUL~Sc) Hydrocolloid Pressure Concentration (psi) ~_bv ~eight: 20% 40~ 60~ 80~ 90~
0 Gurley (gm) 33.6 30.0 29.1 30.8 34.2 Density (g/cc) 0.21 0.21 0.22 0.2/ 0.29 % Increase _0 0 0 0 0 3i.7 Gurley (gm) 13.0 11.9 14.2 23.4 22.7 Density (g/cc) 0.32 0.33 0.32 0.31 0.34 ~ Increase _ 47 6 57 1 45.5 14.8 17.2 107.14 Gurley tgm) 9.9 11 0 11.2 18.2 16.4 Density (g/cc) 0.42 0.41 0.36 0.38 0.41 % Increase 100.0 95 2 63.6 40.7 41.4 178.5 Gurley (gm) 8.1 8.5 7.3 11.7 13.0 Censi'.y (g/cc) 0.50 0.47 0.48 0.44 0.45 ~ Incre~se 138.1 123.8 118.2 63.0 55.2 249.9 Gurley (gm) 6.3 6.8 7.9 8.7 16.2 Density (g/cc) 0.54 0.51 0.52 0.50 0.53 ~ Increase 157.1 142.8 136.4 85.2 82.8 357.0 Guriey (gm) 5.9 6.3 6.9 8.9 9.7 Density (g/cc) 0.62 0.61 0.61 0.54 0.55 ~ Increase 19;.2 100.5 177.3 100.0 89.7 535.5 Gurley (gm) 6.6 6.2 5,9 6.1 6.3 Censity (g/cc) 0.70 0.67 0.68 0.61 0.64 ~ Increase 233.3 219.1 209.1 125.9 120 As in the foregoing example, it can be seen from these data that the uncompacted boards exhibit Gurley Stiffness Values over 25 gm and in most cases over 30 gm, i.e., the board is extremely stiff. Again, when these boards are compacted in accordance with the teac~ings ~53S~)Z
of this invention, the density of the boards are increased by values of from 14.8 to 233.3%, based on the uncompacted den ity. The Gurley Stiffness Values for these compacted boards then ranges from 23.4 gm to a low of 5.9 gm and the compacted boards are generally flexible and usable in absorbent products. It should be noted that even at the moderate increase in density of 14.8%, the Gurley Stiffnes~ Value was reduced from 30.8 gm to 23.4 gm, reduction of about 25~.
Referring now to the drawings, Figs. 4 and 5 illustrate in perspective and traverse cross sectional views, respectively, a first sanitary napkin 40 incorporating the flexible board material of this invention. The napkin 40 comprises an absorbent pad 42 which may be composed of various absorbent materials such as wood pulp, rayon or any of the other commonlv used absorbents. Overlying the face of the pad 42 which is to be worn away from the body is a mens~rual fluid impervious barrier sheet 44 provided to protect the user's clothing from striXe through of body fluids absorbed by the na?kin.
Polyethylene or some other film forming polymer is the material of choice. The entire assembly of pad and barrier sheet are overwrapped with a menstrual fluid pervious cover 46 which may be either a woven or nonwoven material and is commonly comprised of fibers of rayon, polyester, cotton or the like. The napkin 40 is to be placed into the crotch portion of an undergarment and held there by use of a pressure-sensitive adhesive ele~ent 4a which extends longitudinally and centrally on the garment facing side of the napkin. A protective release strip 50 is provided overlying the adhesive element 43 to protect the adhesive element from dirt and unintended attachment prior to use.
In accordance with this invention, a sheet 52 of the flexible hydrocolloidal particle containing board of this invention is placed between the barrier sheet 44 and the :~lS35~)Z
pad 42. Preferably the sheet is smaller in both longitudinal and transverse dimensions than the pad or barrier and is centrally placed therebetween.
~ecause of the highly flexible nature of the board of this invention the sanitary napkin 40 is flexible and comfortable to use. By virtue of the hydrocolloidal particles contained in the boa-d and their high degree o hydrophilicity, the napkin exhibits increased absorption capacity.
Referring now to Figures 6 and 7, shown therein is another embodiment of this inven.ion. As in the previous embodiment, napkin 54 is provided with an absorbent pad 56, a barrier sheet 58 overlying the garment facing side of the pad and a cover material 60 enveloping the barrier and pad asse~bly. Again, an adhesive element 62 and a protective strip 64 for the adhesive element 62 are provided. In this specific embodiment a board 66 is provided but in this instance the board is pcsitioned centrally within pad 56. This may be accomplished by choosing a sliver of material comprising pad 56 which has a width of approximately t~ice the desired width of the napkin, lying the board on one half of this width and folding the pad in half so that the board will be centrally located therein. Again as in the previous embodiment by virtue of the nature of the board of this invention the napkin 54 is both flexible and comfortable in use and has increased absorptive capacity.
