CA1128310A - Thermally activated ink and transfer method - Google Patents
Thermally activated ink and transfer methodInfo
- Publication number
- CA1128310A CA1128310A CA359,104A CA359104A CA1128310A CA 1128310 A CA1128310 A CA 1128310A CA 359104 A CA359104 A CA 359104A CA 1128310 A CA1128310 A CA 1128310A
- Authority
- CA
- Canada
- Prior art keywords
- acid
- recited
- thermally activated
- ink composition
- ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
THERMALLY ACTIVATED INK AND TRANSFER METHOD
ABSTRACT OF THE INVENTION
A thermally activated ink and a thermally activated transfer ribbon, comprising a polymer, oil and oil-gelling agent, are provided. The ink may form a coating on a substrate, such as a ribbon, for use in conjunction with a thermal printer or a nonimpact typewriter, for example, for generating characters on ordinary paper. A method is also provided for generating characters on ordinary paper with a thermal print head.
ABSTRACT OF THE INVENTION
A thermally activated ink and a thermally activated transfer ribbon, comprising a polymer, oil and oil-gelling agent, are provided. The ink may form a coating on a substrate, such as a ribbon, for use in conjunction with a thermal printer or a nonimpact typewriter, for example, for generating characters on ordinary paper. A method is also provided for generating characters on ordinary paper with a thermal print head.
Description
31 ~
BACKGROU21~ OF THE INVENT ION
Thermal printing, because of its simplici-ty and low-noise level, has potenti~lly many advantayes over exi5ting printing methods as a low-cost and rela-tively noise-free method of printing and generating characters. However, the acceptance of thermal printing has not been rapid because of the need for special paper and the nonpermanence of the heat-sensitive paper that is required for thermal printing.
Therefore, a need exists for a thermally activated ink, transfer ribbon and printing method for generating printed characters on ordinary paper. Present commercialized thermal printing can produce only blue or blue-black dye images of low to moderate darkness and opacity. Therefore, a need also exists for a thermal printing ink and method for producing black images having improved contrast and read-ability qualities. A need further exists for a thermally activated ink and method for producing high-quality, non-smudgeable, permanent characters on ordinary paper which characters are flexible and elastic to avoid flaking.
SUMMARY OF THE INVENTION
A thermally activated ink is provided which can be used, for example, in a thermally activated transfer ribbon or thermally activated typewriter ribbon. In another aspec-t, the present i-nvention provides a method for producing black thermal transfer images having improved contrast and read-ability.
In still another aspect, the invention provides a thermally activated ink and transfer ribbon which is able to ~enerate printed characters on ordinary paper. In another aspect, the invention provides a thermally activated ink and transfer ribbon for producing non-smudying images for permanen-t, ~.' `
..
ms/~
, 3~
high-quality documents.
As used herein, "thermally activated ink" is an ink which is solid or dry at ambient temperatures but which ink is a fluid above about 130F. The thermally activated ink compositions of the present invention have sharp melting points to insure that when generating characters, the ink will set quickly to a non-smudgeable, firm solid. The ink compositions according to the present invention are also slightly flexible and elastic so that flaking of the printed characters is avoided.
One embodiment of the present invention comprises a thermally activated ink comprising a polymer, oil and oil-gelling agent. The polymer has a relatively low molecular weight and a low softening point but is a solid at room temperature. In accordance with the presen-t invention, the gelling agent has a relatively low melting point but is also a solid at room temperature. The oil present in the composition of the present invention serves to lower the softening range of the polymer. Preferably, the oil is also a solid at room temperature but has a melting point less than about 100C.
..
~ ms/~
~2~
According to the present invention, the polymer is a polyamide resin or a styrene-allyl alcohol copolymer, having a molecular weight of from about 1,000 to about 10,000. The preferred gelling agent in the ink composition is 12-hydroxystearic acid and the preferred oil is l-eicosene.
Additional components which are generall~ present in the thermally activated ink compositions of the present invention include plasticizers, thickeners, pigments, dispersants and, optionally, dyes to tone or intensify color and solvents.
In another embodiment of the present invention, the thermally activated ink composition forms a film coating on a substrate or support film. The combination of the substrate and the thermally activated ink composition can be used as a thermally activated transfer ribbon in, for example, a thermal printer or typewriter, or other types of thermal printing devices which employ ribbons to generate characters.
In one specific embodiment the invention provides a thermally activated ink composition for use in generating printed characters on ordinary paper with a thermal printer comprising:
(a) a thermally stable polymer having a molecular weight of from about 1,000 to about 10,000 and a softening point of from about 50C. to about 125C. selected from the group consisting of styrene-allyl alcohol copolymers and polyamide resins and present in an amount of from about 25~
to about 45~ by we`ight of the total nonvolatile ink components;
; (b) an oil-gelling agent having a melting point of from about 40C. to about 100C., being further characterized as a i 30 carboxylic acid having eleven to eighteen carbon atoms and 1 to 2 hydroxy groups, the gelling agent being present in an amount of from about 6~ to about 13~ by weight of the total ink nonvolatile components; and - cb/~
3~
(c) an oil that is a dissolving medium for the polvmer and the gelli~g agent, and present in an amount of from about 12~ to about 26~ by weight of the total nonvolatile components.
-4a-cb/~
3~
DETAILED DESCRIPTION O}~' THE INVENTION
According to the invention, a thermally activated ink composition, thermally activated transfer ribbon and thermally activated transfer method are provided. The thermally activated ink co~m.~ositions of the present invention comprise a synthetic polymer, an oil, and oil-gelling agent, and optionally, a solvent for the polymer and oil. In th~
preferred compositions, specific rheology modifying materials, including plasticizers, thickeners and dispersants, are included to provide improved transfer and adherent characteristics. In addition to the presence~of a suitable pigment, a color toner may also be present in the thermally activated ink compositions of the present invention.
The polymer used in the composition according to the present invention has a relatively low molecular weight and a low softening point but is a solid at room temperature and is thermally stable~ "Thermally stable" as used herein means that the polymer does not decompose between about 10C
and about 180C. The polymer present in the composition of the present invention is either a polyamide resin or a styrene-allyl alcohol copolymer, having a molecular weight of from about 1,000 to about 10,000 and a softening point of from about 50C to about 125C.
The preferred polyamide resins used in the compos.ition : of the present invention have a molecular weight of from about 3,000 to about 5,000 and are prepared by reacting dimerized fatty acids with mixtures of linear aliphati.c diamines. Two specific preferred polyamides are sold by the Crosby Chemical Company of New Orleans, Lousiana, under the trade marks "Cropolamid 226" and "Cropolamid 228", and are ; prepared by reacting tall oil dimer acid with mixtures of linear aliphatic diamines. Cropolamid 226 has a ring-and-ball softening point of from about 95C to about 105C and a mc /
3~
viscosity of about 500 centipoises to about 700 centipoises at 160C. Cropolamid 228 has a ring-and-ball softening point of from about 100C to abou-t llO~C and a viscosity of from about 500 centipoises to about 700 centipoises. Another specific preferred polyamide is sold by Victor Wolf Limited of Calyton, Manchester, in Great Britain, under the trade mark "Wolfamid 8W", and is prepared by reacting dimerized vegetable oil fatty acids with a mixture of linear aliphatic . diamines. Wolfamid 8W has a ring-and-ball softening point '`' 10 of from about 95C to about 105C and a viscosity of from about 300 centipoises to about 800 centipoises at 160~C.
The preferred styrene-allyl alcohol copolymer for ; use in the composition according to the present invention has a number-average molecular weight of about 1,600, a hydroxyl content of from about 5.4% to about 6.0% and a Durran softening point of from about 100C to about 110C. This component can be obtained commercially from Mbnsanto Industrial Chemicals Company,of St. Louis, Missouri, under the trade mark "RJ-100". The preferred styrene-allyl copolymer may also be obtained from Aldrich Chemical Company, Inc.,of Milwaukee, Wisconsin. Another commerical styrene-ally aleohol copolymer which can be used in the composition of the present invention has a number-average molecular weigh-t of 1,150 and a hydroxyl content of from about 7.4% to about 8.0%, sold by Monsanto Industrial Chemicals Company of St. Louis, Missouri, under the trade mark "RH-101". However, this copolymer is less satisfactory than the other two preferred styrene-allyl alcohol copolymers because i-t imparts more brittleness to the ink formulation than is ~, usually desired.
The polymer in the ink composition of the present invention is present in an amount oE from about 25% to about ' 45% by weight of the total nonvolatile components and is preEerably present in an amount of about 31.8% by weight of ~/ms 3~
the tot~l ink nonvolatile components, ~s used herein, non-volatile ink components include all ink components as set forth in this d~escription excep-t for the solvent.
The oil present in the composi-tion of the present invention is preferably a solid at ambient temperature. The melting point of the oil is preferably between 25C and less than about 100C. The preferred oil for use in the co~position of the invention is l-eicosene which has a melting point of about 30~C. l-Eicosene is sold in an industrial grade under the trade mark C-20 Alpha Olefin by the Gulf Oil Chemicals Company of Houston, Texas, and also under the trade mark Neodene C-20 by the Shell Chemlcal Company of Houston, Texas.
