CA1065275A - Photoelectrolysis of water by solar radiation - Google Patents
Photoelectrolysis of water by solar radiationInfo
- Publication number
- CA1065275A CA1065275A CA264,876A CA264876A CA1065275A CA 1065275 A CA1065275 A CA 1065275A CA 264876 A CA264876 A CA 264876A CA 1065275 A CA1065275 A CA 1065275A
- Authority
- CA
- Canada
- Prior art keywords
- electrode
- cell
- semiconducting
- electrolyte
- counter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
INVENTION: PHOTOELECTROLYSIS OF WATER
BY SOLAR RADIATION
INVENTOR: ARTHUR J. NOZIK
ABSTRACT OF THE DISCLOSURE
Photoelectrolysis of water by solar radiation to produce hydrogen is achieved using semiconducting thin film electrodes. The cell comprises (a) an electrode comprising at least one thin film semiconducting layer disposed on a sub-strate, each layer having a bandgap which ranges from about 1.3 to 4.0 eV; (b) a counter-electrode; (c) an electrolyte disposed between the thin film semiconducting electrode and the counter-electrode; (d) external bias means between the electrode for biasing the electrode with from 0 to about 1 V; and (e) means for collecting hydrogen produced.
BY SOLAR RADIATION
INVENTOR: ARTHUR J. NOZIK
ABSTRACT OF THE DISCLOSURE
Photoelectrolysis of water by solar radiation to produce hydrogen is achieved using semiconducting thin film electrodes. The cell comprises (a) an electrode comprising at least one thin film semiconducting layer disposed on a sub-strate, each layer having a bandgap which ranges from about 1.3 to 4.0 eV; (b) a counter-electrode; (c) an electrolyte disposed between the thin film semiconducting electrode and the counter-electrode; (d) external bias means between the electrode for biasing the electrode with from 0 to about 1 V; and (e) means for collecting hydrogen produced.
Description
PHOTOELECTROLYSIS OF WATER BY SOLAR RADIATION
BACKGROUND OF THE INVENTION
1. Field of the Invention . .
The invention relates to the production of hydrogen and oxygen by the electrolysis of water and, more particularly, to the production of hydrogen by the photoelectrolysis of water using solar radiation.
BACKGROUND OF THE INVENTION
1. Field of the Invention . .
The invention relates to the production of hydrogen and oxygen by the electrolysis of water and, more particularly, to the production of hydrogen by the photoelectrolysis of water using solar radiation.
2. Description of the Prior Art Two areas that have recently received considerable attention are solar energy conversion and the use of hydrogen as the ultimate fuel for the distribution and interconversion of energy (the hydrogen economy). A coupling of solar energy conver-sion with the hydrogen economy may produce a solution to both energy resource depletion and environmental pollution problems.
Such a coupling may be effected by photolysis, in which sunlight is used to directly decompose water into hydrogen and oxygen.
Preferably, semiconductor electrodes may be employed to facilitate photolytic decomposition by a process known as photoelectrolysis.
A simple model for such a process can be described in terms of conventional photovoltaic devices which comprise an n-p junction.
In photoelectrolytic devices, the n-p junction is replaced by an n-electrolyte-p (or metal) junction. Electron-hole pairs are generated by the absorption of light in either or both semi-conductor electrodes. The electron-hole pairs are separated by the semiconductor-electrolyte junction barrier and are injected at the respective electrodes to produce electrochemical oxida-tion and reduction reactions.
For an n-type electrode, holes combine with hydroxyl ions (OEI ) to produce an anodic oxidation reaction; the reverse process occurs at a p-type or metal electrode where electrons combine with protons (H+) to produce a cathodic re-1~65275 duction reaction. The net effect is a flow of electrons fromthe n-electrode to the p-electrode resulting in reduction at the latter (H2 formation) and oxidation at the former (2) formation).
Previous work reported in the literature has centered on the electrochemical behavior of illuminated semiconductor single crystal electrodes, such as TiO2, GaAs, ZnO, CdS and ZnSe, to produce hydrogen; see, e.g., Vol. 16, Solar Energy, pp. 45-51 (1974) and Vol. 238, Nature, pp. 37-38 (July 7, 1972).
Preliminary investigations on thin film Tio2 electrodes have also been reported; see, e.g., Vol. 121, Journal of Electro-chemical Society, pp. 1160-1167 (1974) and Vol. 122, Journal of Electrochemical Society, pp. 739-742 (1975). Practical cell configurations, however, are not disclosed.
The attraction of photoelectrolysis is that it solves the energy storage problem which plagues the practical implemen-tation of solar energy conversion, and at the same time it has the potential for providing an inexpensive source of hydrogen. However, the current use of single crystal electrodes, which are inherently expensive, and economic considerations relating to other aspects of the cell design, limit its current use. New and more efficient cell designs and materials are required in order to realize the potential of photoelectrolysis.
SUMMARY OF THE INVENTION
In accordance with the invention, a photoelectrolysis cell for producing hydrogen from solar radiation comprises (a) an electrode comprising at least one thin film semiconducting layer, which is disposed on a supporting substrate, each layer having a bandgap which ranges from about 1.3 to 4.0 eV, (b) a counter-electrode, (c) an electrolyte disposed between the thin filmsemiconducting electrode and the counter-electrode, (d) .
, - . - ~ . :
- ~
external bias means between the electrode and the counter-electrode for biasing the electrode with from 0 to about 1 V, and (e) means for collecting the hydrogen produced.
The thin film semiconducting electrode may be either polycrystalline, having a crystallite size ranging from about 25 A to 1 mm, or amorphous. Preferred materials include suit-ably doped TiO2, In203, SnO2, GaAs, GaP, CdS, Si and the titanates MTiO3, where M is at least one element of barium, strontium, the rare earth elements and the transition metal elements.
Graded bandgaps of multiple heterojunction semicon-ducting layers may be used to more effectively utilize a larger portion of the solar spectrum.
The counter-electrode may be either metallic or at least one thin semiconducting film disposed on a supporting sub-strate. If the counter-electrode is metallic, the electrode may comprise either n-type material, such as at least one of the preferred material given above, or p-type material, such as suitably doped GaAs, GaP, CdTe, CuInS2, InP, ZnSe, Cu2S and Si.
If the counter-electrode is semiconducting, the thin semi-conducting film of the counter-electrode has a conductivity type ; opposite to that of the thin film semiconducting layer(s) of the electrode. Further, the total bandgap for all photoactive ; layers of both electrodes ranges from about 1.3 to 5.0 eV.
Simultaneous illumunation of both semiconducting electrodes permits use of a larger portion of the solar spectrum and hence increased conversion efficiency.
The electrolyte may be either liquid or solid having a specific conductivity at least about 10 3 ohm l-cm 1. Liquid electrolytes may be either acidic or basic. Solid electrolytes :
may comprise cationic or anionic polymeric membrane films, such as perfluorosulfonic acid polymer (also known as Nafion~, a trademark of E.I. DuPont de Nemours and Co.) For the case of a solid ~: .
-' 10652'75 .
polymer electrolyte, porous n- and p-type thin semiconducting films comprising the anode and cathode, respectively, of the photoelectrolysis cell are disposed on opposite sides of the polymer electrolyte film, resulting in a totally thin film cell with low internal resistance and, hence, high conversion efficiency of solar energy into hydrogen. Either semiconductor electrode may also be replaced by a porous, thin film metal electrode. The use of n- and p-type electrodes also permits simultaneous illumination of both anode and cathode, resulting in greater conversion - 10 efficiency.
Photosensitive dyes may also be incorporated in the electrolyte to sensitize wide bandgap electrodes to longer wave-- length radiation and thereby increase the conversion efficiency of cells utilizing such electrodes.
BRIEF DESCRIPTION OF THE DRAWING
FIG. 1 is a partly schematic and partly diagrammatic view of apparatus useful in the practice of the invention;
FIG. 2 is a cross-sectional view of an alternate con-figuration of a portion of the apparatus of FIG. l;
FIG. 3 is a cross-sectional view of an embodiment of the invention, utilizing flowing electrolyte and one thin film semiconducting electrode illuminated from one direction;
FIG. 4 is a cross-sectional view of an alternative embodiment of the invention, utilizing flowing electrolyte and two thin film semiconducting electrodes illuminated from all directions; and FIG. 5 is a cross-sectional view of an alternative embodiment of the invention, utilizing a thin film solid electrolyte and two thin film semiconducting electrodes il-luminated from all directions.
,~. . .
-. : ' DETAILED DESCRIPTION OF THE INVENTION
1. ~asic Considerations Photoelectrolysis is defined as a process whereby light absorbed in one or both electrodes of an electrochemical cell generates electron-hole pairs which are separated and injected into the electrolyte at the cathode and anode, respectively, to produce reduction and oxidation reactions. Hence, an overall photochemical reaction is achieved in two steps: (1) the elec-trons (and holes) are first created by photoexcitation of a semiconductor electrode, and (2) the electrons (and holes) drive chemical reactions in an electrochemical cell. Of prime importance is the possibility that this sequence can drive reactions at lower energy levels than can either direct photolysis or electrolysis acting independently.