Figures 8 and 9 illustrate still another sanitary napkin embodying the invention taught herein. Shcwn there is napkin 68 which comprises an absorbent material 70 folded into a generally C shape whose ends abut on the gar~ent facing side of the napkin. Overlying this surface of the napkin is a barrier sheet 72. Within the folds of the C folded material 70 is placed a board of the material of this invention. Again because of the unique character-~L~5350Z
istics of this board, the napkin 68 is soft, flexible, and highly absorbent.
Figures 10 and ll illustrate still another embodiment of this invention, in this case the board of this inven-S tion being employed in a disposable diaper 76. The diaper76 comprises a fluid pervious spacing material 78 which may be made Gf the same woven or non woven materials employed in connection with the sanitary napkins described above. A rectangular pad 80 made of absorbent fibrous material is disposed beneath the facing material and a impervious barrier sheet 84 is used as a backing and generally sealed about its periphery to the facing material 78. As shown in the drawings, sandwiched between the barrier sheet 84 and the pad 80 is a board comprising lS the material of this invention. Once more because of the flexible and absorbent nature of the board, the diaper is comfortable and highly absorbent in use.
Figures 12 and 13 illustrate the flexible board of this invention being employed for use in a catamenial tampon. Illustrated in Figure 86 is a partially rolled tampon blank prior to being compressed into a completed tampon. The blank comprises two rectangular sheets; sheet 88 being an absorbent fibrous material and sheet 90 being the absorbent flexible board of this invention. The two superimposed sheets are rolled into the blank 86 so that alternating layers of the material of sheet 90 and the material of sheet 88 result. The blank is then compressed into the finished tampon shown in Figure 13. The tampon 92 is provided with the usual withdrawal string 9~. In this manner, hydrocolloidal material may be easily distributed, relatively uniformly, throughout the tampon without the need for handling finely divided materials.
Claims (30)
1 A method for producing an absorbent, relatively thick flexible absorbent board of fibrous material comprising:
forming a slurry of water with no more than about 0,1% by weight solids, said solids comprising cellulosic fibers and particulate hydrocolloidal material in a ratio of at least 0.01 grams of hydrocolloidal material per gram of cellulosic fibers; forming a wet web from said slurry;
drying said web to a water content of less than 10.0% by weight to form a undensified dry web, and increasing the density of said dry web by at least 10.0%;
whereby said densified dry web has a high tensile strength, and low stiffness relative to said undensified dry web.
forming a slurry of water with no more than about 0,1% by weight solids, said solids comprising cellulosic fibers and particulate hydrocolloidal material in a ratio of at least 0.01 grams of hydrocolloidal material per gram of cellulosic fibers; forming a wet web from said slurry;
drying said web to a water content of less than 10.0% by weight to form a undensified dry web, and increasing the density of said dry web by at least 10.0%;
whereby said densified dry web has a high tensile strength, and low stiffness relative to said undensified dry web.
2. The method of claim 1 wherein said slurry is formed with no more than about 0.05% by weight solids.
3. The method of claim 1 wherein said solids comprise cellulosic fibers and particulate hydrocolloidal material in a ratio of at least 0.1 gm. of hydrocolloidal materials per gram of cellulosic fibers.
4. The method of claim 1 wherein the density of said dry web is increased by at least 50%.
5. The method of claim 1 wherein said wet web is dried to a water content of less than 5% by weight.
6. The method of claim 1 wherein said wet web has a solid content of not more than 50% based on the weight of the wet web and not less than 2%.
7. The method of claim 1 wherein said dry web is densified by applying a pressure of at least 30 lbs. per square inch.
8. The method of claim 7 wherein said dry web is densified by applying a pressure of at least 150 lbs. per square inch.
9. The method of claim 1 wherein said dry web is densified by compressing with a hydraulic press.
10. The method of claim 1 wherein said wet web is dried by passing hot air over said web.
11. A flexible, absorbent board having a high tensile strength, said board comprising cellulosic fibers and particulate hydrocolloidal material in a ratio of at least 0.01 gm. of hydrocolloidal material per gram of cellulosic fibers;
said board having a tensile strength of at least 10 Kg/cm2 a thickness of at least 0.3 mm, and a Gurley Stiffness of less than 40 gms.;
said board having been compacted in a dry state to a density of at least 110% of the density of the uncompacted dry board.
said board having a tensile strength of at least 10 Kg/cm2 a thickness of at least 0.3 mm, and a Gurley Stiffness of less than 40 gms.;
said board having been compacted in a dry state to a density of at least 110% of the density of the uncompacted dry board.