Other oils which can be used in the composition of the present invention include mineral oil, or the like. Still other oils which can be used in the composition of the present invention are sold by the Shell Chemical Company of Houston, Texas under the trade marks Neodene C-18 and Neodene C-16, both of which are liquid at ambient temperature. Oils which are a solid at ambient temperature are preferred because these oils have less tendency to separate from the other components in the composition and, therefore, compositions according to the invention that contain an oil which is a solid at room temperature will usually have a longer shelf life. According to the invention, the oil is present in the ink composition in an amount of from about 12% to about 26% and preferably the oil is present in an amount of about 19.1% by weight of the total ink nonvolatile. The oil present in the ink composition is a "dissolving medium" for both the polymer and gelling agent, hereinafter described~ As used herein, "dissolving medium" means a component which is capable of ; forming a homogeneous mixture with other components, specifically the polymer and gelling agent.
\~ ms/~
3~
me gellinq agent present in hhe ink co~position of the present invention is a long chain hydrocarbon containing two or more polar groups (-OH, -CO2H). In addition, the gelling agent should be a solid at room temperature and have a relatively low melting point, preferably from abou-t 40C to about 100C, and should be a solid at room temperature. The gelling agent is present in the composition of the present invention in an amount of from about 6% to about 13% and preferably in an amount of about 9.5% by weight of the total ink nonvolatile components. The preferred gelling agent is 12-llydroxystearic acid. 12-hydroxystearic acid is a C18 straight chain fatty acid with an -OH group attached to the hydrocarbon chain, having a melting point of from about 79C
to about 82C. Other gelling agents which may be used in the composition of the present invention include: 11-hydroxypalmitic a¢id; ~-hydroxylauric acid; ll-hydro-xyundecanoic acid; 2-hydroxytetradecanoic acid; 15 hydro-xypentadecanoic acid; 2-hydroxyhexadecanoic acid; 16-hydroxyhexadecanoic acid; 2-hydroxydodecanoic acid; 9,11-dihydroxyundecanoic acid; 3,11-dihydroxytetradecanoic acid;
ll-hydroxytetradecanoic acid; 16-hydroxypalmitic acid;
14-hydroxypalmitic acid 2-hydroxypalmitic acid; and combinations thereof. The presence of the gelling agent in the thermally activated ink composition of the present invention serves to lower the melting point of the polymer ~;
and improve the compati~ility of the oil and polymer.
Preferably, the thermally activated ink composition of the present invention includes a plasticizer which is present in an amount of from about 9% to about 16% by weight of the total ink nonvolatile components and preferably about ; 12.7 by weight of the total ink nonvolatile components. The plasticizer serves to increase the flexibility and transfer-' ' _ ~_ ms/~
~z~
ability of the ink oomposi~ion. The plasticizer should be capable of plasticizing the polymer to increase its adhesion when applied to a substrate or backing, as will be herein-after described in greater de-tail. The plas-ticizer also serves, in combination with the oil, to lower the softening point of the polymer and gelling agent. According to the present invention, the preferred plasticizer is dipropylene glycol dibenzoate. Dipropylene glycol dibenzoate is sold under the trade mark Benzoflex 9-88 by the Velsicol Chemical of Chicago, Illinois. Also, for thermally activating ink compositions based on the polyamide resins, a mixture of N-ethyl-ortho-toluene suflonamides and N-ethyl-para-toluene sufonamides is suitable for use as a plasticizer and is sold under the trade mark of "Santicizer 8" by Monsanto Industrial Chemicals Company of St. Louis, Missouri. For thermally activated ink compositions based on a styrene-allyl alcohol copolymer, dioctyl phthalate or benzyl butyl phthalate may be used as the plasticizer of the compositi~on.
The composition of the present invention may optionally include a solvent for the polymer and gelling agent.
The preferred solvent for the ink composition containing a polyamide resin is a combination of toluene and isoprpyl alcohol in a ratio of toluene to iso~roPvl alcohol of 3:1.
For an ink composition containing a styrene-allyl alcohol copolymer, the preferred solvent is toluene. The solvent should be present in an amount of from about 50% to about 85%
i~ by weight of the total ink composition and is preferably present in an amount of from 65~ y weight of the total ink : composition.
~ The primary purpose of the solvent in the ink composition of the present invention is to facilitate coating ` the compositions on a film base or substrate. ~ significant - _9_ . ms/ Q~-~
. ; ~ , , , . ,. . . , .; ~, , . . . . . . ., .~
~2~3~L~
advantage of the ink composition described is that it can be ground and coated onto a film base while elther dissolved in solvent, or without solvent while molten. The use of solvent is advantageous when low viscosities and thin, uniform coatings, less than 0.0002 inch, are desired, Hot-melt grinding and coating are sometimes advantageous for reasons of economy and to avoid the flammability and vapor emissions of organic solvents. When the ink is applied as a ho~-melt, the ink is formulated without a solvent and is heated to a temperature in excess of its melting point so that the ink is in fluid form when applying it to a substrate.
To obtain the desired rheological properties, a thickener is also present in the ink composition of the present invention~ The thickener preferably comprises hydrophobic fumed silica or fumed silica and has a particle size when present in the final ink composition of about 19 microns or less or a Hegmann reading of 6.5 or better. One suitable thickener is a hydrophobic fumed silica sold under the trade mark "Aerosil R-972" by Degussa, Inc., Chemicals Division, of New York, New York. One specific fumed silica suitable for use as a thickener according to the present inven-tion is sold under the trade mark "Cab-O-Sil" by the Cabot Corporation of Boston, Massachussetts. The thickener should be present in an a~ount of from about 1% to about 3%
by weight of the total ink nonvolatile components and is preferably present in an amount of about 1.3% by weight of ` the total ink nonvolatile components.
In order to facilitate pigment we-tting and grinding, and to improve the flow of melted ink from, for example, a substrate to paper, a dispersant is preferably present in the composition of the present invention. One suitable dispersant is lecithin. One commerical grade of lecithin which can be ~ .~
~ .
,`. -10-ms/'`~
used in accoxdance ~ith the composition of the present invention is sold by the Spencer Kellog Division of Textron, Inc. of Buffalo, New York under the trade mark "Kelecin F."
The dispersant should be present in the ink composition according to the invention in an amount of from about 0.1%
to about 0.2% and is preferably present in an amount of about 0.19~ by weight of the total ink nonvolatile components.
When a commerical grade oil is used, such as "Neodene C-20", "Neodene C-18", "Neodene C-16" or "C-20" Alpha Olefin, generally the oil will contain a small percentage of heavier and lighter hydrocarbons. Because of this, it is often advantageous to include in the ink composition a slightly greater amoun-t of the plasticizer than would be used in an ink composition containing a laboratory grade oil for improved adhesion, transferability and compatability of the ink composition.
, In order to provide the desired ink color, a pigment is present in an amount of from about 15~ to about 25% by weight of the total ink nonvolatile components and preferably is present in an amount of about 19.1% by weight of the total ink nonvolatile components. The ink composition of the ~` present invention allows the use of carbon black as a pigment.
" Preferred pigments include furnace carbon black, alkali blue and iron blue. One preferred type of carbon black is sold by the Cabot Corporation of Boston, Massachussetts, under the trade mark "Mogul L." Another preferred type of furnace carbon black for use as a pigment in the composition of the present invention is sold by the Cities Service, CQlumbian Division of Akron, Ohio under the trade mark "Raven 1255."
Suitable types of blue pigments include, for example, iron blue sold by Hercules Inc. of Wilmington,~Delaware, under the ` trade mark "Hisperse X-3434" and a suitable alkali blue :~, ' \', ms/' pigment is sold by $herwin Williams Chemicals of Cleveland~
Ohio, under the trade mar~ "Powdura Blue CP."
The thermally activated ink composition of the present invention may optionally include a dye as a color toner or intensifier. Typical color toners which may be used in accordance with the composition of the present invention include, for example, Nigrosine Oleate marketed by Dye Specialties of Secaucus, Ne~ Jersey, Flushed Alkali Blue FL-14511 marketed by Sherwin Willlams Co., Cleveland, Ohio, and Methyl Violet Oleate 2:1 marketed by Dye Specialties Co.
of Secaucus, New Jersey.
In one embodiment of the present invention, the thermally activated ink composition forms a thin coating on one side of a substrate or support film, such as a ribbon, for example. In this manner, the thermally activated ink composition of the present invention can be used, for example, in conjunction with a thermal printed head for generating printed characters upon ordinary paper.
The substrate or support film may be constructed ` 20 of polyester, polyethylene, polypropylene, polyvinylchloride or other suitable materials. Since the ink and substrate combination according to -the present invention is suitable for use in conjunction with a thermal print head for generating characters, it is desirable that the substr!ate have minimal thickness to facilitate heat transfer from the thermal print head through the substrate and to the thermally activated ink com~osition forming a coating on the subs~ate and adjacent the paper or sur~o~ upon which is desired to ~:. generate characters. Preferably, the substate or supporting film has a thickness of from about 0.12 mil to about 0.75 mil.