The photoelectrolysis of water is governed by the following process:
- H20(1)--~ H2(g) + 1/2 2(g) (1) ~H = + 68.32 kcal/mole (2.96 eV) ~F = + 56.69 kcal/mole (2.46 eV) For the normal, that is, homogeneous, photolysis of H2O, light with wavelengths less than 2420 A (5.1 eV) is required.
This is because the first step in this reaction path involves electronic excitation of the water molecule to high-lying molecular orbitals; absorption of light by water is not appre-ciable at wavelengths above about 2500 A. However, the maximum photon energy available from the sun (at air mass two) is 4.0 eV, which corresponds to a wavelength of about 3200 A. Hence, direct homogeneous photolysis of water by sunlight is not possible.
; The actual spectral distribution of solar irradiance is shown in Table I.
.
, . - . :: .
----~ 1065Z75 Table I.
Wavelength Photon Energy Percent Solar Engergy Interval, AInterval, eV (at air mass two*) 3200 - 4000 4.0 - 3.1 2.8 4000 - 5000 3.1 - 2.5 12.7 5000 - 6000 2.5 - 2.1 15.4 6000 - 7000 2.1 - 1.8 15.1 7000 - 8000 1.8 - 1.6 13.3 8000 - 9000 1.6 - 1.4 7.7 9000 -10,0001.4 - 1.2 4.4 10,000-25,0001.2 - 0.5 29.0 *Air mass two is defined as the solar energy per unit area im-pinging on the earth's surface when the sun is 60Q from its zenith.
For the normal electrolysis of liquid water, the theoretical decomposition potential is 1.23 eV. In a photoelectrolysis cell, the upper wavelength limit that can be used to decompose H2O is 12,4000/1.23 = 10,000 A. This value is derived by considering the absorption of two photons in the ; 20 cell at hv = 1.23 eV. The two electron-hole pairs provide the two Faradays at 1.23 eV required to satisfy the free energy requirements of reaction (1). The remaining 0.5 eV
needed to satisfy the difference between the chemical energy created (~H) and electrical free energy (~F) used is provided by heat loss from the surroundings. Thus, photoelectrolysis may be viewed as a two-photon process which sensitizes the . -photolysis of water to visible light.
The details of the photoelectrolysis scheme can best be discussed within the framework of the theory of p-n junctions, Schottky barriers, and the photovoltaic effect.
The photoelectrolysis cell can be visualized as an n-p or semiconductor-metal junction which is split and electrolyte interposed between the halves. As a result, one forms either a n-electrolyte-p or semiconductor-electrolyte-metal sandwich.
- At the n-type electrode, hydroxyl anions (OH ) com-bine with holes (h+) to product oxygen and water:
2h + 20H -~ / 2 2 (2) At the p-type or metal electrode, protons (H ) combine with electrons (e ) to produce hydrogen:
2e + 2 H - ~ H2 (3) In an aqueous electrolyte, reactions (2) and (3) occur at the same time. Incoming radiation hv (h is Planck's constant, 6.62 x 10 27 erg sec, and u is the frequency of the radiation in sec 1) must be equal to or greater than the bandgap energy Eg in order to generate electron-hole pairs.
Absorption of bandgap light (h v> Eg) in the n-electrode results in electron-hole pairs which separate in the space charge layer at the surface of the electrode. Hole injection proceeds into the electrolyte, while the electron moves into the bulk of the electrode and around the external circuit to the cathode (counter-electrode). An analagous process occurs when bandgap light is absorbed in a p-electrode. These processes occur at the respective electrodes independently, either with simultaneous illumination or with only one electrode illuminated. Either semiconducting electrode can also be replaced by a metallic electrode.
If the system consists of a semiconductor-electro-lyte-metal sandwich, then the bandgap of the semiconductor must be sufficiently high to provide the energy to drive the photolytic reaction and to overcome other energy losses. The minimum bandgap consistent with these considerations is about .. . . ..
, . . .
. . . , ~ - ' , ~: ' 1065Z7~
1.3 eV. If the system consists of an n-electrolyte-p semi-conductor sandwich, then the sum of the bandgaps of the two electrodes must be equal to the above-mentioned minimum energy.
For the latter case, it is thus possible to greatly increase the conversion efficiency of solar radiation by simultaneous illumination of n- and p-electrodes of smaller bandgaps, since smaller bandgaps semiconductors absorb more light and hence provide higher conversion efficiency.
These considerations can be put into quantitative terms by making an energy balance for the absorbed photon.
If one considers the Schottky analog for the photoelectro-lysis cell, then for bandgap photons (hv > Eg) absorbed, for example, in a cell comprising a TiO2 semiconducting electrode and a platinum metal counter-electrode:
E = VB ~ ~G/2F + VH + iR + (EC-Ef) + npt + nTiO (4) where Eg is the bandgap of the semiconductor (3.0 eV for TiO2), ~ VB the TiO2-electrolyte junction potential barrier (about ; 0.8 eV),~G/2F is the free energy per electron for H2O decompo-sition (1.23 eV), VH is the drop across the Helmholt~ layer of the electrolyte (approximately 0.05 eV), iR is the ohmic loss in the system, (EC-Ef) is the energy difference between the conduction band and the Fermi level in TiO2 (about 0.2 eV) and nPt and nTiO are the respective electrode over-potentials (approximately 0.1 eV for Pt). The estimate for the potential barrier (VB) is determined from a Schottky-Mott plot of l/C2 vs Eb, where C is the depletion layer capacitance and Eb is an applied bias. Values indicated for the other ter~s in Equation (4) are either well-known or have been calculated from basic considerations. All the terms on the right-hand side of equation (4) except for nTiO add up to about 2.3 eV. This leaves about 0.7 eV that can be tolerated as overpotential for the - : . .
` 1065~:75 Tio2 electrode. It is observed that H2 evolution cannot be achieved with TiO2 electrodes unless an anodic bias of about 0.3 to 0.5 volts is provided. This means that the total electron energy input is 3.3 to 3.5 eV and that the overvoltage at the TiO2 electrode is about 0.9 to 1.1 eV. The 2 overvoltage at the TiO2 electrode arises from kinetic limitations on the rate of hole injection from the TiO2 space charge layer into the Helmholtz layer. The theory of this process is not yet understood. It is possible, however, to reduce this overvoltage, for example, by employing other electrode materials, such as CdS or GaP.
Another way to eliminate the need for an external bias in order to generate H2 in the cell is to use the n-electrolyte-p configuration with simultaneous illumination of both electrodes.
When n-type TiO2 is employed as the anode, the bandgap of the p-type electrode would have to be greater than about 0.5 eV in order to achieve decomposition of water.
A major feature of photoelectrolysis is the fact that the potential barrier is created by a semiconductor-electrolyte junction. Such junctions exhibit the followingsignificant differences compared to a solid-state junction.
1. The presence of surface recombination sites does not produce deleterious effects on optical conversion efficiency.
This is because in photoelectrolysis the annihilation of photo-induced carriers at the surface is precisely their desired fate;
these recombination processes result in the relevent electro-chemical oxidation and/or reduction reactions. This means that polycrystalline electrodes with grain boundries producing a large source of surface recombination centers should yield conversion efficiencies comparable to single crystal electrodes. In photo-excited solid-state p-n junctions, surface recombination is strictly deleterious, and polycrystalline junctions yield much _g_ : . . : . , :
lower optical conversion energies than single crystal junctions.
2. The reverse saturation current of the junction is equal to the exchange current of the electrochemical reaction occurring at the electrode and may be much less than the limiting diffusion current of minor carriers. For a p-n junction:
Ij = Io (Exp(qV/kT)-l) (5) where Ij is the junction currentl Io is the reverse saturation current and V is the junction voltage. For a solar cell (constant current source, Is, in parallel with a p-n junction and a load Rl), the maximum efficiency increases with decreasing Io/IS. At a semiconducting-electrolyte junction, the i-V characteristic is described by an analogous equation, and the lower Io value resulting from the electrical chemical exchange current leads to higher theoretical conversion efficiencies for photoeffects.
2. _11 Configuration In accordance with the invention, a photoelectrolysis cell for producing hydrogen from solar radiation comprises (a) - an electrode comprising at least one thin film semiconducting layer which is disposed on a supporting substrate, each layer having a bandgap which ranges from about 1.3 to 4.0 eV; (b) a counter-electrode; (c) an electrolyte disposed between the thin film semiconducting electrode and the counter-electrode; (d) external bias means between the thin film semiconducting electrode and the counter-electrode for biasing the thin film semiconducting electrode with 0 to about 1 V, and (e) means for collecting hydrogen produced.