12. The board of claim 11 comprising cellulosic fibers and particulate hydrocolloidal material in a ratio of at least 0.1 gm. of hydrocolloidal material per gram of cellulosic fibers.
13. The board of claim 11 having a Gurley Stiffness of less than 12 gms.
14. The board of claim 11 having a thickness of at least 0.6 mm.
15. The board of claim 11 having been compacted in a dry state to a density of at least 150% of the density of the uncompacted dry board.
16. The board of claim 11 wherein said particulate hydrocolloidal material can absorb 10 times its dry weigh.
of water.
of water.
17. The board of claim 16 wherein said particulate hydrocolloidal material can absorb from about 15 to about 30 times its dry weight of water.
18. The board of claim 11 wherein said hydrocolloidal material is a polymer having hydrophilic groups bonded to the backbone hereof.
19. The board of claim 11 wherein said hydrocolloidal material is a polysaccharide having bonded to the polymer backbone hydrophilic moieties selected from the group consisting of carboxyalkyl, phosphonoalkyl, sulphoalkyl, or phosphoryl.
20. The board of claim 19 wherein said hydrocolloidal material is crosslinked.
21. The board of claim 19 wherein said hydrocolloidal material is carboxymethylcellulosic.
22. The board of claim 18 wherein said hydrocolloidal material is a polysaccharide having hydrophilic chains grafted thereto.
23. The board of claim 22 wherein said hydrophilic chains have the formula wherein A and B are selected from the group consisting of -OR3, -O(alkali metal), -OHNH3, -NH2, wherein Rl, R2 and R3 are selected from the group consisting of hydrogen and alkyl having 1 to 4 carbon atoms, wherein r is an integer having a value of 0 to about 5000, s is an integer having a value of 0 to about 5000, r plus s is at least 500, p is an integer having a value of zero or 1 and q is an integer having a value of 1 to 4.
24. The board of claim 23 wherein said hydrophilic chains are hydrolyzed polyacrylonitrile chains.
25. The board of claim 23 wherein said hydrophilic chains are copolymers of polyacrylamide and sodium polyacrylate.
26. The board of claim 18 wherein said hydrocolloidal material is a synthetic polymer.
27. The board of claim 26 wherein said synthetic polymer is selected from the group consisting of polyacrylonitrile, grafted polyacrylonitrile, polyvinyl alcohol, hydrophilic polyurethane, poly(alkyl phosphonates), partially hydrolyzed polyacrylamides, sulfonated polystyrene, or poly(alkylene oxide).
28. A sanitary napkin comprising as an absorbent element thereof, a flexible, absorbent board having a high tensile strength, said board comprising cellulosic fibers and particulate hydrocolloidal material in a ratio of at least 0.01 gms of hydrocolloidal material per gram of cellulosic fibers;
said board having a tensile strength of at least 10 Kg/cm2, a thickness of at least 0.3 mm, and a Gurley Stiffness of less than 40 gms.;
said board having been compacted in a dry state to a density of at least 110% of the density of the uncompacted dry board.
said board having a tensile strength of at least 10 Kg/cm2, a thickness of at least 0.3 mm, and a Gurley Stiffness of less than 40 gms.;
said board having been compacted in a dry state to a density of at least 110% of the density of the uncompacted dry board.
29. A disposable diaper comprising as an absorbent element thereof a flexible, absorbent board having 2 high tensile strength, said board comprising cellulosic fibers and particulate hydrocolloidal material in a ratio of at least 0.01 gms of hydrocolloidal material per gram of cellulosic fibers;
said board having a tensile strength of at least 1 Kg/cm2, a thickness of at least 0.3 mm, and a Gurley Stiffness of less than 40 gms.;
said board having been compacted in a dry state to a density of at least 110% of the density of the uncompacted dry board.
said board having a tensile strength of at least 1 Kg/cm2, a thickness of at least 0.3 mm, and a Gurley Stiffness of less than 40 gms.;
said board having been compacted in a dry state to a density of at least 110% of the density of the uncompacted dry board.
30. A catamenial tampon comprising as an absorbent element thereof a flexible, absorbent board having a high tensile strength, said board comprising cellulosic fibers and particulate hydrocolloidal material in a ratio of at least 0.01 gms of hydrocolloidal material per gram of cellulosic fibers;
said board having a tensile strength of at least 10 Kg/cm2, a thickness of at least 0.3 mm, and a Gurley Stiffness of less than 40 gms.;
said board having been compacted in a dry state to a density of at least 110% of the density of the uncompacted dry board.
said board having a tensile strength of at least 10 Kg/cm2, a thickness of at least 0.3 mm, and a Gurley Stiffness of less than 40 gms.;
said board having been compacted in a dry state to a density of at least 110% of the density of the uncompacted dry board.