For practical use, the substrate must possess sufficient tensile strength so that failure of the substate or ribbon .'. .
ms/~'i 3~l~
is minimizedO ~ pxefe~red substrate or support film is sold under the trade marks "Phil~o 308" and "PJX 2074" sold by the Phillips Joanna Company of Ladd, Illinois. Preferably the Philjo 308 has a thickness of about 0.45 mil. In addition, high density polyethylene, tensilized polyethylene tere~hthalate and non-tensilized polye-thylene terephthalate are also suitable for use as the substrate or support film according to the present invention.
According to the present invention, the -thermally activated ink compositions are preferably manufactured according to the following method. First, a "resin solution"
is prepared by dissolving the polymer, gelling agent, oil, plasticizer, and dispersant in the solvent or solven-t blend.
A "premix" is prepared by grinding the thickener and the pigment. Preferably the "premix" is prepared by grinding the thickener and the pigment with about 45% of the "resin solution." The grinding may be accomplished by any suitable apparatus, such as a ball mill, shot mill or sand mill, for example. The ground mixture containing the thickener, pigment and par-t of the "resin solution" should have a ~Iegmann reading of 6.5 or better or a maximum particle size of abaut 19 microns. The final ink composition is prepared by mixing the "premix" containing part of the "resin solution"
with the re~ainder of the "resin solution."
:` As previously described, the thermally activated ink may form a film coating on a substrate or film base to `` provide a thermal transfer ribbon which can be used with, - for example, a thermal printer for producing characters on ordinary paper. The ink is preferably coated at ambient ` 30 temperature of about 25C and at a relative humidity of ~` from about ~5% to about 65~ and dried at about 80C. T~hen coating, for example, a ribbon with the ink composition of .. .
msj ~
~2~13~
the present invention, care should be taken to insure that the ink is cooled ana solidified before the ribbon is wound.
Preferably, the amount of ;nk on the film when the ink is dried is from about 24 oz. of ink per 3000 sq. ft. of film to about 32 oz. weight of ink per 3000 sq. ft. of film.
Thermal printing or generation of characters with the thermally activated ink and transfer ribbon of the present invention requires close contact of the ribbon face to the paper so that during the printing process the melted ink can efficiently flow onto the paper. For best read-ability and contrast, and for efficient transEer of the ink to the surface, a paper that is highly calendared and/or coated with clay and organic binder is recommended.
EX~.PLE 1 Preparation of Thermally Activat d Ink Composition Percent by Percent by Weight Weight (Total) Nonvolatile ~ Components Parts Composition) Components Polymer - Cro~olamid 2261 6.00 14.63 39.45 Gelling Agent - 12-hydroxvstearic acid 1.503.66 9.86 Oil - l-eicosene (laboratory ~rade)3.00 7.32 19.72 Plasticizer - "Benzoflex 9-88 " 1.50 3.66 9.86 Thickener - "Aerosil R-9723"0.02 0.49 1.32 Pigment - "Raven 12554-" 3.~0 7.32 19.72 Dispersant - Kelecin F5 0.01 0.02 0.07 Solvent - 3:1 ~lend of toluene 25.79 62.90 --and isopropyl alcohol lA polyamide resin prepared by reacting tall oil dimer acid with mixtures of linear aliphatic diamines and marketed by the Crosby Chemical Company.
2Dipropylene gylcol dibenzoate marketed by Velsicol Chemical Corp.
The hydrophobic fumed silica marketed by Degussa, Inc., Che~icals Division.
4 Furnace Carbon Black marketed by Cities Service, Columbian Division.
A connerical grade of lecithin marketed by Spencer Kellog Division of Textron, Inc.
--1~--,,~. mS/~
3~
The thermally activated ink composition havin~ the above components was prepared by dissolving "Cropolamid 226,"
12-hydroxystearic acia, l-eicosene, "senzoflex 9-88" and "Kelecin F" in the solvent to form a "resin solution." The "resin solution" was prepared by mixing the components of the "resin solution" at ambient temperature. The "Aerosil R-972" and "Raven 1255" components were ground by ball milling with 17.32 parts of the "resin solution" to form a "premix." The "premix" was ground until it had a Hegmann reading of 6.5 or better, or a maximum particle size of 19 microns or less.
The final ink was prepared by mixing the remaining 20.48 parts of the "resin solution" with the-"premix" at ambient temperature.
A thermally activated transfer ribbon was prepared with the ink composition as formulated in Example 1 by coating the ink composition on 0.45 mil polyethylene copolyme~r film at a relative humidity of from about 45~ to about 65~ and dried in an oven at about 150F. About 28 oz. of ink per 3000 sq. ft. of film was used.
Pre~aration of Thermally Activated Ink Composition Percent by Percent by Weigllt Weight ~Total Nonvolatile Components Parts Co,position) Components Polymer - Cropolamid 226 6.00 12.77 36.98 Gelling A~ent - 12-hydroxystearic acid 1.50 3.19 9.24 Oil - Neodene C-202 3 3.00 6.38 18.48 Plasticizer - "Benzoflex 9-88" 2.50 5.32 15.41 Thickener - "Aerosil R-972"4 , 0.20 0.43 1.23 Pigment - "Raven 1255"56 3.00 6.38 18.48 Dispersant - Kelecin F 0.03 0.06 0.18 Solvent - 3:1 blend of toluene 30.77 65.47 ~-and ispropyl alcohol See Example 1.
~f ms/,~( \~,. . .
~2~3~
2Commercial grade l~eicosene ma~;eted by the Shell Chemical Co.
3 6See Example 1.
A thermally activated ink composition haviny the above ~ormula was prepared aa in Example 1. This ink is also similar to the ink of Example 1 except that a commercial -grade oil was used in this example. Because the commercial grade oil contains a mixture of hydrocarbons lighter and heavier than l-eicosene, this formula contains a grea-ter amount of plasticizer and dispersant for imparting greater stability to the ink composition.
EX~PLE 4 A thermally activated ink composition was prepared as set forth in Example 2 with the following composition: -Percent by Percent by Weight Weight (Total r~onvolatile Component Parts Composition) Cbmponents Polymer ~ "Cropolamid 226" 5.00 10.87 31.80 Cellin~ Agent - 12~hvdroxystearic acid 1.50 3.26 9.54 Oil - "Neodene C-20"2 3 3.00 6.52 19.07 Plasticizer - "Benzoflex 9-88" 2.00 4.35 12.71 mickener - "Aerosil R-972"4 0.20 0.44 1.27 Pig~ent - "Raven 1255"5 6 3.00 6.52 19.07 Dispersant - "Kelecin F" 0.03 0.07 0.19 Solvent - 3:1 blend of toluene30.27 65.80 --and isopropyl alcohol Color toner - Nigrosine Oleate71.00 2.17 6.35 See Example 3 r~arketed by Dye Specialties Co.
A thermally activated ink composition having a blue pigment ~las produced as in Example 2, having the following formula:
ms/~
, 3~.~
Percent by Percent by Weiyh-t Weight (Total Nonvolatile Component Parts Composition Components Poly~.er - "Cropolamid 226" 5.00 10.64 29.90 Gelling Agent - 12-h~droxystearic acid1.50 3.19 8.97 Oil - "Neodene C-20" 3 3.00 6.38 17.94 Plasticizer - "Benzoflex 9-88"2.00 4.26 11.96 Thickener - "Aerosil R-972"4 Ø20 0.43 1.20 Blue Pigment - Hisperse56 4.00 8.51 23.92 Dispersant - "Kelecin" F 0.02 0.04 0.12 Solvent - 3:1 blend of ~oluene30.28 64.42 --and iso~ro~yl alcohol Color Intensifier - flushed 1.00 2.13 5.98 alkali blue7 See Example 3.
5An lron blue pigment marketed by Hercu]es, Inc.
6See Example 3.
Marketed by Sherwin-Williams Co.
While the invention has been described with respect to its preferred embodiments, upon reading the specification it will become apparent that numerous changes, modifications and substitutions can be made and it is intended that they be covered by the invention as set forth in the appended claims. .
msf;, "~
BACKGROU21~ OF THE INVENT ION
Thermal printing, because of its simplici-ty and low-noise level, has potenti~lly many advantayes over exi5ting printing methods as a low-cost and rela-tively noise-free method of printing and generating characters. However, the acceptance of thermal printing has not been rapid because of the need for special paper and the nonpermanence of the heat-sensitive paper that is required for thermal printing.
Therefore, a need exists for a thermally activated ink, transfer ribbon and printing method for generating printed characters on ordinary paper. Present commercialized thermal printing can produce only blue or blue-black dye images of low to moderate darkness and opacity. Therefore, a need also exists for a thermal printing ink and method for producing black images having improved contrast and read-ability qualities. A need further exists for a thermally activated ink and method for producing high-quality, non-smudgeable, permanent characters on ordinary paper which characters are flexible and elastic to avoid flaking.