An example of a cell configuration of the invention is shown in FIG. 1. A cell, generally indicated at 10, comprises an electrode 11 comprising at least one thin film semiconducting layer supported on electrically conducting substrate 12, which is connected to anode lead 13, and a counter-electrode 14, which ':
is connected to cathode lead 15. An electrolyte 16 is disposed between the two electrodes. Incoming radiation h , shown by arrow 17, enters the cell through transparent window 18, e.g., quartz, and illuminates the semiconducting electrode. The incoming radiation initiates injection of holes into the electro-lyte from the anode and electron (e ) movement from the anode lead to the cathode lead through the external circuit. The holes react with OH ions at the surface of the semiconducting electrode to produce oxygen and water (reaction (2) above). The oxygen is collected in space l9o The electrons react with H+ ions at the surface of the counter-electrode to produce hydrogen (reaction (3) above), which is collected in space 20. A conventional bias supply 21, possibly together with an ammeter 22, completes the electrical circuit.
A portion of an alternative configuration of the thin film semiconducting electrode is shown in FIG. 2. This configu-ration reduces the pathlength of incoming radiation 17 by placing ; the transparent window 18 close to the surface of the thin film semi-conducting electrode 11. Or, supporting the semiconducting electrode on a transparent electrically conducting substrate 23 upon which incoming radiation 17 is incident, scattering losses of the incoming radiation due to the electrolyte 16 are eliminated. O-rings 24 enable the structure to be clamped together to prevent loss of electrolyte.
FIG. 3 depicts a cross sectional view of a rectangular pipe 30 which is the essential element of a continuous flow photo-electrolysis cell containing an n-type (or p-type) thin film semi-conducting electrode and a metallic counter-electrode. The top 31 of the pipe consists of glass, which is coated on the inside ~ --with transparent, electrical conductor 32 upon which an electrode 33, comprising at least one thin film semiconducting layer, ' .
~ . . . -''' , : ....... - : - - ' . . . ~ ~
10t~5Z7S
is deposited. The bottom 34 of the pipe is metallic and comprises the counter-electrode. The electrode and counter-electrode are isolated from each other by insulating material 35 which comprises the sides of the pipe. Liquid electrolyte 36 flows through the cell, and 2 and H2 are formed at electrode 33 and counter-electrode 34, respectively, as solar radiation 17 is absorbed in the semiconducting layer of electrode 33. The -generated gases are prevented from mixing by a separator 37 which permits liquid transport but not gas transport. This separator may consist of fritted glass or a membrane material, for example. An external electrical bias 21 is provided as needed to control evolution. The evolved gases are swept along with the electrolyte flow in their respective compartments, and, at the exit of the pipe, the gases are separated from the electrolyte by conventional methods. -FIG. 4 depicts a cross-sectional view of a circular pipe structure 40 which comprises the essential element of a continuous flow photoelectrolysis cell comprising anode 41 and cathode 42 which comprise at least one n-type thin film and at least one p-type thin film, respectively. The electrodes are simultaneously illuminated, using solar concentration techniques.
The n- and p-type thin films are deposited on each half circle of a split metallic tube 43 and are separated from each other by a small insulating section 44. The metallic tube is enclosed by a concentric glass pipe 45, and electrolyte 46 flows through the annular space. 2 and H2 are evolved at anode 41 and cathode 42, respectively, and are prevented from mixing by gas separator 47. Solar radiation 17 impinges on all sides of the pipe, as illustrated by the dotted line, with the aid of solar concentrator 48, which may comprise conventional reflectors, such as a parabolic or a flat mirror, for example. H2 and 2 are carried along with the liquid electrolyte and are separated fromthe liquid at the exit of the pipe by means of conventional gas-liquid separation equipment (not shown). A conventional anodic electrical bias (not shown) between the n- and p-type electrodes is applied as needed to control the rate of H2 and 2 evolution.
FIG. 5 depicts a cross-sectional view of a totally thin film photoelectrolysis cell 50 comprising anode 51 and ;
cathode 52 which comprise at least one n-type thin film and at least one p-type thin film, respectively. The electrodes are deposited on either side of a thin solid polymer electrolyte sheet 53. The polymer sheet is suspended in a glass pipe 54 which has ordinary water 55 flowing through it in con-tact with both the n- and p-type sides of the polymer sheet.
The semiconducting films are sufficiently porous to permit ionic contact between the water and the polymer electrolyte. Solar radiation 17 impinges on the cell and is absorbed in both the n- and p-type semiconducting layers with the aid of solar con-centrators 56, which may comprise conventional reflectors, for example. 2 and H2 are produced at the n- and p-type electrodes, respectively, and are collected and separated as described earlier. An anodic electrical bias 21 is applied between the n- and p-type electrodes to control the rate of 2 and H2 evolution. The porous n- and p-type films have sufficient electrical conductivity, about 1 ohm~l cm~l, or are supported on electrically conducting porous substrates (not shown) so as to provide good electrical contact between the n- and p-type electrodes.
a. Electrode Material The selection of electrode material is constrained by two considerations: (1) the minimum bandgap necessary to dissociate water into hydrogen and oxygen (1.23 eV) and (2) the maximum energy .~ .
.. : ~ ' :.: ' . .
- ~065Z75 available from the sun (4.0 eV). Due to energy losses that may occur, it is preferred that the minimum bandgap be about 1.3 eV. The electrode materials must be stable electrochemically and inert to any reactions in solution. Preferred materials are suitably doped n-type semiconductors such as/ TiO2, In2o3, SnO2, GaAs, GaP, CdS, Si, and the titanates MTiO3, where M is at least one element of barium, strontium, the rare earth elements (atomic number 57 to 71, inclusive) and the transition metal elements (~roups IB through VIIB and VIII
of the Periodic Table). Examples of rare earth and transition metal titanates include LaTiO3 and NiTio3, respectively.
To date, Tio2 is the most useful material developed.
However, TiO2 is a wide bandgap material (Eg = 3.0 eV), and its principle optical absorption is thus not in that region of the solar spectrum to obtain maximum efficiency for cells employing Tio2 electrodes. For such wide bandgap materials, however, there are methods to increase the efficiency. For example, graded band-gaps or multiple heterojunction semiconduction layers may be utilized, with the bandgap of each layer ranging from about 1.3 to 4.0 eV. This comprises joining together two or more semiconducting materials having different bandgaps such that a greater fraction of the solar irradiance is absorbed. For example, TiO2 combined with CdS, GaP, GaAs, CdTe or Si results in solar absorbances ranging from about 25% to 70%; the solar absorption of Tio2 alone is about 3% to 6%. Furthermore, such combinations permit use of semiconductors which by themselves are not chemically inert with respect to the electrolyte. This is accomplished by overcoating the chemically sensitive semi-conductor, such as CdS or GaP, with an inert semiconductor layer, such as TiO2, to protect the chemically sensitive semiconductor from chemical attack by the electrolyte. Also, sensitization of 10~5Z75 the electrolyte, such as with photosensitive dyes, may be used toincrease conversion efficiency. Conventional solar concentra-- tors may be used to further increase conversion efficiency.
While single crystal material may be employed, the electrodes of the invention are in the form of thin films (about 500 A to 10~m), and may be either polycrystalline, with a crystallite size ranging from about 25 A to l mm, or amorphous.
The films are conveniently fabricated by conventional deposition - procedures such as DC sputtering, RF sputtering, chemical ; 10 vapor deposition, thermal evaporation, and anodization or thermal oxidation of metals. ;
The thin film may be formed on a metal substrate in order to achieve appropriate conductivity to the rest of the circuit. However, in such a situation, radiation must pass through the electrolyte and consequently, scattering losses occur. Alternatively, the thin film may be deposited on a transparent electrical conductor such as Cd2SnO4 upon which solar radiation impinges to reduce the scattering losses and to increase the efficiency of the cell. Other known transparent conductors include suitably doped In2O3 and SnO2.
For photoelectrolysis cells of the invention, an extern-al bias may be supplied in order to efficiently generate H2.
The amount of bias depends inverse~ly on bandgap, and reflects 2 over-voltage. Bias can be eliminated by employing materials that do not produce 2' such as a semiconducting thin film electrode of CdS. While lower bandgap materials evidence greater conversion efficiency of optical energy to produce H2, a higher bias is required. For a semiconducting thin film electrode of TiO2, the minimum bias ranges from about 0.3 to 0.5 V, depending on electrolyte pH and rate of H2 evolution desired. ~-A bias greater than about 1.7 V is not useful, since this is the voltage employed in a conventional electrolysis cell. Even a bias greater than about 1 V is considered to use too much electrical energy - : . : . : , . :
.
. . , -.
': ' ~
-`-` 1065Z'75 to be competatively useful. Accordingly, an external bias ranging from 0 to about 1 V is preferred. The bias means may be any conventional bias apparatus known in the art that supplies the requisite voltage.
While n-type semiconducting films are generally preferred as the electrode (when the counter-electrode is metallic), p-type semiconducting films may alternatively be employed. P-type semiconducting materials include suitably doped GaAs, GaP, CdTe, CuInS2, InP, ZnSe, Cu2S and Si. The external bias on the electrode then ranges from 0 to about -1 V.