SUMMARY OF THE INVENTION
A thermally activated ink is provided which can be used, for example, in a thermally activated transfer ribbon or thermally activated typewriter ribbon. In another aspec-t, the present i-nvention provides a method for producing black thermal transfer images having improved contrast and read-ability.
In still another aspect, the invention provides a thermally activated ink and transfer ribbon which is able to ~enerate printed characters on ordinary paper. In another aspect, the invention provides a thermally activated ink and transfer ribbon for producing non-smudying images for permanen-t, ~.' `
..
ms/~
, 3~
high-quality documents.
As used herein, "thermally activated ink" is an ink which is solid or dry at ambient temperatures but which ink is a fluid above about 130F. The thermally activated ink compositions of the present invention have sharp melting points to insure that when generating characters, the ink will set quickly to a non-smudgeable, firm solid. The ink compositions according to the present invention are also slightly flexible and elastic so that flaking of the printed characters is avoided.
One embodiment of the present invention comprises a thermally activated ink comprising a polymer, oil and oil-gelling agent. The polymer has a relatively low molecular weight and a low softening point but is a solid at room temperature. In accordance with the presen-t invention, the gelling agent has a relatively low melting point but is also a solid at room temperature. The oil present in the composition of the present invention serves to lower the softening range of the polymer. Preferably, the oil is also a solid at room temperature but has a melting point less than about 100C.
..
~ ms/~
~2~
According to the present invention, the polymer is a polyamide resin or a styrene-allyl alcohol copolymer, having a molecular weight of from about 1,000 to about 10,000. The preferred gelling agent in the ink composition is 12-hydroxystearic acid and the preferred oil is l-eicosene.
Additional components which are generall~ present in the thermally activated ink compositions of the present invention include plasticizers, thickeners, pigments, dispersants and, optionally, dyes to tone or intensify color and solvents.
In another embodiment of the present invention, the thermally activated ink composition forms a film coating on a substrate or support film. The combination of the substrate and the thermally activated ink composition can be used as a thermally activated transfer ribbon in, for example, a thermal printer or typewriter, or other types of thermal printing devices which employ ribbons to generate characters.
In one specific embodiment the invention provides a thermally activated ink composition for use in generating printed characters on ordinary paper with a thermal printer comprising:
(a) a thermally stable polymer having a molecular weight of from about 1,000 to about 10,000 and a softening point of from about 50C. to about 125C. selected from the group consisting of styrene-allyl alcohol copolymers and polyamide resins and present in an amount of from about 25~
to about 45~ by we`ight of the total nonvolatile ink components;
; (b) an oil-gelling agent having a melting point of from about 40C. to about 100C., being further characterized as a i 30 carboxylic acid having eleven to eighteen carbon atoms and 1 to 2 hydroxy groups, the gelling agent being present in an amount of from about 6~ to about 13~ by weight of the total ink nonvolatile components; and - cb/~
3~
(c) an oil that is a dissolving medium for the polvmer and the gelli~g agent, and present in an amount of from about 12~ to about 26~ by weight of the total nonvolatile components.
-4a-cb/~
3~
DETAILED DESCRIPTION O}~' THE INVENTION
According to the invention, a thermally activated ink composition, thermally activated transfer ribbon and thermally activated transfer method are provided. The thermally activated ink co~m.~ositions of the present invention comprise a synthetic polymer, an oil, and oil-gelling agent, and optionally, a solvent for the polymer and oil. In th~
preferred compositions, specific rheology modifying materials, including plasticizers, thickeners and dispersants, are included to provide improved transfer and adherent characteristics. In addition to the presence~of a suitable pigment, a color toner may also be present in the thermally activated ink compositions of the present invention.
The polymer used in the composition according to the present invention has a relatively low molecular weight and a low softening point but is a solid at room temperature and is thermally stable~ "Thermally stable" as used herein means that the polymer does not decompose between about 10C
and about 180C. The polymer present in the composition of the present invention is either a polyamide resin or a styrene-allyl alcohol copolymer, having a molecular weight of from about 1,000 to about 10,000 and a softening point of from about 50C to about 125C.
The preferred polyamide resins used in the compos.ition : of the present invention have a molecular weight of from about 3,000 to about 5,000 and are prepared by reacting dimerized fatty acids with mixtures of linear aliphati.c diamines. Two specific preferred polyamides are sold by the Crosby Chemical Company of New Orleans, Lousiana, under the trade marks "Cropolamid 226" and "Cropolamid 228", and are ; prepared by reacting tall oil dimer acid with mixtures of linear aliphatic diamines. Cropolamid 226 has a ring-and-ball softening point of from about 95C to about 105C and a mc /
3~
viscosity of about 500 centipoises to about 700 centipoises at 160C. Cropolamid 228 has a ring-and-ball softening point of from about 100C to abou-t llO~C and a viscosity of from about 500 centipoises to about 700 centipoises. Another specific preferred polyamide is sold by Victor Wolf Limited of Calyton, Manchester, in Great Britain, under the trade mark "Wolfamid 8W", and is prepared by reacting dimerized vegetable oil fatty acids with a mixture of linear aliphatic . diamines. Wolfamid 8W has a ring-and-ball softening point '`' 10 of from about 95C to about 105C and a viscosity of from about 300 centipoises to about 800 centipoises at 160~C.
The preferred styrene-allyl alcohol copolymer for ; use in the composition according to the present invention has a number-average molecular weight of about 1,600, a hydroxyl content of from about 5.4% to about 6.0% and a Durran softening point of from about 100C to about 110C. This component can be obtained commercially from Mbnsanto Industrial Chemicals Company,of St. Louis, Missouri, under the trade mark "RJ-100". The preferred styrene-allyl copolymer may also be obtained from Aldrich Chemical Company, Inc.,of Milwaukee, Wisconsin. Another commerical styrene-ally aleohol copolymer which can be used in the composition of the present invention has a number-average molecular weigh-t of 1,150 and a hydroxyl content of from about 7.4% to about 8.0%, sold by Monsanto Industrial Chemicals Company of St. Louis, Missouri, under the trade mark "RH-101". However, this copolymer is less satisfactory than the other two preferred styrene-allyl alcohol copolymers because i-t imparts more brittleness to the ink formulation than is ~, usually desired.
The polymer in the ink composition of the present invention is present in an amount oE from about 25% to about ' 45% by weight of the total nonvolatile components and is preEerably present in an amount of about 31.8% by weight of ~/ms 3~
the tot~l ink nonvolatile components, ~s used herein, non-volatile ink components include all ink components as set forth in this d~escription excep-t for the solvent.
The oil present in the composi-tion of the present invention is preferably a solid at ambient temperature. The melting point of the oil is preferably between 25C and less than about 100C. The preferred oil for use in the co~position of the invention is l-eicosene which has a melting point of about 30~C. l-Eicosene is sold in an industrial grade under the trade mark C-20 Alpha Olefin by the Gulf Oil Chemicals Company of Houston, Texas, and also under the trade mark Neodene C-20 by the Shell Chemlcal Company of Houston, Texas.
Other oils which can be used in the composition of the present invention include mineral oil, or the like. Still other oils which can be used in the composition of the present invention are sold by the Shell Chemical Company of Houston, Texas under the trade marks Neodene C-18 and Neodene C-16, both of which are liquid at ambient temperature. Oils which are a solid at ambient temperature are preferred because these oils have less tendency to separate from the other components in the composition and, therefore, compositions according to the invention that contain an oil which is a solid at room temperature will usually have a longer shelf life. According to the invention, the oil is present in the ink composition in an amount of from about 12% to about 26% and preferably the oil is present in an amount of about 19.1% by weight of the total ink nonvolatile. The oil present in the ink composition is a "dissolving medium" for both the polymer and gelling agent, hereinafter described~ As used herein, "dissolving medium" means a component which is capable of ; forming a homogeneous mixture with other components, specifically the polymer and gelling agent.
\~ ms/~
3~
me gellinq agent present in hhe ink co~position of the present invention is a long chain hydrocarbon containing two or more polar groups (-OH, -CO2H). In addition, the gelling agent should be a solid at room temperature and have a relatively low melting point, preferably from abou-t 40C to about 100C, and should be a solid at room temperature. The gelling agent is present in the composition of the present invention in an amount of from about 6% to about 13% and preferably in an amount of about 9.5% by weight of the total ink nonvolatile components. The preferred gelling agent is 12-llydroxystearic acid. 12-hydroxystearic acid is a C18 straight chain fatty acid with an -OH group attached to the hydrocarbon chain, having a melting point of from about 79C
to about 82C. Other gelling agents which may be used in the composition of the present invention include: 11-hydroxypalmitic a¢id; ~-hydroxylauric acid; ll-hydro-xyundecanoic acid; 2-hydroxytetradecanoic acid; 15 hydro-xypentadecanoic acid; 2-hydroxyhexadecanoic acid; 16-hydroxyhexadecanoic acid; 2-hydroxydodecanoic acid; 9,11-dihydroxyundecanoic acid; 3,11-dihydroxytetradecanoic acid;
ll-hydroxytetradecanoic acid; 16-hydroxypalmitic acid;
14-hydroxypalmitic acid 2-hydroxypalmitic acid; and combinations thereof. The presence of the gelling agent in the thermally activated ink composition of the present invention serves to lower the melting point of the polymer ~;
and improve the compati~ility of the oil and polymer.