B. Counter-Electrode Material The counter-electrode may be either metallic, such as platinum, or semiconducting. If it is semiconducting, it must be of an opposite conductivity type to the semiconducting electrode in the cell. For n-type thin film semiconducting electrodes, p-type counter-electrodes comprising at least one semiconducting layer, must be used. Examples of p-type semiconducting counter-electrodes include suitably doped GaAs, GaP, CdTe, CuInS2, InP, ZnSe, Cu2S and Si. These materials may be in the form of thin films. Use of semi-conducting counter-electrodes requires that the sum of the bandgaps ~..
for all photoactive layers of both electrodes be equal to the energy required to dissociate water and to provide for the other energy loss mechanisms previously described, e.g., a total bandgap for both electrodes ranging from about 1.3 to 5.0 eV. Therefore, use of semiconducting counter-electrodes would permit lower bandgap materials to be employed in the cell than would be required for metallic counter-electrodes and would enable both electrodes to be illuminated by solar radiation, thereby increasing conversion efficiency.
C. Electrolyte The electrolyte must have a sufficiently high conductivity ~065Z75 in order to minimize cell resistance and reduce losses. Preferably, -the specific conductivity is at least about 10 3Ohm l-cm 1.
The electrolyte conveniently is an aqueous solution made appropriately acidic or basic. Examples include 0.1N KOH
and 0.2N H2S04. Alternatively, a solid polymer electrolyte comprising a cationic or anionic polymeric membrane film may be employed. There are many advantages to using the latter:
(1) the thin semiconducting electrode film can be deposited directly onto the polymer electrolyte film, which results in low internal resistance; (2) no free acid or base is present in the cell, which reduces chemical corrosion of the semiconductor electrode; and
Such a coupling may be effected by photolysis, in which sunlight is used to directly decompose water into hydrogen and oxygen.
Preferably, semiconductor electrodes may be employed to facilitate photolytic decomposition by a process known as photoelectrolysis.
A simple model for such a process can be described in terms of conventional photovoltaic devices which comprise an n-p junction.
In photoelectrolytic devices, the n-p junction is replaced by an n-electrolyte-p (or metal) junction. Electron-hole pairs are generated by the absorption of light in either or both semi-conductor electrodes. The electron-hole pairs are separated by the semiconductor-electrolyte junction barrier and are injected at the respective electrodes to produce electrochemical oxida-tion and reduction reactions.
For an n-type electrode, holes combine with hydroxyl ions (OEI ) to produce an anodic oxidation reaction; the reverse process occurs at a p-type or metal electrode where electrons combine with protons (H+) to produce a cathodic re-1~65275 duction reaction. The net effect is a flow of electrons fromthe n-electrode to the p-electrode resulting in reduction at the latter (H2 formation) and oxidation at the former (2) formation).
Previous work reported in the literature has centered on the electrochemical behavior of illuminated semiconductor single crystal electrodes, such as TiO2, GaAs, ZnO, CdS and ZnSe, to produce hydrogen; see, e.g., Vol. 16, Solar Energy, pp. 45-51 (1974) and Vol. 238, Nature, pp. 37-38 (July 7, 1972).
Preliminary investigations on thin film Tio2 electrodes have also been reported; see, e.g., Vol. 121, Journal of Electro-chemical Society, pp. 1160-1167 (1974) and Vol. 122, Journal of Electrochemical Society, pp. 739-742 (1975). Practical cell configurations, however, are not disclosed.
The attraction of photoelectrolysis is that it solves the energy storage problem which plagues the practical implemen-tation of solar energy conversion, and at the same time it has the potential for providing an inexpensive source of hydrogen. However, the current use of single crystal electrodes, which are inherently expensive, and economic considerations relating to other aspects of the cell design, limit its current use. New and more efficient cell designs and materials are required in order to realize the potential of photoelectrolysis.
SUMMARY OF THE INVENTION
In accordance with the invention, a photoelectrolysis cell for producing hydrogen from solar radiation comprises (a) an electrode comprising at least one thin film semiconducting layer, which is disposed on a supporting substrate, each layer having a bandgap which ranges from about 1.3 to 4.0 eV, (b) a counter-electrode, (c) an electrolyte disposed between the thin filmsemiconducting electrode and the counter-electrode, (d) .
, - . - ~ . :
- ~
external bias means between the electrode and the counter-electrode for biasing the electrode with from 0 to about 1 V, and (e) means for collecting the hydrogen produced.
The thin film semiconducting electrode may be either polycrystalline, having a crystallite size ranging from about 25 A to 1 mm, or amorphous. Preferred materials include suit-ably doped TiO2, In203, SnO2, GaAs, GaP, CdS, Si and the titanates MTiO3, where M is at least one element of barium, strontium, the rare earth elements and the transition metal elements.
Graded bandgaps of multiple heterojunction semicon-ducting layers may be used to more effectively utilize a larger portion of the solar spectrum.
The counter-electrode may be either metallic or at least one thin semiconducting film disposed on a supporting sub-strate. If the counter-electrode is metallic, the electrode may comprise either n-type material, such as at least one of the preferred material given above, or p-type material, such as suitably doped GaAs, GaP, CdTe, CuInS2, InP, ZnSe, Cu2S and Si.
If the counter-electrode is semiconducting, the thin semi-conducting film of the counter-electrode has a conductivity type ; opposite to that of the thin film semiconducting layer(s) of the electrode. Further, the total bandgap for all photoactive ; layers of both electrodes ranges from about 1.3 to 5.0 eV.
Simultaneous illumunation of both semiconducting electrodes permits use of a larger portion of the solar spectrum and hence increased conversion efficiency.
The electrolyte may be either liquid or solid having a specific conductivity at least about 10 3 ohm l-cm 1. Liquid electrolytes may be either acidic or basic. Solid electrolytes :
may comprise cationic or anionic polymeric membrane films, such as perfluorosulfonic acid polymer (also known as Nafion~, a trademark of E.I. DuPont de Nemours and Co.) For the case of a solid ~: .
-' 10652'75 .
polymer electrolyte, porous n- and p-type thin semiconducting films comprising the anode and cathode, respectively, of the photoelectrolysis cell are disposed on opposite sides of the polymer electrolyte film, resulting in a totally thin film cell with low internal resistance and, hence, high conversion efficiency of solar energy into hydrogen. Either semiconductor electrode may also be replaced by a porous, thin film metal electrode. The use of n- and p-type electrodes also permits simultaneous illumination of both anode and cathode, resulting in greater conversion - 10 efficiency.
Photosensitive dyes may also be incorporated in the electrolyte to sensitize wide bandgap electrodes to longer wave-- length radiation and thereby increase the conversion efficiency of cells utilizing such electrodes.
BRIEF DESCRIPTION OF THE DRAWING
FIG. 1 is a partly schematic and partly diagrammatic view of apparatus useful in the practice of the invention;
FIG. 2 is a cross-sectional view of an alternate con-figuration of a portion of the apparatus of FIG. l;
FIG. 3 is a cross-sectional view of an embodiment of the invention, utilizing flowing electrolyte and one thin film semiconducting electrode illuminated from one direction;
FIG. 4 is a cross-sectional view of an alternative embodiment of the invention, utilizing flowing electrolyte and two thin film semiconducting electrodes illuminated from all directions; and FIG. 5 is a cross-sectional view of an alternative embodiment of the invention, utilizing a thin film solid electrolyte and two thin film semiconducting electrodes il-luminated from all directions.
,~. . .
-. : ' DETAILED DESCRIPTION OF THE INVENTION
1. ~asic Considerations Photoelectrolysis is defined as a process whereby light absorbed in one or both electrodes of an electrochemical cell generates electron-hole pairs which are separated and injected into the electrolyte at the cathode and anode, respectively, to produce reduction and oxidation reactions. Hence, an overall photochemical reaction is achieved in two steps: (1) the elec-trons (and holes) are first created by photoexcitation of a semiconductor electrode, and (2) the electrons (and holes) drive chemical reactions in an electrochemical cell. Of prime importance is the possibility that this sequence can drive reactions at lower energy levels than can either direct photolysis or electrolysis acting independently.
The photoelectrolysis of water is governed by the following process:
- H20(1)--~ H2(g) + 1/2 2(g) (1) ~H = + 68.32 kcal/mole (2.96 eV) ~F = + 56.69 kcal/mole (2.46 eV) For the normal, that is, homogeneous, photolysis of H2O, light with wavelengths less than 2420 A (5.1 eV) is required.
This is because the first step in this reaction path involves electronic excitation of the water molecule to high-lying molecular orbitals; absorption of light by water is not appre-ciable at wavelengths above about 2500 A. However, the maximum photon energy available from the sun (at air mass two) is 4.0 eV, which corresponds to a wavelength of about 3200 A. Hence, direct homogeneous photolysis of water by sunlight is not possible.
; The actual spectral distribution of solar irradiance is shown in Table I.
.
, . - . :: .
----~ 1065Z75 Table I.
Wavelength Photon Energy Percent Solar Engergy Interval, AInterval, eV (at air mass two*) 3200 - 4000 4.0 - 3.1 2.8 4000 - 5000 3.1 - 2.5 12.7 5000 - 6000 2.5 - 2.1 15.4 6000 - 7000 2.1 - 1.8 15.1 7000 - 8000 1.8 - 1.6 13.3 8000 - 9000 1.6 - 1.4 7.7 9000 -10,0001.4 - 1.2 4.4 10,000-25,0001.2 - 0.5 29.0 *Air mass two is defined as the solar energy per unit area im-pinging on the earth's surface when the sun is 60Q from its zenith.