Preferably, the thermally activated ink composition of the present invention includes a plasticizer which is present in an amount of from about 9% to about 16% by weight of the total ink nonvolatile components and preferably about ; 12.7 by weight of the total ink nonvolatile components. The plasticizer serves to increase the flexibility and transfer-' ' _ ~_ ms/~
~z~
ability of the ink oomposi~ion. The plasticizer should be capable of plasticizing the polymer to increase its adhesion when applied to a substrate or backing, as will be herein-after described in greater de-tail. The plas-ticizer also serves, in combination with the oil, to lower the softening point of the polymer and gelling agent. According to the present invention, the preferred plasticizer is dipropylene glycol dibenzoate. Dipropylene glycol dibenzoate is sold under the trade mark Benzoflex 9-88 by the Velsicol Chemical of Chicago, Illinois. Also, for thermally activating ink compositions based on the polyamide resins, a mixture of N-ethyl-ortho-toluene suflonamides and N-ethyl-para-toluene sufonamides is suitable for use as a plasticizer and is sold under the trade mark of "Santicizer 8" by Monsanto Industrial Chemicals Company of St. Louis, Missouri. For thermally activated ink compositions based on a styrene-allyl alcohol copolymer, dioctyl phthalate or benzyl butyl phthalate may be used as the plasticizer of the compositi~on.
The composition of the present invention may optionally include a solvent for the polymer and gelling agent.
The preferred solvent for the ink composition containing a polyamide resin is a combination of toluene and isoprpyl alcohol in a ratio of toluene to iso~roPvl alcohol of 3:1.
For an ink composition containing a styrene-allyl alcohol copolymer, the preferred solvent is toluene. The solvent should be present in an amount of from about 50% to about 85%
i~ by weight of the total ink composition and is preferably present in an amount of from 65~ y weight of the total ink : composition.
~ The primary purpose of the solvent in the ink composition of the present invention is to facilitate coating ` the compositions on a film base or substrate. ~ significant - _9_ . ms/ Q~-~
. ; ~ , , , . ,. . . , .; ~, , . . . . . . ., .~
~2~3~L~
advantage of the ink composition described is that it can be ground and coated onto a film base while elther dissolved in solvent, or without solvent while molten. The use of solvent is advantageous when low viscosities and thin, uniform coatings, less than 0.0002 inch, are desired, Hot-melt grinding and coating are sometimes advantageous for reasons of economy and to avoid the flammability and vapor emissions of organic solvents. When the ink is applied as a ho~-melt, the ink is formulated without a solvent and is heated to a temperature in excess of its melting point so that the ink is in fluid form when applying it to a substrate.
To obtain the desired rheological properties, a thickener is also present in the ink composition of the present invention~ The thickener preferably comprises hydrophobic fumed silica or fumed silica and has a particle size when present in the final ink composition of about 19 microns or less or a Hegmann reading of 6.5 or better. One suitable thickener is a hydrophobic fumed silica sold under the trade mark "Aerosil R-972" by Degussa, Inc., Chemicals Division, of New York, New York. One specific fumed silica suitable for use as a thickener according to the present inven-tion is sold under the trade mark "Cab-O-Sil" by the Cabot Corporation of Boston, Massachussetts. The thickener should be present in an a~ount of from about 1% to about 3%
by weight of the total ink nonvolatile components and is preferably present in an amount of about 1.3% by weight of ` the total ink nonvolatile components.
In order to facilitate pigment we-tting and grinding, and to improve the flow of melted ink from, for example, a substrate to paper, a dispersant is preferably present in the composition of the present invention. One suitable dispersant is lecithin. One commerical grade of lecithin which can be ~ .~
~ .
,`. -10-ms/'`~
used in accoxdance ~ith the composition of the present invention is sold by the Spencer Kellog Division of Textron, Inc. of Buffalo, New York under the trade mark "Kelecin F."
The dispersant should be present in the ink composition according to the invention in an amount of from about 0.1%
to about 0.2% and is preferably present in an amount of about 0.19~ by weight of the total ink nonvolatile components.
When a commerical grade oil is used, such as "Neodene C-20", "Neodene C-18", "Neodene C-16" or "C-20" Alpha Olefin, generally the oil will contain a small percentage of heavier and lighter hydrocarbons. Because of this, it is often advantageous to include in the ink composition a slightly greater amoun-t of the plasticizer than would be used in an ink composition containing a laboratory grade oil for improved adhesion, transferability and compatability of the ink composition.
, In order to provide the desired ink color, a pigment is present in an amount of from about 15~ to about 25% by weight of the total ink nonvolatile components and preferably is present in an amount of about 19.1% by weight of the total ink nonvolatile components. The ink composition of the ~` present invention allows the use of carbon black as a pigment.
" Preferred pigments include furnace carbon black, alkali blue and iron blue. One preferred type of carbon black is sold by the Cabot Corporation of Boston, Massachussetts, under the trade mark "Mogul L." Another preferred type of furnace carbon black for use as a pigment in the composition of the present invention is sold by the Cities Service, CQlumbian Division of Akron, Ohio under the trade mark "Raven 1255."
Suitable types of blue pigments include, for example, iron blue sold by Hercules Inc. of Wilmington,~Delaware, under the ` trade mark "Hisperse X-3434" and a suitable alkali blue :~, ' \', ms/' pigment is sold by $herwin Williams Chemicals of Cleveland~
Ohio, under the trade mar~ "Powdura Blue CP."
The thermally activated ink composition of the present invention may optionally include a dye as a color toner or intensifier. Typical color toners which may be used in accordance with the composition of the present invention include, for example, Nigrosine Oleate marketed by Dye Specialties of Secaucus, Ne~ Jersey, Flushed Alkali Blue FL-14511 marketed by Sherwin Willlams Co., Cleveland, Ohio, and Methyl Violet Oleate 2:1 marketed by Dye Specialties Co.
of Secaucus, New Jersey.
In one embodiment of the present invention, the thermally activated ink composition forms a thin coating on one side of a substrate or support film, such as a ribbon, for example. In this manner, the thermally activated ink composition of the present invention can be used, for example, in conjunction with a thermal printed head for generating printed characters upon ordinary paper.
The substrate or support film may be constructed ` 20 of polyester, polyethylene, polypropylene, polyvinylchloride or other suitable materials. Since the ink and substrate combination according to -the present invention is suitable for use in conjunction with a thermal print head for generating characters, it is desirable that the substr!ate have minimal thickness to facilitate heat transfer from the thermal print head through the substrate and to the thermally activated ink com~osition forming a coating on the subs~ate and adjacent the paper or sur~o~ upon which is desired to ~:. generate characters. Preferably, the substate or supporting film has a thickness of from about 0.12 mil to about 0.75 mil.
For practical use, the substrate must possess sufficient tensile strength so that failure of the substate or ribbon .'. .
ms/~'i 3~l~
is minimizedO ~ pxefe~red substrate or support film is sold under the trade marks "Phil~o 308" and "PJX 2074" sold by the Phillips Joanna Company of Ladd, Illinois. Preferably the Philjo 308 has a thickness of about 0.45 mil. In addition, high density polyethylene, tensilized polyethylene tere~hthalate and non-tensilized polye-thylene terephthalate are also suitable for use as the substrate or support film according to the present invention.
According to the present invention, the -thermally activated ink compositions are preferably manufactured according to the following method. First, a "resin solution"
is prepared by dissolving the polymer, gelling agent, oil, plasticizer, and dispersant in the solvent or solven-t blend.
A "premix" is prepared by grinding the thickener and the pigment. Preferably the "premix" is prepared by grinding the thickener and the pigment with about 45% of the "resin solution." The grinding may be accomplished by any suitable apparatus, such as a ball mill, shot mill or sand mill, for example. The ground mixture containing the thickener, pigment and par-t of the "resin solution" should have a ~Iegmann reading of 6.5 or better or a maximum particle size of abaut 19 microns. The final ink composition is prepared by mixing the "premix" containing part of the "resin solution"
with the re~ainder of the "resin solution."
:` As previously described, the thermally activated ink may form a film coating on a substrate or film base to `` provide a thermal transfer ribbon which can be used with, - for example, a thermal printer for producing characters on ordinary paper. The ink is preferably coated at ambient ` 30 temperature of about 25C and at a relative humidity of ~` from about ~5% to about 65~ and dried at about 80C. T~hen coating, for example, a ribbon with the ink composition of .. .
msj ~
~2~13~
the present invention, care should be taken to insure that the ink is cooled ana solidified before the ribbon is wound.