For the normal electrolysis of liquid water, the theoretical decomposition potential is 1.23 eV. In a photoelectrolysis cell, the upper wavelength limit that can be used to decompose H2O is 12,4000/1.23 = 10,000 A. This value is derived by considering the absorption of two photons in the ; 20 cell at hv = 1.23 eV. The two electron-hole pairs provide the two Faradays at 1.23 eV required to satisfy the free energy requirements of reaction (1). The remaining 0.5 eV
needed to satisfy the difference between the chemical energy created (~H) and electrical free energy (~F) used is provided by heat loss from the surroundings. Thus, photoelectrolysis may be viewed as a two-photon process which sensitizes the . -photolysis of water to visible light.
The details of the photoelectrolysis scheme can best be discussed within the framework of the theory of p-n junctions, Schottky barriers, and the photovoltaic effect.
The photoelectrolysis cell can be visualized as an n-p or semiconductor-metal junction which is split and electrolyte interposed between the halves. As a result, one forms either a n-electrolyte-p or semiconductor-electrolyte-metal sandwich.
- At the n-type electrode, hydroxyl anions (OH ) com-bine with holes (h+) to product oxygen and water:
2h + 20H -~ / 2 2 (2) At the p-type or metal electrode, protons (H ) combine with electrons (e ) to produce hydrogen:
2e + 2 H - ~ H2 (3) In an aqueous electrolyte, reactions (2) and (3) occur at the same time. Incoming radiation hv (h is Planck's constant, 6.62 x 10 27 erg sec, and u is the frequency of the radiation in sec 1) must be equal to or greater than the bandgap energy Eg in order to generate electron-hole pairs.
Absorption of bandgap light (h v> Eg) in the n-electrode results in electron-hole pairs which separate in the space charge layer at the surface of the electrode. Hole injection proceeds into the electrolyte, while the electron moves into the bulk of the electrode and around the external circuit to the cathode (counter-electrode). An analagous process occurs when bandgap light is absorbed in a p-electrode. These processes occur at the respective electrodes independently, either with simultaneous illumination or with only one electrode illuminated. Either semiconducting electrode can also be replaced by a metallic electrode.
If the system consists of a semiconductor-electro-lyte-metal sandwich, then the bandgap of the semiconductor must be sufficiently high to provide the energy to drive the photolytic reaction and to overcome other energy losses. The minimum bandgap consistent with these considerations is about .. . . ..
, . . .
. . . , ~ - ' , ~: ' 1065Z7~
1.3 eV. If the system consists of an n-electrolyte-p semi-conductor sandwich, then the sum of the bandgaps of the two electrodes must be equal to the above-mentioned minimum energy.
For the latter case, it is thus possible to greatly increase the conversion efficiency of solar radiation by simultaneous illumination of n- and p-electrodes of smaller bandgaps, since smaller bandgaps semiconductors absorb more light and hence provide higher conversion efficiency.
These considerations can be put into quantitative terms by making an energy balance for the absorbed photon.
If one considers the Schottky analog for the photoelectro-lysis cell, then for bandgap photons (hv > Eg) absorbed, for example, in a cell comprising a TiO2 semiconducting electrode and a platinum metal counter-electrode:
E = VB ~ ~G/2F + VH + iR + (EC-Ef) + npt + nTiO (4) where Eg is the bandgap of the semiconductor (3.0 eV for TiO2), ~ VB the TiO2-electrolyte junction potential barrier (about ; 0.8 eV),~G/2F is the free energy per electron for H2O decompo-sition (1.23 eV), VH is the drop across the Helmholt~ layer of the electrolyte (approximately 0.05 eV), iR is the ohmic loss in the system, (EC-Ef) is the energy difference between the conduction band and the Fermi level in TiO2 (about 0.2 eV) and nPt and nTiO are the respective electrode over-potentials (approximately 0.1 eV for Pt). The estimate for the potential barrier (VB) is determined from a Schottky-Mott plot of l/C2 vs Eb, where C is the depletion layer capacitance and Eb is an applied bias. Values indicated for the other ter~s in Equation (4) are either well-known or have been calculated from basic considerations. All the terms on the right-hand side of equation (4) except for nTiO add up to about 2.3 eV. This leaves about 0.7 eV that can be tolerated as overpotential for the - : . .
` 1065~:75 Tio2 electrode. It is observed that H2 evolution cannot be achieved with TiO2 electrodes unless an anodic bias of about 0.3 to 0.5 volts is provided. This means that the total electron energy input is 3.3 to 3.5 eV and that the overvoltage at the TiO2 electrode is about 0.9 to 1.1 eV. The 2 overvoltage at the TiO2 electrode arises from kinetic limitations on the rate of hole injection from the TiO2 space charge layer into the Helmholtz layer. The theory of this process is not yet understood. It is possible, however, to reduce this overvoltage, for example, by employing other electrode materials, such as CdS or GaP.
Another way to eliminate the need for an external bias in order to generate H2 in the cell is to use the n-electrolyte-p configuration with simultaneous illumination of both electrodes.
When n-type TiO2 is employed as the anode, the bandgap of the p-type electrode would have to be greater than about 0.5 eV in order to achieve decomposition of water.
A major feature of photoelectrolysis is the fact that the potential barrier is created by a semiconductor-electrolyte junction. Such junctions exhibit the followingsignificant differences compared to a solid-state junction.
1. The presence of surface recombination sites does not produce deleterious effects on optical conversion efficiency.
This is because in photoelectrolysis the annihilation of photo-induced carriers at the surface is precisely their desired fate;
these recombination processes result in the relevent electro-chemical oxidation and/or reduction reactions. This means that polycrystalline electrodes with grain boundries producing a large source of surface recombination centers should yield conversion efficiencies comparable to single crystal electrodes. In photo-excited solid-state p-n junctions, surface recombination is strictly deleterious, and polycrystalline junctions yield much _g_ : . . : . , :
lower optical conversion energies than single crystal junctions.
2. The reverse saturation current of the junction is equal to the exchange current of the electrochemical reaction occurring at the electrode and may be much less than the limiting diffusion current of minor carriers. For a p-n junction:
Ij = Io (Exp(qV/kT)-l) (5) where Ij is the junction currentl Io is the reverse saturation current and V is the junction voltage. For a solar cell (constant current source, Is, in parallel with a p-n junction and a load Rl), the maximum efficiency increases with decreasing Io/IS. At a semiconducting-electrolyte junction, the i-V characteristic is described by an analogous equation, and the lower Io value resulting from the electrical chemical exchange current leads to higher theoretical conversion efficiencies for photoeffects.
2. _11 Configuration In accordance with the invention, a photoelectrolysis cell for producing hydrogen from solar radiation comprises (a) - an electrode comprising at least one thin film semiconducting layer which is disposed on a supporting substrate, each layer having a bandgap which ranges from about 1.3 to 4.0 eV; (b) a counter-electrode; (c) an electrolyte disposed between the thin film semiconducting electrode and the counter-electrode; (d) external bias means between the thin film semiconducting electrode and the counter-electrode for biasing the thin film semiconducting electrode with 0 to about 1 V, and (e) means for collecting hydrogen produced.
An example of a cell configuration of the invention is shown in FIG. 1. A cell, generally indicated at 10, comprises an electrode 11 comprising at least one thin film semiconducting layer supported on electrically conducting substrate 12, which is connected to anode lead 13, and a counter-electrode 14, which ':
is connected to cathode lead 15. An electrolyte 16 is disposed between the two electrodes. Incoming radiation h , shown by arrow 17, enters the cell through transparent window 18, e.g., quartz, and illuminates the semiconducting electrode. The incoming radiation initiates injection of holes into the electro-lyte from the anode and electron (e ) movement from the anode lead to the cathode lead through the external circuit. The holes react with OH ions at the surface of the semiconducting electrode to produce oxygen and water (reaction (2) above). The oxygen is collected in space l9o The electrons react with H+ ions at the surface of the counter-electrode to produce hydrogen (reaction (3) above), which is collected in space 20. A conventional bias supply 21, possibly together with an ammeter 22, completes the electrical circuit.
A portion of an alternative configuration of the thin film semiconducting electrode is shown in FIG. 2. This configu-ration reduces the pathlength of incoming radiation 17 by placing ; the transparent window 18 close to the surface of the thin film semi-conducting electrode 11. Or, supporting the semiconducting electrode on a transparent electrically conducting substrate 23 upon which incoming radiation 17 is incident, scattering losses of the incoming radiation due to the electrolyte 16 are eliminated. O-rings 24 enable the structure to be clamped together to prevent loss of electrolyte.
FIG. 3 depicts a cross sectional view of a rectangular pipe 30 which is the essential element of a continuous flow photo-electrolysis cell containing an n-type (or p-type) thin film semi-conducting electrode and a metallic counter-electrode. The top 31 of the pipe consists of glass, which is coated on the inside ~ --with transparent, electrical conductor 32 upon which an electrode 33, comprising at least one thin film semiconducting layer, ' .
~ . . . -''' , : ....... - : - - ' . . . ~ ~
10t~5Z7S
is deposited. The bottom 34 of the pipe is metallic and comprises the counter-electrode. The electrode and counter-electrode are isolated from each other by insulating material 35 which comprises the sides of the pipe. Liquid electrolyte 36 flows through the cell, and 2 and H2 are formed at electrode 33 and counter-electrode 34, respectively, as solar radiation 17 is absorbed in the semiconducting layer of electrode 33. The -generated gases are prevented from mixing by a separator 37 which permits liquid transport but not gas transport. This separator may consist of fritted glass or a membrane material, for example. An external electrical bias 21 is provided as needed to control evolution. The evolved gases are swept along with the electrolyte flow in their respective compartments, and, at the exit of the pipe, the gases are separated from the electrolyte by conventional methods. -FIG. 4 depicts a cross-sectional view of a circular pipe structure 40 which comprises the essential element of a continuous flow photoelectrolysis cell comprising anode 41 and cathode 42 which comprise at least one n-type thin film and at least one p-type thin film, respectively. The electrodes are simultaneously illuminated, using solar concentration techniques.
The n- and p-type thin films are deposited on each half circle of a split metallic tube 43 and are separated from each other by a small insulating section 44. The metallic tube is enclosed by a concentric glass pipe 45, and electrolyte 46 flows through the annular space. 2 and H2 are evolved at anode 41 and cathode 42, respectively, and are prevented from mixing by gas separator 47. Solar radiation 17 impinges on all sides of the pipe, as illustrated by the dotted line, with the aid of solar concentrator 48, which may comprise conventional reflectors, such as a parabolic or a flat mirror, for example. H2 and 2 are carried along with the liquid electrolyte and are separated fromthe liquid at the exit of the pipe by means of conventional gas-liquid separation equipment (not shown). A conventional anodic electrical bias (not shown) between the n- and p-type electrodes is applied as needed to control the rate of H2 and 2 evolution.
FIG. 5 depicts a cross-sectional view of a totally thin film photoelectrolysis cell 50 comprising anode 51 and ;
cathode 52 which comprise at least one n-type thin film and at least one p-type thin film, respectively. The electrodes are deposited on either side of a thin solid polymer electrolyte sheet 53. The polymer sheet is suspended in a glass pipe 54 which has ordinary water 55 flowing through it in con-tact with both the n- and p-type sides of the polymer sheet.
The semiconducting films are sufficiently porous to permit ionic contact between the water and the polymer electrolyte. Solar radiation 17 impinges on the cell and is absorbed in both the n- and p-type semiconducting layers with the aid of solar con-centrators 56, which may comprise conventional reflectors, for example. 2 and H2 are produced at the n- and p-type electrodes, respectively, and are collected and separated as described earlier. An anodic electrical bias 21 is applied between the n- and p-type electrodes to control the rate of 2 and H2 evolution. The porous n- and p-type films have sufficient electrical conductivity, about 1 ohm~l cm~l, or are supported on electrically conducting porous substrates (not shown) so as to provide good electrical contact between the n- and p-type electrodes.
a. Electrode Material The selection of electrode material is constrained by two considerations: (1) the minimum bandgap necessary to dissociate water into hydrogen and oxygen (1.23 eV) and (2) the maximum energy .~ .
.. : ~ ' :.: ' . .
- ~065Z75 available from the sun (4.0 eV). Due to energy losses that may occur, it is preferred that the minimum bandgap be about 1.3 eV. The electrode materials must be stable electrochemically and inert to any reactions in solution. Preferred materials are suitably doped n-type semiconductors such as/ TiO2, In2o3, SnO2, GaAs, GaP, CdS, Si, and the titanates MTiO3, where M is at least one element of barium, strontium, the rare earth elements (atomic number 57 to 71, inclusive) and the transition metal elements (~roups IB through VIIB and VIII
of the Periodic Table). Examples of rare earth and transition metal titanates include LaTiO3 and NiTio3, respectively.
To date, Tio2 is the most useful material developed.
However, TiO2 is a wide bandgap material (Eg = 3.0 eV), and its principle optical absorption is thus not in that region of the solar spectrum to obtain maximum efficiency for cells employing Tio2 electrodes. For such wide bandgap materials, however, there are methods to increase the efficiency. For example, graded band-gaps or multiple heterojunction semiconduction layers may be utilized, with the bandgap of each layer ranging from about 1.3 to 4.0 eV. This comprises joining together two or more semiconducting materials having different bandgaps such that a greater fraction of the solar irradiance is absorbed. For example, TiO2 combined with CdS, GaP, GaAs, CdTe or Si results in solar absorbances ranging from about 25% to 70%; the solar absorption of Tio2 alone is about 3% to 6%. Furthermore, such combinations permit use of semiconductors which by themselves are not chemically inert with respect to the electrolyte. This is accomplished by overcoating the chemically sensitive semi-conductor, such as CdS or GaP, with an inert semiconductor layer, such as TiO2, to protect the chemically sensitive semiconductor from chemical attack by the electrolyte. Also, sensitization of 10~5Z75 the electrolyte, such as with photosensitive dyes, may be used toincrease conversion efficiency. Conventional solar concentra-- tors may be used to further increase conversion efficiency.
While single crystal material may be employed, the electrodes of the invention are in the form of thin films (about 500 A to 10~m), and may be either polycrystalline, with a crystallite size ranging from about 25 A to l mm, or amorphous.
The films are conveniently fabricated by conventional deposition - procedures such as DC sputtering, RF sputtering, chemical ; 10 vapor deposition, thermal evaporation, and anodization or thermal oxidation of metals. ;
The thin film may be formed on a metal substrate in order to achieve appropriate conductivity to the rest of the circuit. However, in such a situation, radiation must pass through the electrolyte and consequently, scattering losses occur. Alternatively, the thin film may be deposited on a transparent electrical conductor such as Cd2SnO4 upon which solar radiation impinges to reduce the scattering losses and to increase the efficiency of the cell. Other known transparent conductors include suitably doped In2O3 and SnO2.
For photoelectrolysis cells of the invention, an extern-al bias may be supplied in order to efficiently generate H2.
The amount of bias depends inverse~ly on bandgap, and reflects 2 over-voltage. Bias can be eliminated by employing materials that do not produce 2' such as a semiconducting thin film electrode of CdS. While lower bandgap materials evidence greater conversion efficiency of optical energy to produce H2, a higher bias is required. For a semiconducting thin film electrode of TiO2, the minimum bias ranges from about 0.3 to 0.5 V, depending on electrolyte pH and rate of H2 evolution desired. ~-A bias greater than about 1.7 V is not useful, since this is the voltage employed in a conventional electrolysis cell. Even a bias greater than about 1 V is considered to use too much electrical energy - : . : . : , . :
.
. . , -.
': ' ~
-`-` 1065Z'75 to be competatively useful. Accordingly, an external bias ranging from 0 to about 1 V is preferred. The bias means may be any conventional bias apparatus known in the art that supplies the requisite voltage.
While n-type semiconducting films are generally preferred as the electrode (when the counter-electrode is metallic), p-type semiconducting films may alternatively be employed. P-type semiconducting materials include suitably doped GaAs, GaP, CdTe, CuInS2, InP, ZnSe, Cu2S and Si. The external bias on the electrode then ranges from 0 to about -1 V.
B. Counter-Electrode Material The counter-electrode may be either metallic, such as platinum, or semiconducting. If it is semiconducting, it must be of an opposite conductivity type to the semiconducting electrode in the cell. For n-type thin film semiconducting electrodes, p-type counter-electrodes comprising at least one semiconducting layer, must be used. Examples of p-type semiconducting counter-electrodes include suitably doped GaAs, GaP, CdTe, CuInS2, InP, ZnSe, Cu2S and Si. These materials may be in the form of thin films. Use of semi-conducting counter-electrodes requires that the sum of the bandgaps ~..
for all photoactive layers of both electrodes be equal to the energy required to dissociate water and to provide for the other energy loss mechanisms previously described, e.g., a total bandgap for both electrodes ranging from about 1.3 to 5.0 eV. Therefore, use of semiconducting counter-electrodes would permit lower bandgap materials to be employed in the cell than would be required for metallic counter-electrodes and would enable both electrodes to be illuminated by solar radiation, thereby increasing conversion efficiency.
C. Electrolyte The electrolyte must have a sufficiently high conductivity ~065Z75 in order to minimize cell resistance and reduce losses. Preferably, -the specific conductivity is at least about 10 3Ohm l-cm 1.