Preferably, the amount of ;nk on the film when the ink is dried is from about 24 oz. of ink per 3000 sq. ft. of film to about 32 oz. weight of ink per 3000 sq. ft. of film.
Thermal printing or generation of characters with the thermally activated ink and transfer ribbon of the present invention requires close contact of the ribbon face to the paper so that during the printing process the melted ink can efficiently flow onto the paper. For best read-ability and contrast, and for efficient transEer of the ink to the surface, a paper that is highly calendared and/or coated with clay and organic binder is recommended.
EX~.PLE 1 Preparation of Thermally Activat d Ink Composition Percent by Percent by Weight Weight (Total) Nonvolatile ~ Components Parts Composition) Components Polymer - Cro~olamid 2261 6.00 14.63 39.45 Gelling Agent - 12-hydroxvstearic acid 1.503.66 9.86 Oil - l-eicosene (laboratory ~rade)3.00 7.32 19.72 Plasticizer - "Benzoflex 9-88 " 1.50 3.66 9.86 Thickener - "Aerosil R-9723"0.02 0.49 1.32 Pigment - "Raven 12554-" 3.~0 7.32 19.72 Dispersant - Kelecin F5 0.01 0.02 0.07 Solvent - 3:1 ~lend of toluene 25.79 62.90 --and isopropyl alcohol lA polyamide resin prepared by reacting tall oil dimer acid with mixtures of linear aliphatic diamines and marketed by the Crosby Chemical Company.
2Dipropylene gylcol dibenzoate marketed by Velsicol Chemical Corp.
The hydrophobic fumed silica marketed by Degussa, Inc., Che~icals Division.
4 Furnace Carbon Black marketed by Cities Service, Columbian Division.
A connerical grade of lecithin marketed by Spencer Kellog Division of Textron, Inc.
--1~--,,~. mS/~
3~
The thermally activated ink composition havin~ the above components was prepared by dissolving "Cropolamid 226,"
12-hydroxystearic acia, l-eicosene, "senzoflex 9-88" and "Kelecin F" in the solvent to form a "resin solution." The "resin solution" was prepared by mixing the components of the "resin solution" at ambient temperature. The "Aerosil R-972" and "Raven 1255" components were ground by ball milling with 17.32 parts of the "resin solution" to form a "premix." The "premix" was ground until it had a Hegmann reading of 6.5 or better, or a maximum particle size of 19 microns or less.
The final ink was prepared by mixing the remaining 20.48 parts of the "resin solution" with the-"premix" at ambient temperature.
A thermally activated transfer ribbon was prepared with the ink composition as formulated in Example 1 by coating the ink composition on 0.45 mil polyethylene copolyme~r film at a relative humidity of from about 45~ to about 65~ and dried in an oven at about 150F. About 28 oz. of ink per 3000 sq. ft. of film was used.
Pre~aration of Thermally Activated Ink Composition Percent by Percent by Weigllt Weight ~Total Nonvolatile Components Parts Co,position) Components Polymer - Cropolamid 226 6.00 12.77 36.98 Gelling A~ent - 12-hydroxystearic acid 1.50 3.19 9.24 Oil - Neodene C-202 3 3.00 6.38 18.48 Plasticizer - "Benzoflex 9-88" 2.50 5.32 15.41 Thickener - "Aerosil R-972"4 , 0.20 0.43 1.23 Pigment - "Raven 1255"56 3.00 6.38 18.48 Dispersant - Kelecin F 0.03 0.06 0.18 Solvent - 3:1 blend of toluene 30.77 65.47 ~-and ispropyl alcohol See Example 1.
~f ms/,~( \~,. . .
~2~3~
2Commercial grade l~eicosene ma~;eted by the Shell Chemical Co.
3 6See Example 1.
A thermally activated ink composition haviny the above ~ormula was prepared aa in Example 1. This ink is also similar to the ink of Example 1 except that a commercial -grade oil was used in this example. Because the commercial grade oil contains a mixture of hydrocarbons lighter and heavier than l-eicosene, this formula contains a grea-ter amount of plasticizer and dispersant for imparting greater stability to the ink composition.
EX~PLE 4 A thermally activated ink composition was prepared as set forth in Example 2 with the following composition: -Percent by Percent by Weight Weight (Total r~onvolatile Component Parts Composition) Cbmponents Polymer ~ "Cropolamid 226" 5.00 10.87 31.80 Cellin~ Agent - 12~hvdroxystearic acid 1.50 3.26 9.54 Oil - "Neodene C-20"2 3 3.00 6.52 19.07 Plasticizer - "Benzoflex 9-88" 2.00 4.35 12.71 mickener - "Aerosil R-972"4 0.20 0.44 1.27 Pig~ent - "Raven 1255"5 6 3.00 6.52 19.07 Dispersant - "Kelecin F" 0.03 0.07 0.19 Solvent - 3:1 blend of toluene30.27 65.80 --and isopropyl alcohol Color toner - Nigrosine Oleate71.00 2.17 6.35 See Example 3 r~arketed by Dye Specialties Co.
A thermally activated ink composition having a blue pigment ~las produced as in Example 2, having the following formula:
ms/~
, 3~.~
Percent by Percent by Weiyh-t Weight (Total Nonvolatile Component Parts Composition Components Poly~.er - "Cropolamid 226" 5.00 10.64 29.90 Gelling Agent - 12-h~droxystearic acid1.50 3.19 8.97 Oil - "Neodene C-20" 3 3.00 6.38 17.94 Plasticizer - "Benzoflex 9-88"2.00 4.26 11.96 Thickener - "Aerosil R-972"4 Ø20 0.43 1.20 Blue Pigment - Hisperse56 4.00 8.51 23.92 Dispersant - "Kelecin" F 0.02 0.04 0.12 Solvent - 3:1 blend of ~oluene30.28 64.42 --and iso~ro~yl alcohol Color Intensifier - flushed 1.00 2.13 5.98 alkali blue7 See Example 3.
5An lron blue pigment marketed by Hercu]es, Inc.
6See Example 3.
Marketed by Sherwin-Williams Co.
While the invention has been described with respect to its preferred embodiments, upon reading the specification it will become apparent that numerous changes, modifications and substitutions can be made and it is intended that they be covered by the invention as set forth in the appended claims. .
msf;, "~
Claims (41)
PROPERTY OR PRIVILEGE IS CLAIMED ARE DEFINED AS FOLLOWS:
1. A thermally activated ink composition for use in generating printed characters on ordinary paper with a thermal printer comprising:
(a) a thermally stable polymer having a molecular weight of from about 1,000 to about 10,000 and a softening point of from about 50°C. to about 125°C. selected from the group consisting of styrene-allyl alcohol copolymers and polyamide resins and present in an amount of from about 25%
to about 45% by weight of the total nonvolatile ink components;
(b) an oil-gelling agent having a melting point of from about 40°C. to about 100°C., being further characterized as a carboxylic acid having eleven to eighteen carbon atoms and 1 to 2 hydroxy groups, said gelling agent being present in an amount of from about 6% to about 13% by weight of the total ink nonvolatile components; and (c) an oil that is a dissolving medium for said polymer and said gelling agent, and present in an amount of from about 12% to about 26% by weight of the total nonvolatile components.
(a) a thermally stable polymer having a molecular weight of from about 1,000 to about 10,000 and a softening point of from about 50°C. to about 125°C. selected from the group consisting of styrene-allyl alcohol copolymers and polyamide resins and present in an amount of from about 25%
to about 45% by weight of the total nonvolatile ink components;
(b) an oil-gelling agent having a melting point of from about 40°C. to about 100°C., being further characterized as a carboxylic acid having eleven to eighteen carbon atoms and 1 to 2 hydroxy groups, said gelling agent being present in an amount of from about 6% to about 13% by weight of the total ink nonvolatile components; and (c) an oil that is a dissolving medium for said polymer and said gelling agent, and present in an amount of from about 12% to about 26% by weight of the total nonvolatile components.
2. The thermally activated ink composition as recited in claim 1 wherein said polymer has a molecular weight of from about 3,000 to about 5,000.
3. The thermally activated ink composition as recited in claim 2 wherein said polymer is selected from the group consisting of: polyamide resins prepared from reacting tall oil dimer acid with mixtures of linear aliphatic diamines; polyamide resins prepared from reacting dimerized vegetable oil fatty acids with mixtures of linear aliphatic diamines; and styrene-allyl alcohol copolymers.
4. The ink composition as recited in claim 1 wherein said polymer is a styrene-allyl alcohol copolymer having a molecular weight of about 1,600, a hydroxyl content of from about 5.4% to about 6.0% and a softening range of from about 100°C. to about 110°C.
5. The ink composition as recited in claim 2 wherein said polymer is prepared from reacting tall oil dimer acid with mixtures of linear aliphatic diamines and has a ring-and-ball softening point of from about 95°C. to about 105°C. and a viscosity of from about 500 centipoises to about 700 centipoises at 160°C.