The electrolyte conveniently is an aqueous solution made appropriately acidic or basic. Examples include 0.1N KOH
and 0.2N H2S04. Alternatively, a solid polymer electrolyte comprising a cationic or anionic polymeric membrane film may be employed. There are many advantages to using the latter:
(1) the thin semiconducting electrode film can be deposited directly onto the polymer electrolyte film, which results in low internal resistance; (2) no free acid or base is present in the cell, which reduces chemical corrosion of the semiconductor electrode; and
(3) both the n- and p-type thin film electrodes can be deposited on opposite sides of the polymer electrolyte membrane, which results in a totally thin film photoelectrolysis cell. An example of such a polymer electrolyte is a perfluorinated sulfonic acid polymer (also known as Nafion~, a trademark of E.I. DuPont de Nemours and Co.) which is available in thicknesses ranging from about 0.005 to 0.015 inch.
For sensitizing wide bandgap electrodes to visible light, photosensitive dyes such as rhodamine B, eosine, or crystal violet may be incorporated in the electrolyte to increase conversion efficiency.
The dependence of the conversion efEiciency on semi-conductor bandgap is shown in Table II.
Table II.
Semiconductor MaximumH2 2Evolution, Bandgap, eV Efficiency, %l/m /hr 1.0 45 200 2.0 25 42 3.0 8 17 As noted above, however, the minimum total bandgap required would " 1065Z75 ~
be 1.23 eV for aqueous systems. Lower bandgap materials may be used if another anodic reaction is substituted for 2 evolution - or if simultaneous illumination of n- and p-type semiconducting electrodes is employed.
The efficiencies listed in the Table above are very high compared with those possible by direct photolysis. This is because direct photolysis utilizes only a very small fraction of the available solar spectrum (less than 0.2 ~m). The maximum efficiency will, in practice, be decreased by electron-hole recom-bination, incomplete absorption and electrode polarization effects.Nevertheless, the use of semiconductor electrodes is the most attractive scheme for the photolytic decomposition of water by ~ solar radiation.
; d. Collection of Hydrogen The collection and storage of hydrogen gas produced by photoelectrolysis is easily accomplished by conventional techniques, such as pressurizable tanks, metal absorption of hydrogen to form reversibly decomposable metal hydrides and the like.
EXAMPLES
1. DC Sputterlng DC sputtering was carried out in a vacuum system consisting of an 18 inch glass belljar, controls for gas compo-sition and pressure regulation and a 4 kV source of DC power.
Thin films of rutile (Tio2) were DC sputtered from a polycrystalline rutile target onto substrates of tltanium, zirconium, SnO2 on glass, In203 on glass and fused quartz.
Film characterization was performed on Tio2 supported on fused quartz substrates, since no interference existed from the substrate with respect to optical transmittance and electrical conductivity.
The Tio2 sputtering target consisted of a commercially available 4-1/8 inch by 1/4 inch disc of hot pressed rutile powder.
The substrates were suspended above the target with a special 10652'75 copper platform, and the target-to-substrate distance was fixed at 1-1/4 inch for all experiments. The pressure in the chamber - was held at 30~m of 20~ O2-80% Ar. No external heating or cooling was applied to the substrate holders, and the substrate temperature was determined by the sputtering conditions. Sputtering rates were typically about 200 A/hr.
X-ray examination of TiO2 films on metal substrates sputtered at 2.5 kV in 80% argon indicated that on titanium sub-strates, the film had the rutile structure with a crystallite size of 75 A and a lattice distortion (degree of displacement from normal lattice sites) of 3.5~; on zirconium substrates the film structure was also rutile with a crystallite size of 83 A. The films sputtered onto quartz substrates were amorphous.
Resistivity measurements of TiO2 films sputtered onto quartz substrates alongside the metallic substrates indicate that the conductivity was less than 10 6 ohm 1 cm 1. Hence, the Tio2 film was very lightly doped with donor defects. Capaci-tance measurements on DC sputtered films were found to be indepen-dent of bias.
The i-V characteristics of DC sputtered films in contact with electrolyte were qualitatively similar to those observed for TiO2 single crystals. However, one important difference is that these films were subject to a "forming"
process which consisted of applying a negative bias to the TiO2 electrode (e.g., -5 V for 10 sec); H2 gas was generally evolved during this period.
Immediately after forming, the photocurrent was increased about 10 fold. The forming process was repeatable in that a formed sample which was aged could be reformed to its maximum photo-response at any time.
The photoresponse generally followed the absorption edge;
~065Z75 it peaked at about 3300 to 3500 A and fell to zero at about 4000 A.
2. RF Sputtering RF sputtering was conducted in a vacuum system consisting of an 18 inch stainless steel belljar outfitted with a 2 kW RF
power supply and matching network.
Films of rutile (TiO2) were RF sputtered from a poly-crystalline rutile target onto substrates of titanium, zirconium, In2O3 on glass, and fused quartz. The target consisted of an 8 inch by 1/4 inch disc of hot pressured rutile powder which was specially bonded to a water-cooled target plate. The substrates were positioned on a substrate table located beneath the target.
The substrate table could be heated up to 650C with internal heaters, and the distance from the target varied between 1-1/2 to 3 inches.
The gas pressure and composition could be controlled over wide limits. Initial sputtering runs were made at 10 ~m of 10% 2 ~ 90% Ar.
Initial runs were made at 1000 watts of RF power, 10%
2 ~ 90% Ar, substrate-to-target distance of 2 inches and with the substrate platform heated to temperatures of about 300 to 500C. Under these conditlons, the deposition rate was about 0.35~ m/hr. This was about 10 times the deposition rate achieved with the DC sputtering unit.
The crystal structure was again pure rutile, with crystalline size and lattice distortion dependent upon substrate temperature. Higher temperatures (520C) yielded higher crystal-lite sizes (278 A) and lower lattice distortion (1.9%).
Measurements of the film conductivity (on quartz) and film capacitance (metal-TiO2-electrolyte) again indicated that the Tio2 films had very low conductivity and a large depletion layer width.
1065Z75 : -The i-V characteristies of the RF sputtered films in contact with electrolyte were in general similar to those of DC
sputtered films except that there were differenees with respeet to the forming effect. Some RF films underwent a forming process similar to that for DC films. However, other RF films showed i-V
characteristies which were not significantly improved after a forming operation. These i-V characteristics were stable with time, and gave conversion efficiencies which were about 1/3 those of single crystal TiO2.
3. Thin Films Thin film eleetrodes were studied in apparatus similar to that depieted in FIG. 2. The substrate was sealed from the elee-trolyte with O-rings, and illumination eould be made either through the eleetrolyte (for opaque substrates) or through the transparent eleetrieally eondueting substrates (e.g., Cd2SnO4, In2O3, SnO2). In order to evaluate photoeleetrolysis as a viable energy conversion scheme, it was neeessary to measure the effi-eiency of eonversion of optieal energy into chemical energy (i.e., H2). It was necessary to supply an anodic bias to the TiO2 eleetrode in order to produce H2 evolution. Thus, the balanee between the input eleetrieal bias, the input optical energy and the output ehemieal energy had to be determined. The optieal energy input was measured with a thermopile, the ehemieal energy output was determined by measuring the H2 evolution rate, and the eleetrieal bias power was calculated from the photocurrent and bias voltage.
For TiO2 films sputtered onto titanium, the following results were obtained showing the H2 evolution rate as a fune-tion of anodie bias:
- : . - - - ~ . . : . .
Input H2 . Film Optical Power, mw Bias,Evolution, (3200-4000 A) Volts cc/hr DC Sputtered, Formed 11.5 1.0 0.36 0.8 0.21 0.6 0-09 RF Sputtered, Unformed 18.1 1.0 0.17 0.8 0.12 0.6 0.05 The DC sputtered film was formed at -10 V for 10 seconds; the indicated H2 evolution rates decayed with time after forming.
Unformed DC sputtered films had optical conversion efficiencies of about 0.6% (at +1.0 V).
Unformed RF sputtered films had optical conversion efficiencies of about 1.1% (at +1.0 V), .
For sensitizing wide bandgap electrodes to visible light, photosensitive dyes such as rhodamine B, eosine, or crystal violet may be incorporated in the electrolyte to increase conversion efficiency.
The dependence of the conversion efEiciency on semi-conductor bandgap is shown in Table II.
Table II.
Semiconductor MaximumH2 2Evolution, Bandgap, eV Efficiency, %l/m /hr 1.0 45 200 2.0 25 42 3.0 8 17 As noted above, however, the minimum total bandgap required would " 1065Z75 ~
be 1.23 eV for aqueous systems. Lower bandgap materials may be used if another anodic reaction is substituted for 2 evolution - or if simultaneous illumination of n- and p-type semiconducting electrodes is employed.
The efficiencies listed in the Table above are very high compared with those possible by direct photolysis. This is because direct photolysis utilizes only a very small fraction of the available solar spectrum (less than 0.2 ~m). The maximum efficiency will, in practice, be decreased by electron-hole recom-bination, incomplete absorption and electrode polarization effects.Nevertheless, the use of semiconductor electrodes is the most attractive scheme for the photolytic decomposition of water by ~ solar radiation.
; d. Collection of Hydrogen The collection and storage of hydrogen gas produced by photoelectrolysis is easily accomplished by conventional techniques, such as pressurizable tanks, metal absorption of hydrogen to form reversibly decomposable metal hydrides and the like.
EXAMPLES
1. DC Sputterlng DC sputtering was carried out in a vacuum system consisting of an 18 inch glass belljar, controls for gas compo-sition and pressure regulation and a 4 kV source of DC power.
Thin films of rutile (Tio2) were DC sputtered from a polycrystalline rutile target onto substrates of tltanium, zirconium, SnO2 on glass, In203 on glass and fused quartz.
Film characterization was performed on Tio2 supported on fused quartz substrates, since no interference existed from the substrate with respect to optical transmittance and electrical conductivity.
The Tio2 sputtering target consisted of a commercially available 4-1/8 inch by 1/4 inch disc of hot pressed rutile powder.
The substrates were suspended above the target with a special 10652'75 copper platform, and the target-to-substrate distance was fixed at 1-1/4 inch for all experiments. The pressure in the chamber - was held at 30~m of 20~ O2-80% Ar. No external heating or cooling was applied to the substrate holders, and the substrate temperature was determined by the sputtering conditions. Sputtering rates were typically about 200 A/hr.
X-ray examination of TiO2 films on metal substrates sputtered at 2.5 kV in 80% argon indicated that on titanium sub-strates, the film had the rutile structure with a crystallite size of 75 A and a lattice distortion (degree of displacement from normal lattice sites) of 3.5~; on zirconium substrates the film structure was also rutile with a crystallite size of 83 A. The films sputtered onto quartz substrates were amorphous.
Resistivity measurements of TiO2 films sputtered onto quartz substrates alongside the metallic substrates indicate that the conductivity was less than 10 6 ohm 1 cm 1. Hence, the Tio2 film was very lightly doped with donor defects. Capaci-tance measurements on DC sputtered films were found to be indepen-dent of bias.
The i-V characteristics of DC sputtered films in contact with electrolyte were qualitatively similar to those observed for TiO2 single crystals. However, one important difference is that these films were subject to a "forming"
process which consisted of applying a negative bias to the TiO2 electrode (e.g., -5 V for 10 sec); H2 gas was generally evolved during this period.
Immediately after forming, the photocurrent was increased about 10 fold. The forming process was repeatable in that a formed sample which was aged could be reformed to its maximum photo-response at any time.
The photoresponse generally followed the absorption edge;
~065Z75 it peaked at about 3300 to 3500 A and fell to zero at about 4000 A.
2. RF Sputtering RF sputtering was conducted in a vacuum system consisting of an 18 inch stainless steel belljar outfitted with a 2 kW RF
power supply and matching network.
Films of rutile (TiO2) were RF sputtered from a poly-crystalline rutile target onto substrates of titanium, zirconium, In2O3 on glass, and fused quartz. The target consisted of an 8 inch by 1/4 inch disc of hot pressured rutile powder which was specially bonded to a water-cooled target plate. The substrates were positioned on a substrate table located beneath the target.
The substrate table could be heated up to 650C with internal heaters, and the distance from the target varied between 1-1/2 to 3 inches.
The gas pressure and composition could be controlled over wide limits. Initial sputtering runs were made at 10 ~m of 10% 2 ~ 90% Ar.
Initial runs were made at 1000 watts of RF power, 10%
2 ~ 90% Ar, substrate-to-target distance of 2 inches and with the substrate platform heated to temperatures of about 300 to 500C. Under these conditlons, the deposition rate was about 0.35~ m/hr. This was about 10 times the deposition rate achieved with the DC sputtering unit.
The crystal structure was again pure rutile, with crystalline size and lattice distortion dependent upon substrate temperature. Higher temperatures (520C) yielded higher crystal-lite sizes (278 A) and lower lattice distortion (1.9%).
Measurements of the film conductivity (on quartz) and film capacitance (metal-TiO2-electrolyte) again indicated that the Tio2 films had very low conductivity and a large depletion layer width.
1065Z75 : -The i-V characteristies of the RF sputtered films in contact with electrolyte were in general similar to those of DC
sputtered films except that there were differenees with respeet to the forming effect. Some RF films underwent a forming process similar to that for DC films. However, other RF films showed i-V
characteristies which were not significantly improved after a forming operation. These i-V characteristics were stable with time, and gave conversion efficiencies which were about 1/3 those of single crystal TiO2.
3. Thin Films Thin film eleetrodes were studied in apparatus similar to that depieted in FIG. 2. The substrate was sealed from the elee-trolyte with O-rings, and illumination eould be made either through the eleetrolyte (for opaque substrates) or through the transparent eleetrieally eondueting substrates (e.g., Cd2SnO4, In2O3, SnO2). In order to evaluate photoeleetrolysis as a viable energy conversion scheme, it was neeessary to measure the effi-eiency of eonversion of optieal energy into chemical energy (i.e., H2). It was necessary to supply an anodic bias to the TiO2 eleetrode in order to produce H2 evolution. Thus, the balanee between the input eleetrieal bias, the input optical energy and the output ehemieal energy had to be determined. The optieal energy input was measured with a thermopile, the ehemieal energy output was determined by measuring the H2 evolution rate, and the eleetrieal bias power was calculated from the photocurrent and bias voltage.
For TiO2 films sputtered onto titanium, the following results were obtained showing the H2 evolution rate as a fune-tion of anodie bias:
- : . - - - ~ . . : . .
Input H2 . Film Optical Power, mw Bias,Evolution, (3200-4000 A) Volts cc/hr DC Sputtered, Formed 11.5 1.0 0.36 0.8 0.21 0.6 0-09 RF Sputtered, Unformed 18.1 1.0 0.17 0.8 0.12 0.6 0.05 The DC sputtered film was formed at -10 V for 10 seconds; the indicated H2 evolution rates decayed with time after forming.
Unformed DC sputtered films had optical conversion efficiencies of about 0.6% (at +1.0 V).
Unformed RF sputtered films had optical conversion efficiencies of about 1.1% (at +1.0 V), .
Claims (15)
1. A photoelectrolysis cell for producing hydrogen from solar radiation comprising (a) an electrode comprising at least one thin film semi-conducting layer, which is disposed on a supporting sub-strate, each layer having a bandgap which ranges from about 1.3 to 4.0 eV;
(b) a counter-electrode;
(c) an electrolyte disposed between the electrode and the counter-electrode;
(d) external bias means between the electrode and the counter-electrode for biasing the electrode with from 0 to about 1 V; and (e) means for collecting hydrogen produced.
(b) a counter-electrode;
(c) an electrolyte disposed between the electrode and the counter-electrode;
(d) external bias means between the electrode and the counter-electrode for biasing the electrode with from 0 to about 1 V; and (e) means for collecting hydrogen produced.
2. The cell of claim 1 in which the electrode com-prises a suitably doped n-type composition selected from the group consisting of TiO2, In2O3, SnO2, GaAs, GaP, CdS, Si and MTiO3, where M is at least one element selected from the group consisting of La, Ba, Sr, the rare earth elements and the transition metal elements.
3. The cell of claim 2 in which the electrode com-prises a semiconducting layer of n-type TiO2 and the minimum bias applied ranges from about 0.3 to 0.5 V.
4. The cell of claim 2 in which the electrode comprises an outer, chemically inert, thin film semiconducting layer supported on at least one inner thin film semiconducting layer.
5. The cell of claim 4 in which the electrode com-prises an outer layer of TiO2 and an inner layer of at least one composition selected from the group consisting of CdS, GaP, GaAs, CdTe and Si, with the bandgap of each layer ranging from about 1.3 to 4.0 eV.
6. The cell of claim 1 in which the counter-electrode is metallic.
7. The cell of claim 6 in which the electrode com-prises a n-type semiconducting composition and the bias applied ranges from 0 to about +1 V.
8. The cell of claim 6 in which the electrode com-prises a p-type semiconducting composition and the bias applied ranges from 0 to about -1 V.
9. The cell of claim 8 in which the semiconducting layer comprises a suitably doped p-type composition selected from the group consisting of GaAs, GaP, CdTe, CuInS2, InP, ZnSe, Cu2S and Si.
10. The cell of claim 2 in which the counter-electrode comprises at least one thin film semiconducting layer having a conductivity type opposite to that of the film semiconducting electrode and in which the sum of the bandgap for all photo-active layers of both electrodes ranges from about 1.3 to 5.0 eV.
11. The cell of claim 10 in which the counter-electrode comprises a suitably doped p-type composition selected from the group consisting of GaAs, GaP, CdTe, CuInS2, InP, ZnSe, Cu2S and Si.
12. The cell of claim 1 in which the substrate com-prises a transparent electrically conducting material selected from the group consisting of Cd2SnO4 and suitably doped In2O3 and SnO2.
13. The cell of claim 1 in which the electrolyte com-prises an aqueous solution having a specific conductivity of at least about 10-3 ohm-1cm-1.
14. The cell of claim 1 in which the electrolyte com-prises a solid polymer electrolyte having a specific conductiv-ity of at least about 10-3 ohm-1cm-1.
15. The cell of claim 1 in which the electrolyte includes a photosensitive dye.