6. The ink composition as recited in claim 2 wherein said polymer is a polyamide resin prepared from reacting dimerized vegetable oil fatty acids with mixtures of linear aliphatic diamines and has a ring-and-ball softening point of from about 95°C. to about 105°C. and a viscosity of from about 300 centipoises to about 800 centipoises at 160°C.
7. The ink composition as recited in claim 4, 5 or 6 wherein said polymer is present in an amount of about 31.8% by weight of the total ink nonvolatile components.
8. The thermally activated ink composition as recited in claim 1, 2 or 3 wherein said gelling agent is selected from the group consisting of 12-hydroxystearic acid, 11-hydroxypalmitic acid, .omega.-hydroxylauric acid, 11-hydroxyundecanoic acid, 2-hydroxytetradecanoic acid, 15-hydroxypentadecanoic acid, 2-hydroxyhexadecanoic acid, 16-hydroxyhexadecanoic acid, 2-hydroxydodecanoic acid, 9,10-dihydroxyundecanoic acid, 3,11-dihydroxytetradecanoic acid, 11-hydroxytetradecanoic acid, 16-hydroxypalmitic acid, 14-hydroxypalmitic acid, 2-hydroxypalmitic acid and combinations thereof.
9. The thermally activated ink composition as recited in claim 1, 2 or 3 wherein said gelling agent is 12-hydroxystearic acid present in an amount of about 9.5% by weight of the,total ink nonvolatile components.
10. The thermally activated ink composition as recited in claim 1, 2 or 3 wherein said oil is a long chain hydrocarbon and has a melting point of from about 25°C. to about 100°C.
11. The thermally activated ink composition as recited in claim 1, 2 or 3 wherein:
(a) said oil is 1-eicosene; and (b) said gelling agent is selected from the group con-sisting of 12-hydroxystearic acid, 11-hydroxypalmitic acid, .omega.-hydroxylauric acid, 11-hydroxyundecanoic acid, 2-hydroxy-tetradecanoic acid, 15-hydroxypentadecanoic acid, 2-hydroxy-hexadecanoic acid, 16-hydroxyhexadecanoic acid, 2-hydroxydodecanoic acid, 9,10-dihydroxyundecanoic acid, 3,11-dihydroxytetradecanoic acid, 11-hydroxytetradecanoic acid, 16-hydroxypalmitie acid, 14-hydroxypalmitie acid, 2-hydroxypalmitic acid and combinations thereof.
(a) said oil is 1-eicosene; and (b) said gelling agent is selected from the group con-sisting of 12-hydroxystearic acid, 11-hydroxypalmitic acid, .omega.-hydroxylauric acid, 11-hydroxyundecanoic acid, 2-hydroxy-tetradecanoic acid, 15-hydroxypentadecanoic acid, 2-hydroxy-hexadecanoic acid, 16-hydroxyhexadecanoic acid, 2-hydroxydodecanoic acid, 9,10-dihydroxyundecanoic acid, 3,11-dihydroxytetradecanoic acid, 11-hydroxytetradecanoic acid, 16-hydroxypalmitie acid, 14-hydroxypalmitie acid, 2-hydroxypalmitic acid and combinations thereof.
12. The thermally activated ink composition as recited in claim 1 wherein:
(a) said gelling agent is selected from the group consisting of 12-hydroxystearic acid, ll-hydroxypalmitie aeid, .omega.-hydroxylauric acid, 11-hydroxyundecanoic acid, 2-hydroxy-tetradecanoic acid, 15-hydroxypentadecanoic acid, 2-hydroxy-hexadecanoic acid, 16-hydroxyhexadecanoic acid, 2-hydroxy-dodecanoic acid, 9,10-dihydroxyundecanoic acid, 3,11-dihydroxytetradecanoic acid, 11-hydroxytetradecanoic acid, 16-hydroxypalmitie acid, 14-hydroxypalmitie acid, 2-hydroxy-palmitie acid and combinations thereof; and (b) said oil is selected from the group consisting of l-eicosene and mineral oil.
(a) said gelling agent is selected from the group consisting of 12-hydroxystearic acid, ll-hydroxypalmitie aeid, .omega.-hydroxylauric acid, 11-hydroxyundecanoic acid, 2-hydroxy-tetradecanoic acid, 15-hydroxypentadecanoic acid, 2-hydroxy-hexadecanoic acid, 16-hydroxyhexadecanoic acid, 2-hydroxy-dodecanoic acid, 9,10-dihydroxyundecanoic acid, 3,11-dihydroxytetradecanoic acid, 11-hydroxytetradecanoic acid, 16-hydroxypalmitie acid, 14-hydroxypalmitie acid, 2-hydroxy-palmitie acid and combinations thereof; and (b) said oil is selected from the group consisting of l-eicosene and mineral oil.
13. The thermally activated ink composition as recited in claim 12 further comprising:
(a) a plasticizer present in an amount of from about 9% to about 16% by weight of the total ink nonvolatile components;
(b) a thickener present in an amount of from about 1% to about 3% by weight of the total ink nonvolatile components;
(c) a dispersant present in an amount of from about 0.1% to about 0.2% by weight of the total ink nonvolatile components; and (d) a pigment present in an amount of from about 15%
to about 25% by weight of the total ink nonvolatile components.
(a) a plasticizer present in an amount of from about 9% to about 16% by weight of the total ink nonvolatile components;
(b) a thickener present in an amount of from about 1% to about 3% by weight of the total ink nonvolatile components;
(c) a dispersant present in an amount of from about 0.1% to about 0.2% by weight of the total ink nonvolatile components; and (d) a pigment present in an amount of from about 15%
to about 25% by weight of the total ink nonvolatile components.
14. The ink composition as recited in claim 13 wherein:
(a) said thickener is selected from the group consisting of fumed silica and hydrophobic fumed silica;
(b) said dispersant is lecithin; and (c) said pigment is selected from the group consisting of carbon black alkali blue and iron blue.
(a) said thickener is selected from the group consisting of fumed silica and hydrophobic fumed silica;
(b) said dispersant is lecithin; and (c) said pigment is selected from the group consisting of carbon black alkali blue and iron blue.
15. The ink composition as recited in claim 13 further comprising a color toner.
16. The thermally activated ink composition as recited in claim 13, 14 or 15 wherein said composition forms a film on a substrate, said substrate being suitable for use in conjunction with a thermal print head for generating and transferring characters from the substrate to a surface.
17. The ink composition as recited in claim 13 wherein said polymer is a polyamide resin and said ink composition further comprises a solvent for the polymer, said solvent being present in an amount of from about 50% to about 85% by weight of the total ink composition.
18. The ink composition as recited in claim 17 wherein said solvent is a combination of toluene and isopropyl alcohol, said toluene and isopropyl alcohol being present in a ratio of toluene to isopropyl alcohol of about 3:1.
19. The ink composition as recited in claim 13 wherein said polymer is a styrene-allyl alcohol copolymer, said plasticizer is selected from the group consisting of dioctyl phthalate and benzyl butyl phthalate and said ink composition further comprises a solvent for the polymer, said solvent being present in an amount of from about 50% to about 85% by weight of the total ink composition.
20. A thermally activated transfer ribbon for generating printed characters on ordinary paper comprising:
(a) a substrate; and (b) a thermally activated ink composition forming a film on one side of said substrate, said ink composition comprising a thermally stable polymer having a molecular weight of from about 1,000 to about 10,000 and a softening point of from about 50°C. to about 125°C. selected from the group consisting of styrene-allyl alcohol copolymers and polyamide resins and present in an amount of from about 25%
to about 45% by weight of the total nonvolatile ink components, a gelling agent having a melting point of from about 40°C. to about 100°C., said gelling agent being further characterized as a carboxylic acid having eleven to eighteen carbon atoms and 1 to 2 hydroxy groups and present in an amount from about 6% to about 13% by weight of the total nonvolatile ink com-ponents and an oil that is a dissolving medium for said polymer and said gelling agent said oil present in an amount of from about 12% to about 26% by weight of the total nonvolatile ink components.
(a) a substrate; and (b) a thermally activated ink composition forming a film on one side of said substrate, said ink composition comprising a thermally stable polymer having a molecular weight of from about 1,000 to about 10,000 and a softening point of from about 50°C. to about 125°C. selected from the group consisting of styrene-allyl alcohol copolymers and polyamide resins and present in an amount of from about 25%
to about 45% by weight of the total nonvolatile ink components, a gelling agent having a melting point of from about 40°C. to about 100°C., said gelling agent being further characterized as a carboxylic acid having eleven to eighteen carbon atoms and 1 to 2 hydroxy groups and present in an amount from about 6% to about 13% by weight of the total nonvolatile ink com-ponents and an oil that is a dissolving medium for said polymer and said gelling agent said oil present in an amount of from about 12% to about 26% by weight of the total nonvolatile ink components.
21. The thermally activated transfer ribbon as recited in claim 20 wherein said polymer has a molecular weight of from about 3,000 to about 5,000.
22. The thermally activated transfer ribbon as recited in claim 21 wherein said polymer is selected from the group consisting of: polyamide resins prepared from reacting tall oil dimer acid with mixtures of linear aliphatic diamines;
polyamide resins prepared from reacting dimerized vegetable oil fatty acids with mixtures of linear aliphatic diamines and styrene-allyl alcohol copolymers.
polyamide resins prepared from reacting dimerized vegetable oil fatty acids with mixtures of linear aliphatic diamines and styrene-allyl alcohol copolymers.
23. The thermally activated transfer ribbon as recited in claim 20 wherein said polymer is a styrene-allyl alcohol copolymer having a molecular weight of from about 1,600, a hydroxyl content of from about 5.4% to about 6.0%
and a softening range of from about 100°C. to about 110°C.
and a softening range of from about 100°C. to about 110°C.
24. The thermally activated transfer ribbon as recited in claim 20 wherein said polymer is prepared from reacting tall oil dimer acid with mixtures of linear aliphatic diamines and has a ring-and-ball softening point of from about 95°C. to about 105°C. and a viscosity of from about 500 centipoises to about 700 centipoises at 160°C.
25. The thermally activated transfer ribbon as recited in claim 20 wherein said polymer is a polyamide resin prepared from reacting dimerized vegetable oil fatty acids with mixtures of linear aliphatic-diamines and has a ring-and-ball softening point of from about 100°C. to about 110°C.
and has a viscosity of from about 500 centipoises to about 700 centipoises at 160°C.
and has a viscosity of from about 500 centipoises to about 700 centipoises at 160°C.
26. The thermally activated transfer ribbon as recited in claim 23, 24 or 25 wherein said polymer is present in an amount of about 31.8% by weight of the total ink nonvolatile components.
27. The thermally activated transfer ribbon as recited in claim 20, 21 or 22 wherein said gelling agent is selected from the group consisting of 12-hydroxystearic acid, 11-hydroxypalmitic acid, .omega.-hydroxylauric acid, 15-hydroxy-pentadecanoic acid, 2-hydroxyhexadecanoic acid, 16-hydroxy-hexadecanoic acid, 2-hydroxydodecanoic acid, 9,10-dihydroxy-undecanoic acid, 3,11-dihydroxytetradecanoic acid, 11-hydroxytetradecanoic acid, 16-hydroxypalmitic acid, 14-hydroxypalmitic acid, 2-hydroxypalmitic acid and combinations thereof.
28. The thermally activated transfer ribbon as recited in claim 20, 21 or 22 wherein said gelling agent is 12-hydroxystearic acid present in said ink composition in an amount of about 9.5% by weight of the total ink nonvolatile components.
29. The thermally activated transfer ribbon as recited in claim 20, 21 or 22 wherein said oil is a long chain hydrocarbon and has a melting point of from about 25°C.
to about 100°C.
to about 100°C.
30. The thermally activated transfer ribbon as recited in claim 20, 21 or 22 wherein:
(a) said oil is 1-eicosene; and (b) said gelling agent is selected from the group consisting of 12-hydroxystearic acid, 11-hydroxypalmitic acid, .omega.-hydroxylauric acid, 11-hydroxyundecanoic acid, 2-hydroxy-tetradecanoic acid, 15-hydroxypentadecanoic acid, 2-hydroxy-hexadecanoic acid, 16-hydroxyhexadecanoic acid, 2-hydroxy-dodecanoic acid, 9,10-dihydroxyundecanoic acid, 3,11-dihydroxytetradecanoic acid, 11-hydroxytetradecanoic acid, 16-hydroxypalmitic acid, 14-hydroxypalmitic acid, 2-hydroxy-palmitic acid and combinations thereof.
(a) said oil is 1-eicosene; and (b) said gelling agent is selected from the group consisting of 12-hydroxystearic acid, 11-hydroxypalmitic acid, .omega.-hydroxylauric acid, 11-hydroxyundecanoic acid, 2-hydroxy-tetradecanoic acid, 15-hydroxypentadecanoic acid, 2-hydroxy-hexadecanoic acid, 16-hydroxyhexadecanoic acid, 2-hydroxy-dodecanoic acid, 9,10-dihydroxyundecanoic acid, 3,11-dihydroxytetradecanoic acid, 11-hydroxytetradecanoic acid, 16-hydroxypalmitic acid, 14-hydroxypalmitic acid, 2-hydroxy-palmitic acid and combinations thereof.
31. The thermally activated transfer ribbon as recited in claim 20 wherein:
(a) said gelling agent is selected from the group consisting of 12-hydroxystearic acid, 11-hydroxypalmitic acid, .omega.-hydroxylauric acid, 11-hydroxyundecanoic acid, 2-hydroxytetradecanoic acid, 15-hydroxypentadecanoic acid, 2-hydroxyhexadecanoic acid, 16-hydroxyhexadecanoic acid, 2-hydroxydodecanoic acid, 9,10-dihydroxyundecanoic acid, 3,11-dihydroxytetradecanoic acid, 11-hydroxytetradecanoic acid, 16-hydroxypalmitic acid, 14-hydroxypalmitic acid, 2-hydroxypalmitic acid and combinations thereof; and (b) said oil is selected from the group consisting of 1-eicosene and mineral oil.
(a) said gelling agent is selected from the group consisting of 12-hydroxystearic acid, 11-hydroxypalmitic acid, .omega.-hydroxylauric acid, 11-hydroxyundecanoic acid, 2-hydroxytetradecanoic acid, 15-hydroxypentadecanoic acid, 2-hydroxyhexadecanoic acid, 16-hydroxyhexadecanoic acid, 2-hydroxydodecanoic acid, 9,10-dihydroxyundecanoic acid, 3,11-dihydroxytetradecanoic acid, 11-hydroxytetradecanoic acid, 16-hydroxypalmitic acid, 14-hydroxypalmitic acid, 2-hydroxypalmitic acid and combinations thereof; and (b) said oil is selected from the group consisting of 1-eicosene and mineral oil.
32. The thermally activated transfer ribbon as recited in claim 20, said ink composition further comprising:
(a) a plasticizer present in an amount of from about 9% to about 16% by weight of the total ink nonvolatile components;
(b) a thickener present in an amount of from about 1%
to about 3% by weight of the total ink nonvolatile components;
(c) a dispersant present in an amount of from about 0.1% to about 0.2% by weight of the total ink nonvolatile components; and (d) a pigment present in an amount of from about 15%
to about 25% by weight of the total ink nonvolatile components.
(a) a plasticizer present in an amount of from about 9% to about 16% by weight of the total ink nonvolatile components;
(b) a thickener present in an amount of from about 1%
to about 3% by weight of the total ink nonvolatile components;
(c) a dispersant present in an amount of from about 0.1% to about 0.2% by weight of the total ink nonvolatile components; and (d) a pigment present in an amount of from about 15%
to about 25% by weight of the total ink nonvolatile components.
33. The thermally activated transfer ribbon as recited in claim 31 wherein said polymer is a polyamide resin.
34. The thermally activated transfer ribbon as recited in claim 32 wherein said ink composition is applied to said substrate utilizing a solvent for the polymer, said solvent being present in an amount of from about 50% to about 85% by weight of the total ink composition.
35. The thermally activated transfer ribbon as recited in claim 34 wherein said solvent is a combination of toluene and isopropyl alcohol, said toluene and isopropyl alcohol being present in a ratio of toluene to isopropyl alcohol of about 3:1.
36. The ink composition as recited in claim 34 wherein said polymer is a styrene-allyl alcohol copolymer, said solvent is toluene and said plasticizer is selected from the group consisting of dioctyl phthalate and benzyl butyl phthalate.
37. The thermally activated transfer ribbon as recited in claim 31 or 33 wherein:
(a) said thickener is selected from the group consisting of fumed silica and hydrophobic fumed silica;
(b) said dispersant is lecithin; and (c) said pigment is selected from the group consisting of carbon black, alkali blue and iron blue.
(a) said thickener is selected from the group consisting of fumed silica and hydrophobic fumed silica;
(b) said dispersant is lecithin; and (c) said pigment is selected from the group consisting of carbon black, alkali blue and iron blue.
38. The thermally activated transfer ribbon as recited in claim 31 or 33 said ink composition further comprising a color toner.
39. The thermally activated ink composition as recited in claim 20, 21 or 22 wherein said substrate material is selected from the group consisting of polyester, polyethylene, polypropylene or polyvinylchloride and said substrate has a thickness of from about 0.12 mil to about 0.75 mil.
40. The thermally activated transfer ribbon as recited in claim 21, 22 or 23 wherein said ink is applied to said substrate as a hot-melt.
41. In a method of generating printed characters on ordinary paper with a thermal print head, the improvement comprising aligning a thermally activated transfer ribbon adjacent the thermal print head, said thermally activated transfer ribbon positioned between said print head and the surface to be printed upon and said thermally activated transfer ribbon comprising a substrate and an ink composition as recited in claim 20, 21 or 25, said ink composition forming a film on one side of said substrate adjacent the surface to be printed upon.